激光能量对激光冲击强化45钢摩擦磨损性能的影响

在不同激光能量(4,6,8 J)下对45钢试样表面进行激光冲击强化,研究了激光能量对试样显微硬度、残余应力、微观结构和摩擦磨损性能的影响。结果表明：随着激光能量的增加,45钢的晶格畸变程度、残余压应力、显微硬度和耐磨性能不断提升。在8 J激光能量下,45钢的表面(211)晶面半高宽、残余压应力和显微硬度分别增加到3.50°,500 MPa, 345 HV,摩擦因数和磨损质量损失分别减小到0.61和157 mg,同时磨损表面剥落物最少,犁沟的深度和宽度最小。45钢摩擦磨损性能的提升与激光冲击强化诱导的高密度位错结构和高幅值残余压应力有关。     

ZK60镁合金表面滚压强化试验研究

试验研究了ZK60镁合金表面滚压加工中工艺参数对试件表面粗糙度、表面形貌、表面残余应力和表层显微硬度的影响,结果表明滚压力和重复滚压次数对试件的表面粗糙度、表面形貌以及表面残余应力和表层硬度影响程度较大,滚压速度影响较小。对精车ZK60镁合金试件进行滚压加工,试件表面粗糙度R a、R z最大减小了50.3%和48.1%;残余压应力最大可达-54.55 MPa;显微硬度从试件表层到内部基体材料逐渐降低,表层硬度值最大为92.83 HV 0.25,比基体材料硬度提高了15.32%。     

车削参数对GH4079高温合金表面特征的影响研究

研究车削参数对GH4079高温合金表面特征的影响规律,为车削加工GH4079高温合金选择合理的加工参数提供实验基础依据。采用车削速度为280~560m/min,切削深度为0.5~1.0mm,进给量为0.035~0.088mm/r的车削参数对GH4079高温合金进行车削加工,并用CALISUM表面粗糙度仪、显微硬度仪及X射线应力衍射仪对GH4079高温合金车削表面特征(表面粗糙度、表面显微硬度及表面残余应力)进行测定。GH4079高温合金车削表面粗糙度值在Ra502~Ra1 121nm范围内变化,表面显微硬度值在570.2~677.3HV范围内波动,进给方向残余应力σr(X)呈压应力状态,而垂直于进给方向残余应力σr(Y)呈拉应力状态。研究结果表明:表面粗糙度和表面显微硬度对切削速度的变化最为敏感,表面残余应力对切削深度的变化最敏感;表面粗糙度和表面显微硬度均随切削速度的增加而减小;表面残余压应力随切削深度的增大而增大,表面残余拉应力随切削深度的增大而减小。     

激光冲击强化与喷丸提高不锈钢疲劳性能对比研究

对不锈钢材料1Cr11Ni2W2MoV进行了激光冲击强化和喷丸强化后表面粗糙度和残余应力测试分析,与喷丸相比,激光冲击强化对试件表面形貌和表面粗糙度的影响更小,产生的残余压应力更大。对光滑试件和2种强化后试件的振动疲劳对比试验表明,激光冲击强化能显著提高不锈钢材料振动疲劳寿命,是喷丸的2倍以上。     

激光淬火处理对灰铸铁残余应力与耐磨性能的影响

利用CO2激光对HT200铸铁进行了表面淬火处理,对其微观显微组织和显微硬度进行了分析,用X-350A型应力测试仪测定了其残余应力和残余奥氏体的分布,并进行了耐磨性试验.结果表明,激光淬火后HT200显微硬度由HV250提高到HV530,表面残余应力均为压应力,其值在-300 MPa以上;耐磨性能明显得到提高,并随残余压应力的增加而增大,将有利于提高HT200材料的使用寿命;激光淬火处理诱发的残余奥氏体有利于抑制裂纹的扩展,提高材料的耐磨性能.     

滚压强化对45钢螺纹根部表面完整性的影响研究

采用自制的基于普通车床CA6140的螺纹根部滚压强化装置对45钢螺纹试样进行滚压强化工艺处理。使用三维形貌测量仪、显微硬度计、X射线残余应力检测仪、超景深显微镜等检测设备,对滚压完成后的螺纹根部表面粗糙度、表层显微硬度、残余应力,表层显微组织等表面完整性参数进行检测。通过进行单因素试验,探究了螺纹根部滚压强化工艺参数对表面完整性的影响。45钢螺纹试样经过滚压强化工艺后,其螺纹根部的表面粗糙度S_a由1.71μm减小到0.874μm;螺纹根部形成了明显的晶粒细化层,深度达到了120μm;显微硬度由199.3 HV增加到379.5 HV,硬化程度N=90.4%;表层残余应力呈勺型分布,残余应力在距离表面105μm处达到峰值,为-542 MPa,残余压应力层深度可达700μm。研究结果表明：滚压强化技术可以显著提高螺纹根部的表面完整性,且滚压深度这一工艺参数对其的影响最为显著。     

GH4169高速车削参数对加工表面完整性影响研究

使用PVD-TiAlN涂层硬质合金刀片进行高温合金GH4169的高速车削正交试验,建立了表面完整性特征中表面粗糙度、表面残余应力、显微硬度的经验公式,分析了车削参数对表面完整性各特征量的影响规律,并观测了高速车削加工的表面形貌。结果表明:表面粗糙度随车削速度的增加而减小,随进给量和切削深度的增加而增大,进给量是影响表面粗糙度的最主要因素;随着进给量的增加,表面形貌变差;轴向残余应力表现为压应力,切向残余应力表现为拉应力,减小进给量,降低车削速度可减小车削加工的残余应力,轴向残余应力对进给量最敏感,切向残余应力对切削深度最敏感;显微硬度随车削速度的增大而增加,车削速度是影响显微硬度的主要因素。     

球铁曲轴激光冲击强化实验研究

为了研究激光冲击强化对球铁性能的影响,采用钕玻璃脉冲激光(波长为1054nm,脉冲宽度为23ns)对球墨铸铁(简称球铁)曲轴试样表面进行冲击强化处理,并对其显微硬度、残余应力和疲劳强度进行实验测试与分析。结果表明,在激光功率密度为10.6GW/cm2的强脉冲激光作用下,冲击区的显微硬度明显增加,表层材料的显微硬度比基体约提高65%~75%;冲击区表面存在残余压应力,数值高达-400MPa,使用寿命提高150%。实验结果表明,激光冲击球铁曲轴的强化效果明显。     

7055铝合金高速加工表面完整性对疲劳寿命的影响

为优化高强度铝合金高速铣削工艺参数,提高构件的疲劳寿命,通过高速铣削及疲劳试验,研究了7055铝合金高速铣削工艺参数对表面完整性的影响以及表面完整性对疲劳寿命的影响。结果表明:铣削表面残余应力均呈现为压应力;每齿进给量对表面粗糙度的影响大于铣削速度的影响,铣削速度和每齿进给量对表面显微硬度的影响不显著;7055铝合金试样的疲劳寿命随表面粗糙度增大而降低,随表面残余压应力增大而提高;在试验参数范围内最佳的铣削参数为铣削速度1 100 m/min、每齿进给量0.06 mm/z,试件的表面粗糙度为Ra0.327μm,表面显微硬度为187.44 HV0.025,表面残余应力为-177.7 MPa,疲劳寿命为1.275×105次。     

不同喷丸强度下镍铝青铜的表面喷丸强化效果

采用0.15,0.20,0.25mm的喷丸强度对铸态镍铝青铜进行了表面喷丸强化处理,对比分析了喷丸前后镍铝青铜表层的残余应力、显微硬度、微观形貌及表面粗糙度,并计算了表层的亚晶尺寸和显微畸变。结果表明:随着喷丸强度的提高,镍铝青铜表面的残余压应力和加工硬化程度都逐渐增大;但喷丸强度过大时,表面粗糙度明显增大并伴随有显微裂纹产生,从而导致表层应力释放,使得残余压应力增大幅度下降,减弱了强化效果。     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

一种涡旋压缩机径向随变机构的设计

详细介绍了运用随变原理设计的一种新型径向密封机构的结构特点,工作原理及主要参数的确定方法,该机构可补偿由于涡旋体加工精度不高而造成的功率损失,适用于涡旋压缩机的批量生产。     

Specific features of operation of electrostatic microgenerators of energy

Specific features of operation of one- and two-capacitor microelectromechanical converters (MEMC) of energy of mechanical microscopic vibrations into electric energy with a modulated electrode-gap magnitude and with allowance for the mutual influence of electrical and elastic forces are analyzed, and the characteristics of these two devices are compared. The main factors restricting the increase in MEMC power are demonstrated to be the effects of “collapsing” and the condition of conservation of positive rigidity of the system. Expressions for estimating the limiting MEMC parameters are derived. The possibility of electrical energy generation in the presence of “real“ sources of wide-spectrum microscopic vibrations is considered.     

我校工业设计教育改革初探

针对目前市场对工业设计人才的需求,本文论述了我校在工业设计教育方面的改革措施,着重介绍了我校工业设计教育在软件和硬件方面所进行的一系列的改革。     

某型号飞机起落架支柱减振筒内壁腐蚀原因分析

飞机起落架减振支柱在飞机起落和滑跑时,吸收撞击能量,对飞机安全起降的意义重大.减振筒是减振支柱中的重要部件,本文从工艺流程、理化分析、外场使用和腐蚀机理分析等方面,对减振支柱减振筒内壁的腐蚀原因及危害进行了综合分析,并提出了相应措施.     