Cu-P-Cr-Ni-Mo耐候钢高温变形奥氏体的动态再结晶

用Gleeble-3500热模拟试验机研究了Cu-P-Cr-Ni-Mo耐候钢(%:0.10C、0.075P、0.65Cr、0.22Ni、0.43Mo、0.28Cu)在应变速率0.01～1 s-1、温度850～1150℃时的动态再结晶行为,得出该钢奥氏体区的真应力-真应变曲线和动态再结晶图,分析了变形参数对峰值应力的影响和不同热变形时耐候钢的动态再结晶体积分数与真应变的关系,建立了该钢的奥氏体热变形方程、动态再结晶临界条件回归方程和奥氏体动态再结晶体积分数数学模型。结果表明,随变形温度升高,峰值应力下降;随变形速率增大,峰值应力升高;随Z参数增大即变形温度降低,应变速率增加,发生再结晶的临界应变εc和发生完全再结晶的应变εs均呈线性增加。     

热轧DP600双相钢变形抗力的研究

本文通过Gleeble-1500热模拟机进行单道次压缩试验研究了热轧DP600双相钢低温点和高温点的变形抗力规律,分析了变形温度、变形速率、变形量对变形抗力的影响。结果表明,温度是最主要的影响因素,变形抗力随温度的升高而降低;随变形速率和变形量的增加而增大。对实验数据进行了回归计算,得到了精确度较高的低温点(500~700 ℃)和高温点(700~1200 ℃)周纪华-管克智变形抗力数学模型。该模型可以为实际生产提供指导。     

2205双相不锈钢的高温变形行为研究

在Gleeble-1500热模拟试验机上进行热-力模拟试验,得到实验数据并分析试样的热塑性、变形抗力,并利用金相显微镜对其进行金相组织的分析。在950~1 200℃温度区间进行高温拉伸试验,绘制出样品的热塑性曲线与热强度曲线,通过热塑性曲线说明在950~1 200℃范围内具有良好的塑性,通过热强度曲线可以观察到屈服强度随温度的升高而降低;在变形温度为950~1 200℃,应变速率为0.1,1,5和10 s-1时进行高温压缩试验,绘制出真应力-应变曲线和变形抗力曲线,结果显示,变形抗力随应变量的增大而迅速达到最大值,而后趋于平缓,随着温度的升高,变形抗力呈下降的趋势。     

一种建筑用耐火钢变形抗力模型的建立

利用Gleeble-1500热模拟试验机对一种建筑用耐火钢进行了压缩试验，分析了变形温度、变形速率以及变形量对变形抗力的影响；在变形抗力σ与温度T的关系中，考虑了应变ε和应变速率ε的影响；在应变速率ε的影响指数中，考虑了温度的影响，建立了一种含Nb、Ti等微合金元素建筑用耐火钢应力峰值前的变形抗力模型。     

热轧参数对粗奥氏体晶粒铌钢变形抗力的影响

通过Thermecmastor-Z热模拟试验机,在900-1 050℃以变形速率1-20 s-1、真应变0-0．7研究了晶粒尺寸800μm的铌钢(％:0．05C、1．44Mn、0．13Nb)奥氏体控轧过程的变形抗力,并建立了变形抗力的回归方程。试验结果表明,随温度增高,铌钢在奥氏体区变形抗力递减;在同一温度下,随变形程度增加,钢的变形抗力增加;同时在给定变形程度下,变形抗力随变形速率增大而增大;变形抗力回归方程计算值与实测值相差≤5 MPa。     

SA-335P91耐热钢轧制过程变形抗力模型

利用热模拟试验机,在850~1 150℃、应变量为0.1~0.7和应变速率为1~50 s~(-1)的条件下对耐热钢P91进行高温单道次压缩试验,分析压缩变形温度、压缩变形量和变形速率对材料变形抗力的影响。结果表明,压缩变形温度对材料变形抗力的影响最大,变形温度与变形抗力对数间呈近似线性关系,变形速率和变形量对材料变形抗力也产生较大影响,材料压缩变形抗力受三者共同作用的影响。且在较高变形速率和较低应变速率时,动态再结晶过程都会受到抑制,低应变速率下金属畸变能较低,而高应变速率下金属来不及发生动态再结晶过程。利用多元非线性拟合回归建立了P91变形抗力模型,拟合结果与实测结果吻合程度较好。     

无取向电工钢HW600高温变形抗力的研究

在Gleeble-3500热/力模拟试验机上对HW600钢进行高温压缩试验,研究在不同试验条件下的变形抗力.试验结果表明:变形温度对变形抗力的影响最为显著,在相同的变形速率下,随着变形温度的升高,变形抗力降低;在同一变形温度下,变形速率增大,变形抗力增加;在同一变形温度、变形速率下,随着变形程度的增加,变形抗力急剧增大,真应变达到0.1后,变形抗力增加趋势变缓.     

12Cr2Mo1R钢的变形抗力研究

通过热模拟试验,研究了变形温度、变形速率、变形程度对12Cr2Mo1R钢变形抗力的影响,结果表明,在较低的温度和较高的变形速率下,12Cr2Mo1R钢变形抗力增加显著;在同一下变形程度下,随温度的升高,变形抗力降低。变形温度为800℃、变形速率为15 s-1时,变形抗力最大值为290 MPa;变形温度为1050℃、变形速率为1 s-1,变形抗力最小值为110 MPa。     

SPHC钢热变形行为的研究

 通过在Gleeble 3500热/力模拟实验机上的热压缩实验,研究不同热变形条件下SPHC钢的高温变形抗力,考察变形温度、应变速率及变形程度与变形抗力之间的关系,分析了SPHC钢的动态再结晶机理,最后建立了SPHC钢的变形抗力数学模型,通过回归分析可看出此模型有较高的拟合精度。     

基于Gleeble-1500热/力模拟实验机的轧机轧制力研究

在Gleeble-1500热/力模拟实验机的基础上,用QuikSim管理软件配套记录实验数据,测定Q345钢材的应力-应变曲线,并以Rp0.2作为材料的屈服极限值,得到不同条件下的变形抗力值.通过分析变形速度、变形温度对变形抗力的影响,表明随变形速度的增加,变形抗力提高;随变形温度的升高,变形抗力降低.根据实验所得变形抗力而计算的轧制力能很好的预测粗轧机的轧制力.     

Dynamic Recrystallization Behavior and Microstructure Evolution of Bridge Weathering Steel in Austenite Region

The austenite dynamic recrystallization (DRX) behavior and microstructure evolution of a bridge weathering steel was systematically investigated at a deformation temperature range of 800–1100°C and strain rate of 0.1–10 s^?1 by using hot compression test and optical microscopy. The stress exponent and hot deformation energy were obtained by regression method to determine thermal deformation constitutive equation. The curve of stress versus strain is used, combined with high order polynomial fitting, to accurately determine the critical value of DRX. The relationships between critical strain, critical stress, and Z parameter of the bridge weathering steel were obtained by regression method. Moreover, the influence factors of DRX kinetics of the bridge weathering steel were studied in the light of the experimental results. It is shown that the strain rate has a more significant effect on the rate of DRX than that of the deformation temperature, and there is almost 0.85 orders of magnitude increment in the rate of DRX as the strain rate increases an order of magnitude. The dynamically recrystallized grain size can be decreased with decreasing the deformation temperature and increasing the strain rate during the austenite deformation.     

Resistance of low-carbon microalloyed steel to deformation on hot pressure treatment

The resistance of low-carbon microalloy steel to deformation in hot pressure treatment is investigated. Three types of curves have been identified on the hot-compression diagram and may be used to judge the softening of the steel on deformation at 1050–700°C. The qualitative relation between the compressive strain rate and the temperature range corresponding to each type of curve is described. With increase in compressive strain rate, the resistance to deformation increases in both the γ and γ + α regions. The resistance to deformation is studied as a function of the temperature, with variation in the strain and strain rate. In addition, the strain-rate sensitivity and temperature sensitivity of the resistance to deformation (the mean yield point) are studied as a function of the temperature, the strain, and the strain rate. On the basis of the variation in the resistance to deformation with decrease in temperature, various methods of determining the temperature range of γ → α transformation in the given steels are considered.     

超高压气瓶钢34CrMo4H热压缩流変应力行为

采用Gleeble-3800型热模拟机试验研究了34CrMo4H钢在900～1200℃、应变速率0.1～10s^-1时的高温热压缩行为,分析了热压缩变形时材料的流变应力与变形温度、应变速率之间的关系,确定了该钢的流变应力本构方程。结果表明,34CrMo4H钢在热压缩时流变应力随形变温度的升高而减小,随应变速率的增加而增大。应变速率小于0.1 s^-1时,该钢应力-应变曲线表现出明显的动态再结晶特征。34CrMo4H级钢的变形激活能为395.45kJ/mol。     

RAFM钢应变补偿本构关系及热加工图

低活化铁素体/马氏体(RAFM)钢具有较低的辐照肿胀率和优异的力学性能,被认为是聚变堆首选的结构材料。然而,低活化钢强度高、冷塑性变形抗力大的特点,使其难以通过冷加工或低温加工实现大规模生产。使用MMS-200型热模拟试验机,在变形温度为950～1 200℃、应变速率为0.1～5 s^-1和最大变形量为50%条件下,进行了低活化铁素体/马氏体钢(0.11C-9.4Cr-1.35W-0.22V-0.05Si-0.11Ta-0.50Mn)单道次热压缩试验,研究其热变形行为。基于动态材料模型构建了不同应变量下的低活化钢变形本构方程和热加工图,确定了最优热加工参数,结合金相结果分析了材料变形过程中微观组织演化规律,为低活化钢的热加工成形工艺及组织优化提供理论参考。结果表明,在相同应变速率下,随着变形温度升高,流变应力逐渐降低,在一定变形温度下,流变应力随应变速率增大而增大;温度和应变速率对组织的影响主要取决于变形过程中材料内部发生的动态回复和再结晶等机制的交互作用。使用六阶多项式拟合进行应变补偿建立的低活化钢变形本构方程具有较高的预测精度,平方相关系数为0.972。显微组织...     

半固态高碳工具钢的变形特性

采用Gleeble-1500热/力模拟机，对电磁搅拌法制备的高碳(碳含量大于1％)工具钢半固态坯料进行压缩实验，研究半固态高碳钢在不同变形温度、不同变形速率下的应力一应变关系，同时与相同冷却条件下的常规铸态坯料进行了对比分析。结果表明：在固一液两相区变形时，半固态坯料的流变应力明显低于常规铸态坯料，且随温度的升高而降低；当变形速率降低时，应力峰值升高，同时热软化现象明显。     

Q345B低温变形抗力模型及在矫直工艺中的应用

通过Gleeble-1500热模拟试验机对低合金钢Q345B φ10 mm × 30 mm圆件体试样在450～650℃以0.001～0.1s^-1变形速率进行真应变为0.15拉伸试验。结果表明,低温低变形速率状态下的变形抗力处于弹塑性变形区,线性段较长,当变形量大于0.06以后出现较明显塑性变形,变形抗力的变化规律与较高温状态基本类似。通过采集实验数据,应用Origin软件通过多元非线性回归建立了Q345B钢变形抗力的数学模型。应用该模型结合矫直理论公式计算了中厚板9辊矫直机矫直力,计算结果的相对误差为0.01%～6.71%。     

SAE9310钢热变形行为的研究

利用Gleeble-3500热力模拟试验机,在温度为1123~1423 K,应变速率为0.1~10 s-1,真应变为0.8的条件下,对一种传动部件用高强度渗碳钢(SAE9310钢)进行了高温轴向压缩试验,测得了SAE9310钢的高温流变曲线,并观察其变形后的显微组织。试验结果表明,SAE9310钢的流变应力和峰值应变随着变形温度的升高和应变速率的降低而减小;SAE9310钢在真应变为0.8的条件下,随着变形速率的提高,其发生完全动态再结晶的温度也逐渐升高,当热变形温度高于1323 K时,应变速率在0.1~10 s-1范围内,试验钢均会发生动态完全再结晶;测得9310钢的热变形激活能Q值为416.78 kJ/mol,并确立了其热变形方程。     

CL70车轮钢热压缩流变应力行为

用Gleeble-3800热模拟机研究了CL70车轮钢在应变速率0. 01～10s^-1、900～1300 ℃时的高温热压缩行为,分析了热压缩变形时该钢的流变应力、变形温度及应变速率之间的关系,通过线性回归确定该钢流变应力本构方程。结果表明,CL70钢在高温压缩时流变应力随变形温度的减小而增大,随应变速率升高而增大。当应变速率≤1 s^-1时,CL70钢的流变应力曲线表现为动态再结晶特征。CL70钢的热变形激活能为401.06 kJ/mol。