Texture of Cold Rolled Strip of Fe-3Si Steel Produced by Thin Slab Casting and Rolling

 The hot rolled strip of Fe-3Si steel was experimentally produced by thin slab casting and rolling (TSCR) process in the laboratory. The texture evolution rule was investigated during hot rolling and cold rolling. The texture distribution of cold rolled strips with four kinds of cold rolling reduction schedules was observed through X-ray diffraction method, and the orientation density variation of 1/16 layer, 1/8 layer, 1/4 layer, and 1/2 layer in thickness was analyzed. The cold rolled texture of steel A with four kinds of cold rolling reduction schedules was mainly composed of α and γ fibers. Cold rolling reduction ratio of 70% was more beneficial for obtaining more γ fibers. The γ fiber texture orientation density of {111}<011> and {111}<1 12> was the largest on the 1/8 layer and 1/4 layer and the least on the 1/16 layer and 1/2 layer for steel B. The texture orientation density of {001}-{223}<110> in the α fibers for steel C was increased, but the texture orientation density of {332}-{110}<110> was low.     

大压下率冷轧无取向硅钢织构演变及性能

组织和织构是影响无取向硅钢性能的重要因素。为改善产品性能,研究了冷轧压下率(71.7%~87.0%)对高牌号无取向硅钢组织、织构、磁性能和力学性能的影响。结果表明,随冷轧压下率的增加,退火晶粒平均尺寸先减小后增大;高斯和立方织构强度减弱,γ纤维织构增强,α纤维织构转变为较强的α*({ h, 1, 1}〈1/h, 1, 2〉)织构,并随冷轧压下率的增加而增强,同时其峰值逐渐向{111}面移动;工频铁损P1.5/50、高频铁损P1.0/400和磁极化强度J5000同时降低,屈服强度变化不大,表面硬度逐渐增加。当冷轧压下率由84.7%增至87.0%、厚度减至0.30 mm时,高频铁损降幅是工频铁损的11倍,表面硬度增幅变大。以上研究成果对硅钢减薄后织构及组织的优化提供了很好的指导。     

Fe-6.5%Si钢极薄带的试制

 为了研究Fe-6.5%Si钢极薄带的制备工艺,并获得良好的产品磁性能,以薄带铸轧试验机制备的6.5%Si钢铸带为原料,分别采用一次温轧法、二次温轧法和基于应变诱导无序(DID)原理的高硅钢室温冷轧3种工艺制备出厚度为0.1 mm的Fe-6.5%Si钢。分析结果显示,一次温轧法退火后以高强度γ织构为主,由于压下率达到90%,形变储能高,晶粒尺寸最大,铁损最低,同时磁感也最低;二次温轧的退火板除了γ织构外,还有较强的η织构,故其磁感值高于一次温轧法,该方法得到的6.5%Si钢薄带综合磁性能最优,但生产成本高,效率低;基于DID原理,对6.5%Si钢热轧板在温度为300～450 ℃、压下率为45%～65%的条件下进行温轧,实现了6.5%Si钢软化,随后可将6.5%Si钢室温冷轧至0.1 mm,此时温轧板和冷轧板内部有序相消失,基体变成无序态;室温冷轧板退火后晶粒更细,铁损略有升高。此外,室温冷轧可促进{111}<112>形变晶粒在冷轧剪切带中形核形成有利织构,因此磁感值得到更大提升;采用DID原理进行室温冷轧,效率较高,后续可通过优化退火工艺使其进一步降低铁损,该方法为薄带铸轧工艺批量生产磁性能优异的6.5%Si钢极薄带提供技术参考。     

冷轧压下率对无抑制剂取向硅钢初次再结晶退火的影响

对无抑制剂取向硅钢不同压下率下初次再结晶退火后的显微组织、宏观织构和微观织构进行了研究.结果表明,冷轧板织构主要为α取向线{001}＜110＞、{112}＜110＞和{111}＜110＞织构以及γ取向线{111}＜110＞织构.初次再结晶退火后,α取向线织构减弱,织构主要为γ取向线{111}＜112＞织构.随冷轧压下率的增加,冷轧和初次再结晶织构强度增加.当压下率为88％时,初次再结晶退火后 Goss 织构和{111}＜112＞织构强度最高,最有利于发生二次再结晶.EBSD 分析显示,Goss 取向晶粒大多与{111}＜112＞取向晶粒相邻.提高冷轧压下率,Goss取向晶粒和{111}＜112＞取向晶粒都增加,Goss 取向晶粒偏离理想取向角度减少.     

Effects of Rolling Parameters on Texture and Formability of High Strength Ultra-Low Carbon BH Steel

 The effects of hot rolling and cold rolling parameters on texture and r (plastic strain ratio) value of high strength ultra low carbon bake hardening (ULC-BH) steels are studied with orientation distribution function (ODF) structural analysis method. After hot rolling, the high strength ULC-BH steel sheet has weak γ-fiber with uniform orientation distributions, and weak α-fiber, of which {445}<110> component forms a high intensity peak at coiling temperature of 750 ℃. After cold rolling, both {111}<110>-{111}<112> intensity on the γ-fiber and {111}-{112}<110> intensity on the α-fiber enhanced. As a result of substitutional solute elements Mn and P being added to the steel, strong {112}<110> deformation texture component is observed on α-fiber, especially at 80% cold rolling reduction, and this leads to the strong {111}<112> recrystallization texture after annealing. The increase of cold rolling reduction shifts the maximum intensity on the γ-fiber from {111}<112> to {111}<113>. After annealing, a very strong γ-fiber is obtained, with intensity peak at {111}<112> component when cold rolling reduction reaches 80%. Increasing coiling temperature and cold rolling reduction improve γ-fiber intensity and r value, resulting in good deep drawability.     

Texture of Hot Rolled Strip for Fe-3Si Steel Produced by Thin Slab Casting and Rolling

 Fe-3%Si steel strip was experimental produced by thin slab casting and rolling (TSCR) process in the laboratory. The microstructure and texture of hot rolled strip by different total reduction and rolling schedule was observed through EBSD technique and X-ray diffraction method. The changeable rule of texture density on the α、ε and γ, and fibers was analyzed. When the total reduction was increased from 82.9% to 97.1%,the gradient of microstructure and texture for A steel surface layer and center layer was found, {001}&;#8249;110&;#8250; texture had higher intensity, and {001}&;#8249;110&;#8250; texture was changed to     

Optimizing Cold Rolling and Mode of Annealing of Interstitial‐Free High‐Strength Steel Sheets

Percentage of cold rolling and mode of annealing significantly influence the formation of structures and textures of steel sheets. The objective is to co‐relate the micro‐structures and textures at each step of processing and their effect on mechanical properties. In addition, an attempt has been made to distinguish the batch and continuous mode of annealing. In the present investigation, interstitial free high strength (IF‐HS) steel was first hot rolled to 85‐90%, followed by cold rolling (CR) and then annealed. Annealing was carried out in the batch as well as the continuous mode. It was found that a fine pancake type and strong hot band texture was developed after hot rolling. Its very strong orientations were and . An almost uniform α‐fibre and γ‐fibre were developed at 80% cold reduction. After annealing, the new γ‐fibre was found to be developed replacing the old one for both modes of annealing i.e. batch and continuous. Further, it was observed that the intensity of the γ‐fibre was higher at 80% CR after continuous annealing than after batch annealing. The strain energy introduced during cold rolling could not be removed completely in batch annealing. Therefore, the drawability obtained through continuous annealing was higher than that after batch annealing. The process route of 80% CR and annealing, either in batch or in continuous mode, has developed optimum strength and drawability in steel sheets. Either batch or continuous mode can be used for annealing to cold rolled IF‐HS steel sheets, but the latter one is found to be superior to the former one.     

超低碳烘烤硬化钢板的织构

 研究了罩式退火生产的Ti+Nb超低碳烘烤硬化钢板的织构。主要包括不同冷轧压下率条件下生产的冷轧板和退火板的织构,热轧、冷轧和退火织构演变,退火板不同厚度处的织构。结果表明,在冷轧压下率80%条件下生产的退火板在γ取向线上的织构较为强烈,具有较好的深冲性能;再结晶退火织构对形变织构具有明显的遗传性;退火板不同部位织构具有相似特征,中心{111}织构较多。     

冷轧压下率对IF钢织构的影响

采用CSP工艺生产厚度为3.5 mm的IF热轧钢板,分析了冷轧压下率对冷轧织构、退火织构、各组分含量、{111}/{100}比值的影响。结果表明,采用71.4%的冷轧压下率生产的IF钢{111}织构占比最大,最有利于冲压性能的提高。     

薄板坯连铸连轧流程Fe-3％Si钢冷轧板织构

在实验室按照薄板坯连铸连轧工艺流程试制了Fe-3％Si硅钢热轧板,按照四种冷轧变形制度将热轧板冷轧后采用X射线衍射方法观察了织构分布,分析了14／16层、H／8层、H／4层、H／2层的取向密度变化,研究了热轧和冷轧过程的织构演变规律。试验研究结果为开发薄板坯连铸连轧短流程生产电工钢技术提供理论依据和参考数据。     

Effect of Cold Rolling Reduction Ratio on Microstructure and Magnetic Properties of Secondary Cold-Rolled High-Grade Nonoriented Silicon Steel

Trial production of 0.25 mm-thick thin-gauge high-grade nonoriented silicon steel with a Si content of 3.5% by the secondary cold rolling process is studied. The recrystallization microstructure and magnetic properties are systematically studied by the microstructure, texture evolution, and the effect of two-stage cold rolling reduction ratios (37.5–70.5%) during the whole process. The results show that the magnetic induction intensity B₅₀₀₀ first increases and then decreases; the iron loss first decreases and then increases at the frequencies of 50 and 400 Hz with the reduction of the cold rolling reduction rate in the second stage. The cubic and Goss texture of the finished annealed sheet has the highest strength when the reduction ratio of the second stage cold rolling is 58.3%. The highest magnetic induction intensity, B₅₀₀₀ = 1.671 T. Lowest iron loss, P_1.0/50 = 0.83 W kg⁻¹, P_1.5/50 = 1.98 W kg⁻¹, and P_1.0/400 = 11.94 W kg⁻¹, respectively.     

Textures and Properties of Hot Rolled High Strength Ti-IF Steels

The texture evolution in a high strength Ti-IF steel during the processing of hot rolling, cold rolling, and annealing is studied. For comparison, both ferrite rolling and austenite rolling are employed. It is found that the texture type is the. same after ferrite rolling and austenite rolling, but the texture intensity is much higher in the ferrite rolled sample. Furthermore, texture characteristics at the surface are absolutely different from those at the mid sec tion in both ferrite rolled and austenite rolled samples, as well as under the cold rolled and annealed conditions. The shear texture { 110 } 〈001 〉 disappears and orientation rotates along { 110 } 〈001 〉→ { 554 } 〈 225 〉→ { 111 } 〈 112 〉→{111}〈110〉→{223}〈110〉 during cold rolling. Compared to the austenite rolled sample, the properties of the cold rolled and annealed sheet which is subjected to ferrite rolling are higher.     

Microtexture Evolution and Grain Boundary Character Distribution of Interstitial-Free Steels With Moderate Levels of Cold Rolling Reductions

High-strength interstitial-free steel sheets have very good deep drawability when processed to have {111} recrystallization texture. The microtexture evolution and grain boundary character distribution of interstitial-free steels as a function of moderate levels of cold rolling reductions were investigated by the metallographic microscopy and electron backscatter diffraction technique. The results showed that there was a close relationship between microtexture and grain boundary character distribution for interstitial-free steel, especially the distribution and features of some specific types of coincident-site lattice boundaries. In addition, α-fiber texture was weakened to vanish while γ-fiber texture strengthened gradually as cold rolling reduction was increased from 20% to 75% for cold rolled and annealed samples. Accordingly, increasing the rolling reduction from 20% to 75% would lead to a significant increase in the proportion of Σ3 boundaries. Also, it was found that the microtexture of 20% cold rolled sample would induce a high frequency of Σ11 grain boundaries, but the microtexture of 75% cold rolled sample would produce more Σ7 and Σ17 grain boundaries. It was suggested that texture played a significant role in the formation of grain boundary character distribution.     

摩擦对IF钢铁素体区热轧和退火织构的影响

采用X射线衍射仪分析IF钢铁素体区热轧织构以及退火织构的演化,在实验室热轧机上进行了IF钢的铁素体区热轧,研究了摩擦对IF钢铁素体区热轧、退火织构的影响。结果表明：无润滑轧制时,钢板表层形成强高斯织构组分{110}〈001〉,弱γ纤维织构,导致再结晶织构中高斯组分强度高,γ纤维织构强度低;润滑轧制时,钢板表层高斯织构组分强度降低,{100}〈011〉、γ纤维织构强度提高,退火后γ纤维织构强度提高。钢板中心受摩擦作用影响较小,轧制过程中发展为较强的α和γ纤维织构,退火后γ纤维织构成为主要织构组分。     

薄板坯连铸连轧工艺下Hi-B钢的组织及织构

采用金相显微镜和扫描电镜研究实验室模拟薄板坯连铸连轧（TSCR）工艺试制的高磁感取向硅钢（Hi-B钢）组织、织构的演变特征.研究发现实验室模拟薄板坯连铸连轧工艺试制的Hi-B钢热轧板显微组织及织构在厚度方向上存在不均匀性.常化板表面脱碳层铁素体晶粒明显粗化,常化板织构基本继承了热轧板相应的织构类型,仅织构强度不同.一次大压下率冷轧后,晶粒及其晶界沿轧向被拉长形成鲜明的纤维组织,织构主要为α纤维织构和γ纤维织构,脱碳退火后试样发生回复和再结晶现象并形成初次晶粒组织,脱碳退火后织构分布较为集中.温度升高至1000℃时二次再结晶开始,1010℃时钢中晶粒发生异常长大,高斯织构强度达到61.779.成品磁感为1.915 T,铁损为1.067 W·kg-1.      

B对含P高强度无间隙原子钢{111}面织构的影响

借助光学显微镜(OM)、X射线衍射(XRD)技术及电子背散射衍射(EBSD)技术,分析了2种含P高强度无间隙原子(IF)钢的热轧组织和热轧、冷轧及退火织构,结果表明:不含B与含B的高强IF钢热轧后,均得到多边形铁素体,但不含B热轧板晶粒尺寸较大。2种钢热轧板织构均比较散漫,γ纤维织构强度较弱,而不含B的IF钢经过80%大变形量冷轧以后,获得强的γ纤维织构,{111}面织构的体积分数达到41.41%,而含B的IF钢冷轧后{111}面织构的体积分数为33.83%。含B的IF钢冷轧后{112}110织构组分的体积分数比不含B的IF钢要高。2种实验钢在810℃退火60~180s以后,{111}面织构强度进一步增强,不含B的IF钢退火120s后{111}面织构的体积分数最大达到72.8%,而含B的IF钢退火120s后{111}面织构的体积分数最大达到66.6%。     

0.20 mm薄规格取向硅钢的开发及关键工艺探讨

为开发磁性能优良的0.20 mm薄规格取向硅钢,对该取向硅钢的组织特征,不同冷轧压下率和高温退火气氛对磁性能的影响进行了研究。结果表明：所获得的0.20 mm薄规格取向硅钢成品组织二次再结晶完全,铁损（P1.7/50）为0.89 W/kg,磁感（J800）为1.906 T;热轧和常化1/8层的主要织构组分为Goss织构,冷轧织构为较强的{001}〈110〉,退火织构主要为{411}〈148〉,脱碳晶粒尺寸约为21.17 μm,Goss晶粒极少;0.20 mm薄规格取向硅钢合适的冷轧压下率为91.3 %;高温退火升温段合适的气氛为75% N2。     

SAF 2205双相不锈钢织构与冲压特性

研究SAF 2205双相不锈钢冷轧退火板的冲压特性以及冷轧和退火织构对其冲压性能的影响.实验钢冷轧退火板表现出较差的深冲性能和明显的45°制耳,其r平均值和Δr值分别为0.7和-0.27,这主要与其在冷轧及退火后形成的织构有关.ODF图显示,退火后SAF 2205双相不锈钢中铁素体相未形成γ纤维再结晶织构,仍然为分散的α纤维织构.实验钢中铁素体相的织构强度明显高于奥氏体相,其对钢板成形性的影响更显著,即其各种〈110〉退火织构组分均不利于实验钢r平均值的提高,并且使得Δr<0.此外,奥氏体相的{110}〈001〉织构也对钢板成形性能产生一定程度的影响.      

不同冷轧压下量对亚稳态奥氏体不锈钢00Cr17Ni7织构的影响

 采用X射线衍射技术(XRD)研究了不同冷轧压下量对亚稳态奥氏体不锈钢00Cr17Ni7织构的影响,分析了亚稳态奥氏体不锈钢00Cr17Ni7中马氏体相和奥氏体相的织构变化情况。研究结果表明,不同冷轧压下量下,00Cr17Ni7中的奥氏体相织构主要由Brass{110}<112>、Goss{110}<001>和少量的Copper{112}<111>、S{123}<634>组成,并且随着压下量的增加Brass和Goss织构强度显著提高;同时马氏体相织构主要以{115}<110>、{112}<110> 、{111}<112>、{332}<113>组成,织构的形成主要归因于“Kurdjumov-Sachs取向关系”和“体心立方金属轧制织构类型演变的特点”共同作用的结果。     

Ti-26Nb-4Zr合金冷轧板材的织构和力学性能

采用X射线衍射和室温拉伸方法研究了冷轧变形和固溶处理对Ti-26Nb-4Zr合金板材的织构和力学性能的影响.研究发现,50%冷轧时形成了{001}〈uvw〉织构,随着冷变形量的增加,逐渐形成了{121}〈111〉和{001}〈110〉混合织构,〈110〉方向由与轧制方向垂直转到与轧制方向平行.800℃固溶处理后,随着变形量的增加,{111}〈110〉再结晶织构形成并逐渐增强,但〈110〉方向始终保持与轧制方向平行.由于加工硬化及晶粒细化的作用,导致随着变形量增加,冷轧板材的强度逐渐提高,塑性降低.固溶处理后,由于发生再结晶,使得板材的塑性相比冷轧态明显提高.