非晶态合金在玻璃转变温度附近的粘滞流变与其液态合金的粘度密切相关。在测定了Ni-P二元合金表面张力和密度的基础上,研究了其粘度随温度的变化规律及其非晶态的粘滞流变过程。并得到可描述Ni-P合金从液态到非晶态固体的粘度与温度关系的统一表达式: η=C·exp[(B+bT(1-1/T))/(T-T_(vs)~o)]  相似文献   

2.
1. IntroductionLiquid m etalsare in com m on use in m odern industry/area such ascasting, m etallurgy, w elding,glassform ing,the nuclearindustry and crystalgrow th.In addition,the relation ofthe physicalpropertyand structure change w ith tem perature, concentration and pressure isofgreatinterestto researchersinphysics and m aterials. V iscosity is a basic param eterin discussing the nature and behaviourofm etalm elts,and isone ofbasic propertiessensitive to the m eltstructure. V iscosity m ea…  相似文献   

3.
卢柯  王景唐 《金属学报》1988,24(2):171-175
用经典的相变理论(J-M-A方程)导出了由核长大主导的非晶态合金晶化的峰值温度(T_P)与预存晶核密度(N_0)之间的关系式: T_P~2exp(-Eg/RT_P)=L/N_0~(1/3)其中Eg为核长大激活能,L为常数,R为气体常数.通过对非晶Ni-P合金的预退火处理,获得预存晶核密度不同的非晶态样品,在DSC上测量这些样品的晶化温度.结果表明,上述关系式与实验结果符合很好,利用此关系式可估算出核长大速率常数(U_0),讨论了预退火处理对晶化开始温度T_x及△T_(Px)=T_P—T_x的影响.  相似文献   

4.
Experiments clarified that application of the maximum entropy method to calculate the RDF(radial distribution function)of the Ni-P amorphous alloy from fewer data of its X-raydiffraction data shows a higher resolution and good consistent with known results.It is be-lieved that this method is available for the analysis of amorphous structure.  相似文献   

5.
梁健端  林树智 《金属学报》1989,25(1):141-146
通过实验,证明用最大熵方法从X射线衍射数据求径向分布函数具有忠实于已知信息、高分辨率和所需数据量少等优点,是一个值得推荐的快速优质的方法。  相似文献   

6.
化学镀Ni-P合金镀层在海水中的耐蚀性   总被引:4,自引:0,他引:4  
在Cu-Ni合金表面化学镀Ni-P合金,研究了镀层在3.5%NaCl溶液中的电化学性能,通过失重法测试了Ni-P合金镀层、Cu-Ni合金在静态和动态海水中的腐蚀速率,利用表面分析技术研究了Ni-P合金镀层的组织结构与成份XRD分析结果表明Ni-P镀层是典型的非晶态合金,随着镀层P含量的增加,衍射峰越来越宽化,其非晶化的程度增高.动电位极化试验表明Ni-P镀层的耐蚀性主要受镀层中的P含量的影响,随P含量的增加,镀层的自腐蚀电位正移,腐蚀电流减小;失重试验表明Ni-P合金镀层在静态海水和流动海水中的腐蚀速率大大低于Cu-N合金  相似文献   

7.
本文研究了化学镀Ni-P非晶合金晶化受冷变形的影响.结果表明,冷变形促进了晶化,不仅降低了Ni-P非晶合金的热稳定性,而且在冷变形过程中就有晶化的迹象.  相似文献   

8.
曲哲  谢天生 《金属学报》1990,26(5):107-111
本文报道了Ni-P非晶在不同退火温度下磷的表面偏析和脆化行为及二者之间的关系。发现近表面区在退火过程中形成一个贫磷层,其厚度随温度增加,磷的贫化程度随退火温度加剧。本文从非晶中原子扩散激活能可变化的观点出发,对弛豫过程中元素再分布和脆化机制进行了讨论。  相似文献   

9.
Cu8Zr3和Cu10Zr7相中存在Cu8Zr5和Cu6Zr5团簇结构,它们与Cu-Zr系的两个深共晶点Cu61.8Zr38.2和Cu56Zr44对应. Cu64Zr36是Cu-Zr二元系具有最大玻璃形成能力的成分点.依据形成块体非晶的"变电子浓度线判据",以Cu64Zr36,Cu61.8Zr38.2和Cu56Zr44 3个二元成分为出发点,以Nb元素为第三组元,建立变电子浓度线(Cu64Zr36)100-xNbx,(Cu61.8Zr38.2)100-xNbx和(Cu56Zr44)100-xNbx.采用分步熔炼法,由铜模吸铸法制备直径为3 mm的合金棒.块体非晶的玻璃形成区及玻璃形成能力由XRD和热分析确定.结果表明,添加少量Nb(原子分数,x≤3)可以显著提高Cu-Zr二元系的玻璃形成能力.具有最大Tg/Ti值(0.626)的成分Cu60.3Zr37.2Nb2.5位于具有Cu8Zr5团簇和最深共晶点的Cu61.8Zr38.2向第三组元Nb的连线上.结合Cu-Zr二元体系的团簇结构讨论了Cu-Zr-Nb系块体非晶的形成.  相似文献   

10.
钨铜合金表面化学镀Ni-P镀层性能研究   总被引:2,自引:0,他引:2  
从钨铜合金表面化学镀Ni-P镀层的表面形貌及成分,镀层结构,外观,结合力.硬度,耐磨性,孔隙率,纤焊性等方面进行了检测和表征.结果表明,化学镀Ni-P合金层磷含量为11.37%,属于高磷镀层,主要为非晶型结构,在钨铜合金表面化学镀Ni-P合金可以大大提高钨铜合金的硬度和耐磨性,且Ni-P合金镀层与钨铜合金基体结合强度好,孔隙率低,纤焊性好.  相似文献   

11.
电刷镀非晶态Ni-P合金镀层形貌和结构研究   总被引:1,自引:0,他引:1  
梁平 《腐蚀与防护》2005,26(7):294-296,302
采用电刷镀工艺制备了Ni-P合金镀层,利用金相显微镜、扫描电镜观察了镀层的表面和截面形貌,采用能谱分析、X射线衍射技术测试和分析了Ni-P合金镀层中P元素的含量和镀层的组织结构。实验结果表明:通过该电刷镀工艺可以获得非晶态的Ni-P合金刷镀层。该镀层为柱状组织,镀层表面平整、光滑、致密,但随着刷镀层厚度的不断增加,镀层开始出现微裂纹。  相似文献   

12.
Phosphorus segregation and embrittlement of Ni-P amorphous annealed at the temperaturesbelow crystallization have been investigated.The phosphorus enrichs on free surface and itslevel increases with annealing temperature.This is fairly coincident with the measuredtoughness which decreases with annealing temperature.AES ion-sputtering revealed that aphosphorus depletion zone in the subsurface layers forms due to element redistribution duringannealing.The thickness and amplitude of the phosphorus depletion zone depend on the an-nealing temperature.The formation of depletion zone and the mechanism of embrittlement of Ni-P amorphousduring annealing have been discussed based on the theory of the activation energy of atomicdiffusion in the amorphous being variable.  相似文献   

13.
电沉积Ni-P合金初期沉积行为的研究   总被引:1,自引:4,他引:1  
对Ni-P合金在45钢基体表面的初期沉积行为进行了观察与分析,发现电沉积Ni-P合金镀层的初期沉积行为受到基体材料组织的影响.在退火态45钢表面,Ni-P合金镀层优先在晶界及渗碳体表面形核.由于珠光体组织中含有渗碳体相且具有比较高的晶界密度,因而在沉积初期镀层优先形核和生长.镀层在基体表面是以纳米尺度的晶粒聚集在一起形成的多晶体形式存在的.随着施镀时间的延长,纳米晶多晶体在侧向二维生长的同时,在多晶体聚集的表面上也进行着三维方向的新的一层多晶体的生长。  相似文献   

14.
周根树  杨根仓  周尧和 《金属学报》1995,31(18):266-268
研究了预先净化处理对于非晶态合金的热稳定性的影响。DSC示差热分析结果表明,(Ni_(0.53)Fe_(0.33)Co_(0.14))_(73)B_(17)Si_8Nb_2非晶态合金本身具有较高的热稳定性。净化使该性能进一步提高,并保证较大体积的非晶态合金保持一定的热稳定性。证明了深过冷快淬工艺是制取大体积非晶态合金并提高其使用性能的有效方法。  相似文献   

15.
Zr-二十面体准晶-十次准晶伪三元系中非晶的形成   总被引:3,自引:0,他引:3  
雷奕  黑祖昆  董闯 《金属学报》2003,39(6):573-578
分析了块状非晶与稳定准晶结构上的异同点,选择两种稳定准晶(二十面体准晶和十次准晶)相互混合,在保持准晶二十面体基本结构单元的基础上,增加元素组成的混乱度,再添加有利于形成高配位多面体的元素Zr,用急冷方法制备出非晶合金.对此非晶合金的热力学测试表明,该非晶形成能力和稳定性与Inoue的Zr65Al7.5Cu17.5Ni10非晶相近.  相似文献   

16.
用TEM研究非晶态Ni—P合金薄膜原位加热时的动态晶化过程   总被引:4,自引:0,他引:4  
卢柯  王景唐  董林 《金属学报》1991,27(1):108-114
本文采用原位加热透射电子显微镜观察技术研究了非晶态Ni-P合金薄膜的动态晶化过程。实验结果表明,非晶态合金薄膜在等温退火时,首先在非晶态基体中产生微小的有序原子集团,并长大成取向无规的Ni_3P晶体微粒;然后是晶体的形成和长大。在晶体长大过程中这些晶体微粒通过切变(取向变化)直接沉积在晶体前沿上,而保持其结构形态不变。利用动态录像技术测量了晶化过程中的晶体长大过程,发现晶体在长大过程中有“台阶型”长大,这种“台阶型”长大过程对应于有序原子集团的切变沉积,不同温度下有序原子集团切变沉积使晶体长大速率的变化不同。  相似文献   

17.
非晶态FeNiSiB合金的活性溶解行为研究   总被引:1,自引:0,他引:1  
本文采用动电位扫描技术、化学分析技术及表面分析技术研究非晶态FeNiSiB合金在0.1mol/LH2SO4水溶液中的溶解行为,发现该种非晶合金发生均匀活性溶解,不存在某一种或某几种组元的富集现象。这一行为可以用Bernal模型解释。  相似文献   

18.
不同合金钢材料化学镀Ni-P合金   总被引:1,自引:0,他引:1  
在不同合金钢材料表面成功制备了化学镀Ni-P合金层.形貌与结构分析表明,化学镀Ni-P合金层表面均匀、致密,结构为非晶形和一些微晶;热震试验表明镀层与基体的结合力良好;浓HNO3试验和3.5 mass%NaCl溶液浸泡试验表明镀层的腐蚀速率远低于基体材料,能对基体合金钢起到防护作用.  相似文献   

19.
The effect of pre-annealing treatment on the crystallization kinetics parameters of amorphous Ni-P alloys has been investigated.Experimental results showed that the crystallization tem- perature,T_p and T_x,the apparent activation energy,E_c,as well as the Avrami exponent for isothermal crystallization,n,decrease significantly,while ΔT_(px)=T_p-T_x increases with the elongation of pre-annealing time at 570 K.  相似文献   

20.
卢柯  王景唐 《金属学报》1990,26(5):92-96
本文研究了预退火热处理对非晶态Ni-P合金晶化过程动力学参数的影响,实验结果表明,在570K随着预退火热处理时间的增长,晶化温度T_x和T_p值、晶化过程表观激活能E_c值及等温晶化过程平均Avrami指数值都显著减小,而ΔT_(px)=T_p—T_x值增大。  相似文献   