PP/POE及PP/EPDM共混改性研究

以茂金属聚烯烃弹性体(POE,乙烯-辛烯共聚物)和三元乙丙橡胶(EPDM)作为聚丙烯(PP)的增韧剂,研究了PP/POE及PP/EPDM共混物的加工性能及力学性能。研究结果表明,POE在加工性、增韧改性等方面比EPDM更具有优势。借助扫描电子显微镜(SEM)进一步探讨了共混物的形态结构与性能的关系。     

新型热塑性弹性体增韧聚丙烯的研究

以聚烯烃弹性体(POE,乙烯-辛烯共聚物)为PP的增韧性剂,利用转矩流变仪、差示量热扫描(DSC)及力学性能测试方法,比较研究了PP/POE及PP/EPDM共混物的加工性能、结晶性能及力学性能;结果表明,POE在加工性、改性效果等方面比EPDM更具优势。还探讨了POE用量对PP/CaCO     

PBt-TPE、EPDM、POE等弹性体改性PP性能的研究

研究了自制的聚1-丁烯热塑性弹性体(PBt-TPE)及市售的三元乙丙橡胶(EPDM)和乙烯-辛烯共聚物(POE)3种弹性体改性聚丙烯(PP)共混物的性能,比较了3种改性体(PBr-TPE、EPDM、POE)对PP共混物力学性能和热性能的影响,结果表明3种弹性体对PP具有相似的改性效果,共混物的断裂伸长率和冲击强度等韧性指标均有明显改善;PBt-TPE在某些方面可替代EPDM作为PP的改性剂,其工业化产品将具有明显的价格优势.     

聚丙烯的增韧改性

研究了POE ,EPDM ,EVA和EAA4种改性剂对PP性能的影响。结果表明 ,POE和EPDM对PP冲击强度提高较大 ,且POE对PP弯曲和拉伸强度降低较小 ,PP/POE的热性能和加工性能都较PP/EPDM共混材料优良     

PP/POE共混物力学性能研究

用双螺杆挤出机制备了聚丙(烯PP)/聚烯烃弹性(体POE)共混物,研究了POE用量对PP/POE共混物冲击性能、拉伸性能及弯曲性能的影响。结果表明:随着POE含量的增加,PP/POE共混物的冲击强度明显提高;拉伸强度及拉伸模量弯、曲强度及弯曲模量、断裂伸长率及断裂强度均减小。     

降解PP/EPDM共混物的力学性能

用过氧化二异丙苯(DCP)将聚丙烯(PP)降解,制备降解PP与三元乙丙橡胶(EPDM)共混物,测试降解PP/EPDM共混物的冲击和拉伸性能,研究共混物的脆—韧转变,结果发现温度和EPDM含量对PP/EPDM共混物的韧性影响规律是相同的,增加温度和增加EPDM含量都能使PP/EPDM共混物的韧性增加。     

基本断裂功方法表征PP及弹性体增韧PP的冲击韧性

将基本断裂功(EWF)方法应用于聚丙烯(PP)、PP/(乙烯/丙烯/二烯)共聚物(EPDM)和PP/(乙烯/1-辛烯)共聚物(POE)共混体系的冲击韧性表征。结果表明,加入EPDM或POE后,共混物的比基本断裂功we和比塑性形变功βwp均有提高,说明弹性体的加入提高了材料抵抗裂纹扩展的能力和发生塑性形变的能力。含质量分数8%EPDM或POE的PP共混物的we和βwp高于含1%EPDM或POE的PP共混物。通过对试样冲击断面和应力发白区域的观察证实了EWF方法表征的结果。EWF方法为评价聚合物材料的断裂行为提供了更多的数据,是一种表征材料冲击韧性的极好的方法。     

PP/共聚PP/POE汽车保险杠专用料的研制

研制了PP／共聚PP／聚烯烃弹性体(POE)汽车保险杠专用料，介绍了POE的结构特点，探讨了POE及共聚PP含量对PP力学等性能的影响。结果表明，POE对PP的增韧优于(乙烯/丙烯／二烯)共聚物(EPDM)，共聚PP在PP／共聚PP／POE体系中也起到增韧作用，该共混料可以满足汽车保险杠性能的要求。     

高模量弹性体对PP结晶行为及力学性能的影响

应用DSC和力学性能测试研究了PP/OTE、PP/EPDM共混物的结晶行为和它们的增韧作用。结果表明 ,烯烃类热塑性弹性体 (以下简称OTE)对PP的结晶性能无明显影响 ,EPDM对PP成核速率有促进作用。PP/OTE在赋予PP较好低温韧性的同时 ,使共混物的刚性得以适度兼顾 ,且易于加工。PP/OTE共混体系的综合性能优于PP/EPDM共混物     

动态硫化PP/EPDM热塑性弹性体的研究进展

阐述了动态硫化聚丙烯(PP)/三元乙丙橡胶(EPDM)共混型热塑性弹性体的发展历史和发展状况;概述了动态硫化PP/EPDM共混型热塑性弹性体的硫化体系及硫化原理;总结了共混体系的成份配置和工艺条件对PP/EPDM共混物性能和结构的影响;简述了动态硫化PP/EPDM热塑性弹性体的研究现状与应用;最后展望了动态硫化PP/EPDM热塑性弹性体的发展趋势。     

Polymer blends based on polyolefin elastomer and polypropylene

A new family of homogeneous polyolefin polymers that exhibit unique molecular and rheological properties designated polyolefin elastomers (POEs) are characterized by a narrow molecular weight and high degrees of comonomer distribution. Because these copolymers are often elastomeric in nature, one of the uses for these materials is as impact properties improver for brittle polymers such as polypropylene at low temperatures. In this work a study was carried out about the effectiveness of the polyethylene elastomer (POE) as an impact modifier for polypropylene in relation to the traditional modifier EPDM. In this study the flow properties of of the POE/PP and EPDM/PP blends were also evaluated. The blends were analyzed by solid-state ¹³C nuclear magnetic resonance (¹³C-NMR) spectroscopy, scanning electron microscopy (SEM), and differential scanning calorimetry (DSC). The results showed that PEE/PP and EPDM/PP blends present a similar crystalline behavior, which resulted in a similar mechanical performance of the blends, on the composition analyzed. It was also verified that the POE/PP blend presents lower torque values than the EPDM/PP blend, which indicates a better processability when POE is used as an impact modifier. © 1997 John Wiley & Sons, Inc. J Appl Polym Sci 66: 2005–2014, 1997     

交联硫化体系对PP／POE／EPDM热塑性弹性体性能的影响

采用动态硫化法制备聚丙烯／聚烯烃弹性体／三元乙丙橡胶（PP/POE／EPDM）共混型热塑性弹性体,研究了交联前后不同POE／EPDM并用对比体系力学性能的影响。采用交联剂过氧化二异丙苯（DCP）及DCP／S硫化体系对PP／POE／EPDM体系进行硫化,研究了力学性能的变化。结果表明,EPDM可有效降低材料的硬度和断裂永久变形。助交联剂硫黄（S）对PP／POE／EPDM体系有较好的硫化作用,固定DCP用量为3份,S用量为0．4份时,体系力学性能最佳,交联对体系硬度影响很小。     

高流动性PP增韧体系流变性能的研究

利用毛细管流变仪和转矩流变仪对高流动性聚丙烯（PP）增韧体系的流变性能进行分析,讨论了聚烯烃弹性体（POE）、三元乙丙橡胶（EPDM）=增韧母料和降温母料等助剂对高流动性PP共混体系流变性能的影响,并对PP/POE共混体系和PP/EPDM共混体系的转矩流变曲线进行了对比,考察了不同共混体系的微观结构、力学性能和加工性能。     

聚烯烃改性PET的研究

通过PET与PP、HDPE、EPDM挤出共混，注射模塑制得试样。经DTA、SEM和力学性能测试，表征了共混体系的热行为、结构形态和力学性能。结果表明，在PET/PP(EPDM、HDPE)共混体系中，加入少量的PP-g-MI(EPDM-g-MAH、PE-g-MI)，可较好地改善PEt与PP(EPDM、HDPE)之间的相容性，使分散相在PET基体连续相中分散均匀，分散相尺寸减小，增加了两相间界面的粘结力；同时对PET的结晶有较强的促进作用，使其冷结晶温度降低，改善了PET的加工性能；并且能大幅度提高共混物的冲击强度。     

不同弹性体增韧聚丙烯的研究

通过双螺杆挤出机制备了三种不同的弹性体EPR、EPDM、POE与PP的共混物,测试了共混物的力学性能, 比较了三种弹性体的增韧效率。结果表明:三种弹性体都是PP有效的增韧剂,其中POE的增韧效率最高,其冲击强度是纯PP的25倍。通过扫描电镜观察了弹性体在PP中的分散,发现POE在基体中相区尺寸最小,其冲击强度最大;EPDM相区尺寸最大,其冲击强度最小,这意味着共混物的相形态与性能有很好的相关性,三种弹性体在PP中分散尺寸不同的主要原因是由于弹性体与PP的黏度比不同引起的。DMA分析表明低模量的弹性体有利于提高共混物的韧性。     

EPDM/POE/PP热塑性硫化橡胶材料的制备及性能研究

以三元乙丙橡胶(EPDM)/乙烯-辛烯共聚物(POE)/聚丙烯(PP)为原料,在PP含量固定的情况下,将POE部分取代EPDM,采用动态硫化技术制备出EPDM/POE/PP三元热塑性橡胶材料(TPV),研究不同含量的POE对材料力学性能、流变性能和微观形貌的影响。结果显示,随着POE含量的增加,三元TPV材料的硬度和熔体质量流动速率不断增大;拉伸强度和断裂伸长率呈线性增大,当EPDM/POE/PP比例为45/40/15时,材料力学性能达到最大值。流变性能和微观形貌分析结果表明,EPDM/POE/PP三元TPV材料具有良好的综合性能。     

高流动性聚丙烯增韧体系的研究

比较了聚烯烃弹性体、三元乙丙橡胶等对聚丙烯的改性效果,讨论了在增韧母料和降温母料的共同作用下这两种增韧剂的不同影响,对不同体系的扫描电镜结果和结晶参数进行了分析。     

EPDM／PP共混物的形态结构与性能

用透射电镜分析比较了EPDM／PP共混物硫化前后的形态结构及力学和加工性能,讨论了共混设备、硫化体系对EPDM／PP共混物硫化前后形态结构及力学与加工性能的影响,揭示了共混物形态结构与力学及加工性能的关系。