钇掺杂TiO2/膨润土复合光催化剂降解染料X-3B的研究

以膨润土为载体,钛酸四丁酯和氯化钇为原料,采用溶胶-凝胶法制备钇掺杂TiO2/膨润土纳米复合光催化剂,在太阳光照射下,通过染料活性艳红X-3B的降解反应,考察其光催化活性.实验结果表明：随着光照时间的延长,染料活性艳红X-3B的特征峰540 nm强度逐渐减弱,2 h后可彻底消失,脱色率达96.86%;染料活性艳红X-3B的降解速率随着外加氧化剂H2O2的增多而增大,但过量的H2O2也会抑制复合光催化剂的活性;在强酸和强碱条件下,染料活性艳红X-3B的降解率较高.     

TiO_2薄膜制备条件对甲醛光催化降解性能的影响

以钛酸丁酯为前驱体,用溶胶-凝胶法制备了TiO2薄膜,并进行了甲醛的光催化降解实验,考察了制备条件对光催化降解性能的影响。结果表明,适宜的制备工艺条件为:溶胶体系pH=3,溶胶配方中V(钛酸丁酯)∶V(无水乙醇)∶V(水)∶V(冰醋酸)=5∶34∶2∶2,干溶胶在600℃下活化5h,制成的薄膜光催化降解甲醛降解率大于50%。     

铝合金表面制备TiO_2薄膜及其性能

采用溶胶凝胶法,以钛酸丁酯、聚乙二醇、乙酰丙酮、三乙醇胺等为实验原料,利用自制的浸渍提拉装置在铝合金基底上制备TiO2薄膜。使用X射线衍射仪(XRD)、扫描电子显微镜(SEM)表征TiO2薄膜的结构和形貌,以甲基橙溶液的光催化降解为反应模型,评价了TiO2薄膜的光催化活性。结果表明,采用三乙醇胺和乙酰丙酮制备的TiO2薄膜均为锐钛矿相;较三乙醇胺相比,乙酰丙酮做水解抑制剂制备的TiO2薄膜形貌平整,表面龟裂少,结构致密,样品的光催化效果好。     

不同离子掺杂TiO2薄膜及光催化活性研究

采用溶胶-凝胶法分别制备了掺杂Fe^3＋、Cu^2＋、Zn^2＋、Ce^3＋和La^3＋5种不同离子的纳米级TiO2薄膜,使用TiO2薄膜对亚甲基蓝溶液进行光催化试验。研究表明,在5种掺杂离子中,其La^3＋的掺杂效果最好,当La^3＋的适宜含量为1.8%（质量分数）时,掺杂与未掺杂的XRD图谱基本一致;掺入La^3＋离子使得TiO2的晶粒变小,可抑制晶相向金红石相转变;随着焙烧温度的升高TiO2晶粒逐渐变大,温度为700℃时,其粒径为27.6nm,TiO2为混合晶型（锐钛矿型和金红石型）,其活性最高。     

掺杂Cu的TiO_2纳米管的制备及光催化性能研究

采用恒电位阳极氧化法,在纯钛片上制得TiO2纳米管阵列,利用SEM、XRD、UV-DRS等进行了形貌、晶型和吸收光谱的表征和分析,并通过光催化降解甲基橙考量掺杂Cu前后的TiO2纳米管阵列的光催化性能。结果表明,掺杂Cu后的TiO2纳米管阵列吸收光谱带的加宽大大拓展了其光响应范围,并产生浅势肼-肖特基势垒,使得其光催化活性有了显著提高。     

S掺杂TiO_2/粉煤灰复合材料的制备及光催化性能的研究

以钛酸四丁酯为前驱体,粉煤灰为载体,采用溶胶凝胶法制备了掺杂不同质量分数S的TiO2/粉煤灰复合纳米材料。用红外光谱(IR)、X射线衍射(XRD)、扫描电镜(SEM)及能谱分析(EDS)等测试手段对其进行了表征,以甲基橙的降解为模型反应,评价了试样光催化活性。结果表明,掺杂TiO2/粉煤灰具备较高可见光催化活性,原因是掺杂的硫取代TiO2中的晶格氧形成Ti—S键,使TiO2的带隙能窄化引起对可见光的响应,增强催化剂对可见光的吸收,与未掺杂的TiO2/粉煤灰相比较,掺杂负载型二氧化钛催化剂能够获得更高的光催化活性。     

掺杂改性纳米TiO_2光催化剂的制备及表征

对纳米TiO2光催化剂的溶胶-凝胶法合成工艺方法进行了改进。分别考察了不同掺杂金属离子(Fe3+、Cu2+、Pb2+)的不同掺杂量对TiO2的晶相和晶粒尺寸、光学性能、以及其光催化降解性能的影响。所得到的改性纳米TiO2光催化剂,扩大了对可见光响应范围,提高了光催化降解效率,对进一步利用太阳能治理工业有机废水有重要的参考价值。     

TiO_2光催化剂掺杂改性的研究新进展

TiO2作为一种重要的光催化剂,对其进行掺杂改性可以有效的提高光催化活性。本文通过介绍金属与非金属的单掺、共掺对其光催化活性的影响,综述了近年来TiO2光催化剂在掺杂改性方面的研究进展。提出TiO2光催化剂在改性过程中亟待解决的问题及其在实际应用中的发展。     

玻璃表面上掺杂ZnFe2O4的TiO2薄膜光催化性能的研究

采用溶胶－凝胶法在玻璃表面制备了掺杂ZnFe2O4的TiO2薄膜，通过改变ZnFe2O4的掺杂量和薄膜的热处理温度，研究了ZnFe2O4对TiO2薄膜光催化性能的影响。利用紫外光谱、SEM、XRD等测试手段指出了在TiO2薄膜中掺杂ZnFe2O4后，能较大幅度地提高TiO2薄膜的光催化活性。     

钴掺杂TiO_2纳米管阵列的制备及其光催化性能研究

采用阳极氧化法在钛箔上制备了钴掺杂TiO2纳米管阵列,利用场发射扫描电子显微镜(FSEM)、X射线衍射仪(XRD)对TiO2纳米管的形貌和结构进行表征,并对其光催化活性进行了测试.研究结果表明:钴被成功地掺杂到纳米管阵列中;电解液中钻的掺入对纳米管阵列的形貌没什么影响;掺杂溶液离子浓度对催化剂活性有一定影响,但影响不大,掺杂离子浓度为0.016mol/L所得样品活性最好;煅烧温度对纳米管的晶型结构和光催化活性有显著影响.     

磁控溅射法制备As-S玻璃薄膜

采用磁控溅射法在ITO导电玻璃上制备As-S玻璃薄膜,采用XRD、透可见-红外性能、扫描电镜、XPS等现代测试手段,研究薄膜的结晶形态、光学性质和成分。结果发现,利用磁控溅射方法得到了透过率较高、光学质量优良、没有明显的缺陷的As-S硫系玻璃薄膜,XPS光电子能谱结果显示薄膜As/S摩尔比为0.686,大于设计组成。     

Photocatalytic Water Splitting on Visible Light-responsive TiO2 Thin Films Prepared by a RF Magnetron Sputtering Deposition Method

The development of visible light-responsive TiO₂ (Vis-TiO₂) thin films has been achieved by applying a radio-frequency magnetron sputtering deposition (RF-MS) method. Pt-loaded Vis-TiO₂ thin films act as photocatalysts to decompose water involving sacrificial reagent such as methanol or silver nitrate even under visible light (λ ≧ 420 nm) irradiation. It was also found that Pt-loaded Vis-TiO₂ thin films decompose pure water into H₂ and O₂ stoichiometrically under light irradiation of wavelengths longer than 390 nm. Vis-TiO₂ thin films exhibit columnar structures perpendicular to the substrate and a declined composition of the O/Ti ratio from the surface (O/Ti = 2.00) to bottom (O/Ti = 1.93). This unique structure (anisotropic structure) of Vis-TiO₂ can be considered an important factor in the modification of the electronic properties of Vis-TiO₂ thin films, enabling the absorption of visible light. Furthermore, the effect of the Pt loadings on the photocatalytic activity of the TiO₂ thin films was investigated and the optimum Pt loading was determined to be 21 μ g/cm² as Pt metal     

磁控溅射法制备纳米Cu薄膜及其微结构的研究

采用磁控溅射法制备出以ITO为基底的纯Cu薄膜,考察溅射时间和基底温度等工艺条件对生长Cu薄膜的影响.用电子扫描显微镜(SEM)、X射线衍射仪(XRD)对薄膜的形貌、厚度和结构进行表征.实验结果表明:在一定范围内调控衬底温度和溅射时间,可获得不同形貌、尺寸和厚度的Cu薄膜,所得薄膜的晶体结构为面心立方结构,均沿(111...     

工艺因素对磁控溅射法制备钛酸锶钡薄膜性能的影响

磁控溅射技术在薄膜制备领域有着广泛的应用.本文在介绍磁控溅射法制备薄膜材料的基本原理和流程基础之上,详细分析了溅射工艺参数(溅射功率、温度、溅射气压、氧分压)对BST薄膜性能的影响,并提出了研究中需要解决的一些问题.     

工艺参数对磁控溅射WO_3薄膜电致变色性能的影响

本文采用磁控溅射法制备了用于电致变色器件的WO_3薄膜,用X射线衍射仪(XRD)、场发射扫描电镜(FE-SEM)、紫外-可见分光光度计(UV-Vis)对其物相组成、微观形貌以及电致变色性能进行了表征。结果表明:在溅射压强为2 Pa、氩氧比为60:20时所制备的WO_3薄膜厚度适中,且有利于离子的嵌入/脱出,而以此薄膜制备的电致变色器件光调制范围最大,褪色时间最短,着色效率达82.9 cm~2/C。     

磁控溅射法制备染料敏化太阳能电池Pt对电极

采用磁控溅射法,通过控制溅射时间在导电基底FTO上制备出了具有不同载Pt量的Pt/FTO对电极,分析了对电极的表面形貌、晶相结构、透过率等。同时,对不同光照模式下组装的染料敏化太阳能电池(dye sensitized solar cells,DSSCs)的光电性能进行了考察。实验表明,正照射模式下,溅射30 s制备的Pt/FTO对电极能获得优异的光电性能,其组装电池的最高能量转换效率达到8.3%,在正照射模式下具有很好的应用前景;由于所制备对电极透光性较差,背照射模式下组装电池的光电性能较低。     

Ag掺杂TiO_2催化降解活性印染废水

以钛酸四丁酯、硝酸银为原料,通过溶胶-凝胶(sol-gel)法制备了掺杂不同含量银的TiO2纳米粉体,并将其应用于活性染料—活性红195、活性黄145及活性蓝19的印染废水的光催化降解。结果表明:适量的银掺杂可有效提高TiO2对活性染料光催化降解活性;当pH为6~8、银掺杂量为0.6%(Ag/TiO2摩尔比)、活化温度为500℃、催化剂用量为0.1 g/L时,光催化降解效率最高,分别为92.5%(活性红195)、90.8%(活性黄145)、83.6%(活性蓝19)。     

离线双银Low-E镀膜玻璃膜系开发浅谈

阐述了采用真空磁控溅射原理生产双银Low-E镀膜玻璃膜系的一种新的开发思路,通过对双银Low-E膜系的实际开发过程分析,提出了双银Low-E镀膜玻璃膜系的开发过程中应注意的问题,并对实际生产提供了指导性建议。     

磁控溅射法制备铁氧体薄膜的磁性能研究

采用溶胶-凝胶法制备纳米晶镍锌钴铁氧体/二氧化硅复合粉体,并将该粉体制成靶材.采用磁控溅射法在单晶硅基底和玻璃基底上沉积镍锌钴铁氧体复合薄膜,并对其进行磁性能研究.研究结果表明:镍锌钴铁氧体/二氧化硅复合薄膜具有较好的软磁性能;在相同的溅射条件下,两种基片上的薄膜的矫顽力都较小,但硅基片上薄膜的饱和磁化强度较玻璃基片上的大,软磁性能更好;经后退火处理,薄膜的饱和磁化强度得到明显地提高,软磁性能得到改善.