Computer controlled detonation spraying of WC/Co coatings containing MoS2 solid lubricant

Composite WC/Co + MoS₂ coatings were deposited onto steel substrates by Computer Controlled Detonation Spraying using three spraying modes: very cold, cold and normal. Maximal content of MoS₂ in a sprayed powder was 10 wt.%. Characterization of coatings was made with chemical and phase analyses, microhardness measurement, morphology and microstructure investigation. X-ray diffraction study shows that residual MoS₂ exists only in coatings obtained at very cold and cold spraying modes. At normal spraying mode complete decomposition of the solid lubricant occurs during spraying. From the engineering point of view, the coating applied at the cold mode using a powder containing 10 wt.% MoS₂ is the most promising. Such a coating has microhardness of 650 HV_0.2 and a porosity of 10%.     

Microstructure and stresses in HVOF sprayed iron aluminide coatings

The microstructure and state of stress present in Fe₃Al coatings produced by high velocity oxygen fuel (HVOF) thermal spraying in air at varying particle velocities were characterized using metallography, curvature measurements, x-ray analysis, and microhardness measurements. Sound coatings were produced for all conditions. The microstructures of coatings prepared at higher velocities showed fewer unmelted particles and a greater extent of deformation. Residual stresses in the coatings were compressive and varied from nearly zero at the lowest velocity to approximately −450 MPa at the highest velocity. X-ray line broadening analyses revealed a corresponding increase in the extent of cold work present in the coating, which was also reflected in increased microhardness. Values of mean coefficient of thermal expansion obtained for assprayed coatings using x-ray analysis were significantly lower than those for powder and bulk alloy.     

Cold-Sprayed Magnesium Coatings Deposited with Helium and Air

Cold-sprayed magnesium coatings have been little researched although cold spraying has been applied to deposit a large number of materials such as metals,metal matrix composites.In the present study,helium gas and air were employed as the propelling gases to deposit Mg coatings under the temperature of 600℃and 630℃.The effect of gas types on the coating microstructure was investigated.It is much interesting to find that the particle deposition efficiency using helium gas as propelling gas is lower than that using air.This suggests that strong erosion occurred during cold spraying using helium gas.The porosity of the coating using helium gas is lower than that using air.In addition,the in-flight particle velocity was also simulated by the FLUENT software to explore the effect of gas types.The modeled results show that the in-flight particle velocity using helium is higher than the erosion velocity of Mg particle.     

Influence of Helium and Nitrogen Gases on the Properties of Cold Gas Dynamic Sprayed Pure Titanium Coatings

This study investigates the effect of propellant gas, helium, and nitrogen during cold spraying of titanium coatings. Coatings were characterized by SEM and were evaluated for their deposition efficiency (DE), microhardness, and porosity. In selected conditions, three particle velocities were investigated in which for each condition, the propelling gases?? temperature and pressure were attuned to attain similar particle velocities for each gas. Observations show that loosely bonded particles can be detached by high-pressure supersonic gas stream. Selected coatings were characterized by XPS to analyze the occurrence of oxidation and nitridation. Although generally accepted that coating characteristics can be affected by particle temperature, results show that for the same particle velocity, DE and coating density are also a function of substrate temperature. In addition, a thick and fully dense cold sprayed titanium coating was achieved with optimized spray parameters and nozzle using helium. The corresponding average particle velocity was 1173 m/s.     

Bonding mechanism in cold gas spraying

Cold gas spraying is a relatively new coating process by which coatings can be produced without significant heating of the sprayed powder. In contrast to the well-known thermal spray processes such as flame, arc, and plasma spraying, in cold spraying there is no melting of particles prior to impact on the substrate. The adhesion of particles in this process is due solely to their kinetic energy upon impact. Experimental investigations show that successful bonding is achieved only above a critical particle velocity, whose value depends on the temperature and the thermomechanical properties of the sprayed material. This paper supplies a hypothesis for the bonding of particles in cold gas spraying, by making use of numerical modelling of the deformation during particle impact. The results of modelling are assessed with respect to the experimentally evaluated critical velocities, impact morphologies and strengths of coatings. The analysis demonstrates that bonding can be attributed to adiabatic shear instabilities which occur at the particle surface at or beyond the critical velocity. On the basis of this criterion, critical velocities can be predicted and used to optimise process parameters for various materials.     

Substrate roughness and thickness effects on cold spray nanocrystalline Al−Mg coatings

Nanocrystalline Al−Mg coatings were produced using the cold gas dynamic-spraying technique. Unsieved Al−Mg powder of average nanocrystalline grain size in the range of 10 to 30 nm and with a particle size distribution from 10 to >100 μm was used as the feedstock powder. The resulting coatings were evaluated using scanning electron microscopy (SEM), transmission electron microscopy, as well as microhardness and nanoindentation measurements. Coating observations suggest that the wide particle size distribution of the feedstock powder has a detrimental effect on the coating quality but that it can be successfully mitigated by optimizing the spraying parameters. Nanohardness values close to 3.6 GPa were observed in both the feedstock powder and coatings, suggesting the absence of cold-working hardening effects during the process. The effects of the substrate surface roughness and thickness on coating quality were investigated. The deposited mass measurements performed on the coatings showed that the effect of using different grit sizes for the substrate preparation is limited to small changes in the deposition efficiency of only the first few layers of deposited material. The SEM observation showed that the substrate surface roughness has no significant effect on the macrostructures and microstructures of the coating. The ability to use the cold gas dynamic spraying process to produce coatings on thin parts without noticeable substrate damage and with the same quality as coatings produced on thicker substrates was demonstrated in this work. The original version of this paper was published in the CD ROM Thermal Spray Connects: Explore Its Surfacing Potential, International Thermal Spray Conference, sponsored by DVS, ASM International, and IIW International Institute of Welding, Basel, Switzerland, May 2–4, 2005, DVS-Verlag GmbH, Düsseldorf, Germany.     

Bonding,Reactivity, and Mechanical Properties of the Kinetic-Sprayed Deposition of Al for a Thermally Activated Reactive Cu Liner

Pure Al coatings were fabricated on Cu substrates via kinetic spraying to produce a thermally activated reactive Cu liner. The coatings need to endure high-strain rate severe plastic deformation and react with oxygen during penetration or after penetration of the liner. In this study, the Al powder underwent large exothermic reactions with a small particle size and fast heating rate, as determined from the differential scanning calorimetric analysis. Process optimization of the Al deposition was facilitated by defining the “critical velocity” of an Al particle in the kinetic spraying process based on numerical modeling and computations using ABAQUS finite element codes. The simulation results revealed that the critical velocity of an Al particle at room temperature (RT) is 780 m/s and it decreases as the particle temperature increases. Certain process conditions resulted in improved coating properties as the temperature of the particles was affected by the process gas temperature and pressure. The mechanical properties such as the bond strength of the coatings formed under various process conditions were evaluated and compared. The relationships between the resulting properties, processing conditions, and the structures of the coatings are discussed.     

Warm Spray Forming of Ti-6Al-4V

Warm spray (WS) is a modification of high-velocity oxy-fuel spraying, in which the temperature of the supersonic gas flow generated by the combustion of kerosene and oxygen is controlled by diluting the combustion flame with an inert gas such as nitrogen. The inert gas is injected into the mixing chamber placed between the combustion chamber and the powder feed ports, thus the temperature of the propellant gas can be controlled from ~700 to 2,000 K. Since WS allows for higher particle temperatures in comparison to cold spray, warm sprayed particles are more softened upon impact, thus resulting in greater deformation facilitating the formation of shear instability for bonding. Recently, the combustion pressure of WS has been increased from 1 (low-pressure warm spray) to 4 MPa (high-pressure warm spray) in order to increase the velocity of sprayed particles. Effects of spray parameters on microstructure, mechanical properties, and splats formation of Ti-6Al-4V were systematically studied. Obtained coatings were examined by analyzing the coating cross-section images, microhardness as well as oxygen content. In addition, flattening ratio of splats was calculated as a function of nitrogen flow rate. It was found that the increased particle velocity caused by the increased combustion pressure had significant beneficial effects in terms of improving density and controlling the oxygen level in the sprayed Ti-6Al-4V coatings.     

冷喷涂TC4涂层临界沉积速度计算及制备涂层性能研究

目的研究冷喷涂TC4涂层的临界沉积速度及粒子温度对临界沉积速度的影响规律,并研究气体压强对沉积涂层性能的影响规律。方法理论研究上,采用有限元LS-DYNA软件中的Johnson-Cook塑性模型,选取3D164计算单元建立模型,研究粒子在不同温度和不同速度下碰撞基体后的形貌特征,确定粒子沉积临界速度。试验研究上,采用N_2作为冷喷涂驱动气体,在TC4合金上制备TC4涂层,然后采用SEM、Image J图像分析软件、硬度计等分析已沉积涂层的孔隙率和硬度等性能。结果 25、400、500、600℃温度下,计算表明10μm的TC4合金粒子在TC4基板上的临界沉积速度分别为730、465、392、361 m/s,即随粒子温度升高,粒子临界沉积速度降低,粒子沉积成涂层更容易。采用冷喷涂工艺在TC4基板上沉积TC4涂层,在N_2温度600℃、气体压力3 MPa的条件下,制备的TC4涂层厚度约1000μm,与TC4钛合金基体结合紧密,涂层孔隙率约为6.46%。结论气体温度升高,粒子临界沉积速度降低;气体压强变大,制备的涂层厚度就大且更加致密。     

An analysis of the cold spray process and its coatings

In this study, computational fluid dynamics (CFD) and extensive spray tests were performed for detailed analyses of the cold spray process. The modeling of the gas and particle flow field for different nozzle geometries and process parameters in correlation with the results of the experiments reveal that adhesion only occurs when the powder particles exceed a critical impact velocity that is specific to the spray material. For spherical copper powder with low oxygen content, the critical velocity was determined to be about 570 m/s. With nitrogen as the process gas and particle grain sizes from 5–25 μm, deposition efficiencies of more than 70% were achieved. The cold sprayed coatings show negligible porosity and oxygen contents comparable to the initial powder feedstock. Therefore, properties such as the electrical conductivity at room temperature correspond to those of the bulk material. The methods presented here can also be applied to develop strategies for cold spraying of other materials such as zinc, stainless steel, or nickel-based super-alloys.     

Oxidation resistance of TiAl3-Al composite coating on orthorhombic Ti2AlNb based alloy

The TiAl₃-Al composite coating on orthorhombic Ti₂AlNb based alloy was prepared by cold spray. Oxidation in air at 950 °C indicated that the bare alloy exhibited poor oxidation resistance due to the formation of TiO₂/AlNbO₄ mixture and intended to scale off at the TiO₂ rich zone. A nitride layer about 2 µm was formed under the oxide layer. The oxygen invaded deeply into the alloy and caused severe microhardness enhancement in the near surface region. The TiAl₃-Al composite coating exhibited parabolic oxidation kinetics and showed no sign of degradation after oxidized up to 1098 h at 950 °C in air under quasi-isothermal condition. No scaling of the coating was observed after oxidized at 950 °C up to the tested 150 cycles. The major oxide in the oxidized coating was Al₂O₃. The AlTi₂N, TiAl and small amount of TiO₂ were also observed in the oxidized coating. The EPMA and microhardness tests showed that inward oxygen diffusion was prevented by the interlayer, which was formed between the composite coating and the substrate during heat-treatment. Microstructure analyses demonstrated that the interlayer play a major role in protecting the substrate alloy from high temperature oxidation and interstitial embrittlement.     

Development of cold work tool steel based-MMC coating using HVOF spraying and its HIP densification behaviour

The aim of the present study is to develop a Fe-based metal matrix composite (MMC) coating using high velocity oxy-fuel spraying (HVOF) process. A ledeburitic high alloyed cold work tool steel (X220CrVMo13-4) and NbC with an average size of 2 µm at different volume fractions have been considered as metal matrix and hard particles respectively. MMC coatings were deposited on austenitic stainless substrates and the coatings were subsequently densified by hot isostatic pressing (HIP) with and without encapsulation. Microstructural analysis of the as-sprayed and HIPed coatings were characterized by SEM and XRD methods. Results showed that the feedstock preparation involving fine NbC was an influencing factor on the coating deposition. A relatively homogeneous dispersion of fine NbC up to 30 vol.% in cold work tool steel matrix was possible using optimized HVOF spraying. Besides, HVOF spraying and its subsequent HIP treatment induced significant microstructural and phase changes in the MMC coatings. The study showed the potential of HVOF spraying for the development of steel based MMC coatings and its subsequent densification can be achieved by HIP process with and without encapsulation.     

New developments in cold spray based on higher gas and particle temperatures

In cold spraying, bonding is associated with shear instabilities caused by high strain rate deformation during the impact. It is well known that bonding occurs when the impact velocity of an impacting particle exceeds a critical value. This critical velocity depends not only on the type of spray material, but also on the powder quality, the particle size, and the particle impact temperature. Up to now, optimization of cold spraying mainly focused on increasing the particle velocity. The new approach presented in this contribution demonstrates capabilities to reduce critical velocities by well-tuned powder sizes and particle impact temperatures. A newly designed temperature control unit was implemented to a conventional cold spray system and various spray experiments with different powder size cuts were performed to verify results from calculations. Microstructures and mechanical strength of coatings demonstrate that the coating quality can be significantly improved by using well-tuned powder sizes and higher process gas temperatures. The presented optimization strategy, using copper as an example, can be transferred to a variety of spray materials and thus, should boost the development of the cold spray technology with respect to the coating quality. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Effects of heating temperature and duration on the microstructure and properties of the self-healing coatings

The present work investigates how the heating temperature and duration affect the properties of the self-healing coating on martensitic steels. The coating composed of TiC + mixture (TiC/Al₂O₃) + Al₂O₃ is fabricated by means of air plasma spraying. The thermal shock test is performed at 600 °C, 700 °C and 800 °C, respectively, to evaluate the thermal-mechanical stability of the coating. The cross-section morphology of the samples after 1 h, 9 h, 18 h and 30 h of heat treatment shows that the porosity of the coating decreases with the increase of heating duration. The evaluation of electrochemical performance by electrochemical impedance spectroscopy shows that the corrosion resistance of the coating after being heated for 18 h is much better than the other samples due to the process of the inner layer being compacted in the coating. The adhesive tensile strength test between coating and substrate shows that the adhesive strength of the coatings is higher than 9 MPa within 40 h of heat treatment at 600 °C. The residual stress reaches a minimum value after the coating was heated for 9 h at 600 °C, then increases with the heating duration after 9 h. Energy dispersive X-ray analysis at the Vickers indentation indicates that the oxygen content at the crack position increases significantly after being heated for 30 h at 600 °C. These experimental results suggest that this coating can meet the requirement of application under the actual temperature conditions.     

Cold spraying of Al-Sn binary alloy: Coating characteristics and particle bonding features

In this study, Al-Sn binary alloy coatings were prepared with Al-10 wt.% Sn (Al-10Sn) and Al-20 wt.%Sn (Al-20Sn) gas atomized alloy powders by low pressure cold spray process. The microstructure and microhardness of the coatings were characterized. The deposition efficiency of Al-Sn and pure aluminum powder were tested on sand blasted substrates of Al6061, copper and SUS304. To investigate the particle bonding features of Al-10Sn powder, the wipe test was carried out on polished substrate surfaces. The average critical velocity of Al-Sn alloy powders was estimated combining with the deposition efficiency. The results proved that Al-Sn coatings with dense and uniform structure can be deposited successfully by low pressure cold spray with helium as the propellant gas. The weight content of tin in Al-Sn coating is 12% and 22% for Al-10Sn and Al-20Sn coating, respectively. With the increase of tin content in feedstock powder, the as-sprayed coatings present similar microhardness of 73 and 74 for Al-10Sn and Al-20Sn while, on the other hand, the deposition efficiency decreased. Bonding features of Al-10Sn particles indicated that the melting of tin phase occurred on the contact interface during particle impacting. This melting of tin phase and low strength of tin may affect the particle bonding process and hence increase the critical velocity for Al-Sn binary alloy powders.     

Microstructure and magnetic properties of HVOF thermally sprayed Fe75Si15B10 coatings

Partially amorphous Fe₇₅Si₁₅B₁₀ coatings were prepared from nanostructured feedstock powders by using high velocity oxy-fuel spraying. Scanning electron microscopy, X-ray diffraction, Vickers indenter and magnetic measurements were used to investigate microstructural, structural, microhardness and magnetic properties of the coatings. The Rietveld refinement of the X-ray diffraction patterns reveals the presence of an amorphous phase, nanocrystalline α-Fe(Si,B) structure having a lattice parameter close to 0.2841 nm and an average crystallite size of about 78-83 nm in addition to small amounts of Fe₃O₄ oxide (104 nm) and Fe₂B boride (151 nm), which disappear completely with increasing coating thickness. Coercivity and microhardness values are 15.5 Oe and 478 Hv, respectively, for 84 μm thickness.     

Deposition effects of WC particle size on cold sprayed WC-Co coatings

The WC particle size and its influence on the deposition of Co-based cermets are examined. Micron and nanostructured powders with similar Co content were employed. Varying the WC particle size influenced significantly the deposition efficiency of the coating process. Micrometer-structured WC-Co feedstocks did not permit coating build up when processed under comparable or elevated thermal spray parameters used for the nanostructured WC-Co feedstocks. In addition, micrometer-structured WC-Co coatings exhibited a conjoint erosion and deposition effect on the surface. Fine WC particles (< 1 μm) were observed near the substrate interface and larger WC particles (1-2 μm) in the vicinity of the coating surface. These observations indicate the existence of a critical WC particle size for deposition by the cold spray method and that the size criteria arises due to the formation and cohesion mechanisms within the coating layer.Nanostructured test specimens displayed (i) a dense microstructure with little presence of porosity, (ii) a crack free interface between the coating and substrate that indicated good adhesion, and (iii) no observable phase changes. The XRD patterns of each powder and their respective coatings did not have observable peak differences but the diffraction peak broadening of coatings indicated that there was grain refinement during the coating process. Furthermore, all nanostructured as-sprayed WC-Co coatings exhibited Vickers hardness values above HV1000. The nanostructured WC-Co coatings demonstrated adhesive strengths that exceeded the limits of the glue (60 MPa).     

Cold gas dynamic spraying of iron-base amorphous alloy

This paper describes recent efforts to synthesize iron-base amorphous alloys coatings using cold gas dynamic spraying. Characterization of the gas-atomized iron-base (Fe-Cr-Mo-W-C-Mn-Si-Zr-B) powder shows that the powder is fully amorphous when the particle diameter is below 20 μm. The coatings produced were composed of the same microstructure as the one observed in the feedstock powder. The overall deformation suggests the occurrence of a localized deformation process at the particle/particle boundary and a possible adiabatic deformation softening inside the powder particles during splat formation. The synthesis of fully amorphous, porous-free coatings using cold gas dynamic spraying was demonstrated in this work. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

TiAlNb intermetallic compound coating prepared by high velocity oxy-fuel spraying

Ti_28.35Al_63.4Nb_8.25 (at.%) intermetallic compound coatings were sprayed onto 316 L stainless steel substrates by HVOF processes using various parameters. By varying the grit blasting pressure between 0.11 and 0.55 MPa, the effects of substrate roughness on the adhesion of TiAlNb thermal sprayed coatings were investigated. The microstructure, porosity and microhardness of the coatings were characterized by SEM, XRD, Image Analysis and Vickers hardness analysis. The tensile adhesion test (TAT) specified by ASTM C 633-79 was used to measure the tensile bonding strength of the coating. The results show that the coatings with substrate roughness of 8.33 μm displayed the best combined strength. TiAlNb coatings had a lamellar microstructure with different spraying parameters. The porosity, bonding strength, microhardness of coatings were assessed in relation to the spraying processes. The thickness of bond coat on the bond strength of coatings was also discussed.     

Aluminium coating of lead zirconate titanate—A study of cold spray variables

Cold spray was used to deposit conductive aluminium coatings onto lead zirconate titanate (PZT) piezoceramics. The optimisation of processing parameters was explored. Grain removal from the PZT surface due to the impact of Al particles was reduced by increasing the average particle velocity. Surface domain reorientation was detected by X-ray diffraction (XRD). Substrate temperatures during spraying were maintained at a low level by controlling the upstream, cold spray temperature and robot movement. The electrical resistance of the cold sprayed aluminium was 9.9 ± 0.5 μΩ cm. The impedance characteristics of poled specimens were shown to be unchanged by cold spray.