硅烷改性氟代聚丙烯酸酯乳液的合成及其应用

在阳/非离子表面活性剂及引发剂作用下,将甲基丙烯酸十二氟庚酯、甲基丙烯酸十二醇酯、丙烯酸羟丙酯、甲基丙烯酸二甲氨乙酯、乙烯基三乙氧基硅烷进行乳液共聚,制得了硅烷改性的阳离子氟代聚丙烯酸酯乳液(FL-HDV)。用红外光谱(FT-IR)和核磁共振氢谱(1H NMR)对FLHDV主组分的结构进行了表征,用X射线光电子能谱仪(XPS)对乳液的成膜表面成分进行分析和表征,并讨论了硅烷改性前后及不同的整理工艺对其在涤纶织物上应用性能的影响。结果表明,与未用硅烷改性的氟代聚丙烯酸酯乳液(FLDH)对比,硅烷改性可以提高含氟聚合物的交联度,进而增加织物的拒水拒油性。XPS分析和接触角测定结果表明,在涤纶纤维表面明显存在有FLHDV膜,使得纤维与空气的界面上富集着疏水的含氟链段,而硅氧基团与纤维表面结合,从而赋予涤纶良好的拒水拒油性。在不同的工艺条件下,一浸一轧工艺处理的织物具有更高的拒水拒油等级,且弯曲刚度略低,柔软度较好。     

阳离子氟代聚丙烯酸酯乳液的制备及应用

以(NH4)2S2O8作引发剂,阳、非离子表面活性剂作乳化剂,将甲基丙烯酸十二氟庚酯(RfAA)、丙烯酸丁酯(BA)、甲基丙烯酸二甲氨乙酯(DM)以及丙烯酸羟丙酯(HPAA)进行乳液聚合,制得了一种稳定的阳离子氟代聚丙烯酸酯乳液(PCFBA)。用红外光谱(IR)、核磁共振氢谱(1HNMR)对PCFBA主组分的结构进行了表征。用扫描电镜SEM、接触角测量仪、电脑测控柔软度仪等研究了PCFBA在棉纤维织物表面的成膜性及应用性能。结果表明,PCFBA可在纤维表面形成相对均匀的疏水膜,该膜附着在纤维表面,能使整理后棉织物与水的接触角达到134.5°、静态吸水时间超过6 h;当PCFBA用量从0.3 g/100 mL H2O增大到1 g/100 mL H2O时,水在其整理的棉纤维织物表面的接触角从128.2°增大到134.5°,而棉织物的白度则由85.44°略降至84.40°。     

氟代聚丙烯酸酯改性聚氨酯复合乳液的制备及其疏水性

为了提高聚氨酯-丙烯酸酯复合乳液的耐水性和耐溶剂性,将聚氨酯溶液作为反应介质,以丙烯酸十二氟庚酯(FA)和丙烯酸羟丙酯为单体,偶氮二异丁腈为引发剂,在溶液中进行聚丙烯酸酯自由基聚合,然后用N-甲基二乙醇胺进行亲水基扩链,通过溶液聚合相转化法制得新型阳离子氟代聚丙烯酸酯改性聚氨酯复合乳液。通过红外光谱、透射电镜、光电子能谱仪和接触角测定仪分别对复合乳液的结构、乳胶粒形态、膜表面的化学元素组成及疏水性进行了研究。结果表明,含氟链段成功接入了大分子链中,乳液形成稳定的核-壳结构,在膜材料表面形成了主要由含氟丙烯酸酯链段组成的界面,FA的引入可使复合乳液胶膜与水的接触角(PUA膜与水的接触角)由65°提高至98°。     

环氧树脂/聚丙烯酸酯乳液的制备及其应用

以环氧树脂改性聚丙烯酸酯乳液制备了水性超薄膨胀型防火涂料专用乳液,其可作为涂层的成膜物质。采用FTIR、DSC、TGA、SEM等对乳液性能,及乳液对防火涂料性能的影响进行了考察。结果表明:与聚丙烯酸酯乳胶膜相比,环氧树脂改性的聚丙烯酸酯乳胶膜的吸水率更低,为7.3%,交联度更高,达84.6%,耐水性更好;玻璃化转变温度(Tg)从8.8℃提高到24.4℃,乳胶膜最大热失重速率所对应温度从361.2℃提高到390.3℃。与使用聚丙烯酸酯乳液相比,使用环氧树脂改性过的聚丙烯酸酯乳液作为成膜物质的防火涂层质量损失率从27.6%减小到25.2%,膨胀倍率从9.5增加到20.4,钢板背面温度从328℃降低到221℃。以环氧树脂改性过的聚丙烯酸酯乳液作为防火涂料的成膜物质,使涂层在受热膨胀后能形成致密的、均匀的蜂窝状泡孔,可获得较好的耐火性能。     

有机氟、硅改性聚丙烯酸酯无皂乳液的制备

采用核壳乳液聚合方法,以反应型乳化剂壬基酚聚氧乙烯醚硫酸铵DNS-458、甲基丙烯酸甲酯和丙烯酸丁酯为聚合单体,甲基丙烯酸十二氟庚酯和乙烯基三甲氧基硅烷为功能单体,制备了有机氟、硅改性聚丙烯酸酯无皂乳液织物整理剂,并研究了乳化剂用量、功能单体用量对合成反应的影响.结果表明:有机氟、硅聚丙烯酸酯乳液最佳制备条件为DNS-...     

聚氨酯改性氟代聚丙烯酸酯的合成及应用

在聚氨酯预聚体中,以全氟己基乙基丙烯酸酯（C6F）、丙烯酸羟丙酯（HPAA）为聚合单体,偶氮二异丁腈(AIBN)为引发剂进行自由基聚合,制得聚氨酯改性的氟代聚丙烯酸酯（PUAF）。通过红外光谱、场发射扫描电镜（FE-SEM）等对PUAF的结构、成膜形貌以及应用性能进行研究。PUAF能在纤维表面形成一层致密的疏水膜。在PUAF的用量为1g/100g乙酸乙酯,并在180℃高温烘焙定型1.5min的工艺条件下,织物与水的接触角达到133.5?。     

纳米SiO2／氟改性聚丙烯酸酯复合乳液的制备

以正硅酸乙酯为前驱物,采用溶胶一凝胶法原位制备纳米Si02粒子,然后通过细乳液聚合制得纳米Si02／氟改性聚丙烯酸酯复合乳液。采用傅里叶变换红外光谱（FTIR）和动态光散射（DLS）对产物进行了表征。研究了含氟单体和纳米Si02用量对复合乳胶膜性能的影响。结果表明：随着氟含量的增加,乳胶膜的水接触角增加,吸水性降低;体系中加入纳米Si029可以降低聚合物乳胶膜的吸水率。     

聚四氟乙烯改性聚丙烯酸酯乳液的制备与表征

采用外来种子乳液聚合方法,用反应单体对外来种子聚四氟乙烯乳液进行浸泡、溶胀,然后引发聚合反应制得聚四氟乙烯改性的聚丙烯酸酯乳液。傅立叶变换红外光谱、透射电镜等对改性乳液的表征显示聚四氟乙烯和聚丙烯酸酯间存在作用,研究了乳胶粒的微观结构,推测出乳胶粒核壳部分的组成成分,分析了改性复合粒子的形成机理,指出进一步控制乳胶粒生成种类的单一性或者将微米级颗粒(改性聚四氟乙烯乳胶粒)与纳米级颗粒(纯丙乳胶粒)优化共存于同一体系可作为下一步研究的方向。该研究为化学惰性物质用于改性研究提供了一条新思路。     

聚丙烯酸酯乳液在织物涂层上的应用

一、概述目前,世界上可作为涂布的合成聚合物有聚氨酯、丙烯酸酯、硅酮弹性体、聚氯乙烯以及橡胶类等。聚氨酯与硅酮弹性体所制成的涂布性能优良,但成本较高;聚氯乙烯耐侯性较差;而聚丙烯酸酯乳液具有成本低,耐侯性好,色泽浅,透明度高,耐热,耐磨,且成膜性好,同织物结合力强等优点。同时聚丙烯酸酯乳液是以水为介质,在生产过程中不需要回收装置,不存在污染源,是目前值得推广应用的一种涂布方法。用聚丙烯酸酯乳液在织物上进行涂布     

氟代聚丙烯酸酯无皂乳液整理剂的防水防油性能研究

本文采用无皂乳液聚合法,以全氟烷基酯（FEA）为功能单体,制备了一种氟代聚丙烯酸酯无皂乳液整理剂,并对其乳液颗粒粒径大小及分布和高分子溶液表面活性进行了研究。通过对棉织物进行防水防油整理应用实验,详细考察了该织物整理剂的使用质量百分数和烘焙温度对防水防油性能的影响,并测试了其他应用性能。结果表明,通过该防水防油剂处理的织物有优异的防水防油性能,处理后的织物表面动态防水性可达90分,防油性可达5级,对水的接触角可达142.5°,对石蜡油的接触角可达126?,并且有良好的耐水洗性和常规应用性能。     

Preparation of light-responsive block copolymer modified cellulose nanocrystal@polydopamine particle and its application in fluorinated polyacrylate film

Light-responsive cellulose nanocrystal@polydopamine (CNC@PDA) modified fluorinated polyacrylate was synthesized by Pickering emulsion polymerization with light-responsive block copolymer modified CNC@PDA as stabilizer. The epoxy groups in poly(acrylic acid-co-acrylamide)-b-poly(glycidyl methacrylate)-b-poly(hexafluorobutyl acrylate-co-coumarin) amphiphilic triblock copolymer reacted with the hydroxyl and amino groups on the surface of CNC@PDA to form the modified CNC@PDA. The successful preparation of modified CNC@PDA was confirmed by means of FT-IR, XRD, TG, UV–Vis, surface tension measurement, and X-ray photoelectron spectroscopy (XPS) techniques. The results showed that the modified CNC@PDA had light-responsive and amphiphilic properties, and could be used as stabilizer to form stable Pickering emulsion. And the influence of modified CNC@PDA dosage on emulsion polymerization and film performance was systematically studied. The latex particle size decreased initially with increasing modified CNC@PDA dosage, from 0.6 to 1.0 wt%, and then increased. The mechanical, self-healing, and water–oil repellent properties of film were enhanced initially with increasing modified CNC@PDA dosage, from 0.6 to 1.0 wt%, and then declined. Atomic force microscope confirmed that the latex film had a rough surface. Moreover, the latex film comprising 1.0 wt% modified CNC@PDA presented not only high tensile strength (4.92 MPa), large elongation at break (657.70%), and superior oil/water repellency but also excellent self-healing property.     

聚丙烯酸酯的乳液聚合及其吸油性能研究

以丙烯酸十二酯、丙烯酸丁酯等为原料,采用乳液聚合法合成了聚丙烯酸酯树脂。讨论了乳化剂、搅拌速度、反应温度对聚丙烯酸酯乳液性能的影响,考察了单体配比、引发剂用量、交联剂种类及用量、致孔剂用量等对聚丙烯酸酯树脂吸油性能的影响。发现当反应单体丙烯酸丁酯与丙烯酸十二酯的摩尔比为3∶1,交联剂二乙烯基苯用量为单体质量的2%,引发剂过硫酸铵用量为单体质量的2%,致孔剂乙酸乙酯用量为单体质量的50%时,合成的聚丙烯酸酯树脂对煤油、甲苯和CCl4的吸收率分别为7.12、18.10和33.39g·g-1,表现出良好的吸油性能。     

含氟苯丙无皂乳液的合成及其在涂料中的应用

以过硫酸铵(APS)为引发剂,将丙烯酸丁酯(BA)、苯乙烯(ST)、丙烯酸(AA)与甲基丙烯酸十二氟庚酯(DFMA)通过无皂乳液聚合法制备了含氟苯丙无皂乳液(BSAD)。通过IR、TEM、粒度仪及Zeta电位分析仪表征了乳液主组分结构、乳胶粒形貌、粒径分布及Zeta电位,并考察了丙烯酸钠、引发剂APS、DFMA的用量及反应温度对乳液性能的影响。并将该乳液与纳米TiO2等复配制备了氟碳涂料。结果表明,当丙烯酸钠质量分数为12%,APS质量分数为1%,反应温度为78℃时,乳液性能最佳,此时凝胶率为0.8%,耐水性大于168 h,单体转化率为97.1%;当DFMA质量分数为25%时,涂膜疏水性最佳,水接触角达到113°,吸水率为6.4%;制得的氟碳涂料的附着力、硬度、耐水性等都获得了令人满意的效果。     

Synthesis and characterization of fluoropolymer modified polyacrylate in emulsion polymerization

A novel method to produce fluorine‐containing polyacrylate emulsion is presented. It is prepared by the copolymerization of n‐methyl methacrylate, n‐styrene, n‐butyl acrylate, and α‐methacrylic acid in the presence of swollen particles of PTFE. The structure and properties of the polymers are characterized by GPC, PSD, SEM, and XPS. The number‐average molar mass (Mn) 51,332, and the polydispersity 5.8688 are obtained. The mean diameter of latex particles is 300nm. Scanning electron microscopy reveals that particles of the emulsion are well dispersed. Meanwhile, the F_1S content of the surface on the latex membrane is 8.99%. It is shown that the method of mixing micron and nanometer‐sized particles should be made the next step of research. It is also proved that inertia polymers can be used in emulsion property modification. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 99: 558–562, 2006     

聚丙烯酸酯涂料的制备

以甲基丙烯酸甲酯(MMA)、丙烯酸丁酯(BA)、丙烯酸(AA)为单体,以十二烷基苯磺酸钠为乳化剂,当m(BA)∶m(MMA)∶m(AA)=33∶17∶1,通过乳液聚合制得丙烯酸酯类乳液,再加入填料及各种助剂,经过高速搅拌、均质而出料。并且讨论了乳化剂及引发剂用量对乳液聚合、乳液及涂料性能的影响。     

含氟聚（甲基）丙烯酸酯乳液的研究进展

含氟聚(甲基)丙烯酸酯乳液具有合成简便和性能易调等优点,所得涂膜表面能低、耐污性能好、化学稳定性优异,因而在水性氟碳涂料领域受到广泛关注。含氟聚(甲基)丙烯酸酯单体的化学组成对乳液和涂膜性能影响很大。该文分类总结了含氟核心单体包括含氟烷基(甲基)丙烯酸酯、含氟杂原子(甲基)丙烯酸酯、含氟芳香(甲基)丙烯酸酯、含氟(甲基)丙烯酰胺和含氟磺酰胺(甲基)丙烯酸酯等的结构与乳液和涂膜性能的关系,然后对含氟聚(甲基)丙烯酸酯单体和乳液的合成方法进行归纳,最后简要介绍含氟聚(甲基)丙烯酸酯乳液的应用,并对乳液研究存在的问题和未来的发展方向进行展望。     

细乳液聚合制备改性硅溶胶／聚丙烯酸酯复合乳液

常温下一步法制备改性硅溶胶,并通过细乳液聚合制备改性硅溶胶／聚丙烯酸酯复合乳液。考查了温度对聚合速率和单体转化率的影响以及不同乳化剂含量下聚合过程中乳胶粒粒径的变化情况;测试了乳胶膜的吸水率,并用接触角法表征了乳胶膜的表面自由能。     

丙烯酸酯无皂乳液聚合反应机理及应用进展

丙烯酸酯无皂聚合乳液在涂料印花粘合剂中占有重要地位,在功能性微球及无机复合材料制备方面的应用也日益广泛。本文阐述了丙烯酸酯无皂乳液聚合的机理及应用进展。     

聚丙烯酸酯反相破乳剂的制备及其现场应用研究