阻燃POM的热降解动力学研究

采用双螺杆挤出机制备了APP/MC/DPER/novolak阻燃POM材料,对材料进行了TGA测试,采用Flynn-WallOzawa方法、Starink方法两种动力学方法研究了阻燃POM的热降解动力学。由这两种方法计算得到的结果较为吻合,结果表明,阻燃剂的添加使POM材料的热降解活化能先下降后升高,说明阻燃剂先于POM分解并生成耐热性好的残炭。     

聚甲醛的热氧降解研究

本文用动态热重分析方法研究了聚甲醛的热氧降解动力学,采用Ozawa方法,计算了POM热氧降解反应的活化能,反应级数和频率因子。根据寿命和活化能的关系,估算了POM在氮气中的使用寿命。     

聚甲醛纤维制备工艺及其性能的研究

以聚甲醛(POM)切片为原料,在200～210℃进行熔融纺丝制得POM长丝。利用DSC、Olympus偏光显微镜、单纱电子强力仪测定了POM纤维结晶度、熔点、取向度和纤维的机械性能;研究了后处理对POM纤维性能的影响以及拉伸对POM纤维耐酸碱性能的影响。结果表明:(1)POM纤维耐碱性良好,拉伸可以提高POM纤维结晶度、取向度、断裂强度以及耐酸性,但是使断裂伸长率减小;最佳拉伸温度在110℃左右,拉伸倍率在6～8之间。(2)热定形温度对POM纤维结晶度和熔点影响不大,延长热定形时间使POM结晶度、熔点降低;最佳热定形条件为在140℃下热定形4min。(3)经过拉伸热定形后的POM纤维的最大断裂强度和断裂伸长率分别为7.41cN/dtex和19.2%。     

HBS改性聚甲醛的热稳定性

通过热重分析(TGA)研究聚甲醛(POM)、POM/抗氧剂1010、POM/1010/HBS体系的热稳定性,并通过Flynn-Wall-Ozawa法和Coats-Redfern法分析其非等温热降解动力学,计算得到动力学参数.结果表明:在失重率为1%时,POM/1010/HBS的温度高出纯POM 28.7 ℃;随着热失重率的提高,POM、POM/1010体系的降解活化能均呈下降趋势,而加入HBS后,体系的降解活化能呈上升趋势;说明热稳定剂HBS与抗氧剂1010有较好的协同作用,能够有效提高POM的热稳定性.     

二步法制备高强度聚甲醛纤维的工艺及性能研究

首先采用熔融纺丝工艺制备聚甲醛(POM)初生纤维,然后采用二级热箱对初生纤维进行热拉伸及热定型,制备高强度POM纤维;根据POM初生纤维的熔融结晶曲线和等温结晶性能,确定了初生纤维的热拉伸温度;研究了拉伸倍数对纤维力学性能、结晶度和取向度的影响。结果表明:POM初生纤维的热拉伸温度即第一级热箱温度为155℃,热定型温度即第二级热箱温度为120℃;POM纤维的拉伸强度和结晶度随拉伸倍数的增大先增加后降低,初生纤维经9倍拉伸时均达到最大;POM纤维取向度随拉伸倍数的增加而增加,初生纤维经9倍拉伸后趋于稳定;POM初生纤维经9倍拉伸时,所得POM纤维的拉伸强度达到最大值为1.23 GPa,断裂伸长率为21.07%。     

二氧环戊烷含量对聚甲醛性能的影响

通过对工业化聚甲醛(POM)共聚合配比中二氧戊烷(DOX)含量的优化,获得最优的二氧环戊烷配比。通过测试POM粉料与粒料的热失重率和流体流动速率(MFR),观测DOX含量对POM热稳定性能的影响。通过测试POM造粒材料后的弯曲模量、热变形温度及拉伸强度等指标,观测DOX含量对POM热稳定性的影响。结果表明:DOX含量由3%降到2.6%时,POM的热稳定性无明显变化,弯曲模量有一定提高。     

聚甲醛的熔融纺丝温度

通过熔融指数测定、红外光谱分析、重均相对分子质量测定、DSC测试分析了纺丝温度对聚甲醛（POM）流动性、热降解性的影响以及对POM纤维机械性能的影响,从而探讨出聚甲醛的最佳纺丝温度。结果表明：聚甲醛在高温下主要发生热氧降解,随着纺丝温度的升高,POM热降解速度加快,导致相对分子质量降低,熔点下降 ;POM的最佳纺丝温度为200℃,在此温度制备出的POM纤维强度达6.1cN/dtex.     

热拉伸工艺对聚甲醛纤维结构与性能的影响

采用自主开发的熔融纺丝设备制备了聚甲醛(POM)初生纤维,将POM初生纤维在130℃下,经热辊或热管在不同拉伸倍数下进行热拉伸制得POM纤维,研究热拉伸工艺对POM纤维结构与性能的影响。结果表明:随着拉伸倍数的增大,POM纤维取向度、结晶度和断裂强度逐渐增大,条干均匀性逐渐得到改善;在相同拉伸倍数(5~7)下,热辊拉伸得到的POM纤维比热管拉伸得到的POM纤维的取向度和结晶度高、强度好,但条干不匀率高;热管拉伸可实现高倍拉伸,最高可拉伸14倍,而热辊拉伸最高可拉伸7倍;热管拉伸14倍时制得的POM纤维力学性能最佳,其断裂强度可达10.76 cN/dtex,断裂伸长率为9.6%;热辊拉伸7倍时,制得的POM纤维力学性能最佳,其断裂强度可达6.92 cN/dtex,断裂伸长率为12.8%。     

纤维化对聚甲醛/聚乳酸共混物热分解和预期寿命的影响

利用熔融共混法制备了聚乳酸(PLA)含量为10%的聚甲醛/聚乳酸(POM/10PLA)共混物,并采用熔融纺丝工艺制备了POM/10PLA纤维。利用热分析仪研究了POM/10PLA共混物及其纤维的热解行为,并采用Flynn&Wall方法和Toop方法分析了POM/10PLA纤维的热解动力学,预测了其寿命。结果表明,纤维化有利于提高POM/10PLA共混物的热稳定性和预期寿命。     

氧化镁对聚甲醛热稳定作用和成核作用研究

研究了氧化镁用作聚甲醛(POM)的甲酸吸收剂对POM的热稳定作用。通过热失重率、TGA、平衡扭矩和力学性能的测试，确定了氧化镁的最佳用量范围。同时，在研究中发现氧化镁对POM有结晶成核作用，可有效提高POM的力学性能。     

聚甲醛的耐光稳定化研究

讨论了聚甲醛（POM）的光老化机理、光老化特征及各种添加剂对POM的光稳定化作用，以及添加剂配合法、其它聚合物单独添加法、其它聚合物配合法等对POM耐光稳定化的效果和相应的光稳定化机理。     

Creep rupture properties of homopolymer,copolymer, and terpolymer based on poly(oxymethylene)

Polyacetal copolymers were prepared by cationic ring‐opening copolymerizations of 1,3,5‐trioxane (TOX) with 1,3‐dioxolane (DOX), and polyacetal terpolymers were prepared by terpolymerizations of TOX, DOX, and 2‐ethylhexyl glycidyl ether (EHGE). Polyacetal polymers with three different structures such as polyacetal homopolymers, polyacetal copolymers, and polyacetal terpolymers were compared in the mechanical properties and the creep characteristics, and discussed from the view point of the polymer structure. The polyacetal copolymers and the polyacetal terpolymers were determined by ¹H‐MNR measurement. About 80 mol % of DOX and EHGE amounts in feed were incorporated randomly into the each polymer. From the plots of the degree of crystallinity (X_c) versus the tensile strength, the tensile strength and crystallintiy of the polyacetal homopoymers are higher than those of the polyacetal copolymers and the polyacetal terpolymers. However, the tensile strength does not decrease linearly with a decrease in the crystallinity among the polyacetal polymers with three different structures, the polyacetal homopolymer, the polyacetal copolymers, and the polyacetal terpolymers. Creep rupture was characterized by the activation volume, υ_c, value in Zhurkov's equation, which can be estimated from the slope in the plots of load versus log (rupture time) at 80°C. The polyacetal polymers with higher molecular weight have larger values of the activation volume than those with lower molecular weight. When the activation volume values are compared among the polyacetal polymers with the same molecular weights, they increase in the following order: the polyacetal homopolymers < the polyacetal copolymers < polyacetal terpolymers. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

新型聚丙烯稳定化体系的应用研究

通过与常规受阻胺类光稳定剂Tinuvin622、Chimassorb944的对比配方实验，考核了复合型光稳定剂BW-6911对聚丙烯的光稳定化效果及耐热氧老化协同效应，建立了新型聚丙烯稳定化体系。     

聚甲醛的制备、特性及应用

介绍聚甲醛树脂的制备方法，包括均聚甲醛及共聚甲醛制备中的单体合成与精制、聚合物合成、聚合物热稳定化方法和原理，并介绍了聚甲醛树脂的特性和主要应用领域。     

聚甲醛的合金化及复合增强研究

介绍聚甲醛（POM）合金化及复合增强等方面研究的进展。在合金化方面,论述了POM难于合金化的原因、传统型POM／PUR－T合金的现状、POM合金化的新方法及其相容化机理等;在复合增强方面,论述了使用长玻纤、碳纤维、短玻纤、玻璃微珠、滑石粉或酞酸钾晶须等对POM进行复合增强的目的、复合体系的性能及特点等。     

工程塑料改性及成型加工技术特集之二 聚甲醛的改性

采用革新的聚合技术和最适宜的材料组成的聚甲醛 ,比之以往的聚甲醛 ,其蠕变性能大幅地提高。介绍了具有此优异特性的新牌号树脂 ,讨论了对蠕变特性的看法和改性方法     

减小聚甲醛注塑制品收缩率的工艺研究

对聚甲醛注塑制品的成型工艺进行了研究，从熔体温度、成型时间、模具温度、背压等几个方面探讨了减小聚甲醛注塑制品收缩率的方法。     

POM的摩擦磨耗性能改进

介绍聚甲醛作为耐摩擦自润滑材料的评价指标,各种润滑剂对聚甲醛摩察磨耗性能的改进效果,以及在聚甲醛分子上导入润滑性链段的方法等。     

聚甲醛的成型加工

介绍聚甲醛（POM）的成型条件与性能的关系,着重阐述了POM挤出成型、注射成型的基本条件,以及注射成型中常见的制品缺陷及其解决措施等。     

聚甲醛在沸水中的老化行为

本文考察了聚甲醛在沸水中的老化行为。结果表明，在沸水处理过程中，因沸水所引起的聚甲醛化学性质的变化较小。其老化现象主要表现为，试样表现的龟裂，添加剂的析出，变色以及拉伸断裂伸长率的下降等力学性能方面的变化。