Crystallization, structure and properties of plasticized poly(l-lactide)

Poly(l-lactide) (PLA) was plasticized with poly(ethylene glycol)s having M_w of 400 and 600 g/mol. In addition to poly(ethyne glycol)s with hydroxyl end groups, monomethyl ethers of poly(ethylene glycol) having M_w of 550 and 750 g/mol, with chains terminated with hydroxyl groups and methyl groups, were used. The effect of different end groups on the plasticization of both amorphous and semicrystalline PLA was studied. The crystallization, structure, thermal and tensile properties of PLA and PLA with 5 and 10 wt% of plasticizers were explored. No marked effect induced by different end groups of plasticizers was found. All the plasticizers used decreased T_g and increased the ability of PLA to cold crystallization. While an amorphous plasticized PLA could be deformed to about 550%, a semicrystalline PLA with the same total plasticizer content exhibited nonuniform plasticization of the amorphous phase and less ability to the plastic deformation. Nevertheless, a 20% elongation at break was achieved for a semicrystalline PLA with 10 wt% of the plasticizer. The plastic deformation of both neat and plasticized PLA was associated with crazing.     

Miscibility and hydrolytic degradation in alkaline solution of poly(l-lactide) and poly(methyl methacrylate) blends

Poly(l-lactide) (PLLA) was melt blended with poly(methyl methacrylate) (PMMA) using a two-roll mill. The miscibility and hydrolytic degradation of the blend films were characterized. It was found that PLLA/PMMA blend has high miscibility in the amorphous state because only single T_g was observed in the DSC and DMA measurements. In alkaline solution, the hydrolytic degradation rate of the blends whose PMMA content is higher than 30 wt% was decelerated while the rate of the blends whose PMMA content is lower than 30 wt% was accelerated. That is, the hydrolytic degradation rate of the blends could be widely controlled by PMMA content in the blend. It was also found that only PLLA was hydrolyzed and eluted into alkaline solution, while PMMA remained during alkaline hydrolysis.     

Mechanical properties, morphologies, and crystallization behavior of plasticized poly(l-lactide)/poly(butylene succinate-co-l-lactate) blends

The blends of poly(l-lactide) (PLLA) with poly(butylene succinate-co-l-lactate) (PBSL) containing the lactate unit of ca. 3 mol% and Rikemal PL710 (RKM) which is a plasticizer mainly composed of diglycerine tetraacetate were prepared by melt-mixing and subsequent injection molding. The studied RKM content of the PLLA/PBSL/RKM blends was 0-20 wt%, and the PLLA/PBSL weight ratio was 100/0 to 80/20. Although elongation at break in the tensile test did not increase by the addition of 10 wt% RKM to PLLA, the addition of a small amount of PBSL to the PLLA/RKM blend caused a considerable increase of the elongation. The SEM and DSC analyses revealed that all the PLLA/PBSL/RKM blends are immiscible blends where the PBSL particles are finely dispersed, and that there is some compatibility between PLLA-rich phase and PBSL-rich phase in the amorphous state when the RKM content is 20 wt%. As a result of investigation of the crystallization behavior by DSC and polarized optical microscopic measurements, it was revealed that the addition of RKM causes the acceleration of crystalline growth rate at a lower annealing temperature, and the addition of PBSL mainly enhances the formation of PLLA crystal nucleus.     

Crystallization and morphology of stereocomplexes in nonequimolar mixtures of poly(l-lactic acid) with excess poly(d-lactic acid)

Crystallization of nonequimolar compositions of poly(d-lactic acid) with low-molecular-weight poly(l-lactic acid) (PDLA/LM_w-PLLA) blends leads to formation of various fractions of stereocomplexed PLA (sc-crystallites) and homocrystallites (PDLA or PLLA). For the PDLA/LM_w-PLLA blends within the composition window of LM_w-PLLA content between 30 and 50 wt%, only sc-crystal exists and no homocrystal is present. On the other hand, for PDLA/LM_w-PLLA blends with excess PDLA, e.g. PDLA/LM_w-PLLA = 90/10, atomic-force microscopy (AFM) characterization on various stages of crystallization of sc-PLA crystal with PDLA homocrystal shows a repetitive stacking of excess PDLA on pre-formed sc-PLA crystal serving as crystallizing templates. The crystallization initially begins with string-like (fibril-like) PDLA lamellae, followed with PDLA aggregating on sc-PLA crystal into a bead-on-string crystal, then growing to thicker irregularly-shaped dough-like lamellae. Repetitive growth cycle from strings to bead-on-string lamellae continues on top of the dough-like lamellae as new substrates, until ending impingement of the PDLA spherulites.     

Broadband dielectric spectroscopic characterization of the hydrolytic degradation of carboxylic acid-terminated poly(d,l-lactide) materials

Broadband dielectric spectroscopy was used to examine carboxylic acid-terminated poly(d,l-lactide) samples that were hydrolytically degraded in 7.4 pH phosphate buffer solutions at 37 °C. The dielectric spectral signatures of degraded samples were considerably more distinct than those of undegraded samples and a T_g-related relaxation associated with long range chain segmental mobility was seen. For both degraded and undegraded samples, a relaxation peak just beneath a DSC-based T_g was observed, which shifts to higher frequency with increasing temperature. Thus, this feature is assigned as the glass transition as viewed from the dielectric relaxation perspective. Linear segments on log-log plots of loss permittivity vs. frequency, in the low frequency regime, are attributed to d.c. conductivity. An upward shift in relaxation peak maximum, f_max, observed especially after 145 d of immersion in buffer, implies a decrease in the time scale of long range segmental motions with increased degradation time.Permittivity data for degraded and undegraded materials were fitted to the Havriliak-Negami equation with subtraction of the d.c. conductivity contribution to uncover pure relaxation peaks. Parameters extracted from these fits were used to construct Vogel-Fulcher-Tammann-Hesse (VFTH) curves and distribution of relaxation time, G(τ), curves for all samples. It was seen that the relaxation times for the α-transition in both degraded and undegraded samples showed VFTH temperature behavior. G(τ) curves showed a general broadening and shift to lower τ with degradation, which can be explained in terms of a broadening of molecular weight within degraded samples and faster chain motions.     

Dielectric study on dynamics and conformation of poly(d,l-lactic acid) in dilute and semi-dilute solutions

Fractionated samples of d,l-poly(lactic acid) (PLA) were prepared and the dielectric normal mode relaxation was studied for dilute and semi-dilute solutions of the PLA in a good solvent benzene. Results indicate that in the dilute regime the normal mode relaxation time is proportional to [η]M_w in agreement with the Rouse-Zimm theory, where [η] and M_w denote the intrinsic viscosity and weight average molecular weight, respectively. The dielectric relaxation strength which is proportional to the mean square end-to-end distance 〈r²〉 increases with increasing M_w with the power of 2ν, where ν is the excluded volume parameter determined from [η]. The relaxation time in the semi-dilute regime increases with increasing concentration C due to increases of the entanglement density and the friction coefficient. The relaxation time corrected to the iso-friction state agrees approximately with the dynamic scaling theories. The relaxation strength decreases with increasing concentration indicating that 〈r²〉 decreases on account of the screening of the excluded volume effect. The concentration dependence of 〈r²〉 agrees approximately with the scaling theory proposed by Daoud and Jannink.     

Controlled crystal nucleation in the melt-crystallization of poly(l-lactide) and poly(l-lactide)/poly(d-lactide) stereocomplex

Among the various inorganic nucleators examined, Talc and an aluminum complex of a phosphoric ester combined with hydrotalcite (NA) were found to be effective for the melt-crystallization of poly(l-lactide) (PLLA) and PLLA/poly(d-lactide) (PDLA) stereo mixture, respectively. NA (1.0 phr (per one hundred resin)) can exclusively nucleate the stereocomplex crystals, while Talc cannot suppress the homo crystallization of PLLA and PDLA in the stereo mixture. Double use of Talc and NA (in 1.0 phr each) is highly effective for enhancing the crystallization temperature of the stereo complex without forming the homo crystals. The stereocomplex crystals nucleated by NA show a significantly lower melting temperature (207 °C) than the single crystal of the stereocomplex (230 °C) in spite of recording a large heat of crystallization ΔH_c (54 J/g). Photomicrographic study suggests that the spherulites with a symmetric morphology are formed in the stereo mixture added with NA while the spherulites do not grow in size in the mixture added with Talc. The exclusive growth of the stereocomplex crystals by the melt-crystallization process will open a processing window for the PLLA/PDLA.     

Spherulite growth of l-lactide copolymers: Effects of tacticity and comonomers

The spherulite growth behavior and mechanism of l-lactide copolymers, poly(l-lactide-co-d-lactide) [P(LLA-DLA)], poly(l-lactide-co-glycolide) [P(LLA-GA)], and poly(l-lactide-co-ε-caprolactone) [P(LLA-CL)] have been studied using polarization optical microscopy in comparison with poly(l-lactide) (PLLA) having different molecular weights to elucidate the effects of incorporated comonomer units. The incorporation of comonomer units reduced the radius growth rate of spherulites (G) and increased the induction period of spherulite formation (t_i), irrespective of the kind of comonomer unit. Such effects became remarkable with the content of comonomers. At a crystallization temperature (T_c) of 130 °C, the disturbance effects of comonomers on the spherulite growth decreased in the following order: d-lactide>glycolide>ε-caprolactone, when compared at the same comonomer unit or reciprocal of averaged l-lactyl unit sequence length (l_l). The t_i estimation indicated that the glycolide units have the lowest disturbance effects on the formation of spherulite (crystallite) nuclei. The PLLA having the number-average molecular weight (M_n) exceeding 3.1×10⁴ g mol⁻¹ showed the transition from regime II to regime III at T_c=120 °C, whereas PLLA with the lowest M_n of 9.2×10³ g mol⁻¹ crystallized solely in regime III kinetics and the copolymers excluding P(LLA-DLA) with 3% of d-lactide units crystallized solely according to regime II kinetics. The nucleation and front constant for regime II and III [K_g(II), K_g(III), G₀(II), and G₀(III), respectively] estimated with each (not with a fixed for high-molecular-weight PLLA) decreased with increasing the amount of defects per unit mass of the polymer for crystallization, i.e. with increasing the comonomer content and the density of terminal group through decreasing the molecular weight.     

Synthesis and characterization of poly(l-glutamic acid)-block-poly(l-phenylalanine)

Poly(γ-benzyl l-glutamate)-block-poly(l-phenylalanine) was prepared via the ring opening polymerization of γ-benzyl l-glutamate N-carboxyanhydride and l-phenylalanine N-carboxyanhydride using n-butylamine·HCl as an initiator for the living polymerization. Polymerization was confirmed by ¹H-nuclear magnetic resonance spectroscopy and matrix assisted laser desorption ionization time of flight mass spectroscopy. After deprotection, the vesicular nanostructure of poly(l-glutamic acid)-block-poly(l-phenylalanine) particles was examined by transmission electron microscopy and dynamic light scattering. The pH-dependent properties of the nanoparticles were evaluated by means of ζ-potential and transmittance measurements. The results showed that the block copolypeptide could be prepared using simple techniques. Moreover, the easily prepared PGA-PPA block copolypeptide showed pH-dependent properties due to changes in the PGA ionization state as a function of pH; this characteristic could potentially be exploited for drug delivery applications.     

Crystallization behavior of poly(l-lactic acid)

The crystallization behavior of poly(l-lactic acid) was studied in the range of 80-160 °C. The peak crystallization time (τ_p) was defined and obtained from the crystallization isotherm measured with a differential scanning calorimeter (DSC). Isothermal crystallization temperature (T_c) dependence of log(τ_p) discretely changed at 113 °C (= T_b). The linear growth rate of spherulite, G, was measured with a polarizing microscope. The T_c dependence of G and the size of the spherulite also discretely changed at T_b. Crystal structures for samples isothermally crystallized at temperatures which were higher and lower than T_b were orthorhombic (α-form) and trigonal (β-form), respectively. The discrete change of the crystallization behavior was explained by the formation of different crystal.     

Melting behavior of poly(l-lactic acid): X-ray and DSC analyses of the melting process

To clarify the melting behavior of poly(l-lactic acid) (PLLA), the wide-angle X-ray diffraction patterns of the isothermally crystallized PLLA samples (ICSs) were successively obtained during heating. We have already suggested the discrete change in the crystallization behavior of PLLA at a crystallization temperature (T_c) of 113 °C (= T_b) and formation of two crystal modifications for the ICSs obtained in the temperature range T_c ≤ T_b and T_c ≥ T_b. It was elucidated from the change in the X-ray diffraction pattern that the phase transition from the low-temperature crystal modification (α′-form) to the high-temperature one (α-form) occurred in a range 155-165 °C for the ICSs(T_c ≤ T_b), and that the crystal structure for the ICSs(T_c ≥ T_b) did not change. Recrystallization during heating, which is the origin of the multiple melting behavior, was proved by the increase in the diffraction intensity before steep decrease due to the final melting. A temperature derivative curve of the X-ray diffraction intensity almost coincided with the DSC melting curve.     

Hydrolytic degradation of poly(d,l-lactide) as a function of end group: Carboxylic acid vs. hydroxyl

d,l-Lactide was initiated with 1,4-butanediol in the presence of stannous octoate catalyst to provide hydroxyl-terminated poly(d,l-lactide) at 5000 and 20,000 g/mol. Portions of these materials were reacted with succinic anhydride in the presence of 1-methylimidazole to convert the hydroxyl functionality to succinic acid-terminated polymers in relatively high yield. The four materials were placed in a 7.4 pH buffered saline solution at 37 °C and monitored up to 180 days for their relative moisture uptake and weight loss behaviors. Carboxylic acid functionality displayed a dramatic effect on the moisture uptake behaviors for the 5000 and 20,000 g/mol polymers when compared to their respective hydroxyl functional materials. Carboxylic acid functionality significantly increased the hydrolytic degradation rate and mass loss behavior for the 5000 g/mol material, but did not affect the hydrolytic degradation rate for the higher molecular weight sample. These results suggest that moisture uptake is not the rate limiting step for the hydrolytic degradation high molecular weight poly(d,l-lactide).     

Crystallization behavior of linear 1-arm and 2-arm poly(l-lactide)s: Effects of coinitiators

Linear 1-arm and 2-arm poly(l-lactide) [i.e., poly(l-lactic acid) (PLLA)] polymers having relatively low number-average molecular weights (M_n) (≤5 × 10⁴ g mol⁻¹) were synthesized by ring-opening polymerization of l-lactide initiated with tin(II) 2-ethylhexanoate (i.e., stannous octoate) and coinitiators of l-lactic acid, 1-dodecanol (i.e., lauryl alcohol), and ethylene glycol (these PLLA polymers are abbreviated as LA, DN, and EG, respectively). For M_n below 1.5 × 10⁴ g mol⁻¹, non-isothermal crystallization during heating and isothermal spherulite growth were disturbed in linear 2-arm PLLA (EG) compared to those in linear 1-arm PLLA (LA and DN). This finding indicates that the chain directional change, the incorporation of the coinitiator moiety as an impurity in the middle of the molecule, and their mixed effect disturbed the crystallization of linear 2-arm PLLA compared to that of linear 1-arm PLLA, in which the chain direction is unvaried and the coinitiator moiety is incorporated in the chain terminal. Also, the finding strongly suggests that the reported low crystallizability of multi-arm PLLA (arm number ≥ 3) compared to that of linear 1-arm PLLA is caused not only by the presence of branching points but also by the chain directional change, the incorporation of the coinitiator moiety in the middle of the molecule, and their mixed effect. The effects of the chain directional change and the position of the incorporated coinitiator moiety on the crystallization and physical properties of linear 1-arm and 2-arm PLLA decreased with an increase in M_n.     

Isothermal and non-isothermal crystallization behavior of poly(l-lactic acid): Effects of stereocomplex as nucleating agent

The effects of incorporated poly(d-lactic acid) (PDLA) as poly(lactic acid) (PLA) stereocomplex crystallites on the isothermal and non-isothermal crystallization behavior of poly(l-lactic acid) (PLLA) from the melt were investigated for a wide PDLA contents from 0.1 to 10 wt%. In isothermal crystallization from the melt, the radius growth rate of PLLA spherulites (crystallization temperature (T_c)≥125 °C), the induction period for PLLA spherulite formation (t_i) (T_c≥125 °C), the growth mechanism of PLLA crystallites (90 °C≤T_c≤150 °C), and the mechanical properties of the PLLA films were not affected by the incorporation of PDLA or the presence of stereocomplex crystallites as a nucleating agent. In contrast, the presence of stereocomplex crystallites significantly increased the number of PLLA spherulites per unit area or volume. In isothermal crystallization from the melt, at PDLA content of 10 wt%, the starting, half, and ending times for overall PLLA crystallization (t_c(S), t_c(1/2), and t_c(E), respectively) were much shorter than those at PDLA content of 0 wt%, due to the increased number of PLLA spherulites. Reversely, at PDLA content of 0.1 wt%, the t_c(S), t_c(1/2), and t_c(E) were longer than or similar to those at PDLA content of 0 wt%, probably due to the long t_i and the decreased number of spherulites. This seems to have been caused by free PDLA chains, which did not form stereocomplex crystallites. On the other hand, at PDLA contents of 0.3-3 wt%, the t_c(S), t_c(1/2), and t_c(E) were shorter than or similar to those at PDLA content of 0 wt% for the T_c range below 95 °C and above 125 °C, whereas this inclination was reversed for the T_c range of 100-120 °C. In the non-isothermal crystallization of as-cast or amorphous-made PLLA films during cooling from the melt, the addition of PDLA above 1 wt% was effective to accelerate overall PLLA crystallization. The X-ray diffractometry could trace the formation of stereocomplex crystallites in the melt-quenched PLLA films at PDLA contents above 1 wt%. This study revealed that the addition of small amounts of PDLA is effective to accelerate overall PLLA crystallization when the PDLA content and crystallization conditions are scrupulously selected.     

pH-dependent self-assembly of amphiphilic poly(l-glutamic acid)-block-poly(lactic-co-glycolic acid) copolymers

A novel biodegradable AB-type diblock copolymer poly(L-lactic- co-glycolic acid)-block-poly(l-glutamic acid) (PLGA-b-PGA) was synthesized by a macromolecular coupling reaction between carboxyl-terminated PLGA and amino-terminated poly(γ-benzyl-glutamate) (PBLG) and the subsequent elimination of the protecting benzyl group. The structures of PLGA-PGA and its precursors were confirmed by Fourier transform infrared spectroscopy (FT-IR), ¹H nuclear magnetic resonance (¹H NMR) spectroscopy and gel permeation chromatography (GPC). This synthetic strategy simplified a former synthesis process of polypeptide-poly(l-lactic acid)(PLA); by using this new synthetic route the molecular weight and block ratio of PLGA-PGA could be easily controlled by adjusting the chain length of PLGA/PGA. The pH sensitivity and self-assembly behavior of PLGA-PGA copolymer were investigated by environmental scanning electron microscopy (ESEM), transmission electron microscopy (TEM) and dynamic light scattering (DLS). The results showed that the copolymer exhibited high pH responses, and the morphologies of the copolymer aggregates underwent four stages orderly with the pH increase (pH = 3-9): a disorganized form, micelles, semi-vesicles with thick walls and vesicles. Such a pH-dependent self-assembly process of the copolymer is promising for drug control release and bio-applications.     

Functionalized micelles from new ABC polyglycidol-poly(ethylene oxide)-poly(d,l-lactide) terpolymers

New ABC type terpolymers of poly(ethoxyethyl glycidyl ether)/poly(ethylene oxide)/poly(d,l-lactide) were obtained by multi-mode anionic polymerization. After successive deprotection of the ethoxyethyl groups from the first block, highly hydroxyl functionalized copolymers of polyglycidol/poly(ethylene oxide)/poly(d,l-lactide) were obtained. These copolymers form elongated ellipsoidal micelles by direct dissolution in water. The micelles consist of a poly(d,l-lactide) core and stabilizing shell of polyglycidol/poly(ethylene oxide). The hydroxyl groups of polyglycidol blocks situated at the micelle surface provide high functionality, which could be engaged in further chemical modification resulting in a potential drug targeting agents. The micellization process of the copolymers in aqueous media was studied by hydrophobic dye solubilization, static and dynamic light scattering, and transmission electron microscopy.     

Transcrystalline structures of poly(l-lactide)

Poly(l-lactide) (PLLA) film containing transcrystalline (TC) structures can easily be obtained by placing PLLA films melted between two poly(tetrafluoroethylene) (PTFE) sheets, followed by isothermal crystallization at 122 °C. The fine structures of the PLLA-TC film were studied by various structural techniques such as X-ray diffractometry, optical microscopy and transmission electron microscopy. We also examined the purification effect upon the morphology of PLLA-TC film. The formation of the TC structures revealed that one-dimensional spherulitic growth occurred from the assembling impurities as nucleation agent near the PTFE substrate in the heterogeneous nucleation system. We found that the b-axis of PLLA crystal was parallel to the lamellae growth direction confirmed using X-ray diffraction. The precipitated PLLA film crystallized in a similar process exhibited scanty TC textures, suggesting that the existence of impurity in the PLLA sample was an important factor for the formation of those structures.     

Ring-opening polymerization of l-lactide catalyzed by a biocompatible calcium complex

A novel calcium complex, [(DAIP)₂Ca]₂ (where DAIP-H = 2-[(2-dimethylamino-ethylimino)methyl]phenol), is prepared in a one flask reaction by condensation of Ca(OMe)₂ with DAIP-H in toluene/THF. Experimental results show that in the presence of various alcohols, [(DAIP)₂Ca]₂ efficiently initiates the ring-opening polymerization of l-lactide in a controlled fashion, yielding polymers with expectative molecular weight and low polydispersity indexes. Furthermore, kinetic studies show a first-order dependency on both [LA] and [BnOH].     

Poly(l-lactic acid) short fibers prepared by solvent evaporation using sodium tripolyphosphate

A porous material consisting of biodegradable polymer fibers may be one of the best candidates for implants used in the regeneration of damaged tissue, because it has a continuous pore structure that would allow ingrowth of nutriments, tissues, blood vessels or cells. In the present work, short fibers of biodegradable poly(l-lactic acid) (PLLA) were successfully prepared by the dropwise addition of PLLA dissolved in methylene chloride to a poly(vinyl alcohol) (PVA) solution containing sodium tripolyphosphate with stirring. It was suggested that droplets of the PLLA solution form spheres coated with PVA, which are then deformed into fibrous shapes due to stirring. The length of fibers was 200-800 μm and was controlled by the stirring rate, the PLLA concentration of the droplets and the PVA concentration. A PLLA porous block could be easily prepared by sintering the PLLA fibers at 173 °C for 10 min. The material had a continuous pore structure with the average pore size of approximately 40 μm and porosity of about 80%.     

Poly(l-lactide) brushes on magnetic multiwalled carbon nanotubes by in-situ ring-opening polymerization

Biodegradable poly(l-lactide) (PLLA) has been covalently grafted onto the surface of magnetic multiwalled carbon nanotubes (m-MWCNTs) by in-situ ring-opening polymerization of lactide. The content of grafting PLLA can be controlled by adjusting the feed ratio of monomer to m-MWCNTs. FT-IR and Raman spectroscopy confirm that PLLA have been covalently attached to the sidewalls of m-MWCNTs. Thermal gravimetric analysis (TGA) indicates that the composites of PLLA grafted m-MWCNTs have a polymer weight percentage of ca. 25.6-33.7 wt%. The scanning eletron microscopy (SEM) and transmission electron microscopy (TEM) are utilized to image the PLLA grafted m-MWCNTs, showing relatively uniform polymer layer coated on the surface of m-MWCNTs. The composites of PLLA grafted m-MWCNTs exhibit superparamagnetic behavior at room temperature and are aligned under a low magnetic field.