掺玻璃粉水泥净浆水化性能

以废弃啤酒瓶制成玻璃粉,配制掺玻璃粉水泥净浆.测试掺玻璃粉水泥净浆抗压强度;采用X射线衍射分析、热重-差热分析、扫描电子显微镜分析及能谱分析技术研究掺玻璃粉水泥净浆水化产物的种类、含量、微观形貌及元素组成.结果表明:随着玻璃粉掺量(质量分数)的增加,水泥净浆抗压强度减小.掺玻璃粉水泥净浆水化产物主要有C-S-H凝胶、Ca(OH)2及少量钙矾石、水化铝酸钙等.由于玻璃粉的火山灰反应消耗Ca(OH)2,随着玻璃粉掺量的增加和龄期的延长,水泥净浆水化产物中Ca(OH)2含量(质量分数)逐渐减少.掺玻璃粉水泥净浆微观结构较为致密,其水化产物C-S-H凝胶形态与纯水泥净浆有所不同,多由不规则的短柱状及薄片状凝胶粒子交叉结合在一起形成网络结构,为低钙硅比(质量比)C-S-H凝胶.玻璃粉具有火山灰活性.     

外加剂对粉煤灰、矿渣双掺水泥净浆水化影响

通过水泥净浆试验,确定了掺加聚羧酸、萘系、氨基磺酸盐类减水剂对掺粉煤灰、矿粉及粉煤灰、矿粉双掺水泥水化过程的影响。本文通过强度及X衍射、扫描电镜等测试手段,从微观及宏观对三种外加剂对多组分水泥水化过程的影响作了介绍。     

沸石细度及掺量对水泥性能影响研究

研究了混合材掺量40%下明矾石（石膏）-沸石不同比例对抗折强度、抗压强度及流动性的影响,阐明了明矾石（石膏）-沸石体系作为混合材对水泥水化的影响机制。研究表明,明矾石与石膏的最佳比例为2:1,在此比例下明矾石作为混合材的力学性能最优。沸石比例越小,相同龄期下硬化体强度越低。28d龄期,沸石掺量25%时抗压强度为47.03MPa,相对于空白样降低12.97%;沸石掺量35%时仍然能达到46.61MPa,与空白样相比下降了11.90%。流动性与沸石掺量呈线性关系,沸石掺量越高,流动性越差。综合力学性能及流动性,确定混合材掺量40%下明矾石（石膏）：沸石最佳配比为10(5):25。沸石越多,体系反应活性越高,相同龄期下水化产物越多,反应越快,强度越高。     

蒸养参数对水泥净浆水化性能的影响

研究了在蒸汽养护条件下蒸养参数(静养时间、恒温时间及恒温温度)对水泥净浆水化性能的影响,揭示上述各因素与水泥净浆化学结合水量之间的关系,并且提出各蒸养参数的参考指标值;试验结果表明,在其他条件相同的情况下,预养阶段是蒸养过程必不可少的环节,且预养时间不宜低于2h;为避免胶凝材料的后期水化性能遭到破坏,恒温阶段的恒温时间不宜超过8h,恒温温度不宜超过60℃。     

煤矸石细度和掺量对水泥性能的影响

研究了热活化煤矸石的细度和掺量对水泥浆体流动度、凝结时问,水泥硬化浆体抗压强度、化学结合水量和微观结构的影响．结果表明：提高热活化煤矸石的细度和掺量,水泥浆体的流动度降低,凝结时间延长;水泥浆体的抗压强度和化学结合水量随热活化煤矸石细度的提高而增大,随掺量的增加而减少．热活化煤矸石的细度和掺量对水泥硬化浆体的孔结构分布和形貌也有较明显的影响．     

不同钢渣掺量对UHPC性能的影响研究

钢渣作为大宗固体废弃物在建筑材料领域的应用是节能减排的重要途经之一。本文研究了不同钢渣掺量对UHPC工作性、力学性能及收缩性能的影响规律,并通过TG/DTG及SEM分析其水化机理。结果表明,随着钢渣掺量的增加,UHPC的流动度呈不同程度增加,早期抗压强度和抗折强度降低幅度较大,但后期力学性能差距逐渐减小。UHPC的自收缩性能随着钢渣掺量的增加呈降低趋势。钢渣粉掺量占总胶凝材料的18%时,制备的UHPC的工作性能和自收缩性能仍较为优异,水化28d后力学性能增长较快。     

大掺量磨细矿渣对水泥基无收缩灌浆料的性能影响研究

实验以普通硅酸盐水泥和硫铝酸盐水泥复合胶凝体系为基体材料,以高炉粒化矿渣作为掺合料,掺加早强剂、消泡剂、减水剂等外加剂制备无收缩水泥基灌浆材料。试验采用单一变量法,分析各组分的掺量对水泥基无收缩灌浆砂浆体系流动度、凝结时间等新拌性能以及力学性能、膨胀性能等硬化性能的影响,确定各组分的最佳掺量,并利用X射线衍射分析、扫描电镜等现代材料测试方法对砂浆的微观结构和水化产物进行研究。     

石膏掺加量对粉煤灰水泥性能的影响

石膏掺加量对粉煤灰水泥的凝结时间、安定性、强度等性能均有影响。实验表明：这种影响与石膏掺量对粉煤灰水泥中粉煤灰水化度的影响是密切相关的。     

高掺量矿渣水泥的水化物相分析

采用粒化高炉矿渣为主要原料,掺加一定比例的自制复合激发剂M,配制出高掺量矿渣水泥利料,采用X射线衍射仪(XRD)、差热分析(DTA)和扫描电子显微镜(SEM),对其水化物相进行研究,实验结果表明:自制复合激发剂对高掺量矿渣水泥材料具有良好的激发作用.     

粉煤灰细度和掺量对水泥基材料性能的影响

比较了不同细度和掺量的粉煤灰对水泥基材料工作性能、水化性能以及胶砂流动性、强度的影响。结果表明：粉煤灰的掺入对提高浆体的流动性有明显改善作用，不同细度的粉煤灰对浆体流动性的改善程度不同；粉煤灰掺入使浆体的凝结时间明显延长，并使早期化学结合水量和早期强度降低。粉煤灰的掺入提高了砂浆流动性，降低了早期强度，但后期强度可赶上甚至超过不掺粉煤灰的砂浆强度。     

如何提高水泥石的弹性模量

通过正交试验设计探讨了水泥石弹性模量与石英粉、石英砂掺量以及水灰比之间的关系.试验结果表明:随着石英砂掺量的增加,水泥石的弹性模量有了很大的提高,最高达到了56 GPa;同时,石英粉的掺量变化与水灰比的不同也会对试验结果产生一定的影响.这是由于石英砂的增加,促进了水泥的水化,形成了结晶核心,同时起到密实填充作用.此次试验对于提高陶粒混凝土弹性模量具有参考价值.     

降低含胶粉水泥石干燥收缩的研究

对含胶粉水泥石的干燥收缩变化规律进行了研究。测试结果表明,在为期1年的测试龄期内,水泥石的干燥收缩率逐渐增加,同时随着胶粉掺量的增加而增大。抑制含胶粉水泥石干缩的研究结果表明,在前期缺乏水养护的条件下,膨胀剂对干燥收缩变形有一定效果,但是不明显;采用促强减缩剂能够有效降低含胶粉水泥石的干燥收缩变形,并且大幅度延缓干缩变形的速率。     

纳米硅粉对水泥硬化浆体的改性研究

与普通硅粉相比,纳米硅粉具有更加优异的火山灰活性,在水泥基材料改性研究中,掺加性能优异的纳米硅粉成为一种新的探索.分析了普通硅粉和纳米硅粉的颗粒细度、晶体结构及火山灰活性,通过掺加纳米硅粉的水泥硬化浆体强度性能试验研究,结合试验测试和理论分析,探讨了纳米硅粉在水泥硬化浆体中的作用机理,为纳米硅粉应用于高性能水泥基材料的研究奠定理论和试验基础.     

电极对加速氯离子透过水泥石性能的影响

本文研究了加速氯离子渗透过水泥石试验中铜电极和不锈钢对试验结果的影响;研究表明：铜电极在试验过程中腐蚀严重,产生大量沉淀物,导致阳极溶液中氯离子浓度和通过试件电流值的测量结果偏小;不锈钢电极在试验过程中表面有轻微点蚀,底部腐蚀较严重,同时也产生沉淀物,致使测量结果偏小,但效果好于铜电极.     

Effects of mineral admixtures on the thermal expansion properties of hardened cement paste

Concrete is a heterogeneous composite material with multiple components that have different thermal expansion properties. Internal stresses are generated if the concrete is rapidly heated or cooled, causing cracking in the micro- or macro-scale. If the coefficient of thermal expansion (CTE) of hardened cement pastes (HCP) is adapted, the thermal stress caused by the mismatch of thermal expansion properties of the components can be mitigated. The effects of the commonly used mineral admixtures (fly ash, ground granulated blast furnace slag and silica fume) on the thermal expansion properties of HCP are investigated. The thermal dilation rates (TDR) of HCP in which Portland cement is partially replaced with mineral admixtures are tested with a dilatometer and the CTE are derived. Replacing Portland cement with mineral admixtures is found to lower the CTE of HCP, which is beneficial for mitigating the thermal mismatch between the HCP and the aggregates. The extent of this lowering effect increases with the increasing replacement proportions of mineral admixtures in the pastes. Through quantitative determination of the porosity and the amount of portlandite in the paste and microscopic observations, it is revealed that the effects of the mineral admixtures are mainly due to the change of the porosity and the amounts of hydration products in the pastes.     

Effects of water–cement ratio and curing time on the critical pore width of hardened cement paste

Mercury intrusion porosimetry (MIP) test is one of the techniques that have been widely used for analyzing the pore size distribution of hardened cement paste (hcp) and also for the determination of the critical pore width. This study presents the test results of the MIP experiments obtained for three different hcp specimens with the water–cement ratios of 0.26, 0.34, and 0.42 which had been cured for 7, 28, and 365 days under water. Thus, the effects of water–cement ratio and curing time on the critical pore width of hcp were investigated. Test results have shown that, within the limits of the work, and in case of complete hydration, the critical pore width of the hcp seems to be independent of water–cement ratio and is of the order of 25 nm. This value can be considered as the critical pore width of the portland cement gel.     

硬化混凝土中水泥用量的测定方法概述

水泥用量是混凝土配合比的重要参数,测定混凝土中的水泥用量对耐久性判断及配合比检查具有重要意义。硬化混凝土中的水泥用量可用化学分析方法及光学显微镜法测得。化学分析法又分为水泥溶解法与可溶性SiO2和CaO分析法,光学显微镜法包括荧光显微镜和扫描电镜。重点对化学分析方法的测定原理、试验方法及结果计算做了介绍,评价了各种方法的精密度与准确性,并总结了可能对测定造成影响的因素。     

高掺量煅烧煤矸石粉胶结料的力学和水化特性研究

研究了煅烧煤矸石-水泥熟料-石膏胶材体系的力学和水化特性。结果表明,煅烧煤矸石适当取代部分熟料制备的胶凝材料具有较好的力学性能,最佳取代量为35%,7d和28d强度可达23.8MPa和29MPa。无水硫酸钠的掺入可明显提升胶材体系的早期和后期强度,最佳掺量为5%,3d、7d和28d强度分别提升100%、32.4%和40%。利用XRD和SEM对胶凝材料改性前后的物相组成分析发现,无水硫酸钠的掺入使体系早期生成了大量的Ca(OH)2贯穿于C-S-H凝胶中,且Ca(OH)2的存在加速石膏溶解,加快AFt生成,填充孔隙,使体系结构致密,提高了早期强度。     

超细粉煤灰及其在水泥净浆中的水化特征研究