Selective synthesis of mixed alcohols from syngas over catalyst Fe2O3/Al2O3 in slurry reactor

The Fe₂O₃/Al₂O₃ catalyst was studied to selectively synthesize mixed alcohols from syngas in a continuously stirred slurry reactor with the oxygenated solvent Polyethylene Glycol-400 (PEG-400). The selectivity of mixed alcohols in the products reached as high as 95 wt.% and the C₂₊ alcohols (mainly ethanol) was more than 40 wt.% in the total alcohol products at the reaction conditions of 250 °C, 3.0 MPa, H₂/CO = 2 and space velocity = 360 ml/g_cat h. The hydrogen temperature programmed reduction (H₂-TPR) and X-ray photoelectron spectroscopy (XPS) measurements of the catalyst confirmed that the FeO phase was responsible for the high selectivity to mixed alcohols in the process. And the oxygenated solvent PEG-400 was also necessary for the selective synthesis of mixed alcohols in the reaction system.     

High-temperature close coupled catalysts Pd/Ce-Zr-M/Al2O3 (M = Y, Ca or Ba) used for the total oxidation of propane

A series of high-temperature close coupled catalysts Pd/Ce-Zr-M/Al₂O₃ (M = Y, Ca or Ba) were prepared by ultrasonic-assisted successive impregnation. The catalysts were subjected to a series of characterization measurements. The results of activity evaluation show that Y is the best promoter for propane total oxidation, especially at the calcination temperature of 1100 °C. It is interesting that although the BET specific surface areas and the dispersion of Pd species decrease, the Y-promoted catalyst calcined at 1100 °C shows higher catalytic activity than the corresponding one calcined at 900 °C and better sulfur-resisting performance. The results of TEM, TPHD and CO chemisorption indicate that Y can remarkably increase the dispersion of Pd species. However, the dispersion is hard to be connected with the activity increase as the calcination temperature is elevated from 900 to 1100 °C. The change of active phases and the interaction between Pd species and the supports may account for the activity enhancement. Combined with XRD, H₂-TPR and O₂-TPD results, it is deduced that the coexistence of metallic Pd and PdO species in the catalysts calcined at 1100 °C may be also favorable to C₃H₈ oxidation. In a word, Pd/Ce-Zr-Y/Al₂O₃ is indeed a promising high-temperature close coupled catalyst applicable to high temperature.     

Phase diagram of the Al2O3-HfO2-Y2O3 system

The phase diagram of the Al₂O₃-HfO₂-Y₂O₃ system was first constructed in the temperature range 1200-2800 °C. The phase transformations in the system are completed in eutectic reactions. No ternary compounds or regions of appreciable solid solution were found in the components or binaries in this system. Four new ternary and three new quasibinary eutectics were found. The minimum melting temperature is 1755 °C and it corresponds to the ternary eutectic Al₂O₃ + HfO₂ + Y₃Al₅O₁₂. The solidus surface projection, the schematic of the alloy crystallization path and the vertical sections present the complete phase diagram of the Al₂O₃-HfO₂-Y₂O₃ system.     

Effects of Al2O3 addition on the sintering behavior and microwave dielectric properties of CaSiO3 ceramics

The effects of Al₂O₃ addition on the densification, structure and microwave dielectric properties of CaSiO₃ ceramics have been investigated. The Al₂O₃ addition results in the presence of two distinct phases, e.g. Ca₂Al₂SiO₇ and CaAl₂Si₂O₈, which can restrict the growth of CaSiO₃ grains by surrounding their boundaries and also improve the bulk density of CaSiO₃-Al₂O₃ ceramics. However, excessive addition (≥2 wt%) of Al₂O₃ undermines the microwave dielectric properties of the title ceramics since the derived phases of Ca₂Al₂SiO₇ and CaAl₂Si₂O₈ have poor quality factor. The optimum amount of Al₂O₃ addition is found to be 1 wt%, and the derived CaSiO₃-Al₂O₃ ceramic sintered at 1250 °C presents improved microwave dielectric properties of ?_r = 6.66 and Q × f = 24,626 GHz, which is much better than those of pure CaSiO₃ ceramic sintered at 1340 °C (Q × f = 13,109 GHz).     

Efficient production of hydrogen and multi-walled carbon nanotubes from ethanol over Fe/Al2O3 catalysts

Fe/Al₂O₃ catalysts with different Fe loadings (10-90 mol%) were prepared by hydrothermal method. Ethanol decomposition was studied over these Fe/Al₂O₃ catalysts at temperatures between 500 and 800 °C to produce hydrogen and multi-walled carbon nanotubes (MWCNTs) at the same time. The results showed that the catalytic activity and stability of Fe/Al₂O₃ depended strongly on the Fe loading and reaction temperature. The Fe(30 mol%)/Al₂O₃ and Fe(40 mol%)/Al₂O₃ were both the effective catalyst for ethanol decomposition into hydrogen and MWCNTs at 600 °C. Several reaction pathways were proposed to explain ethanol decomposition to produce hydrogen and carbon (including nanotube) at the same time.     

Pulsed electric current sintering of transparent Cr-doped Al2O3

Pulsed electric current sintering (PECS) was applied to obtain transparent ruby polycrystals. Al₂O₃-Cr₂O₃ powder mixture was prepared by drying an aqueous slurry consisting of Al₂O₃ and Cr(NO₃)₃ followed by PECS consolidation in vacuum at a sintering temperatures ranging from 1100 to 1300 °C with various heating rates between 2 and 100 °C/min and under an applied pressures from 40 to 100 MPa. Slow heating rate and high-pressure lead to highly densified and transparent Cr-doped Al₂O₃ polycrystals at sintering temperature of 1200 °C.     

Effect of CeO2 addition on densification and microstructure of Al2O3-YSZ composites

Alumina (Al₂O₃) and alumina-yttria stabilized zirconia (YSZ) composites containing 3 and 5 mass% ceria (CeO₂) were prepared by spark plasma sintering (SPS) at temperatures of 1350-1400 °C for 300 s under a pressure of 40 MPa. Densification, microstructure and mechanical properties of the Al₂O₃ based composites were investigated. Fully dense composites with a relative density of approximately 99% were obtained. The grain growth of alumina was inhibited significantly by the addition of 10 vol% zirconia, and formation of elongated CeAl₁₁O₁₈ grains was observed in the ceria containing composites sintered at 1400 °C. Al₂O₃-YSZ composites without CeO₂ had higher hardness than monolithic Al₂O₃ sintered body and the hardness of Al₂O₃-YSZ composites decreased from 20.3 GPa to 18.5 GPa when the content of ZrO₂ increased from 10 to 30 vol%. The fracture toughness of Al₂O₃ increased from 2.8 MPa m^1/2 to 5.6 MPa m^1/2 with the addition of 10 vol% YSZ, and further addition resulted in higher fracture toughness values. The highest value of fracture toughness, 6.2 MPa m^1/2, was achieved with the addition of 30 vol% YSZ.     

Sintering of Al2O3-SiC composite from sol-gel method with MgO, TiO2 and Y2O3 addition

Al₂O₃-SiC composite ceramics were prepared by pressureless sintering with and without the addition of MgO, TiO₂ and Y₂O₃ as sintering aids. The effects of these compositional variables on final density and hardness were investigated. In the present article at first α-Al₂O₃ and β-SiC nano powders have been synthesized by sol-gel method separately by using AlCl₃, TEOS and saccharose as precursors. Pressureless sintering was carried out in nitrogen atmosphere at 1600 °C and 1630 °C. The addition of 5 vol.% SiC to Al₂O₃ hindered densification. In contrast, the addition of nano MgO and nano TiO₂ to Al₂O₃-5 vol.% SiC composites improved densification but Y₂O₃ did not have positive effect on sintering. Maximum density (97%) was achieved at 1630 °C. Vickers hardness was 17.7 GPa after sintering at 1630 °C. SEM revealed that the SiC particles were well distributed throughout the composite microstructures. The precursors and the resultant powders were characterized by XRD, STA and SEM.     

Luminescent properties of a novel afterglow phosphor Sr3Al2O5Cl2:Eu,Ce

A series of Eu²⁺ and Ce³⁺ doped/co-doped Sr₃Al₂O₅Cl₂ afterglow phosphors that presented various bright colors were successfully synthesized via high temperature solid state reaction. The structure and luminescence properties of the obtained samples were characterized by X-ray powder diffraction (XRD), photoluminescence (PL) spectra and decay curves as well as the thermoluminescence (TL) glow curves. The XRD results showed that all the phase could be indexed to the orthorhombic structure with the space group P2₁2₁2₁. After being exposed to a 254 nm or 365 nm mercury lamp, blue/yellow-orange afterglow emissions with broad bands peaking around 620 nm/435 nm, which were ascribed to the characteristic 4f⁶5d–4f⁷/5d¹–4f¹ transitions of Eu²⁺/Ce³⁺, could be observed in phosphors of Sr₃Al₂O₅Cl₂:Eu²⁺/Sr₃Al₂O₅Cl₂:Ce³⁺, respectively. Because of the overlap spectral range between the Sr₃Al₂O₅Cl₂:Eu²⁺ and Sr₃Al₂O₅Cl₂:Ce³⁺ phosphors, the energy transfer (ET) from Ce³⁺ to Eu²⁺ occurred. The related ET process was discussed in detail. Moreover, the incorporation of Ce³⁺ could significantly prolong the afterglow duration of Sr₃Al₂O₅Cl₂:Eu²⁺ phosphor, which was due to the increase of trap concentration. Consequently, 6 h of the afterglow duration could be observed in Sr₃Al₂O₅Cl₂:1.0%Eu²⁺, 0.5%Ce³⁺ sample, exhibiting much longer than that of Sr₃Al₂O₅Cl₂: 1.0%Eu²⁺ (3 h). From the afterglow decay curves and the fitting results, the optimal concentration of Ce³⁺ for the enhanced afterglow property was experimentally determined to be 0.5%.     

(Ba0.5Sr0.5)TiO3 modification on etched aluminum foil for electrolytic capacitor

A new method was proposed to form (Ba_0.5Sr_0.5)TiO₃–Al₂O₃ composite oxide film on etched aluminum foils. The specimens were covered with (Ba_0.5Sr_0.5)TiO₃ (BST) layer by dip-coating in citrate solution and subsequent heat-treatment under 400–650 °C, finally by anodizing in a hot boracic acid and borate solution. The BST powders heated under different temperatures were characterized by X-ray diffraction (XRD) and the specific capacitance of the coated specimens heat-treated under different temperatures and times was measured. It is found that the specific capacitance increases initially with enhancing the temperature and reaches to maximum at 550 °C, but slightly decreases with the heat-treatment time. The capacitance was increased by about 35% after BST coating.     

Preparation of columbite MgNb2O6 and ZnNb2O6 ceramics by reaction-sintering

Columbite MgNb₂O₆ (MN) and ZnNb₂O₆ (ZN) ceramics produced by the reaction-sintering process were investigated. Secondary phases Mg_0.652Nb_0.598O_2.25 and Mg_0.66Nb_11.33O₂₉ were found in MgNb₂O₆ pellets. After 1250 °C sintering for 2 h, a density 4.85 g/cm³ (97.1% of the theoretical value) was obtained in MgNb₂O₆ pellets. In ZnNb₂O₆ pellets, no secondary phase formed. The maximum density 5.55 g/cm³ (98.7% of the theoretical value) occurs at 1200 and 1180 °C sintering for 2 and 4 h, respectively.     

Synthesis of compounds, Li(MMn11/6)O4 (M = Mn1/6, Co1/6, (Co1/12Cr1/12), (Co1/12Al1/12), (Cr1/12Al1/12)) by polymer precursor method and its electrochemical performance for lithium-ion batteries

The compounds, Li(MMn_11/6)O₄ (M = Mn_1/6, Co_1/6, (Co_1/12Cr_1/12), (Co_1/12Al_1/12), (Cr_1/12Al_1/12)) are synthesised by the polymer precursor method. The structure and the morphology of the compounds are studied by the Rietveld refined X-ray diffraction (XRD), and transmission electron microscopy (TEM) techniques, respectively. Density and the Brunauer, Emmet and Teller surface area (BET) of the compounds are also studied. The cobalt doped compound, Li(Co_1/6Mn_11/6)O₄ is found to be nanosized particles in the range of 60-100 nm, when compared to the other compounds in our present study. The oxidation state and the local structure of the compounds are analysed by the X-ray absorption spectroscopy (XAS) technique. Cyclic voltammetry (CV) and the galvanostatic charge-discharge cycling (30 mA g⁻¹) studies are made in the voltage range of 3.5-4.3 V at room temperature for all the compounds under study. The bare and (Co_1/6), and (Co_1/12Cr_1/12) substituted spinels are cycled at high current rates of 1, 2 and 5C (assuming 1C∼120 mA g⁻¹). Cycling results of Co-substituted spinels show better and long-term capacity retention at all the current rates. At the end of the second cycle, Li(Co_1/6Mn_11/6)O₄ compound delivers a discharge capacity value of 100 (±3) and 87 (±3) mAh g⁻¹ for the current rate of 2 and 5C, respectively. An excellent capacity retention value of 94% is observed at the end of the 1000 cycles for both 2 and 5C rates.     

Synthesis and properties of (BaxPb1−x)(Zn1/3Nb2/3)O3 relaxor ferroelectric ceramics using a reaction-sintering process

(Ba_xPb_1−x)(Zn_1/3Nb_2/3)O₃ (BPZN; x = 0.06–0.1) relaxor ferroelectric ceramics produced using a reaction-sintering process were investigated. Without any calcination involved, the mixture of raw materials was pressed and sintered directly. BPZN ceramics of 100% perovskite phase were obtained. Highly dense BPZN ceramics with a density higher than 98.5% of theoretical density could be obtained. Maximum dielectric constant K_max 13,500 (at 75 °C), 19,600 (at 50 °C) and 14,800 (at 28 °C) at 1 kHz could be obtained in 6BPZN, 8BPZN and 10BPZN, respectively. Dielectric maximum temperature (T_max) in BPZN ceramics via reaction-sintering process is lower than BPZN ceramics prepared via B-site precursor route.     

Processing and physical properties of Al2O3/aluminum alloy composites

Porous aluminum oxide (Al₂O₃) preforms were formed by sintering in air at 1200 °C for 2 h. A356, 6061, and 1050 aluminum alloys were infiltrated into the preforms by squeeze casting in order to fabricate Al₂O₃/A356, Al₂O₃/6061, and Al₂O₃/1050 composites, respectively, with different volumes of aluminum alloy content. The content of aluminum alloy in the composites was 10–40% by volume. The resistivity of Al₂O₃/A356, Al₂O₃/6061, and Al₂O₃/1050 composites decreased dramatically from 6.41 × 10¹² to 9.77 × 10⁻⁴, 7.28 × 10⁻⁴, and 6.24 × 10⁻⁴ Ω m, respectively, the four-points bending strength increased from 397 to 443, 435.1, 407.2 MPa, respectively, and the deviations were smaller than 2%. From SEM microstructural analysis and TEM bright field images, the pore volume fraction and the relative density of the composites were the most important factors that affected the physical and mechanical properties. The ceramic phase and alloy phase in Al₂O₃/aluminum alloy composites were found to be homogenized and uniformly distributed using electrical and mechanical properties analysis, microstructure analysis, and image analysis.     

Corrosion mechanisms of Al2O3/MgAl2O4 by V2O5, NiO, Fe2O3 and vanadium slag

The effects of V₂O₅, NiO, Fe₂O₃ and vanadium slag on the corrosion of Al₂O₃ and MgAl₂O₄ have been investigated. The specimens of Al₂O₃ and MgAl₂O₄ with the respective oxides above mentioned were heated at 10 °C/min from room temperature up to three different temperatures: 1400, 1450 and 1500 °C. The corrosion mechanisms of each system were followed by XRD and SEM analyses. The results obtained showed that Al₂O₃ was less affected by the studied oxides than MgAl₂O₄. Alumina was only attacked by NiO forming NiAl₂O₄ spinel, while the MgAl₂O₄ spinel was attacked by V₂O₅ forming MgV₂O₆. It was also observed that Fe₂O₃ and Mg, Ni, V and Fe present in the vanadium slag diffused into Al₂O₃. On the other hand, the Fe₂O₃ and Ca, S, Si, Na, Mg, V and Fe diffused into the MgAl₂O₄ structure. Finally, the results obtained were compared with those predicted by the FactSage software.     

Hydrogen production by oxidative steam reforming of methanol using ceria promoted copper–alumina catalysts

The performance of different Cu/CeO₂/Al₂O₃ catalysts of varying compositions is investigated for the oxidative steam reforming of methanol (OSRM) in order to produce the hydrogen selectively for polymer electrolyte membrane (PEM) fuel cell applications. All the catalysts were prepared by co-precipitation method and characterized for their surface area, pore volume and oxidation–reduction behavior. The effect of various operating parameters studied are as follows: reaction temperature (200–300 °C), contact-time (W/F = 3–15 kg_cat s mol^− 1) and oxygen to methanol (O/M) molar ratio (0–0.5). The steam to methanol (S/M) molar ratio = 1.5 and pressure = 1 atm were kept constant. Among all the catalysts studied, catalyst Cu–Ce–Al:30–20–50 exhibited 100% methanol conversion and 179 mmol s^− 1 kg_cat^− 1 hydrogen production rate at 280 °C with carbon monoxide formation as low as 0.19%. The high catalytic activity and hydrogen selectivity shown by ceria promoted Cu/Al₂O₃ catalysts is attributed to the improved specific surface area, dispersion and reducibility of copper which were confirmed by characterizing the catalysts through temperature programmed reduction (TPR), CO chemisorption, X-ray diffraction (XRD) and N₂ adsorption–desorption studies. Reaction parameters were optimized in order to produce hydrogen with carbon monoxide formation as low as possible. The time-on-stream stability test showed that the Cu/CeO₂/Al₂O₃ catalysts were quite stable.     

Brazing of Al2O3 to Ti-6Al-4V alloy with in situ synthesized TiB-whisker-reinforced active brazing alloy

65.9Cu-24.4Ti-9.7TiB₂ (wt.%) composite filler was used to join Al₂O₃ and Ti-6Al-4V alloy. 30 vol.% TiB whiskers were in situ synthesized as reinforcements in joints. Brazing temperature was 890 °C, 910 °C, 930 °C, 950 °C and 970 °C, and the holding time was 0, 5, 10, 20, and 30 min. The microstructure and mechanical properties of brazed joints were analyzed by scanning electron microscope equipped with energy dispersive spectrometer, shear test and nano-indentation test. Results show that reaction layer Ti₄(Cu,Al)₂O forms at Al₂O₃/brazing alloy interface. The reaction between TiB₂ powders and Ti atoms in brazing alloy brings on in situ synthesizing TiB whiskers in (Ti,Al)₂Cu and AlCu₂Ti intermetallics. Formation of TiB whiskers minimizes the mismatch of thermal expansion coefficient between Al₂O₃ and brazing alloy, and makes the ductile-rigid-ductile multiple layer present in joints, which reduces residual stress of joints. The maximum shear strength of joints can reach 143.3 MPa when the brazing temperature is 930 °C, and holding time is 10 min.     

The performances of higher alcohol synthesis over nickel modified K2CO3/MoS2 catalyst

Ni modified K₂CO₃/MoS₂ catalyst was prepared and the performance of higher alcohol synthesis catalyst was investigated under the conditions: T = 280–340 °C, H₂/CO (molar radio) = 2.0, GHSV = 3000 h^− 1, and P = 10.0 MPa. Compared with conventional K₂CO₃/MoS₂ catalyst, Ni/K₂CO₃/MoS₂ catalyst showed higher activity and higher selectivity to C₂⁺OH. The optimum temperature range was 320–340 °C and the maximum space-time yield (STY) of alcohol 0.30 g/ml h was obtained at 320 °C. The selectivity to hydrocarbons over Ni/K₂CO₃/MoS₂ was higher, however, it was close to that of K₂CO₃/MoS₂ catalyst as the temperature increased. The results indicated that nickel was an efficient promoter to improve the activity and selectivity of K₂CO₃/MoS₂ catalyst.     

Fuel mixture approach for solution combustion synthesis of Ca3Al2O6 powders

Single-phase 3CaO·Al₂O₃ powders were prepared via solution combustion synthesis using a fuel mixture of urea and β-alanine. The concept of using this fuel mixture comes from the individual reactivity of calcium nitrate and aluminum nitrate with respect to urea and β-alanine. It was proved that urea is the optimum fuel for Al(NO₃)₃ whereas β-alanine is the most suitable fuel for Ca(NO₃)₂. X-ray diffraction and thermal analysis investigations revealed that heating at 300 °C the precursor mixture containing the desired metal nitrates, urea and β-alanine triggers a vigorous combustion reaction, which yields single-phase nanocrystalline 3CaO·Al₂O₃ powder (33.3 nm). In this case additional annealing was no longer required. The use of a single fuel failed to ensure the formation of 3CaO·Al₂O₃ directly from the combustion reaction. After annealing at 900 °C for 1 h, the powders obtained by using a single fuel (urea or β-alanine) developed a phase composition comprising of 3CaO·Al₂O₃, 12CaO·7Al₂O₃ and CaO.