5A02铝合金与镀锌钢CO2激光熔-钎焊接工艺

利用激光熔-钎焊实现了5A02铝合金板和镀锌钢板的优质连接。对焊缝的金相分析表明,接头钢母材未发生熔化,钢一侧为钎焊,铝一侧为熔焊;对接头的组织和结构分析表明,在焊缝金属和镀锌板的界面区形成的金属间化合物,主要成分为Fe6AlSi、FeAl和FeAl3;拉伸试验表明,焊接接头的抗拉强度可达155.720 MPa,约为5A02铝合金母材抗拉强度的76.97%,试样断裂在铝合金母材热影响区,接头的断裂主要是塑性断裂,但有脆性断裂的痕迹。     

铝/钢激光-MIG复合热源熔-钎连接试验研究

基于激光-MIG复合热源焊接实现了5A02铝合金与镀锌钢、镀铝钢及非镀层Q235钢的优质、高效熔-钎连接,并对焊缝的成形、接头的性能及微观结构作了分析.结果表明,利用该连接方法可以在高速焊接条件下实现铝/钢熔-钎连接,最高焊接速度可达5 m/min;得到的熔-钎接头的抗拉强度接近于该铝合金熔化焊接头的抗拉强度,接头的抗剪强度高于90 MPa;焊缝钎接界面处生成的金属间化合物主要为Fe_3Al、FeAl_2、Fe_2Al_5、FeAl_3,金属间化合物层厚度太薄或太厚均会影响接头的强度,化合物层厚度在1.5～4 μm范围内最佳.     

铜/镀锌钢异种金属Nd:YAG激光-脉冲MIG复合热源钎接焊

将激光一电弧复合热源焊接应用于铜与钢的熔一钎连接,用该焊接方法实现了T2紫铜合金板与镀锌钢板的优质连接。结果表明,焊接接头钢母材未发生熔化而铜合金母材熔化,其焊缝与钢母材为钎焊连接,拉伸试验中试样的断裂位置发生在焊缝铜母材热影响区,焊接热影响区略有软化。断口分析发现,接头的断裂属于塑性断裂。高倍电镜分析表明,焊缝钎焊连接界面处未见钢溶蚀及Cu沿铁素体晶界侵入现象;能谱分析结果表明,焊接接头中Cu,Fe原子分别向对方基体进行了良好的扩散,二者在钎焊连接界面处形成了Cu—Fe固溶体,并且在接头的钎焊连接界面处有Si元素的富集现象。     

几种铝钢异种金属熔钎焊工艺的对比与分析

采用脉冲旁路耦合电弧MIG焊、CMT及激光焊方法实现铝/镀锌钢板搭接焊,对焊缝界面微观组织、形貌及元素成分进行了观察分析,并测试了其力学性能.结果表明,三种焊接方法均可以实现铝/镀锌钢板异种金属的优质连接,获得成形良好的焊缝,搭接接头的抗拉剪强度均可以达到铝合金母材的80%以上,拉伸试样断裂在焊缝铝合金母材热影响区.当母材热输入及工艺合适时,三种方法下搭接接头界面处均形成一主要成分为Fe₂Al₅和FeAl₃,平均厚度约为8 μm的金属间化合物,而且控制金属间化合物的生成是获得铝/钢焊接优质接头的关键.     

5A02/Q235钢Nd:YAG激光-脉冲MIG复合热源熔-钎连接

研制开发了铝/钢特种钎剂,利用研制开发的铝/钢特种钎剂成功地实现了5A02铝合金板与普通Q235冷轧钢板的大光斑Nd∶YAG激光-脉冲MIG复合热源熔-钎连接,并对焊缝的成形、接头的性能及成分、钎剂中各成分的作用进行了分析.结果表明,涂有KAlF4 Sn Zn配方钎剂的Q235试板得到的焊缝成形美观,并且焊接过程稳定;拉伸试验中试样的破坏位置发生在铝母材的焊接热影响区,铝母材热影响区略有软化,接头抗拉强度可达167.3 MPa,约为5A02铝合金母材抗拉强度的83.6%,与5A02铝合金熔化焊接头的强度相当,接头的断裂方式为混合断裂;剪切试验中接头的最高抗剪强度可达106.3 MPa.扫描电镜分析表明,在接头钎焊连接界面处生成了一层厚度约为3.27 μm的金属间化合物层;能谱测试结果表明,Al,Fe原子在钎焊界面处扩散较为充分.     

送丝速度对铝/钢激光填丝熔钎焊性能的影响

采用光纤激光器对铝/钢异种金属搭接接头进行激光填丝熔钎焊试验研究。分析了送丝速度对焊缝成形质量、金属间化合物层厚度及力学性能的影响。试验结果表明,选择适当的送丝速度,利用铝和钢的不同熔点,使铝母材刚好熔化但是钢母材不熔化,熔化的铝母材与填充金属一起铺展在钢母材表面并与其实现钎焊连接,可形成优质的熔钎焊接头。当送丝速度小于3. 5 m/min时,易形成硬脆性金属间化合物而导致焊缝开裂。金属间化合物层厚度应控制在一定范围内,方可保证接头性能。当送丝速度为4. 5 m/min时,焊接接头强度有所提高,其线载荷达到203. 5 N/mm,约为铝合金母材抗拉强度的83. 7%。     

钛合金激光-电弧复合热源焊接工艺

对钛合金厚板进行激光-电弧复合焊接,并对焊接接头能进行试验研究,结果表明,激光-电弧复合热源焊接新工艺实现了对钛合金厚板的优质高效连接,焊接接头的抗拉强度平均在950 MPa以上,达到母材强度的95%以上;平均冲击强度高于567.3 kJ/m2;疲劳强度在600 MPa水平可达0.7～1万次,550 MPa水平可达3～...     

铝合金/钢异种金属熔-钎焊技术研究进展

文中分析了铝及铝合金与钢异种金属焊接时存在的问题,认为铝合金/钢熔-钎焊接是最适合铝合金/钢复合结构制造的焊接技术.介绍了熔-钎焊接的概念及特点,综述了国内外激光熔-钎焊、TIG熔-钎焊、MIG熔-钎焊、CMT熔-钎焊以及激光+MIG电弧复合熔-钎焊等焊接工艺方法在铝合金与钢异种金属连接中的研究现状,并对比了各种工艺方...     

铝-钢异种金属电子束扫描焊接接头力学性能分析

针对2mm厚的3A21防锈铝合金和3 mm厚的304不锈钢采用对接的方式进行了不等厚板电子束扫描焊接。通过拉伸试验机、维氏硬度测试仪和扫描电镜等设备对接头的力学性能和断口形貌进行了测试和分析。结果表明:在合适的工艺下铝-钢异种金属电子束扫描焊接接头成形良好,无气孔、裂纹等缺陷;电子束流和电子束偏移距离对接头的力学性能有较大的影响,接头力学性能最大可达112.6 MPa,接近铝母材的87%。焊接接头由钢侧熔化区、铝-钢界面连接区和铝侧熔化区三部分组成,铝-钢界面连接区主要由脆硬的Fe-Al金属间化合物组成,是接头的薄弱环节。硬度的分布与接头的形貌有关,铝-钢界面连接区的硬度最大,铝侧和钢侧熔化区的硬度都分别要比铝母材和钢母材的硬度高,接头的断裂方式为韧脆混合型断裂。     

基于实船对过渡接头法焊接钢-铝异种金属进行探究

从钢-铝异种金属焊接现状和钢-铝结构过渡接头性能特点出发,介绍了钢-铝过渡接头结构形式、焊接接头连接形式和相关节点设计要求。结合多艘次铝合金船舶建造检验,对过渡接头结构形式、结构尺寸、焊接工艺参数优化和选取、实际焊接要求等予以分析。船舶建造完成后及营运过程中未发现过渡接头复合界面出现分层缺陷,其设计和工艺对其它船舶有一定指导意义。     

铝钢异种材料焊接研究现状与发展

对近年来铝钢异种材料之间的各种常见的焊接方法(压焊、熔焊和钎焊)的研究进展进行了综述,认为铝钢异种材料连接时,金属间化合物层的控制是获得优质连接接头的关键.详细阐述了传统铝钢压焊和钎焊在控制金属间化合物层厚度方面的优势,并且指出了其在工业实际生产中的不足.详细介绍了铝钢熔焊方法和工艺的最新进展,对铝钢熔焊的研究方向进行了预测.     

大厚度船用高强钢激光-电弧复合焊技术研究

为实现大厚度高强钢全熔透单道对接焊,针对厚度20mm的AH32船用高强钢,采用15kW大功率CO_2激光进行激光-电弧复合焊接.分析了工件坡口、焊接速度、送丝速度、离焦量、装配间隙等规范参数对焊缝成型影响;通过金相观察以及显微硬度测定分析了接头组织性能.结果表明:通过激光功率等焊接规范匹配,激光-电弧复合焊接能实现20mm厚板的全熔透单道对接;钝边为8mm的Y形坡口有助于提高厚板激光-电弧复合焊缝熔透能力;降低焊接速度有利于提高熔深能力;工件厚度较大时,装配间隙对焊缝熔深能力的影响较为显著;接头硬度表明厚板激光复合焊焊缝纵向热循环模式存在较大差异.     

超薄不锈钢板的点焊工艺

通过对超薄不锈钢板的点焊试验，得到了可行的工艺参数，获得了外观良好及性能合格的接头，解决了超薄钢板点焊的工艺问题。     

海洋平台焊接技术及发展趋势

焊接技术是海洋平台建造的关键工艺。随着深海油气资源的勘探开发,海洋平台用钢向着高强度、大厚度、良好的低温韧性等方向发展,国内海洋平台焊接技术存在自动化水平低、焊接效率低、焊接质量波动大等问题,严重制约着国内海洋工程装备制造的发展。大厚度高强钢的高效焊接技术、高强钢焊接热影响区的脆化和软化、焊接结构的应力与变形控制是现阶段海洋平台焊接亟待解决的问题。窄间隙焊接、激光电弧复合焊、K-TIG、热丝TIG是新型的高效高质量焊接工艺,适用于海洋平台用钢的焊接,可进一步深入研究并在海洋平台建造领域推广应用。     

Welding of aluminium alloy by using filler-added laser-arc hybrid welding process

Laser-arc hybrid welding is considered to be an efficient, practical welding process because its deposited metal from welding wire can increase gap-bridging ability and prevent welding defects such as undercutting or underfilling. The deposition rate from welding wire, however, cannot be adjusted independently on the welding current under the stable welding conditions because it is necessary to maintain a constant arc voltage. Although the combination of a higher deposition rate and a lower welding current is sometimes needed, for example during the welding of a thin sheet, a high deposition rate generally accompanies with a high welding current in the conventional laser-arc hybrid welding. In order to solve the above-mentioned problems, the authors have proposed a novel method, a filler-added laser-arc hybrid welding (FLA welding) process, to increase a deposition rate without increasing the welding current itself in the welding of aluminium alloy. As a result, gap-bridging ability can be increased in the welding of both thin and thick plates. In this paper, the welding of aluminium alloy butt joints by using FLA welding process is discussed.     

低合金高强钢激光-电弧复合热源焊接冷裂纹敏感性分析

通过扩散氢含量测定,并利用经验公式计算JFE980S低合金高强钢冷裂纹敏感性和焊前预热温度,同时采用斜Y形坡口试验、金相试验以及残余应力测定等方法,研究低合金高强钢抗冷裂性能,对比分析了激光-电弧复合焊和MAG焊工艺对接头抗冷裂性能的影响.结果表明,激光复合焊抗冷裂性优于MAG焊方法.因复合焊加入了激光,使得焊缝熔深增加,拘束减小,并且激光在前,对焊接试板有一定的预热作用,使冷裂纹形成倾向进一步降低,特别是在无法预热的情况下,激光复合焊更能够体现出优势.     

Braze‐welding of electrical conductors to concentric plugs

In resistance spot welding of thin sheet–thick sheet–thick sheet joint, when the sheet thickness ratio is large (sheet thickness ratio = total thickness of sheet joint/thickness of the thin sheet positioned on the outside of the joint), how to stably secure the nugget between the thin sheet and the adjoining thick sheet is a key issue. If the sheet thickness ratio is so large, nugget formation between the thin sheet and thick sheet is extremely difficult. In order to control of the nugget (position of formation, shape, etc. of the nugget) during welding for three sheets joint with a high sheet thickness ratio, optimum welding process was investigated. The developed ‘two-step force, two-step current’ welding process was suitable for high sheet thickness ratio joint and relaxed the constraints on the sheet thickness ratio. In Step 1 (first part of welding period) of the welding process, a nugget is reliably formed between the thin sheet and thick sheet by applying conditions of low electrode force, short welding time, and high current. In the subsequent Step 2 (second part of welding period), a nugget is formed between the two thick sheets by applying high welding force and a long welding time. In the weld results of a three sheet joint (0.7+2.3+2.3 mm; sheet thickness ratio: 7.6) using mild steel GA (0.7 mm) as the thin sheet and 780 MPa high strength GA (2.3 mm) in the two thick sheets, ‘two-step force, two-step current’ spot welding process showed the wide available welding current range.     

基于BP神经网络遗传算法的薄板CMT点焊变形

焊接是汽车车身制造的一个关键环节,焊接质量的好坏严重影响汽车车身质量,所以焊接参数的选择至关重要. 针对薄板焊接质量控制问题,论文利用BP神经网络解决非线性问题的优势,建立焊接变形量与工艺参数之间映射关系模型;结合遗传算法构建基于遗传神经网络焊接的工艺参数优化系统;同时设计正交试验,将该方法与正交试验法相对比. 结果表明,该方法可以有效地实现CMT(cold metal transfer)点焊焊接变形预测与工艺参数优化. 通过预测模型给出合理参数,指导钢薄板和铝合金薄板的CMT点焊变形试验,提高焊接的效率.     

采用非夹层液相扩散焊连接铝基复合材料

采用真空扩散焊焊接铝基复合材料ＳｉＣｗ／６０６１Ａｌ通过系列试验研究了焊接工艺参数对接头强度的影响。结果表明：该材料扩散焊时,焊接温度是影响接头强度的主要工艺参数,当焊接温度介于基体铝合金液－固两相温度区间时,接合面上出现了液态基体金属,可获得较高的接头强度。