Process and characterisation of chemical bath deposited manganese sulphide (MnS) thin films

Manganese sulphide (MnS) thin films have been deposited by a simple and inexpensive chemical bath deposition (CBD) method using thioacetamide as a sulphide ion source from an aqueous medium. The effect of preparative parameters on the film growth and quality has been studied. The MnS films have been characterised by XRD, TEM, SEM, EDAX, RBS, optical absorption and (time resolved microwave conductivity) TRMC techniques for their structural, compositional, and optical properties. The as-deposited MnS film on glass substrate consists of nanocrystalline grains. The film consists of mixed (cubic and hexagonal) phases. The optical band gap of the film is estimated to be 3.02 eV.     

Optical and electrical properties of p-type AgInSnxS2−x (x = 0–0.04) thin films prepared by spray pyrolysis

AgInSn_xS_2−x (x = 0–0.2) polycrystalline thin films were prepared by the spray pyrolysis technique. The samples were deposited on glass substrates at temperatures of 375 and 400 °C from alcoholic solutions comprising silver acetate, indium chloride, thiourea and tin chloride. All deposited films crystallized in the chalcopyrite structure of AgInS₂. A p-type conductivity was detected in the Sn-doped samples deposited at 375 °C, otherwise they are n-type. The optical properties of AgInSn_xS_2−x (x < 0.2) resemble those of chalcopyrite AgInS₂. Low-temperature PL measurements revealed that Sn occupying an S-site could be the responsible defect for the p-type conductivity observed in AgInSn_xS_2−x (x < 2) thin films.     

Preparation and characterization of C60S16 and C70S48 thin films

In this study, we have investigated different methods for preparation of thin films of C₆₀ and C₇₀-sulfur compounds. Films of good quality were obtained by reaction of amorphous C₆₀ and C₇₀ films with a saturated sulfur solution in toluene at 40°C or with saturated sulfur vapour at a temperature of 140°C for several hours. The quality of the fullerene-sulfur films were strongly dependent on the microstructure of the initially deposited fullerene film and the synthesis temperature. X-ray diffraction analyses showed that both methods lead to the formation of films consisting of C₆₀S₁₆ and C₇₀S₄₈ (space groups C 2/c and Amm2, respectively). C₆₀S₁₆ films synthesised on Al₂O₃(012) and Si(100) substrates were texture-free while C₇₀S₄₈ films typically exhibited a preferential (100) orientation. The films were also characterised by Raman and IR- spectroscopy, which confirmed that the interactions between the fullerene molecules and the S₈ rings are weak. The fullerene-sulfur compounds were found to be unstable at high vacuum conditions. Both materials C₆₀S₁₆ and C₇₀S₄₈ are non-conductive at room temperature with conductivities less then 10⁻⁵ (Ω/cm).     

Structural, dielectric and optical properties of Ba(Ti, Zr)O3 thin films prepared by chemical solution deposition

Ba(Ti_0.95Zr_0.05)O₃ (BTZ) thin films grown on Pt/Ti/SiO₂/Si(100) substrates were prepared by chemical solution deposition. The structure and surface morphology of BTZ thin films has been studied by X-ray diffraction (XRD) and scanning electron microscope (SEM). At 100 kHz, the dielectric constant and dissipation factor of the BTZ film are 121 and 0.016, respectively. The ellipsometric spectrum of the BTZ thin film annealed at 730 °C was measured in the range of wavelength from 355 to 1700 nm. Assuming a five-layer model (air/surface roughness layer/BTZ/interface layer/Pt) for the BTZ thin films on platinized silicon substrates, the optical constant spectra (refractive index n and the extinction coefficient k) of the BTZ thin films were obtained.     

Epitaxial and polycrystalline BaFe12O19 thin films grown by chemical vapour deposition

Epitaxial and polycrystalline barium hexaferrite BaFe₁₂O₁₉ thin films were prepared by metalorganic chemical vapour deposition (MOCVD). Films were grown by a liquid MOCVD technique which aim is to control precisely the precursor vapour pressures. Two kinds of substrates were used: sapphire (001) and silicon thermally oxidized. On Si/SiO₂ films are polycrystalline and the magnetization is isotropic. On Al₂O₃ (001), structural studies reveal the films to be predominantly single phase, well crystallized without annealing procedure and with the c-axis perpendicular to the film plane; epitaxial relationships between the film and the substrate were determined. The magnetic parameters, deduced from vibrating sample magnetometer measurements, show a high dependence of the magnetization with the orientation of the field with respect to the surface of the film.     

Influence of the sputtering system''s vacuum level on the properties of indium tin oxide films

The influence of the chamber residual pressure level in the radio frequency magnetron sputtering process on the electrical, optical and structural properties of indium thin oxide (ITO) is investigated. Several ITO films were deposited at various residual pressure levels on Corning glass using In₂O₃:SnO₂ target in argon atmosphere and without the addition of oxygen partial pressure. It is found that a very good vacuum is associated to metallic films and results in less transparent ITO films, with some powder formation on the surface. On the contrary highly transparent and conducting films are produced at a higher residual pressure. The best deposition conditions are addressed for ITO films as transparent conducting oxide layers in silicon heterojunction solar cells. Using the optimal vacuum level for ITO fabrication, a maximum short circuit current of 36.6 mA/cm² and a fill-factor of 0.78 are obtained for solar cells on textured substrates with a device conversion efficiency of 16.2%.     

Microstructure, crystallinity, and properties of low-pressure MOCVD-grown europium oxide films

A study of growth, structure, and properties of Eu₂O₃ thin films were carried out. Films were grown at 500–600 °C temperature range on Si(1 0 0) and fused quartz from the complex of Eu(acac)₃·Phen by low pressure metalorganic chemical vapor deposition technique which has been rarely used for Eu₂O₃ deposition. These films were polycrystalline. Depending on growth conditions and substrates employed, these films had also possessed a parasitic phase. This phase can be removed by post-deposition annealing in oxidizing ambient. Morphology of the films was characterized by well-packed spherical mounds. Optical measurements exhibited that the bandgap of pure Eu₂O₃ phase was 4.4 eV. High frequency 1 MHz capacitance–voltage (C–V) measurements showed that the dielectric constant of pure Eu₂O₃ film was about 12. Possible effects of cation and oxygen deficiency and parasitic phase on the optical and electrical properties of Eu₂O₃ films have been briefly discussed.     

The influence of film structure on In2O3 gas response

This paper reports the influence of In₂O₃ film structure on gas-sensing characteristics measured in steady state and transient modes. Films were deposited by spray pyrolysis from InCl₃–water solutions. Correlation between gas-sensing parameters and structural parameters such as film thickness (20–400 nm), grain size (10–70 nm), refractive index and film texture (I(400)/I(222)) were established. It was shown that grain size and porosity are the parameters of In₂O₃ films that best control gas response to ozone. In the detection of reducing gases, the influence of film structure is less important. Decreases in film thickness, grain size and degree of texture are the best way to decrease time constants of the gas response of In₂O₃-based gas sensors.     

Highly conducting indium tin oxide (ITO) thin films deposited by pulsed laser ablation

Highly conducting and transparent indium tin oxide (ITO) thin films were prepared on SiO₂ glass and silicon substrates by pulsed laser ablation (PLA) from a 90 wt.% In₂O₃-10 wt.% SnO₂ sintered ceramic target. The growths of ITO films under different oxygen pressures (P_O2) ranging from 1×10⁻⁴–5×10⁻² Torr at low substrate temperatures (T_s) between room temperature (RT) and 200°C were investigated. The opto-electrical properties of the films were found to be strongly dependent on the P_O2 during the film deposition. Under a P_O2 of 1×10⁻² Torr, ITO films with low resistivity of 5.35×10⁻⁴ and 1.75×10⁻⁴ Ω cm were obtained at RT (25°C) and 200°C, respectively. The films exhibited high carrier density and reasonably high Hall mobility at the optimal P_O2 region of 1×10⁻² to 1.5×10⁻² Torr. Optical transmittance in excess of 87% in the visible region of the solar spectrum was displayed by the films deposited at Po₂≥1×10⁻² Torr and it was significantly reduced as the P_O2 decreases.     

Properties of thin In2O3 and SnO2 films prepared by corona spray pyrolysis, and a discussion of the spray pyrolysis process

Thin films of doped In₂O₃ and SnO₂ were prepared by the “corona spray pyrolysis” technique with a deposition efficiency of 80%. The electrical and optical properties of the films were determined. A transmission of 88% in the visible region and an IR reflection of more than 90% were the maximum values obtainable for a doped In₂O₃ film.

A detailed discussion of the physical and chemical processes that occur during spray pyrolysis is presented to aid the understanding of this coating technique.

A minimum temperature of about 350°C for the formation of In₂O₃ was empirically confirmed.

Furthermore the powdery precipitate obtained during deposition of In₂O₃ was clearly identified as polycrystalline In₂O₃ formed by a homogeneous reaction.     

Spray deposition of lanthanum selenide (La2Se3) thin films from non-aqueous medium and their characterizations

The spray pyrolysis technique was employed to prepare lanthanum selenide (La₂Se₃) thin films on ordinary glass and fluorine doped tin oxide (FTO) coated glass substrates under optimized conditions. The preparative parameters are optimized to get good quality of La₂Se₃ thin films. X-ray diffraction (XRD) study reveals that only cubic La₂Se₃ is formed with a grain size of about 42 nm. The direct optical band gap is estimated to be 2.6 eV. The dispersions of dielectric constant and dielectric loss are studied with the variation of frequency. The room temperature electrical resistivity of the films is found to be of the order of 10⁵ Ω cm. The film is found to be a p-type semiconductor.     

Structural, electrical, and optical studies on rapid thermally processed ferroelectric BaTiO3 thin films prepared by metallo-organic solution deposition technique

Polycrystalline BaTiO₃ thin films having the perovskite structure were successfully produced on platinum coated silicon, bare silicon, and fused quartz substrate by the combination of the metallo-organic solution deposition technique and post-deposition rapid thermal annealing treatment. The films exhibited good structural, electrical, and optical properties. The electrical measurements were conducted on metal-ferroelectric-metal (MFM) and metal-ferroelectric-semiconductor (MFS) capacitors. The typical measured small signal dielectric constant and dissipation factor at a frequency of 100 kHz were 255 and 0.025, respectively, and the remanent polarization and coercive field were 2.2 μC cm⁻² and 25 kV cm⁻¹, respectively. The resistivity was found to be in the range 10¹⁰–10¹² Ω·cm, up to an applied electric field of 100 kV cm⁻¹, for films annealed in the temperature range 550–700 °C. The films deposited on bare silicon substrates exhibited good film/substrate interface characteristics. The films deposited on fused quartz were highly transparent. An optical band gap of 3.5 eV and a refractive index of 2.05 (measured at 550 nm) was obtained for polycrystalline BaTiO₃ thin film on fused quartz substrate. The optical dispersion behavior of BaTiO₃ thin films was found to fit the Sellmeir dispersion formula well.     

Indium-doped ZnO thin films deposited by the sol–gel technique

Conducting and transparent indium-doped ZnO thin films were deposited on sodocalcic glass substrates by the sol–gel technique. Zinc acetate and indium chloride were used as precursor materials. The electrical resistivity, structure, morphology and optical transmittance of the films were analyzed as a function of the film thickness and the post-deposition annealing treatments in vacuum, oxygen or argon. The obtained films exhibited a (002) preferential growth in all the cases. Surface morphology studies showed that an increase in the films' thickness causes an increase in the grain size. Films with 0.18 μm thickness, prepared under optimal deposition conditions followed by an annealing treatment in vacuum showed electrical resistivity of 1.3 × 10^− 2 Ωcm and optical transmittance higher than 85%. These results make ZnO:In thin films an attractive material for transparent electrodes in thin film solar cells.     

Preparation of porous CdIn2S4 photocatalyst films by hydrothermal crystal growth at solid/liquid/gas interfaces

A chemical method has been used to prepare highly crystalline porous CdIn₂S₄ photocatalyst films at low temperature on a glass substrate. The conversion of cadmium and indium salts with thiourea on CdIn₂S₄ powder particles into CdIn₂S₄ has been achieved via hydrothermal reaction, which acts as a “glue” to connect the original CdIn₂S₄ particles chemically thus forming a mechanically stable photocatalyst film.     

Preparation and characterization of LiNiVO4 powder and non-stoichiometric LiNixVyOz films

Inverse spinel type structured oxide, LiNiVO₄, was synthesized by using solid-state method and the crystalline powder was characterized by Rietveld refinement and X-ray photoelectron spectroscopy. Non-stoichiometric lithium nickel vanadate thin films were prepared by physical vapour deposition technique. The amorphous films were characterized by Rutherford back-scattering spectroscopy (RBS), nuclear reaction analysis (NRA), Auger electron spectroscopy (AES), X-ray diffraction (XRD), scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM) analytical methods. Films crystal growth at various temperatures was also studied by XRD and SEM. The HRTEM analysis of sputtered film shows nanocrystalline domains of NiO and LiNiVO₄ phases with characteristic lattice parameters of the host compound and the results correlate well with the XRD data. Electrochemical properties of the films were discussed.     

Investigation on the cross sensitivity of NO2 sensors based on In2O3 thin films prepared by sol-gel and vacuum thermal evaporation

In₂O₃ thin films have been prepared from commercially available pure In₂O₃ powders by high vacuum thermal evaporation (HVTE) and from indium iso-propoxide solutions by sol-gel techniques (SG). The films have been deposited on sapphire substrates provided with platinum interdigital sputtered electrodes. The as-deposited HVTE and SG films have been annealed at 500°C for 24 and 1 h, respectively. The film morphology, crystalline phase and chemical composition have been characterised by SEM, glancing angle XRD and XPS techniques. After annealing at 500°C the films’ microstructure turns from amorphous to crystalline with the development of highly crystalline cubic In₂O_3−x (JCPDS card 6-0416). XPS characterisation has revealed the formation of stoichiometric In₂O₃ (HVTE) and nearly stoichiometric In₂O_3−x (SG) after annealing. SEM characterisation has highlighted substantial morphological differences between the SG (highly porous microstructure) and HVTE (denser) films. All the films show the highest sensitivity to NO₂ gas (0.7–7 ppm concentration range), at 250°C working temperature. At this temperature and 0.7 ppm NO₂ the calculated sensitivities (S=R_g/R_a) yield S=10 and S=7 for SG and HVTE, respectively. No cross sensitivity have been found by exposing the In₂O₃ films to CO and CH₄. Negligible H₂O cross has resulted in the 40–80% relative humidity range, as well as to 1 ppm Cl₂ and 10 ppm NO. Only 1000 ppm C₂H₅OH has resulted to have a significant cross to the NO₂ response.     

GaGeTe films as phase-change optical recording media

Ga₂₀Ge₃₀Te₅₀ thin films deposited by vacuum evaporation on various substrates have been studied for their structural and optical properties. The as-deposited amorphous films were crystallized by thermally annealing them. The optical constants of the amorphous films indicate semiconducting behaviour (n> k). The optical bandgap (E_g) determined from Tauc's plot is 0.7 eV. The change in reflectance on crystallization has been utilized to obtain maximum optical contrast by optimising the thickness of the film.     

Structure and conducting properties of La0.5Sr0.5CoO3−δ films on YSZ

La_0.5Sr_0.5CoO_3−δ (LSCO) thin films were deposited on yttria stabilized zirconia (YSZ) substrates by pulsed laser deposition (PLD) for application to thin film solid oxide fuel cell electrodes. During the deposition, the substrate temperature was varied from 450 to 750°C, and the oxygen pressure in the chamber was varied from 80 to 310 mTorr. Films deposited at 650°C and an oxygen background pressure of 150 mTorr were mostly (100) oriented. Deposition at higher temperatures or under lower oxygen pressures lead to mostly (110) oriented films. Films with low electrical resistivity of 10⁻³ Ω·cm were obtained.     

Microwave dielectric properties of W-doped Ba0.6Sr0.4TiO3 thin films grown on (001) MgO by pulsed laser deposition with a variable oxygen deposition pressure

The microwave dielectric properties of Ba_0.6Sr_0.4TiO₃ 1 mol% W-doped thin films deposited using pulsed laser deposition, are improved by a novel oxygen deposition profile. The thin films were deposited onto (001) MgO substrates at a temperature of 720 °C. A comparison is made between three different oxygen ambient growth conditions. These include growth at a single oxygen pressure (6.7 Pa) and growth at two oxygen pressures, one low (6.7 Pa) and one high (46.7 Pa). Films were deposited in a sequence that includes both a low to high and a high to low transition in the oxygen deposition pressure. Following deposition, all films were post-annealed in 1 atm of oxygen at 1000 °C for 6 h. The dielectric Q (defined as 1 / tanδ) and the dielectric constant, ε_r, were measured at room temperature, at 2 GHz, using gap capacitors fabricated on top of the dielectric films. The percent dielectric tuning (defined as (ε_r(0 V) − ε_r(40 V)) / ε_r(0 V) × 100) and figure of merit (FOM) (defined as percent dielectric tuning × Q(0 V)) were calculated. The film deposited using the two-stage growth conditions, 6.7 / 46.7 Pa oxygen, showed a maximum Q(0 V) value with high percent dielectric tuning and gave rise to a microwave FOM twice as large as the single stage growth condition. The improved dielectric properties are due to initial formation of a film with reduced interfacial strain, due to the formation of defects at the film/ substrate interface resulting in a high Q(0 V) value, followed by the reduction of oxygen vacancies which increases the dielectric constant and tuning.     

应力对蓝宝石衬底上生长二氧化钒薄膜结构和光电性能的调控

利用脉冲激光沉积技术在蓝宝石衬底上生长不同厚度的VO₂薄膜, 对薄膜的结构、表面形貌和光电性能进行研究。结果表明: 所沉积的VO₂薄膜为具有单晶性能、表面平整的单斜晶相的VO₂薄膜, 相变前后, 方块电阻的变化可达到3~4个数量级, 在波长为2500 nm的透过率变化最高可达56%, 优化的可视透过率(T_lum)和太阳能调节率( ∆T_sol )为43.2%和8.7%。薄膜受到的应力对VO₂薄膜有重要影响, 可以通过调节薄膜的厚度对VO₂薄膜光电性能实现调控。当VO₂薄膜厚度较小时, 薄膜受到拉应力, 拉应力能使相变温度显著降低, 金属-绝缘体转变性能(MIT)不但与载流子浓度的变化相关, 而且还受载流子迁移率变化的影响;当VO₂薄膜厚度较大时, 薄膜受到压应力, VO₂薄膜的相变温度接近块体VO₂的相变温度, MIT转变主要来自于载流子浓度在相变前后的变化, 其载流子迁移率几乎不变。