化学镀铟锌电极在KOH溶液中的析氢行为

采用析氢实验、线性电位扫描和交流阻抗法,研究了Zn电极、In电极和化学镀铟锌电极在碱性溶液中的析氢行为.结果表明:镀铟锌电极能提高锌表面的析氢过电位,有效抑制锌的析氢反应和锌在碱性溶液中的自腐蚀.锌表面的铟层越厚,这种抑制作用越强;但铟对锌在碱性溶液中的阳极行为影响不大.     

复合添加剂对锌在KOH溶液中电化学行为的影响

采用失重法、电化学方法、扫描电镜等方法研究了咪唑、聚乙二醇400及由两者组成的复合添加剂对锌在3mol/L KOH溶液中的电化学行为的影响.结果表明:单一添加剂及其组合均具有一定的缓蚀作用,但与单一添加剂相比,由咪唑和聚乙二醇400组成的复合添加剂缓蚀效果明显更好,这是由于咪唑和聚乙二醇400之间产生了协同作用所致,这种协同作用表现在有咪唑存在的情况下,聚乙二醇400更容易吸附在锌电极的表面,此外,两者能发挥自身的优势,弥补对方在结构上的不足,提高缓蚀效果.     

Effect of Sn/Zn ratio on structure and photoluminescence properties of SnO2@ZnO composites

ABSTRACT

The SnO₂@ZnO composites, with Sn/Zn molar ratio (Sn/Zn–ratio) from 4:1 to 8:1, were successfully prepared via two–step hydrothermal method. The microstructure and morphology of the as–prepared Sn/Zn–ratio–dependence SnO₂@ZnO composites were investigated. Furthermore, a reasonable growth mechanism of SnO₂@ZnO composites was proposed and the results indicated that the dispersity of SnO₂ nanowires on the ZnO nanorods surface was obviously influenced by the Sn/Zn–ratio. The photoluminescence (PL) properties of the Sn/Zn–ratio–dependence SnO₂@ZnO composites were investigated. The results showed the opposite intensity change of ultraviolet (UV) and visible emission while the Sn/Zn–ratio increased. In addition, the possible emission mechanisms were also discussed that the UV emission is attributed to free–exciton recombination at the near–band edge and the potential difference between SnO₂ and ZnO result in the visible emission.     

碱锰电池密封圈防爆压力检测装置的改进

对原有装置进行改进,增加了可编程序逻辑控制器、电子阀门、数字压力智能表及电脑数据自动传输记录模块等电器控制环节,设计了碱锰电池密封圈防爆压力检测装置.该检测装置具有检测精度高、稳定性好、操作方便等特点,测试数据的标准偏差由原先的0.3降低至0.1之内.     

Sintering behaviors and electrical properties of transparent conducting In6Sn2–x ZnxO13–x ceramics with different Sn/Zn ratio

In the indium tin zinc oxide (In₆Sn_2–x Zn_xO_13–x ; ITZO) ceramics, the atomic ratio of Sn⁴⁺ and Zn²⁺ was changed, and the solubility limit, phase development process, microstructure evolution and electrical characteristics of the sintered specimens were examined. When Sn⁴⁺ and Zn²⁺ were added with the 1:1 ratio, ITZO single phase was observed, while various kinds of second phases developed when the ratio goes away from 1:1. The generation of the second phases resulted in the decrease in the solubility limit of Sn⁴⁺ and Zn²⁺. The second phases affect the microstructure and electrical characteristics.     

碱锰电池用大功率无汞锌粉的雾化装置

设计了自由降落式喷嘴雾化装置,采用六孔啧料架,通过改进喷射孔间距、喷射角,降低雾化能耗,增加锌粉比表面积,提高碱锰电池的大功率性能.在0.8 MPa的气压下,获得粒径小于150μm的锌粉超过80％;不规则形态的锌粉比表面积达0.013 m2/g,体积平均粒径达141 μm.用该锌粉制备的LR6电池的1 500 mW、6...     

金属单质对锌电极电化学行为的影响

为了寻找碱性溶液中锌电极的代汞缓蚀剂，应用腐蚀实验、极化曲线及循环伏安等方法，研究了Ｐｂ、Ｃｄ、Ｉｎ、Ｈｇ和Ｂｉ等金属对锌电极电化学行为的影响。考虑到各种添加剂对锌电极电化学行为的影响主要是在电极与溶液之间的界面上，采用置换反应的方法将所研究的金属添加到锌电极表面。此方法既简单，又能使添加物均匀分布在锌的表面上，有效地影响锌电极的表面性质。实验结果表明：分别将Ｐｂ、Ｃｄ、Ｉｎ、Ｈｇ加到锌粉表面能增加锌电极氢的超电势，在腐蚀实验中明显地降低了氢气的析出量，但从阳极极化曲线可以看到这些金属均阻化锌的阳极氧化；Ｂｉ的加入则表现出相反的性质，它降低了氢在锌电极上的析出超电势，故而使含Ｂｉ的锌粉在腐蚀实验中析氢量增加，不过它却能促进锌的阳极氧化反应     

KOH溶液中添加剂影响锌电化学性能的研究

采用电化学方法、扫描电镜以及组装实体电池放电测试等方法研究了硝酸铋[Bi (NO3)3]、十二烷基苯磺酸钠(SDBS)及由两者组成的复合添加剂对锌在3 mol/L KOH溶液中的电化学性能的影响,结果表明:所研究的添加剂均具有一定的缓蚀作用,但与单一添加剂相比,复合添加剂的缓蚀效率更高,这归因于复合添加剂之间的协同作用...     

电解质溶液对EMD电化学行为的影响

采用微电极研究了电解二氧化锰(EMD)在不同中性电解质溶液中的电化学行为,结果表明:EMD在MgSO4溶液中有特殊的电化学特性,Mg2 对EMD的氧化还原过程有影响.循环伏安初期,在-0.15 V处有1个还原峰,在0.50 V和1.00 V处有2个氧化峰.经过5次循环以后,在0.20 V处出现1个新的氧化峰.XRD图谱证实,EMD在MgSO4溶液中的还原过程有物相变化.     

Effects of lithography non-uniformity on device electrical behavior. Simple stochastic modeling of material and process effects on device performance

Understanding how lithographic material and processing, affect linewidth roughness (LWR), and finally device operation is of immense importance in future scaled MOS transistors. The goal of this work is to determine the impact of LWR on device operation and to connect material and process parameters with it. To this end, we examine the effects of photoresist polymer length and acid diffusion length on LWR and transistor performance. Through the application of a homemade simulator of the lithographic process, it is shown that photoresists with small polymer chains and small acid diffusion lengths form lines with low LWR and thus lead to transistors with more reliable electrical performance.     

热处理对Pt/C和PtRu/C催化剂活性的影响

对商业Pt/C和PtRu/C催化剂进行真空加热处理,研究热处理对催化剂微观结构变化及甲醇氧化的影响.X射线衍射光谱法(XRO)和热重(TG)研究结果表明:低温(210℃以下)真空加热处理对Pt/C和PtRu/C催化剂活性金属组分的晶体结构和催化剂表面处于活性位置(Pt-C结合位置)的碳原子数没有较大影响.电化学测试结果表明:热处理后的商业Pt/C和PtRu/C催化剂对甲醇氧化活性均高于初始催化剂,而且180℃加热处理的Pt/C和PtRu/C催化剂对甲醇催化氧化性能最好,其电化学稳定性在热处理前后基本保持不变.     

锌铟合金电极在KOH溶液中电化学行为的研究

采用析氢实验、线性电位扫描和交流阻抗法,研究了锌、铟和锌铟合金电极在碱性溶液中的电化学行为。结果表明,合金中的铟能提高锌表面的析氢过电位,有效抑制缓解锌上的析氢反应和锌的阳极氧化,从而抑制锌在碱液中的自腐蚀。合金中铟的含量越高,这种抑制作用越强。此外,合金中的铟能扩大锌的活化电位区,有效改善锌在KOH溶液中的放电性能。     

碱性Zn-NiOOH/MnO2一次电池的性能研究

研制了以NiOOH与MnO2混合作正极活性物质、锌为负极的新一代实用碱性一次电池,弥补了目前广泛使用的碱锰电池大负荷放电性能不佳的缺陷。这种碱性Zn-NiOOH/MnO2电池1000mA大负荷放电至1.2V高压段的容量比碱锰电池提高了3.6倍,71!高温储存7d后,再放电至1.2V时容量保持率可达到73.8%,在室内储存1a后1000mA放电至1.2V的容量保持率还可达到85.6%。对这一新型电池在不同负荷下的放电容量和储存性能也进行了研究。     

五氧化二钒薄膜/电解液界面电化学研究

以晶态V2O5(c-V2O5)为原料,采用熔融淬冷法成功制取了V2O5薄膜电极,研究了该电极电化学阻抗谱(EIS)的基本形状及其随电位的变化,并用等效电路拟合了不同电位下的EIS,同时系统地测试分析了与电极材料性质和电极荷电状态相联系的一些参数。对引起这些界面参数变化的可能原因进行了解释。     

碱性体系中添加剂对铝阳极电化学性能的影响

为了提高碱性电池中铝阳极的活化性能、降低其析氢腐蚀,用析氢速率、开路电压测试和塔菲尔曲线、交流阻抗方法,系统的研究了多种添加剂对铝阳极的电化学性能的影响。结果表明:KCl、MnCl2、K2MnO4、Na2WO3、NH2CH2COOH对铝阳极的开路电位负移和抑制析氢均有良好的效果。复配添加剂K2MnO4+KCl和ZnO+KCl分别对铝阳极具有显著的活化作用,并且对抑制析氢有明显的作用。     

添加剂对铝阳极电化学性能的影响

为了提高铝的耐蚀性以及活化性能,用电化学方法研究了在4 mol/L KOH溶液中,添加剂Ca(OH)2、C4H4O6KNa以及Na2SnO3对铝阳极(99.999%)电化学性能的影响.结果表明:添加饱和Ca(OH)2 C4H4O6KNa能有效抑制腐蚀,当c(C4H4O6KNa)=15 mmol/L时,Al的缓蚀率达83.54%,且开路电位Eocp负移出现最大值达-1.751 V;添加10 mmol/L Na2SnO3在4 mol/L KOH 15 mmol/L C4H4O6KNa 饱和Ca(OH)2中,不仅使铝的腐蚀速度进一步降低(缓蚀率达86.35%),又能最大程度提高铝阳极的活化,Eocp负移程度最大达-1.800 V.     

锌粉在碱性介质中的析氢行为

通过析氢量测试研究了三种不同来源的锌粉在碱性锌电池电解质（ＫＯＨ溶液）中的动态析氢行为以及电解质浓度和两种有机抑制剂及一种无机抑制剂对析氢行为的影响,对锌粉在碱性介质中的析氢动力学进行了讨论。针对析氢反应的特性,选择的无机析氢抑制剂包含的主要成分为能与锌作用后形成高氢过电位合金薄层的无机化合物和助溶剂,因而可以减缓锌电极上析氢反应的阴极过程或提高阴极反应的位垒;而有机析氢抑制剂的主要成分为能在锌表面形成极薄吸附保护层的表面活性剂,它能有效地抑制锌电极上析氢反应的阳极过程或提高阳极反应的位垒。实验结果表明：所用析氢抑制剂的抑制效率可以达到大约１３％。同时还提出了筛选应用于干电池中的析氢抑制剂的基本思想。     

添加剂对锌银蓄电池性能的影响

在锌银蓄电池的电解液中加入3～5g/L的铬酸铅添加剂,明显减少了金属银在隔膜上的沉积,同时减少了对隔膜的氧化作用,进而减缓短路的发生,延长了电池的使用寿命.添加剂的使用,对电池的正常使用没有影响.     

碱性介质中吐温20对锌电极电化学行为的影响

利用循环伏安法以及动电位扫描法考察了吐温20作为电解液添加剂对锌电极在1.0 molL-1 KOH溶液中电化学行为的影响,结果证明适宜浓度的吐温20能显著影响锌电极的电化学行为.吐温20对锌电极具有一定的缓蚀作用,其缓蚀作用主要是由于覆盖效应,吐温20对锌电极在锌电极表面的吸附行为符合Freundlich等温式.适宜浓度的吐温20对锌电极的阴极过程有显著的抑制作用,推断其可有效减缓锌电极产生枝晶和变形.