纳米TiO2溶胶的制备及其性能北大核心

以钛酸丁酯为前驱体,无水乙醇为溶剂,三乙醇胺为稳定剂,氨水为催化剂,采用溶胶-凝胶法制备了纳米TiO2溶胶。探讨了加水方式、加水量、无水乙醇用量、稳定剂和催化剂用量、pH值和反应温度对凝胶时间的影响。采用Zetasizer Nano-ZS型马尔文粒度仪和UV-Vis 8500型双光束紫外/可见分光光度计对TiO2粒径和紫外光透过率进行表征。结果表明:制备TiO2溶胶的较优工艺参数为n(钛酸丁酯)∶n(无水乙醇)∶n(水)∶n(三乙醇胺)∶n(氨水)=1∶45∶40∶1∶0.8,pH值为8.5,水浴反应温度为55℃。制备的TiO2溶胶平均粒径为50.7 nm,且具有较低的紫外线透过率。     

纳米TiO_2溶胶的制备及其性能

以钛酸丁酯为前驱体,无水乙醇为溶剂,三乙醇胺为稳定剂,氨水为催化剂,采用溶胶-凝胶法制备了纳米TiO_2溶胶。探讨了加水方式、加水量、无水乙醇用量、稳定剂和催化剂用量、pH值和反应温度对凝胶时间的影响。采用Zetasizer Nano-ZS型马尔文粒度仪和UV-Vis 8500型双光束紫外/可见分光光度计对TiO_2粒径和紫外光透过率进行表征。结果表明:制备TiO_2溶胶的较优工艺参数为n(钛酸丁酯)∶n(无水乙醇)∶n(水)∶n(三乙醇胺)∶n(氨水)=1∶45∶40∶1∶0.8,pH值为8.5,水浴反应温度为55℃。制备的TiO2溶胶平均粒径为50.7 nm,且具有较低的紫外线透过率。     

掺锌纳米TiO_2光催化性能研究

以钛酸四丁酯、硝酸锌为主要原料,采用溶胶-凝胶法制备掺锌纳米TiO2微粒.以罗丹明B为目标降解物,考察了掺锌纳米TiO2粉体的光催化活性.结果表明:300℃焙烧4.5 h时,得到的催化剂活性最高.在紫外光照射下,催化效果明显优于太阳光照射(在紫外光下,pH值为2时,用1 g/L掺锌2.7%纳米TiO2光照70 min,罗丹明B的降解率接近100%;在太阳光下,pH值为10时,用4 g/L掺锌3.0%纳米TiO2光照120 min,罗丹明B的降解率达93%).     

混凝—光催化连用技术处理纸浆中段废水

福建省光催化重点实验室郑堰日等人以钛酸丁酯、正硅酸乙酯、无水乙醇等为原料,采用Sol-Gel法制备TiO2-SiO2光催化剂,通过单因素实验得到最佳制备工艺条件为:n(钛酸丁酯):n(正硅酸乙酯)为2.33:1,煅烧温度600℃,煅烧时间3h,反应溶液pH值3。当进水CODCr379.5mg.L-1,TiO2-SiO2光催化剂的投加量0.5mg.L-1,紫外光照时间3h时,出水CODCr达到67.8mg.L-1。TiO2-     

掺镧TiO_2光催化降解罗丹明B的研究

采用溶胶-凝胶法制备了掺镧TiO2微粒.以罗丹明B为目标降解物,分别在太阳光和紫外灯下照射,考察了掺镧TiO2光催化活性.结果表明:在紫外光下,pH值为6时,用4 g/L掺镧0.25%TiO2降解罗丹明B光催化活性最佳;在太阳光下,pH值为6时,用5 g/L掺镧0.075%TiO2降解罗丹明B光催化活性最佳;加入H2O2都能提高光催化效果,在太阳光下,由于TiO2和H2O2的协同作用,催化降解率能达到90%以上.     

纳米TiO_2负载棉织物的光催化性能

以钛酸丁酯(TBT)为前驱体,在超声低温条件下,在棉织物表面原位生成纳米级锐钛矿型TiO2,并对其光催化性能进行了研究。通过均匀试验设计,以在紫外光和可见光辐射下亚甲基蓝脱色率为评价目标值,对钛酸丁酯、冰乙酸及超声时间三个因素进行回归分析,得出优化工艺:钛酸丁酯4 m L,超声2.5 h,紫外光下脱色率为85.94%;钛酸丁酯4 m L,超声5.5 h,可见光下脱色率为76.58%。并对比了超声及常规水热法处理后负载TiO2织物的光催化性能。X射线衍射(XRD)分析可知,溶液中残留的TiO2粉体主要为锐钛矿型,粒径5.3 nm;扫描电镜(SEM)观察发现,棉织物表面不均匀分布大量纳米级TiO2颗粒;紫外-可见光谱(UV-VIS)测试显示,负载TiO2的织物在紫外光区有明显吸收,可见光区吸收平台上移,超声及水热处理时间的延长有利于增强织物对紫外和可见光的吸收。     

纳米TiO2-PASS复合絮凝剂的制备及其性能

采用溶胶-凝胶法制备了纳米TiO2-PASS复合絮凝剂,对所得复合絮凝剂的成分、结构与光催化性能的关系进行研究,并采用XRD、FI-IR对样品进行表征.结果表明,TiO2-PASS复合絮凝剂的最佳制备条件为PASS用量2mL、钛酸丁酯用量5mL、无水乙醇用量24mL、冰乙酸用量1mL、去离子水用量3mL、浓盐酸用量0.3mL.光催化实验结果表明,当复合絮凝剂煅烧温度500℃、模拟染料废水pH=2.0、光照时间120min时光催化性能最佳,活性艳兰废水的脱色率达到95%.XRD、FI-IR图谱表明PASS掺杂的样品晶型均为锐钛矿型,PASS的掺杂改变了TiO2晶相转变温度,提高了TiO2晶体结晶度和粒子尺寸,有利于复合絮凝剂性能的发挥.     

织物负载TiO_2光催化剂的制备及活性红MS光催化动力学

实验采用溶胶一凝胶法制备纳米TiO2溶胶,棉织物经过浸渍TiO2溶胶-烘干-焙烘法处理,在织物表面低温制备TiO2薄膜.采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)等方法对样品结构和形貌进行分析和表征.在紫外灯照射下,以活性红MS为降解物,研究了制备条件包括TiO2浓度、TiO2溶胶pH值、焙烘温度和焙烘时间对薄膜光催化性能的影响.结果表明在低温下制备的TiO2主要是锐钛矿型,并且薄膜的光催化活性与处理工艺有关.在TiO2浓度为0.423 mol/L.TiO2溶胶pH值为1.67、焙烘温度为80℃、焙烘时间为2 min的条件下,活性红MS的光催化降解速率常数最大,拟合紫外光下光催化薄膜降解活性红MS为一级反应.     

溶胶-凝胶法制备二氧化钛及其光催化降解性能

以钛酸丁酯[Ti(OC_4H_9)_4]作为钛源,采用溶胶-凝胶法制备二氧化钛(TiO_2)光催化剂。以甲基橙降解率为评价指标,检测无水乙醇、冰乙酸、蒸馏水与钛酸丁酯物质的量比、煅烧温度、煅烧时间等因素对TiO_2光催化降解性能的影响,以确定TiO_2优化制备工艺,并通过XRD、TEM进行表征。结果表明,TiO_2的优化制备工艺为:无水乙醇、冰乙酸、蒸馏水与钛酸丁酯物质的量比15∶3∶8∶1,煅烧温度550℃,煅烧时间3 h;在此工艺下制得的TiO_2为锐钛矿型,颗粒大小为10～25 nm,对甲基橙的降解率在3 h内可达79.7%,比工业TiO_2(P25)的降解率高9.9%。     

以废皮屑为原料制备的胶原基絮凝剂对中段废水有显著的絮凝作用

福建省光催化重点实验室郑堰日等人以钛酸丁酯、正硅酸乙酯、无水乙醇等为原料,采用Sol—Gel法制备TiO2-SiO2光催化剂,通过单因素实验得到最佳制备工艺条件为：n（钛酸丁酯）：力（正硅酸乙酯）为2．33：1,煅烧温度为600℃,煅烧时间为3h,     

罗汉果皂苷分离纯化

采用薄层层析色谱和制备高效液相色谱对罗汉果提取物组分A进行纯化,结果表明,硅胶薄层色谱法的最佳展开剂配比为正丁醇:冰醋酸:水＝4:1:2;而制备高效液相色谱法的色谱条件为：ODS柱(φ20mm×250mm)、流动相30%甲醇溶液、流速8mL/min、检测波长210nm,按峰分步收集。经薄层色谱和高效液相色谱纯度鉴定,得到罗汉果提取物的三个组分A1、A2和A3。     

A novel vitamin C analog, 2-O-(beta-D-Glucopyranosyl)ascorbic acid: examination of enzymatic synthesis and biological activity

2-O-(beta-D-Glucopyranosyl)ascorbic acid (AA 2 beta G) isolated from a popular traditional Chinese food (Lycium fruit) was synthesized using cellulase derived from Trichoderma sp. with cellobiose as a glucose donor. 6-O-(beta-D-Glucopyranosyl)ascorbic acid as well as AA 2 beta G was also synthesized in this reaction. The vitamin C activity of AA 2 beta G was also evaluated using inherently scorbutic (osteogenic disorder Shionogi [ODS]) rats. The rats were fed vitamin C-deficient food and water containing AA 2 beta G for 21. AA 2 beta G supported their growth and the level of vitamin C in tissues was moderately maintained. The vitamin C level in some tissues depended on the hydrolytic activity of AA 2 beta G (beta-glucosidase activity) although the correlation was not statistically significant (P=0.08). The results indicate that AA 2 beta G has pro-vitamin C activity.     

Optimization of Processing Parameters for the Preparation of Flounder Frame Protein Product

Flounder frame was used as a raw material for the preparation of protein product. Processing parameters were evaluated using both fresh and frozen ground frames. The results indicate the following optima: (1) pH of extraction medium, ii; (2) extraction time, 60 min; (3) volume to weight ratio, 10: 1; (4) extraction temperature, 23°C. Isoelectric precipitation was conducted at pH 5 using KCI or H₃PO₄. Results indicate that NaOH was more effective than Ca(OH)₂ in solubilizing frame protein at pH 11. Ground frozen flounder frames gave a 10% decrease in protein extractability when compared to fresh frames using NaOH as the extractant and a 22% decrease when Ca(OH)₂ was employed as the extractant. Approximately 70% of the protein is recovered using the NaOH-HCI system.     

无皂苯丙乳液制备及表面施胶增强效果研究

以聚乙烯醇和丙酮为分散剂,苯乙烯、丙烯酸丁酯为单体,甲基丙烯酸缩水甘油酯为功能性单体,过硫酸钾为引发剂,采用无皂乳液聚合法合成无皂苯丙乳液.分析结果表明,无皂苯丙乳液胶粒粒径小且分布均匀、分散性好.用乳液浸渍处理纸张,不但具有施胶和增湿强效果,同时也能提高纸张的强度性能和印刷性能.将合成的无皂苯丙乳液与氧化淀粉复配对纸张性能改善的效果比单一使用氧化淀粉的效果好.施胶量较少时,无皂苯丙乳液与氧化淀粉复配不具有施胶和增湿强效果,但可改善纸张强度性能.     

从小麦麸皮中提取植酸钙的生产工艺

采用稀酸萃取加碱中和沉淀法从小麦麸皮中提取植酸钙。利用正交法找出了最佳工艺条件:反应温度30℃、水料浸提比8∶1、浸泡酸度pH为2~2.5、絮凝剂为5%的氯化钠、浸泡时间为6h~8 h、中和剂采用Ca(OH)2和10%的NaOH溶液、中和酸度为先用Ca(OH)2中和pH至5,再加10%的NaOH溶液中和pH至7.5左右。     

湿地松KP浆高白度完全无氯漂白的研究

本文研究了湿地松ＫＰ浆的完全无氯（ＴＣＦ）漂白。结果表明，ＯｐＸＰ（Ｘ－活化处理）漂序可把纸浆漂至７５％（ＳＢＤ）以上的白度，ＯＸＰＸＰ漂序白度可达到９０％（ＳＢＤ）。该工艺的关键是选用了Ｘ木素活化剂，经活化的纸浆可漂性大大提高，１％Ｈ２Ｏ２漂白白度增值可达３０％（ＳＢＤ）以上。     

反相乳液聚合制备阳离子改性接枝淀粉

本实验以淀粉、丙烯酰胺、阳离子单体(二甲基二烯丙基氯化铵)为原料,采用过硫酸铵--尿素氧化还原引发体系,以油酸失水山梨醇酯为乳化剂,通过反相乳液聚合技术,合成阳离子改性淀粉接枝共聚物.分析讨论了单体配比、乳化剂用量、引发剂用量及油水体积比等合成条件对共聚物性能的影响,并采用正交实验方法对合成条件进行了优化.     

Photocatalytic activity for degradation of nitrogen oxides over visible light responsive titania-based photocatalysts

This study investigates photocatalytic degradation of nitrogen oxides overtitania-based photocatalysts illuminated by ultraviolet and visible light. The TiO2 photocatalyst was synthesized in a sol-gel process using titanium butoxide as the precursor. After calcination between 150 and 300 degrees C, the synthesized TiO2 responded strongly to visible light photocatalytically degrading NO(x), probably because of the existence of carbonaceous species that act as sensitizers. The optimum calcination temperature was found to be around 200 degrees C. Additionally, platinum ion-doped TiO2 was prepared by impregnation using Pt(NH3)4(NO3)2 as a dopant, which improved the photocatalytic activity that degraded NO(x) in the visible light region. The Pt ion was doped in oxide form at the surface of TiO2 and was expected to be responsible for sensitization. At an optimum calcination temperature of around 200 degrees C, the Pt ion-doped TiO2 exhibited higher activity in the further oxidation of NO2 to NO3- clearly reducing NO2 selectivity. The TiO2 catalysts chemically prepared by either the sol-gel process or impregnation exhibited stronger activity than conventional TiO2 when illuminated under a fluorescent lamp. Rinsing with water was responsible for the restored reactivity of prepared TiO2 catalysts for NO(x) degradation.     

乙氧酰胺苯甲酯表面分子印迹聚合物的制备与吸附特性

合成功能单体N,O-双异丁烯酰乙醇胺（N,O-bismethacryloyl ethanolamine,NOBE）,采用表面分子印迹技术,以硅胶为载体,乙二醇二甲基丙烯酸酯（ethylene glycol dimethacrylate,EGDMA）为交联剂,制备乙氧酰胺苯甲酯（ethopabate,ETP）分子印迹聚合物（molecularly imprinted polymers,MIPs）。采用正交试验方法,对ETPNOBE物质的量比、ETP-EGDMA物质的量比和致孔剂种类3 个因素进行考察,结果表明：3 个影响因素主次顺序为致孔剂种类＞ETP-NOBE物质的量比＞ETP-EGDMA物质的量比;当致孔剂为乙腈、ETP-NOBE-EGDMA的物质的量比为1∶2∶20时,所制备的ETP-MIPs印迹效果最佳。Scatchard模型研究发现存在两类结合位点,高亲和位点与低亲和位点的平衡离解常数Kd和最大表观结合量Qmax分别为Kd1=1.608 μg/mL,Qmax1=1.101 μg/mg;Kd2=0.109 μg/mL,Qmax2=0.172 μg/mg。     

CMS-Fe2+络合物对降低卷烟烟气部分有害物质的研究

以羧甲基淀粉钠(CMS)为原料,采用配位Fe2+形成新的络合物,并通过正交实验对CMS-Fe2+络合物最佳配比进行了优化,结果表明:在反应体系pH7.0,络合时间3h,硫酸亚铁铵与CMS的质量分数比1.2:1,抗氧化剂添加量50%的条件下,络合物中Fe2+的质量含量为4.06%。通过离子色谱法和氢火焰离子检测器分别对氨和巴豆醛进行标气检测,结果表明,CMS-Fe2+络合物几乎完全能去除氨,降低巴豆醛为16.99%,这为CMS-Fe2+络合物作为滤嘴添加剂选择性吸附烟气中部分有害成分奠定了一定的理论和应用基础。