The influence of the stabilizer/SWNT ratio on the transport behavior of latex‐based polymer nanocomposites is examined in an effort to improve electrical conductivity while maintaining or improving the Seebeck coefficient (i.e., thermopower). Results show that phonon and electron transport are significantly affected by tube/tube junctions, and the carrier transport across the junctions can be manipulated by altering the stabilizer concentration. Electrical conductivity of composites containing 10 wt.‐% SWNT nearly doubles, becoming greater than 900 S · m?1, by changing the SWNT:GA ratio from 1:3 to 10:1, while thermal conductivity and Seebeck coefficient remain relatively constant (near 0.25 W · m‐K?1 and 40 µV · K?1, respectively).
Summary: An organic‐inorganic hybrid material consisting of a 3‐(methacryloxy)propyl functionalized SiO2/MgO framework was synthesized. This hybrid was successfully reacted with styrene, butyl acrylate and butyl methacrylate via a free radical emulsion polymerization to form polymer composites. The polymer composites were investigated by means of FT‐IR spectroscopy, TGA, DSC and rheometry. It is shown that the polymer is linked covalently to the organic/inorganic hybrid. Although the polymer content is rather low, the composites exhibit a polymer‐like character and enhanced mechanical properties compared to the corresponding homopolymers.
Summary: Syntactic foams containing 0.9, 1.76, 2.54, 3.54 and 4.5 vol.‐% of E‐glass fibres in the form of chopped strands were processed and subjected to three‐point bending tests. The results showed that introduction of chopped strand fibres into the syntactic foam system increased the flexural strength. The values increased with the amount of fibres in the foam system except for the one containing 3.5 vol.‐% of fibres, which showed a lower value than other fibre‐reinforced systems, thereby deviating from the trend. This exception was attributed to the difference in processing route adopted for this particular fibre‐bearing foam. However, in general, the incorporation of chopped strand fibres improved the flexural behaviour of the syntactic foam system without much variation in density, thus making reinforced syntactic foams to act as better and improved core materials for sandwich applications.
Fibre‐debonding and protuberance, and river pattern in a failed sample. 相似文献
The influence of screw speed on the electrical and rheological percolation of HIPS/MWCNT composites prepared via melt mixing was investigated. Microscopic examination of these composites using POM, FESEM and HRTEM revealed optimum MWCNT dispersion was achieved at intermediate screw speeds. On addition of MWCNTs to HIPS, the electrical conductivity of HIPS increased by up to 12 orders of magnitude. At screw speeds up to 100 rpm an electrical percolation of 1–3 wt.‐% was achieved. This increased to 3–5 wt.‐% when the screw speed was increased to 150 rpm. The onset of a rheological percolation was detected for an MWCNT loading of 5 wt.‐%, irrespective of screw speed employed. An up‐shift in the Raman G‐band of 24 cm?1 was observed, implying strong interfacial interaction between HIPS and MWCNTs.
A strategy is described to prepare epoxy resin nanofibers by combining coaxial electrospinning and traditional hot‐curing processes. Core/sheath nanofibers with diameters of 480 ± 80 nm are prepared at flow rates of 0.1 and 2 mL h?1 for the core (20% w/v EP and 6% w/v curing agent in ethanol/acetone) and sheath (10% PVP in ethanol) fluids. After the curing of the nanofibers and selective removal of the sheath PVP, EP nanofibers with an average diameter of 210 ± 60 nm are obtained. ATR‐FTIR analysis shows that the EP nanofibers display no obvious difference compared with an EP film cast from the core solution. The method presented allows to develop functional EP nanoproducts and to prepare heat‐cured resin nanofibers.
Summary: An original direct melt extrusion processing of nylon 6/clay nanocomposites was reported based on pristine (Na+‐based) montmorillonite as well as a simple approach using a typical two‐screw extruder. By the application of intercalation agents as the thermodynamic assistants, this method is as an appropriate procedure for industrialized manufacture together with much lowered production cost. Interestingly enough, the synergistic effects of montmorillonite with other inorganic particulates was observed for the first time here.
X‐ray diffraction patterns of pristine MMT and nylon 6/MMT composites with grouped intercalation agents. 相似文献
Low‐MW urethanes were investigated to control domain formation as well as inhibiting cleavage reactions during vapor phase polymerization of PEDOT. A diurethanediol (DUDO) was identified as a highly efficient mediator for the process, resulting in PEDOT films exceeding conductivities of 1 000 S · cm?1. All the urethanes investigated had the desired inhibiting effect on the polymerization, but all apart from DUDO also introduced unwanted domain formation on the micrometer scale. The addition of PEG generally improved conductivity by suppressing the domain formation and, with an optimized combination of DUDO and PEG, conductivities over 1 200 S · cm?1 were achieved.
To enhance adhesion properties of PEO on wood fibers, block polymers of PEO and 2‐(dimethylamino)ethyl methacrylate were synthesized. The polymers were further modified to obtain strongly cationic species. The resulting polymers were used as additives in paper sheets. Papers were studied by DMA in a controlled‐humidity chamber. Addition of the PEO block co‐polymers enhanced paper strength. The strength of the paper sheets was highest when polymer with molecular weight of 400 kg · mol?1 was used as an additive. Highly cationic block co‐polymers increased moduli of paper sheets more than their weakly cationic analogs, which indicated strong interaction with fiber surfaces. Strength of the paper sheets decreased both with increased temperature and humidity.
TPU was infiltrated into vertically aligned, 3.5 mm‐long MWNT forests to produce continuously reinforced anisotropic nanocomposites, and thermomechanical and electrical testing has revealed multifunctionality which shows promise for numerous applications. A 1000% increase in the storage modulus at 70 °C was observed as compared to the neat TPU, and these continuously aligned composites showed electrical conductivity two orders‐of‐magnitude greater (≈1.5 S · cm?1) than randomly aligned composites prepared using CNTs from these forests. The heightened improvement for the continuously reinforced composite appears to be owed to the extremely high aspect ratio of these CNTs and the interconnected network which remains after infiltration.
PVA is reinforced with SWCNTs using green tea extract as a dispersant to achieve good dispersion of the SWCNTs in an organic solvent and finally high‐performance composite fibers. A combination of green tea extract/DMSO/SWCNT/PVA is found to disperse larger aggregates of SWCNTs to individual or thin bundles of a few nanotubes. Incorporation of 0.5 wt% SWCNTs into PVA fibers yields a tensile strength of 2.42 GPa, a Young's modulus of 46 GPa, toughness of 105 J · g?1 at a failure strain of 11%, and a loop strength of 245 MPa, much higher than the values of commercial PVA fibers. The incorporation of highly dispersed SWCNTs suppresses the fibrillation tendency of the PVA fibers. The applied load is effectively transferred from the matrix to the SWCNTs.
Coaxial electrospinning using surfactants as sheath fluid for preparing high‐quality polymer nanofibers is studied. PAN nanofibers are fabricated using this process with Triton X‐100 solutions in DMF. FESEM demonstrates that the Triton X‐100 solution has a significant influence on the quality of the nanofibers. The nanofiber diameters can be controlled by adjusting the concentration of Triton X‐100 in the sheath fluids with a scaling law D = 640 C?0.32. The mechanism of the influence of Triton X‐100 solutions on the formation of PAN fibers is discussed and it is demonstrated that coaxial electrospinning with surfactant solution is a facile method for achieving high‐quality polymer nanofibers.
Summary: Novel formaldehyde resins bearing diaminodiphenylmethane groups were synthesized by the polymerization of a mixture of diaminodiphenylmethane (DDM), cyclohexanone (CHx) and o‐cresol (o‐Cz) with formaldehyde (FA) in the presence of an acid catalyst (HCl). The resins obtained were characterized by spectral, elemental and thermal analysis and used as a hardener for epoxy resins. The curing and temperature behavior of these epoxy resin/formaldehyde systems were investigated using differential scanning calorimetry and thermogravimetry techniques. The resins had good thermal stability and the activation energies of degradation reactions had values between 70–98 kJ · mol?1.
The curing reaction of epoxy resins with the DDM/CHx/o‐Cz/formaldehyde resins. 相似文献
Elastomeric EPDM fibers with diameters of 200–400 nm are prepared by coaxial electrospinning of PVP/EPDM fibers, subsequent vulcanization of the polymers and finally removal of the outer PVP layer using ethanol. The initially applied PVP layer restricts the elastic recovery of the EPDM fibers. The crosslinking density of the EPDM fibers reaches 8.44 × 10?5 mol · cm?3. The original morphology of EPDM is preserved after removing the PVP layer. The ultrafine EPDM fibers are expected to be useful in many fields, such as brittle plastics toughening, as well as applications in extremely high or low temperatures.
Summary: Fibrillar silicate (FS)/rubber nanocomposites were successfully prepared by directly mixing modified FS with rubber matrix. It is found that FS could be separated into nano‐fibrils with diameters less than 100 nm by the shear forces during mixing. The stress‐strain characteristics of these composites are similar to those for short micro‐fiber/rubber composites (SFRC). Nevertheless, these FS/rubber composites have some outstanding advantages over the conventional SFRC, even though the reinforcing effect of FS is restricted due to its small shape aspect ratio. More importantly, the differences in mechanical properties of the composites in the two different directions show that SBR/FS and NBR/FS composites both exhibit obvious anisotropy, which strongly depends on the preparation process, FS concentration, and rubber matrix. These factors were thoroughly investigated in this paper, and it can be concluded that the anisotropy of the composites was due to the orientation of nano‐fibrils.
Aramid (kevlar‐49) fibers were surface treated by two different methods to induce roughness and then used to produce unidirectional nylon 66 based composites. The transcrystallinity generated around the treated fibers was characterized by SEM and polarized light microscopy and compared with the regular transcrystalline layers produced by pristine aramid under the same processing conditions. The treated fibers generated a double transcrystalline layer, the inner layer being thinner and more compact than the regular nylon 66 transcrystallinity. In addition, mechanical testing of the composites showed the longitudinal Young's modulus of the treated fiber composites to be significantly higher than the control in a wide range of fiber volume fractions.
Polarized light microscopy picture of double transcrystallinity in Br/NH3 treated aramid fiber reinforced nylon 66. 相似文献
Summary: Halogen‐free, flame retardant low density polyethylene (LDPE) composites, using magnesium hydroxide sulfate hydrate (MHSH) whiskers as a flame retardant, combined with microencapsulated red phosphorous (MRP) as a synergist, have been prepared using a two‐roll mill. Their fire properties were determined by using the limiting oxygen index (LOI), the UL‐94 test and cone calorimetry. The results showed that MRP was a good synergist in improving the flame retardance of the LDPE/MHSH whisker system. Poly[ethylene‐co‐(vinyl acetate)] (EVA), used as a compatibilizer, increased the fire performance of LDPE/MHSH whisker composites.
Pressure‐sensitive adhesives (PSA) were microencapsulated using simple and complex coacervation and aminoplaste. The microcapsules thus prepared were characterized by FTIR spectroscopy, particle size distribution, rheological behavior, and peeling tests. The microcapsules were isolated and found to be out of sticky indicating that the PSAs were indeed encapsulated. The prepared suspensions were deposited at the surface of a paper sheets and the dried labels were then pressed against each other. The ensuing complex was then characterized in terms of peeling forces and showed that the encapsulation using aminoplaste technique of a commercial PSA yielded peel energy of 170 J · m?2, which constitutes the recovering of about 68% of the adhesive power of the original nonencapsulated PSA.
The serviceability of non‐return valves has a major influence on the productivity of the injection molding process. During a meeting of experts held at our Institute, it was seen that closing behavior and wear are the key problems encountered in practice. The conducted investigations to tackle these questions have shown that both an improved closing behavior and a lower level of wear can be achieved by reducing the inside radius of the locking ring.
Pressure profile over the length of a non‐return valve (n = 0.4; = 25 000 mm3/s). 相似文献
This paper reports on a temperature‐controlled, solution‐based method to prepare diamine crosslinked Matrimid aerogels. Addition of a diamine to a preheated polymer solution resulted in a well‐dispersed solution, allowing formation of a homogeneous gel upon cooling. The gels (studied by FTIR and AFM) were dried by solvent extraction with supercritical CO2. The resulting aerogels showed surface areas of approximately 150 m2 · g?1 and porosities of 0.66–0.69 mL · g?1 with polymer domains and pore sizes of tens of nanometers. A room temperature‐prepared, inhomogeneous aerogel gave approximately 250 m2 · g?1 and 0.31 mL · g?1 with meso‐ and micropores. SEM images of the aerogels show similar surface features as AFM images of the Matrimid solvent gels.
Summary: The radical polymerization of different substituted methyl 2‐(bicyclo[3.1.0]hex‐1‐yl) acrylates, 1a – f , was initiated by 2,2′‐azoisobutyronitrile (AIBN) at 65 °C in chlorobenzene. The radical homopolymerization of 1a – f occurred through the opening of the cyclopropane ring, and lead to polymers with number‐average molecular weights of 13 000 to 434 400 g · mol?1 and glass transition temperatures between 77 and 121 °C. The monomers 1a – f showed a similar reactivity to MMA (in the copolymerization with MMA). Selected monomers were determined to be diluent monomers for dental filling composites and enable the preparation of composites that show a significantly reduced polymerization shrinkage, compared to composites based on dimethacrylate diluents.