18Ni马氏体时效钢热处理工艺的研究

采用正交试验法探究了固溶温度、固溶时间、时效温度及时效时间对提高18Ni （2240 M Pa级）马氏体时效钢力学性能以及细化晶粒所发挥的作用,并研究了其最佳热处理工艺。研究表明,固溶时间的影响最为显著,时效时间的影响最不明显。将晶粒平均直径细化到Φ7μm时,抗拉强度可提高约100 M Pa。     

1 900 MPa级超高强度不锈钢的研制

研制出一种R≥1900 MPa的铬-镍-钴-钼系大规格棒材((φ)200 mm)超高强度马氏体时效不锈钢,通过研究热处理工艺对八种不同成分的铬-镍-钴-钼系马氏体时效不锈钢力学性能的影响,进一步优化了合金成分.结果表明:优化成分后得到一种高强(Rm=1940 MPa)、高韧(AKU2=55J,KIC=104 MPa·(√)m)的马氏体时效不锈钢.     

淬火态中碳钢温锻成形行为的研究

将相变与形变晶粒细化有效地结合，开发了中碳钢在马氏体状态下的温锻塑性成形工艺。研究表明，马氏体相变钢在500～600℃保温适当时间后快速形变，其塑性指标、成形性能比传统的退火态钢要好，变形抗力基本相同。形变时通过位错运动、孪晶及动态再结晶使铁素体组织得到细化，平均晶粒尺寸小于1μm，通过应变诱导使碳化物以颗粒状形态在晶界和晶内析出，并均匀弥散地分布在细小的铁素体基体中，使材料具有较高的强韧性和热稳定性。     

热循环对Cu-Zn-Al合金记忆效应的影响

利用相变参数测量、变温金相观察、Ｘ－射线衍射等方法研究了热循环对Ｃｕ－Ｚｎ－Ａｌ合金马氏体相变和双向记忆效应的影响。热循环使合金相变点升高，可逆马氏体量减少，记忆性能衰减，滞后环宽度变窄。在组织结构上，伴随着热循环，合金有序度降低，并出现高度稳定的残留马氏体。使晶粒粗化，提高合金Ａｌ质量分数，适当提高约束加热训练温度均可改善合金抗热循环性能。     

铅-钙-锡-铝合金固溶后时效过程中的不连续脱溶与再结晶行为

采用光学显微镜、场发射扫描电镜、EDS能谱仪和显微硬度计等研究了Pb-0.05%Ca-1.5%Sn-0.026%Al(质量分数)合金经不同工艺固溶后在100℃时效过程的不连续脱溶与再结晶行为。结果表明:该合金经不同工艺固溶后晶粒尺寸均约为1 000μm;经270℃保温30 min后空冷+310℃保温30 min水冷固溶(A工艺)再时效35 h后的晶粒细化至300～400μm,经270℃保温30 min水冷(B工艺)再时效12 h后的晶粒细化至60μm;由于不连续脱溶组织形核、生长使原有晶粒细化,实现了不借助塑性变形的再结晶;在不同固溶工艺下,合金时效时发生不连续脱溶所需保温时间及晶粒细化的程度也不同;随保温时间延长,A工艺处理合金的硬度曲线出现两处峰值,二次硬化相均为(PbSn)3Ca,B工艺处理合金的硬度曲线无规律可循,且细晶组织不稳定。     

等离子体源渗氮2Cr13马氏体不锈钢的耐磨与耐腐蚀性能

对2Cr13马氏体不锈钢进行450℃×6h的等离子体源渗氮处理,对比研究了渗氮前后该钢表层的显微组织、物相组成以及耐磨和耐腐蚀性能。结果表明:渗氮后不锈钢表层形成了厚约18μm,由αN、ε-Fe3N和γ′-Fe4N组成的化合物层,以及组织明显细化的氮扩散层,氮原子渗透深度达20μm;渗氮后不锈钢的表面硬度高达1 350HV,摩擦因数低于未渗氮处理的,磨损机制由未渗氮处理的黏着磨损转变为氧化磨损,耐磨性能明显高于未渗氮处理的;在质量分数3.5%NaCl溶液中,未渗氮不锈钢的阳极极化曲线仅呈现活化溶解特征,渗氮后则呈现活化溶解、自钝化和点蚀击穿特征,且自腐蚀电位提高至-104mV,耐腐蚀性能显著提高。     

晶粒尺寸对低层错能Fe-Mn-Si-Al奥氏体合金钢准静态力学性能的影响

在不同温度(700,730,800,900,1 000,1 100,1 200℃)下对低层错能Fe-29.8Mn-5.0Si-1.7Al合金钢冷轧板进行退火处理,研究了原始奥氏体晶粒尺寸对其准静态力学性能和变形过程中相变行为的影响规律。结果表明:随退火温度(高于730℃)升高,合金钢发生明显静态再结晶,晶粒尺寸增加,组织均为单一奥氏体;再结晶退火合金钢在拉伸变形过程中均发生ε马氏体相变,细晶(奥氏体晶粒尺寸小于21μm)有助于合金钢获得高屈服强度和高抗拉强度,粗晶(奥氏体晶粒尺寸大于90μm)内部形成了均匀分布且相互交截的多变体ε马氏体,有利于提高其塑性。     

奥氏体晶粒细化的研究

在Gleeble1500热模拟机上以SS400钢为研究对象，用冷加工 回火再结晶和冷加工 a→γ逆相变等工艺，研究了冷变形对马氏体(铁素体)再结晶行为的影响以及奥氏体晶粒细化的方法。结果表明：低温变形对板条马氏体的再结晶行为有一定影响，并且由于低温变形后快速升温的铁素体回复、再结晶与奥氏体(铁素体)相变等相继发生，从而得到比较细小的奥氏体晶粒。     

DP800冷轧双相钢组织性能的研究

通过研究临界区加热温度、过时效温度对超高强低碳冷轧双相钢力学性能和组织的影响,结果发现,马氏体和新生铁素体晶粒在1 μm左右时,含有50%左右马氏体的双相钢同样能够保证良好的塑性;在缓冷速度5℃/s和急冷温度700℃不变的情况下,随着加热温度的升高,马氏体的体积分数变化不明显;马氏体分解是300℃过时效比250℃过时效抗拉强度下降40 MPa左右的主要原因;过时效时铁素体中部分位错发生回复、松弛、形成亚结构,使屈服强度降低.     

00Cr12Ni10MoTi马氏体时效不锈钢的晶粒长大

对00Cr12Ni10MoTi马氏体时效不锈钢材料的晶粒长大规律进行研究,发现奥氏体化温度对00Cr12Ni10MoTi马氏体时效不锈钢的晶粒影响较大,温度低于900℃时,晶粒遗传原始锻态的晶粒形貌;900℃时,奥氏体重新形核、长大,奥氏体晶粒明显细化;温度高于1 050℃时发生明显粗化。工程化热处理时的低加热速率和低冷却速率对00Cr12Ni10MoTi马氏体时效不锈钢的性能几乎没有影响,而模拟工程化热处理得到综合性能良好的00Cr12Ni10MoTi马氏体时效不锈钢。     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

盘丝极心偏对三爪自定心卡盘找标精度影响的分析

三爪自定心卡盘作为机床的主要附件,已有一百多年的发展历史,尽管目前随着数控技术的不断发展,越来越多地需求高速动力卡盘,但三爪自定心卡盘目前仍有一定的市场。 要保证卡盘可靠地夹紧工件,必须使其有可靠的夹持精度;要保持卡盘的精度,必须要严格控制各零部件公差及误差,如盘丝的极心偏。 　　极心偏是形成圆的渐开线的基圆圆心 (极心 )与盘丝内孔中心不同心所造成的偏差值。它对卡盘精度的影响分两种情况,一是卡爪夹持弧采用配磨,二是卡爪夹持弧采用单磨。本文主要探讨配磨时的影响。 　　卡爪夹持弧采用配磨,即每台卡盘整体…     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

圆柱面素线的直线度公差带解析

详细分析了圆柱面素线的直线度公差带在新旧标准中定义和解释的区别，并从对圆柱面素线实际要素检测的角度，提出了推行新标准的实际意义。     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。     

广州地铁APM列车制动机理分析

根据广州市珠江新城旅客自动运输系统(APM)列车的运行特点,介绍APM列车制动系统的制动方式及其特点,分析APM列车动态制动和摩擦制动的工作机理及其区别和联系,阐明APM列车制动系统的电控制过程和气控制过程,从而为APM列车制动系统的维护和管理提供一定的依据.     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

活塞销孔加工工艺的改进

我公司于８０年代末引进Aspera公司年产８０万台冰箱（冷柜）压缩机生产线及软件技术，在压缩机加工中，活塞销孔（如图１所示）的加工是难点之一。用镗床加工，质量一直难以达到要求，废品率很高。后来我们将Aspera公司的加工工艺即精镗后滚光改为精镗后用金刚石铰刀粗、精铰孔，由此解决了这个技术难题。（１）原意大利Aspera公司工艺简述其工艺流程为：钻６．５通孔→扩孔至７＋０．１→粗镗７．４７３＋０．０３６、圆柱度０．０１→精镗至７．９３５＋０．００６、圆柱度０．００２→滚光７．９３８＋０．００６、圆柱度０…     

我校工业设计教育改革初探

针对目前市场对工业设计人才的需求,本文论述了我校在工业设计教育方面的改革措施,着重介绍了我校工业设计教育在软件和硬件方面所进行的一系列的改革。