镁合金钨极氩弧焊接头深冷强化机制

针对镁合金焊接接头软化问题,文中提出了AZ31镁合金TIG焊接接头深冷强化方法,进行了镁合金TIG焊接工艺试验和焊接接头的-160℃,8 h深冷处理试验;深冷处理使镁合金焊接接头抗拉强度从212.4 MPa提高到246.6 MPa;用X射线衍射仪(XRD)和透射电子显微镜(TEM)等观测了焊接接头深冷前后的微观组织与结构,分析了焊接接头深冷强化机理.结果表明,深冷处理使镁合金TIG焊接接头形成亚晶结构,第二相Mg17Al12颗粒弥散析出,提高了基体连续性,第二相颗粒数量增加,使接头组织细化并获强化,深冷处理使焊接接头的晶粒发生转动与位错转化为位错环,使接头组织产生孪晶,强化了焊接接头.     

基于CDM法AZ31B镁合金焊接接头疲劳评定

采用临界距离法(CDM)中的点法和线法对AZ31B镁合金对接接头和横向十字接头进行疲劳评定.对两种焊接接头进行了疲劳试验,采用ANSYS有限元软件建模分析,计算出两种评定方法的局部应力参量Δσloc,拟合出相应的S-N曲线,并与疲劳试验结果进行了对比分析.结果表明,采用CDM法可以对镁合金焊接接头进行疲劳评定,其评定结果与疲劳试验结果相符合.依据应力集中大小可以有效预测疲劳断裂位置,在2×106循环次数下,两种焊接接头点法的疲劳强度分别为79.55和49.10MPa,线法的疲劳强度分别为79.01和44.38MPa.     

Improving the fatigue property of welded joints for AZ31 magnesium alloy by ultrasonic peening treatment

The fatigue property of AZ31 magnesium alloy and its TIG welded joints were investigated. The ultrasonic peening treatment (UPT) was used to improve the fatigue property of the TIG welded joints, which was treated at the weld toe by the UPT process. The test results show that the fatigue strength of the base metal of AZ31 magnesium alloys is 57.8 MPa, and those of the fillet joint and the transverse cross joint are respectively 20.0 MPa and 17.2 MPa at 2×106 cycles. The fatigue strengths of two kinds of welded joints treated by the UPT are respectively 30.3 MPa and 24.7 MPa, which have been improved by 51.5% and 43.6%, respectively. The fatigue life of the fillet joint specimens is prolonged by about 2.74 times and the fatigue life of the transverse cross joint specimens is prolonged by about 1.05 times when the stress range is at 40.0 MPa.     

Fatigue crack growth behaviour of pulsed current gas tungsten arc, friction stir and laser beam welded AZ31B magnesium alloy joints

The laser beam welded joints offered better resistance against the growing fatigue cracks compared to friction stir welded and pulsed current gas tungsten arc welded AZ31B magnesium alloy joints. The formation of very fine grains in weld region, higher fusion zone hardness, uniformly distributed fine precipitates and favourable residual stress field of the weld region are the main reasons for superior fatigue performance of laser beam welded joints of AZ31B magnesium alloy.     

微弧表面处理对AZ31B镁合金耐腐蚀及耐腐蚀疲劳性能的影响

采用微弧表面处理技术(微弧氧化MAO和微弧复合MCC)在AZ31B镁合金基体上制备出不同断面结构的防护涂层。通过电化学腐蚀及腐蚀疲劳测试方法,研究了MAO、MCC涂层的电化学腐蚀及腐蚀疲劳性能。结果表明,生长10 min的MAO涂层具有较好的耐电化学腐蚀性能。MAO涂层表面存在微孔和微裂纹,在应力条件下微孔和微裂纹作为疲劳断裂的裂纹萌生点,可加速裂纹的萌生与扩展,使其腐蚀疲劳寿命相较AZ31B合金基体降低了55%。而具有MCC涂层的AZ31B合金试样腐蚀疲劳极限为(64.0±5.4) MPa,比AZ31B合金基体提高了59%。在低应力载荷下(＜80 MPa),微弧复合涂层试样的腐蚀疲劳强度得到明显提高。     

AZ31B/LY12的搅拌摩擦焊研究

针对异种材料AZ31B镁合金与LY12铝合金进行了搅拌摩擦焊技术研究,结果表明,当选定恰当的焊接工艺参数时,AZ31B/LY12搅拌摩擦焊接是可行的,能得到外观形貌基本良好的接头.同时镁铝合金的片层结构由于材料的彼此挤压而相互挤入,发生明显的变形,从而导致焊接接头的力学性能较母材有所降低.     

铝合金焊接接头冲击强化的性能

为了提高铝合金焊接接头的力学性能,试验分别采用超声波和调Q脉冲YAG激光对A6061-T6铝合金焊接接头焊趾附近处进行冲击强化,研究了超声波和激光冲击强化下铝合金焊接接头的性能.两种冲击强化模式下,铝合金焊接接头焊趾处近表面均发生了冲击强化效果,并产生了较大的残余压应力,超声波和激光冲击强化后产生的最大残余压应力分别为 -158 MPa和 -145 MPa左右.超声波与激光冲击强化铝合金焊接接头的疲劳寿命差别不大,均比焊态下试样的疲劳寿命提高1倍以上.两种冲击强化方法的疲劳试验样件断裂位置均发生在基体金属上,而焊趾处没有疲劳裂纹产生.     

TIG填锌丝对接焊接镁铝异种金属

采用普通TIG电弧作为焊接热源,对镁铝异种金属进行填加锌丝的对接焊试验.并利用金相显微镜、电子探针（EPMA）、万能力学性能拉伸机等现代分析手段对所得到的接头进行测试分析.结果表明,采用这种工艺得到了锌基的合金化焊缝,实现了6061铝合金和AZ31B镁合金的连接,焊缝主要由MgZn2和少量的铝、锌的固溶体构成,焊缝和铝...     

Improving wear resistance and corrosion resistance of AZ31 magnesium alloy by DLC/AlN/Al coating

A novel protective coating, consisting of three layers (top: diamond-like carbon, middle: aluminum nitride, bottom: aluminum), was deposited on the surface of AZ31 magnesium alloy layer by layer. Nano-indenter, electrochemical system and tribological tester were performed to investigate the hardness, wear resistance and corrosion resistance of the coated AZ31 magnesium alloy, respectively. The DLC/AlN/Al coating improved the magnesium alloy's surface hardness and reduced its friction coefficient, which consequently induced a great improvement of the magnesium alloy's wear resistance. Furthermore, the corrosion resistance of the AZ31 magnesium alloy with the DLC/AlN/Al coating was also enhanced with the corrosion current density decreasing from 2.25 × 10⁻⁵ A/cm² to 1.28 × 10⁻⁶ A/cm² in a 3.5 wt.% NaCl solution.     

工艺参数对镁合金焊接接头力学性能的影响

采用GTAW焊接5mm厚的AZ31镁板.通过对接头力学性能和显微组织分析,研究工艺参数对AZ31焊接接头组织和性能的影响.试验结果表明,焊接电流通过作用于焊接线能最影响晶粒结晶过程.当焊接电流为70A时,镁合金焊接接头的力学性能达到最佳值.此时,焊接接头的成型系数为3.51,抗拉强度为201.7MPa,断面收缩率为8.4%,伸长率为12.18%,硬度为62.3HV.     

Friction stir welding of AZ31 magnesium alloy

Friction stir welding (FSW) is an new solid-phase joining technology which has more advantages over fusion welding methods in welding of aluminum and other non-ferrous metals. The effects of welding parameters on mechanical properties and microstructure during friction stir welding of AZ31 magnesium alloy were studied in this paper. Microstructures and mechanical properties of the joints were investigated by means of optical microscopy, scanning electric microscopy ( SEM ) , micro-hardness analysis, and tensile test. Experimental results show that the magnesium alloy can be successfully welded by FSW method, and the ultimate tensile strength (UTS) of FSW joint reaches up to 90 percent of base metal. The microstructures of welded joints exhibit the variation from dynamically recrystallized fine grains to greatly deformed grains. Hardness in nugget zone was found lower than the base metal but not too obvious.     

磁场下镁合金A-TIG接头成形性及显微组织分析

在对5 mm厚的AZ31B镁合金板材进行A-TIG焊焊接过程中引入外加纵向磁场,试验所用的活性剂是以氧化物为基的活性剂,试验中改变磁场参数,对焊接接头的成形性、组织及性能进行试验和检测,研究磁场参数对镁合金A-TIG焊过程的影响规律.结果表明,活性剂及磁场共同作用可以改善焊接接头的成形性和组织形态,在磁场频率为10 Hz,磁场电流为2 A时,焊接接头的成形系数和性能得到了最佳值,此时成形系数为2.304,硬度为980.98 MPa;外加磁场通过电磁搅拌作用与活性剂相结合,改变了熔池的流行形态,使金属液由四周向中心流动并伴有搅拌,进而使焊缝熔深增大的同时细化组织,改善接头力学性能.     

Fatigue behavior of friction stir spot welded AZ31 Mg alloy sheet joints

The fatigue behavior of friction stir spot welded (FSSW) AZ31 magnesium alloy sheet joints was investigated by tension–compression of fatigue test. The results suggest that all the fatigue failures occur at the stir zone of the FSSW AZ31 sheet joints, and all cracks initiate at the stir zone outer edge between the upper and lower sheet. When the cycle force equals 1 kN, the crack propagates along the interface of heat-affected zone and thermo-mechanical zone, simultaneously across the direction of force; while the cycle force equals 3 kN, the crack propagates along the diameter of stir zone and shear failure occurs finally. Moreover, the transverse microsections indicate that there is a tongue-like region at the outer edge of stir zone between the two AZ31 sheets, and the direction of tongue-like region is toward outside of the stirred zone and all fatigue cracks initiate at the tongue-like region.     

Stirring brazing of dissimilar Al/Mg alloy without flux in air

AZ31B magnesium alloy and 2024 aluminum alloy were successfully jointed at aid of mechanical stirring with Sn-Zn-Al filler metal. The microstructure, fracture morphologies, and mechanical properties of joint were investigated. The results show that Mg-Al intermetallic compounds can be avoided by the process. But, a small quantity of porosity is found in the joint. The sheafing strength of joint interface adjacent to magnesium alloy is 35.4 MPa for formation of Mg-Sn intermetallic compounds, which is about 46 % of that of filler metal. While, the shearing strength of joint interfaces adjacent to aluminum alloy is 70.4 MPa for formation of Zn-Sn-Al solid solution, which is about 92 % of that of filler metal.     

轧制工艺对AZ31B镁合金薄板组织与性能的影响

研究了轧制温度和轧制速度对AZ31B镁合金薄板微观组织演变和力学性能的影响。结果表明,轧辊加热有利于镁合金薄板成型;AZ31B镁合金在低温或低速轧制时薄板纵向组织为大量的切变带,切变带区域包含大量孪晶组织,横向组织为含极少量孪晶的等轴晶组织;在轧制温度为400℃和轧制速度为16m/min轧制时,由于动态再结晶,横纵截面组织均为等轴晶。AZ31镁合金薄板的最佳轧制制度为轧辊温度为70℃、轧制温度为400℃、轧制速度为6m/min,此工艺轧制的薄板横向抗拉强度、屈服强度和伸长率分别为350MPa、300MPa和12%,纵向为345MPa、290MPa和11.2%,纵向与横向性能差别明显减小。     

AZ31镁合金及其TIG焊接接头断裂机理研究

对AZ31镁合金及其焊接接头进行拉伸、冲击和疲劳试验,分析了镁合金的断裂机理及疲劳裂纹扩展方向.母材拉伸试验结果表明,试样几乎没有缩颈,抗拉强度为236.29 MPa;焊接接头的抗拉强度为185.68 MPa,拉伸断裂从焊接接头焊趾部位启裂,抗拉强度为母材的78%.冲击试验在-80～340 ℃进行,结果表明,在较低温度下AZ31镁合金冲击韧性较小,断口为准解理形貌的脆性断裂;随着温度的增加,断裂形式由准解理+韧窝形貌的混合断裂过渡为韧性断裂;在常温下焊缝中心的冲击韧性比母材的高,但热影响区的冲击韧性较差.AZ31B镁合金母材的疲劳强度为66.72 MPa,对接接头的疲劳强度为39.00 MPa;母材疲劳断口由解理台阶组成,为脆性断裂;焊接接头疲劳断口由解理和准解理台阶组成,为脆性断裂.     

AZ31B镁合金及其焊接接头的疲劳断裂机理

对AZ31B镁合金进行疲劳实验,在2×106循环次数下,母材、对接接头、横向十字接头和侧面连接接头的疲劳强度分别为66.72,39.00,24.38和24.40MPa。采用光学显微镜对裂纹扩展特征进行分析,结果表明,AZ31B母材的疲劳裂纹宏观扩展路径平滑,但微观观察发现疲劳裂纹扩展方向曲弯,有些裂纹分成两岔;裂纹尖端扩展均为沿晶扩展。焊接接头裂纹均在焊趾部位起裂,对接接头和横线十字接头的裂纹沿着热影响区扩展;侧面连接接头的裂纹起裂位于焊脚部位。采用扫描电子显微镜对疲劳断裂机理进行分析。疲劳断口由准解理或解理台阶组成,均为脆性断裂,断口中存在二次裂纹,对接接头中存在疲劳条纹,其间距约为5μm。     

Effects of pin diameter on microstructures and mechanical properties of friction stir spot welded AZ31B magnesium alloy joints

Abstract

The effects of pin diameter on the microstructure and mechanical properties of friction stir spot welded AZ31B magnesium alloy joints were investigated using microstructural observations, tensile tests and microhardness tests. The results showed that with an increase in the pin diameter, the height and width of the curved interface in the friction stir spot welded AZ31B magnesium alloy joints increased because of the strong effect of stirring and high temperature obtained when large sized pins were adopted. An increase in the pin diameter led to the coarsening of α-Mg grains in the stir zone, thermomechanical affected zone and heat affected zone because of heat generation, resulting in the decrease in microhardness of stir zone, thermomechanical affected zone and heat affected zone. The tensile shear force of the friction stir spot welded AZ31B magnesium alloy joints increased with the increase in pin diameter because the height and width of the curved interface dominated the failure of the specimens.     

镁合金AZ31搅拌摩擦焊接头的微观组织

采用搅拌摩擦焊接法焊接了镁合金AZ31, 研究了焊接参数对焊接接头微观组织和显微硬度的影响. 结果表明 焊接接头成形良好, 焊缝没有气孔、裂纹和夹渣, 焊缝区的显微硬度比母材稍有降低, 但降低幅度不大.     

Effect of antimony on microstructure and performance of AZ31 magnesium alloy welded joint

0Introduction Magnesiumalloyisthelighteststructuralmetalinin dustrialapplicationwithhighspecificstrengthandrigidity, gooddimensionalstability.Forthisreasonmagnesiumal loyshavehighpotentialforusingasstructuralpartsinau tomobileandelectronicdeviceapplica…