Investigation on the corrosion and oxidation resistance of Ni-Al2O3 nano-composite coatings prepared by sediment co-deposition

Ni-Al₂O₃ composite coatings were prepared by using sediment co-deposition (SCD) technique from a Watt's type electrolyte containing nano-Al₂O₃ particles. The corrosion resistance and high temperature oxidation resistance of resulting composite coatings were investigated. It was found that the incorporation of nano-Al₂O₃ particles in Ni matrix refined the Ni crystal and changed the preferential orientation of composite coatings. Meanwhile, the corrosion and oxidation resistance were improved after the incorporation of nano-Al₂O₃ particles into Ni matrix. The nano-Al₂O₃ content in deposits plays an important role for improving the corrosion and oxidation protection. The corrosion and oxidation resistance of Ni-Al₂O₃ nano-composite coatings produced via SCD technique are superior to that of CEP technique. Compared to pure Ni and Ni-Al₂O₃ composite coatings fabricated using CEP technique, the Ni-7.58 wt.% Al₂O₃ composite coating obtained by SCD technique exhibits better corrosion resistance and enhanced high temperature oxidation resistance. Moreover, the mechanism of corrosion and high temperature oxidation resistance of Ni-Al₂O₃ nano-composite coatings are discussed.     

Microstructure and mechanical properties of Al2O3-Cr2O3 composite coatings produced by atmospheric plasma spraying

Al₂O₃, Al₂O₃-Cr₂O₃ and Cr₂O₃ coatings were deposited by atmospheric plasma spraying. Phase composition of powders and as-sprayed coatings was determined by X-ray diffraction. Electron probe microanalyzer was employed to investigate the polished and fractured surface morphologies of the coatings. Mechanical properties including microhardness, fracture toughness and bending strength were evaluated. The results indicate that the addition of Cr₂O₃ is conducive to the stabilization of α-Al₂O₃. Compared with the pure Al₂O₃ and Cr₂O₃ coatings, Al₂O₃-Cr₂O₃ composite coatings show lower porosities and denser structures. Heterogeneous nucleation of α-Al₂O₃ occurs over the isostructural Cr₂O₃ lamellae and partial solid solution of Al₂O₃ and Cr₂O₃ might be occurring as well. Furthermore, grain refining and solid solution strengthening facilitate the mechanical property enhancement of Al₂O₃-Cr₂O₃ composite coatings.     

Thermal conductivity and thermal cycle life of La2O3 and HfO2 doped ZrO2-Y2O3 coatings produced by EB-PVD

The effects of La₂O₃ and HfO₂ addition on thermal conductivity and thermal cycle life of EB-PVD YSZ coatings were investigated. La₂O₃ and HfO₂ were selected as additives, because they significantly suppress the sintering of YSZ. The developed coating showed low thermal conductivity as well as high resistance to sintering. Burner rig tests confirmed that the developed coating have a superior thermal insulating effect and have a longer life than that of a coating with conventional composition.     

Effect of applied current on the electrodeposited Ni-Al2O3 composite coatings

Nano-sized Al₂O₃ ceramic particles (50 nm) were co-deposited with nickel using electrodeposition technique to develop composite coatings. The coatings were produced in an aqueous nickel bath at different current densities and the research investigated the effect of applied current on microstructure and thickness of the coatings. The variation in some mechanical properties such as hardness, wear resistance, and the adhesive strength of the composite coatings is influenced by the applied current and this was also studied. The morphology of the coatings was characterized by scanning electron microscopy and energy dispersive X-ray spectroscopy. The hardness, wear resistance, and bond strength of the coatings were evaluated by Vickers micro-hardness test, pin-on-disc test, and tensile test, respectively. Results showed that the Al₂O₃ particles were uniformly distributed in the coatings, and the coatings deposited at a current density of 0.01 A/cm² was most favorable in achieving a maximum current efficiency which causes the co-deposition of a maximum amount of Al₂O₃ particles (4.3 wt.%) in the coatings. The increase in Al₂O₃ particles in the coatings increased the mechanical properties of the Ni-Al₂O₃ composite coatings by grain refining and dispersion strengthening mechanisms.     

The effect of plasma spray parameters on the cavitation erosion of Al2O3-TiO2 coatings

This paper reports a study of how the choice of plasma spray parameters, used during deposition of Al₂O₃-13%TiO₂ coatings on carbon steel, influences the cavitation erosion properties of such coatings. The parameters studied are the power feeding rate and hydrogen flow rate. The surface and cross section of coatings before and after cavitation were also observed by scanning electron microscopy (SEM). The phases present in the coatings were characterized by X-ray diffraction method (XRD). The microscopic observations were used to study the inter-lamellar connection, porosity, unmelted particles and so on inside the coating. We also measured the roughness, microhardness, adhesion strength and cavitation erosion of the coatings. The XRD results showed that the coating includes different allotropes of Al₂O₃ such as α and γ. The cavitation erosion studies of the coatings were conducted by ultrasonic cavitation testing on the basis of ASTM G32 standard. It was found that cavitation erosion is accelerated around the unmelted particles and porosities. The results reveal that the cavitation resistance of the coating is determined by its microstructure and that increasing discontinuities (inside the coating) reduce its cavitation resistance. We have found that the coating obtained at hydrogen gas flow rate of 16 L/min and powder feeding rate of 20 g/min has the best cavitation resistance.     

过渡材料对等离子喷涂Al2O3梯度陶瓷涂层性能影响

针对Al2O3陶瓷涂层结合强度低、孔隙率高的实际,选择NiAl金属间化合物和金属铜粉作为过渡材料,利用等离子喷涂制备Al2O3梯度陶瓷涂层,并对梯度涂层进行组织形貌观察,测试结合强度和孔隙率.结果表明,梯度涂层的组织表现出宏观的不均匀性和微观连续性的分布特征,NiAl和Cu是金属基体与Al2O3涂层之间过渡层的理想材料,可以有效地提高涂层的结合强度,而Cu-Al2O3梯度涂层又比NiAl-Al2O3梯度涂层结合强度高;梯度涂层的孔隙率远低于双涂层的孔隙率,在Cu-Al2O3梯度涂层中随Al2O3含量的增加,涂层的孔隙率降低,而且孔隙率低于NiAl-Al2O3梯度涂层.     

Synthesis and characterization of Y3Al5O12 and ZrO2-Y2O3 thermal barrier coatings by combustion spray pyrolysis

Y₃Al₅O₁₂ and ZrO₂-Y₂O₃ (8 mol% YSZ) coatings for potential application as thermal barrier coatings were prepared by combustion spray pyrolysis. Thermal cycling of as deposited coatings on stainless steel and FeCrAlY bond coat substrates was carried out at 1000 °C and 1200 °C to determine the thermal fatigue response. Structural and morphological studies on Y₃Al₅O₁₂ and 8 mol% YSZ coatings before and after thermal cycling have been carried out. It has been noted that the coatings on FeCrAlY substrates remain intact after 50 cycles between room temperature and 1200 °C, whereas the coatings on stainless steel show some minor damage such as peeling off near the periphery after 50 cycles at 1000 °C. Thermal diffusivity values of Y₃Al₅O₁₂ and 8 mol% YSZ films were measured by using photo thermal deflection spectroscopy and the values are lower than those of coatings produced by conventional techniques such as EBPVD and APS.     

Influences of annealing temperature on microstructure and mechanical properties of Mo-La2O3

Influences of annealing temperature on the microstructure and mechanical properties of Mo-La₂O₃ were investigated. Effects of annealing temperature on tensile properties, fracture toughness, and microhardness are discussed. Microstructure and fracture morphology of Mo alloys are observed by optical microscope, SEM, and TEM. The results indicate that grain size increased while tensile strength, fracture toughness, and microhardness decreased with increasing annealing temperature. Larger La₂O₃ particles are located at grain boundaries or sub-boundaries, while the majority of smaller La₂O₃ particles are located within the grain. The strengthening effect is quantitatively assessed, which yielded a predicted yield strength in good agreement with measurements.     

Effect of Bi2O3 on structure and wetting studies of Bi2O3-ZnO-B2O3 glasses

Glasses with different Bi₂O₃ contents (37-42 mol%) have been prepared by conventional melt quench technique. The IR and Raman studies indicate that these glasses are made up of [BiO₆], [BiO₃], [BO₃] and [BO₄] basic structural units. The vibrations of [BiO₃] and [BO₃] become stronger as the content of Bi₂O₃ increases, which makes glass structure loosened. Viscosity of the glasses was measured by using a Rheotronic III paralleled plate rheometry, which shows that the viscosity of glass samples decreased when the content of Bi₂O₃ increased at the same temperature (400-460 °C). The temperature range which suits for glasses sealing was calculated by using the approximation of Arrhenian behaviour. The wetting performance of Bi₂O₃-ZnO-B₂O₃ glasses was described by using high-temperature microscope, which also proves that the structure of investigated Bi₂O₃-ZnO-B₂O₃ glasses become loosened due to the increasing of the content of Bi₂O₃.     

等离子喷涂Cu-Al2O3梯度涂层的组织与耐磨性分析

针对纯陶瓷涂层由于结合强度低、孔隙率高、影响涂层耐磨性的实际,用等离子喷涂法制备了Cu-Al2O3梯度涂层,用电子扫描显微镜(SEM)、金相显微镜等手段对涂层进行微观组织和成分分析,用自制销盘式固定磨料磨损试验机,检测了Cu-Al2O3梯度涂层的耐磨料磨损性能.结果表明,采用等离子喷涂法制备的Cu-Al2O3梯度涂层无明显的组织突变和宏观层间界面,涂层的组织表现出宏观不均匀性和微观连续性分布特征;梯度涂层中当Al2O3含量(质量分数,%)达到80%时(GC6),涂层的耐磨性最高,约为基体的3倍,随着Al2O3含量继续增大,纯陶瓷涂层(GC7)的耐磨性有所下降.     

国外多孔基体氧化铝/氧化铝复合材料工程应用进展

氧化铝/氧化铝复合材料(Al2O3/Al2O3)是20世纪90年代兴起的一类连续陶瓷纤维增强陶瓷基复合材料,已经发展为与SiC/SiC、C/SiC等非氧化物陶瓷基复合材料并列的一类陶瓷基复合材料。与非氧化物陶瓷基复合材料相比,Al2O3/Al2O3具有长时抗氧化、高温耐腐蚀、低成本等独特优势,已经在航空发动机、地面燃气轮机等军民两用热结构材料领域展现出广阔的应用前景。本文从材料应用的角度出发,系统分析阐述了目前在Al2O3/Al2O3占主导地位的多孔基体Al2O3/Al2O3(P-Al2O3/Al2O3)的增韧机制、成型工艺和性能特点,重点归纳了国外近年来P-Al2O3/Al2O3的工程化应用进展及前景,最后指出了P-Al2O3/Al2O3存在的局限性并展望了未来发展方向,旨在为国内Al2O3/Al2O3体系发展提供借鉴和参考。     

Hot corrosion behaviour of plasma sprayed YSZ/Al2O3 dispersed NiCrAlY coatings on Inconel-718 superalloy

Oxide dispersed NiCrAlY bond coatings have been developed for enhancing thermal life cycles of thermal barrier coatings (TBCs). However, the role of dispersed oxides on high temperature corrosion, in particular hot corrosion, has not been sufficiently studied. Therefore, the present study aims to improve the understanding of the effect of YSZ dispersion on the hot corrosion behaviour of NiCrAlY bond coat. For this, NiCrAlY, NiCrAlY + 25 wt.% YSZ, NiCrAlY + 50 wt.% YSZ and NiCrAlY + 75 wt.% YSZ were deposited onto Inconel-718 using the air plasma spraying (APS) process. Hot corrosion studies were conducted at 800 °C on these coatings after covering them with a 1:1 weight ratio of Na₂SO₄ and V₂O₅ salt film. Hot corrosion kinetics were determined by measuring the weight gain of the specimens at regular intervals for a duration of 51 h. X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy techniques were used to determine the nature of phases formed, examine the surface attack and to carry out microanalysis of the hot corroded coatings respectively. The results show that YSZ dispersion causes enhanced hot corrosion of the NiCrAlY coating. Leaching of yttria leads not only to the formation of the YVO₄ phase but also the destabilization of the YSZ by hot corrosion. For the sake of comparison, the hot corrosion behaviour of a NiCrAlY + 25 wt.% Al₂O₃ coating was also examined. The study shows that the alumina dispersed NiCrAlY bond coat offers better hot corrosion resistance than the YSZ dispersed NiCrAlY bond coat, although it is also inferior compared to the plain NiCrAlY bond coat.     

La2O3含量对Al2O3/Cu基复合材料组织与性能的影响

以La₂O₃粉、Al粉、CuO粉为反应物原料、纯铜为基体,采用原位合成技术和近熔点铸造法制备颗粒增强Cu基复合材料,研究La₂O₃对Al-CuO体系制备的Cu基复合材料组织及性能的影响。结果表明：添加La₂O₃可获得纳米Al₂O₃颗粒,且弥散分布于Cu基体中,制备的材料组织更加细小、均匀,其材料的电导率及摩擦磨损性能明显提高。当添加0.6%wtLa₂O₃,复合材料的电导率达到90.2%IACS,磨损量达到最小,相比未添加La₂O₃,其导电率提高10.1%,磨损量减小36.6%。     

Effects of K2O-Li2O doping on surface and catalytic properties of Fe2O3/Cr2O3 system

The effects of K₂O and Li₂O-doping (0.5, 0.75 and 1.5 mol%) of Fe₂O₃/Cr₂O₃ system on its surface and the catalytic properties were investigated. Pure and differently doped solids were calcined in air at 400-600 °C. The formula of the un-doped calcined solid was 0.85Fe₂O₃:0.15Cr₂O₃. The techniques employed were TGA, DTA, XRD, N₂ adsorption at −196 °C and catalytic oxidation of CO oxidation by O₂ at 200-300 °C. The results revealed that DTA curves of pure mixed solids consisted of one endothermic peak and two exothermic peaks. Pure and doped mixed solids calcined at 400 °C are amorphous in nature and turned to α-Fe₂O₃ upon heating at 500 and 600 °C. K₂O and Li₂O doping conducted at 500 or 600 °C modified the degree of crystallinity and crystallite size of all phases present which consisted of a mixture of nanocrystalline α- and γ-Fe₂O₃ together with K₂FeO₄ and LiFe₅O₈ phases. However, the heavily Li₂O-doped sample consisted only of LiFe₅O₈ phase. The specific surface area of the system investigated decreased to an extent proportional to the amount of K₂O and Li₂O added. On the other hand, the catalytic activity was found to increase by increasing the amount of K₂O and Li₂O added. The maximum increase in the catalytic activity, expressed as the reaction rate constant (k) measured at 200 °C, attained 30.8% and 26.5% for K₂O and Li₂O doping, respectively. The doping process did not modify the activation energy of the catalyzed reaction but rather increased the concentration of the active sites without changing their energetic nature.     

Mechanical and tribological performance of Al2O3-TiO2 coatings elaborated by flame and plasma spraying

Mechanical properties and wear rates of Al₂O₃-13 wt.% TiO₂ (AT-13) and Al₂O₃-43 wt.% TiO₂ (AT-43) coatings obtained by flame and atmospheric plasma spraying were studied. The feed stock was either ceramic cords or powders. Results show that the wear resistance of AT-13 coatings is higher than that of AT-43 and it seems that the effect of hardness on wear resistance is more important than that of toughness. Additionally, it was established that, according to conditions used to elaborate coatings and the sliding tribological test chosen, spray processes do not seem to have an important effect on the wear resistance of these coatings.     

Structure stability and corrosion resistance of nano-TiO2 coatings on aluminum in seawater by a vacuum dip-coating method

A stable nano-TiO₂ coating was prepared by vacuum dip-coating TiO₂ sol-gel onto the anodized aluminum surface. The effect of vacuum dip-coating method and anodization pretreatment on compactness and stability of the coatings was proved. The structure and composition of the coatings were characterized by means of scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results indicate that the surface of coatings is uniform and compact, with high load capacity. The particles of TiO₂ anatase is filled into the Al₂O₃ nano-pores formed by anodization. The electrochemical measurements show that the nano-TiO₂ coatings significantly decrease the corrosion currents densities (i_corr), as simultaneously increased the values of polarization resistance (R_t) of aluminum. It indicates the nano-TiO₂ coatings exhibit excellent anticorrosion properties in sterile seawater at the room temperature.     

Al_2O_3/MoS_2复合涂层的制备及摩擦磨损性能

以大气等离子喷涂工艺制备的Al_2O_3陶瓷涂层为模板,利用陶瓷涂层中存在的孔隙和微裂纹,采用水热反应在其内部原位合成具有润滑特性的MoS_2,制备出Al_2O_3/MoS_2的复合涂层。结果表明,通过水热反应在陶瓷涂层原有的微观缺陷中成功合成了MoS_2,合成的MoS_2固体粉末呈类球形状,并且这球状的粉末是由纳米片层状的MoS_2搭建组成的。摩擦试验结果表明,与纯Al_2O_3涂层相比,复合涂层中由于MoS_2润滑膜的形成,其摩擦因数和磨损率都显著降低,且载荷越大,复合涂层的摩擦性能越好。     

Microwave ECR plasma CVD of cubic Y2O3 coatings and their characterization

Yttrium oxide (Y₂O₃) thin films are deposited by microwave electron cyclotron resonance (ECR) plasma assisted metal organic chemical vapour deposition (MOCVD) process at a substrate temperature of 350 °C using indigenously developed metal organic precursors (2,2,6,6-tetra methyl-3,5-heptane dionate) yttrium, commonly known as Y(thd)₃ synthesized by ultrasound method. The deposited coatings are characterized by X-ray photoelectron spectroscopy, glancing angle X-ray diffraction, scanning electron microscopy, EDS and infrared spectroscopy. The characterization results indicate that it is possible to deposit non-porous coatings with excellent uniformity of a single phase cubic Y₂O₃ on various substrates by this process at reasonably low substrate temperature that is desirable in various manufacturing processes.     

Al2O3/TiB2/Al复合材料的微观结构和高温力学性能

以细雾化铝粉和TiB₂颗粒为原料,通过粉末冶金和热轧制制备微米TiB₂和纳米Al₂O₃颗粒增强铝基复合材料。室温时,由于TiB₂和Al₂O₃的综合强化作用,Al₂O₃/TiB₂/Al复合材料的屈服强度和抗拉强度分别为258.7 MPa和279.3 MPa,测试温度升至350℃时,TiB₂颗粒的增强效果显著减弱,原位纳米Al₂O₃颗粒与位错的交互作用使得复合材料的屈服强度和抗拉强度达到98.2MPa和122.5 MPa。经350℃退火1000 h后,由于纳米Al₂O₃对晶界的钉扎作用抑制晶粒长大,强度和硬度未发生显著的降低。     

ZrB2增韧Al2O3陶瓷制备工艺及其对复相陶瓷力学性能影响

Al₂O₃陶瓷因具有很高的强度和耐蚀性受到广泛关注。但由于相对较差的韧性限制了其广泛应用。Al₂O₃陶瓷增韧的方式很多,本文采用微米ZrB₂来增韧氧化铝陶瓷,探讨复相陶瓷烧结工艺,并研究工艺参数对复相陶瓷力学性能及韧性的影响。结果表明：采用单因素法得到两种陶瓷最佳工艺参数分别是纯α-Al₂O₃陶瓷烧结温度为1500℃,成型压力为450MPa,保温时间为8h,球料比为1/2,保压时间为10min;ZrB₂(wt,20%)+α-Al₂O₃ (wt,80%)复相陶瓷烧结温度为1450℃,成型压力为450MPa,保温时间为8h,球料比为1/2,保压时间为10min。其中成型压力、烧结温度和保温时间对复相陶瓷硬度及致密度影响最大。ZrB₂的加入,在降低陶瓷烧结温度的同时,可以将纯α-Al₂O₃陶瓷的断裂韧性由5.2±0.3MPa.m^_1/2提高到6.7±0.2MPa.m^_1/2。