Preparation,characterization, and photoluminescence study of PVA/ZnO nanocomposite films

ZnO nanoparticles with average diameter of 25 nm were synthesized by a modified sol–gel method and used in the preparation of (in wt.%) (100 − x) poly(vinyl alcohol) (PVA)/x ZnO nanocomposite films, with x = 0, 1, 2, 3, 4, and 5. The PVA/ZnO films were exposed to UV radiation for 96 h and their thermal, morphological, and spectroscopic properties were investigated. In inert atmosphere, the nanocomposite films showed lower thermal stability than the pure PVA film, and the calorimetric data suggest an interaction between PVA and ZnO in the nanocomposite films. Some crystalline phases could be seen in the films with ZnO, and a direct dependence on the ZnO concentration was also observed. The original structure of ZnO nanoparticles remained unaltered in the PVA matrix and they were uniformly distributed on the film surface. The roughness of the PVA film was not modified by the addition of ZnO; however, it increased after 96 h of UV irradiation, more significantly in the nanocomposite films. The films showed an absorption band centered at 370 nm and a broad emission band in the UV–vis region when excited at 325 nm.     

Electrical and optical ethanol sensitivity of thermally oxidized zinc oxide films

Zinc oxide (ZnO) films have been prepared by thermal oxidation of vacuum deposited zinc (Zn) films onto glass substrate kept at room temperature (35 °C). The structural, electrical, optical and gas sensing properties of films annealed at 350 and 500 °C have been investigated. X-ray diffraction measurements indicate that the ZnO films oxidized at these temperatures are polycrystalline in nature with (101) as preferential crystallographic orientation. Practically no change in lattice parameters of ZnO films is observed when oxidation temperature is increased from 350 to 500 °C. Field emission scanning electron microscopy shows nanoparticles and nanowires at the surface of the ZnO films oxidized at 350 and 500 °C, respectively. At room temperature (35 °C), the film oxidized at 350 °C shows a gradual increase of response up to 96% for 2000 ppm exposure of ethanol, while film oxidized at 500 °C could detect a response of 99% for 500 ppm beyond which it saturates. An increase in the optical absorbance of the film has also been observed when ethanol concentration increases from 50 to 200 ppm beyond which no significant change is noticed even up to 2000 ppm.     

Effect of annealing temperature on ZnO:Al/p-Si heterojunctions

Al-doped, zinc oxide (ZnO:Al) films with a 1.2 at.% Al concentration were deposited on p-type silicon wafers using a sol-gel dip coating technique to produce a ZnO:Al/p-Si heterojunction. Following deposition and subsequent drying processes, the films were annealed in vacuum at five different temperatures between 550 and 900 °C for 1 h. The resistivity of the films decreased with increasing annealing temperature, and an annealing temperature of 700 °C provided controlled current flow through the ZnO:Al/p-Si heterojunction up to 20 V. The ZnO:Al film deposited on a p-type silicon wafer with 1.2 at.% Al concentration was concluded to have the potential for use in electronic devices as a diode after annealing at 700 °C.     

Improving the conductance of ZnO thin film doping with Ti by using a cathodic vacuum arc deposition process

The Ti-doped ZnO films compared to un-doped ZnO films were deposited onto Corning XG glass substrates by using a cathodic vacuum arc deposition process in a mixture of oxygen and argon gases. The structural, electrical and optical properties of un-doped and Ti-doped ZnO films have been investigated. When the Ti target power is about 750 W, the incorporation of titanium atoms into zinc oxide films is obviously effective. Additionally, the resistivity of un-doped ZnO films is high and reduces to a value of 3.48 × 10⁻³ Ω-cm when Ti is incorporated. The Ti doped in the ZnO films gave rise to the improvement of the conductivity of the films obviously. The Ti-doped ZnO films have > 85% transmittance in a range of 400-700 nm.     

Porous nanostructured ZnO films deposited by picosecond laser ablation

Porous nanostructured polycrystalline ZnO films, free of large particulates, were deposited by picosecond laser ablation. Using a Zn target, zinc oxide films were deposited on indium tin oxide (ITO) substrates using a picosecond Nd:YVO₄ laser (8 ps, 50 kHz, 532 nm, 0.17 J/cm²) in an oxygen atmosphere at room temperature (RT). The morpho-structural characteristics of ZnO films deposited at different oxygen pressures (150–900 mTorr) and gas flow rates (0.25 and 10 sccm) were studied. The post-deposition influence of annealing (250–550 °C) in oxygen on the film characteristics was also investigated. At RT, a mixture of Zn and ZnO formed. At substrate temperatures above 350 °C, the films were completely oxidized, containing a ZnO wurtzite phase with crystallite sizes of 12.2–40.1 nm. At pressures of up to 450 mTorr, the porous films consisted of well-distinguished primary nanoparticles with average sizes of 45–58 nm, while at higher pressures, larger clusters (3.1–14.7 μm) were dominant, leading to thicker films; higher flow rates favored clustering.     

Novel synthesis of aligned Zinc oxide nanorods on a glass substrate by sonicated sol-gel immersion

For the first time, aligned ZnO nanorod structured thin films have been synthesized on a glass substrate, which had been coated with an Al-doped ZnO thin film, using the sonicated sol-gel immersion method. These nanorods were found to have an average diameter of 100 nm and an average length of 500 nm, with hexagonal wurtzite phase grew preferentially along the c-axis direction. A sharp ultra-violet (UV) emission centred at 383 nm corresponding to the free exciton recombination was observed in a room temperature photoluminescence (PL) spectrum. The prepared ZnO nanorod structured thin film is transparent in the visible region with an average transmittance of 78% in the 400-800 nm wavelength range and high absorbance properties in the UV region (< 400 nm). The results indicate that the prepared ZnO nanorods are suitable for ultra-violet photoconductive sensor applications.     

Highly luminescent columnar ZnO films grown directly on n-Si and p-Si substrates by low-temperature electrochemical deposition

In this study, nanocolumnar zinc oxide thin films were catalyst-free electrodeposited directly on n-Si and p-Si substrates, what makes an important junction for optoelectronic devices. We demonstrate that ZnO thin films can be grown on Si at low cathodic potential by electrochemical synthesis. The scanning electron microscopy SEM showed that the ZnO thin films consist of nanocolumns with radius of about 150 nm on n-Si and 200 nm on p-Si substrates, possess uniform size distribution and fully covers surfaces. X-ray diffraction (XRD) measurements show that the films are crystalline material and are preferably grown along (0 0 2) direction. The impact of thermal annealing in the temperature range of 150-800 °C on ZnO film properties has been carried out. Low-temperature photoluminescence (PL) spectra of the as-prepared ZnO/Si samples show the extremely high intensity of the near bandgap luminescence along with the absence of visible emission. The optical quality of ZnO thin films was improved after post-deposition thermal treatment at 150 °C and 400 °C in our experiments, however, the luminescence intensity was found to decrease at higher annealing temperatures (800 °C). The obtained results indicate that electrodeposition is an efficient low-temperature technique for the growth of high-quality and crystallographically oriented ZnO thin films on n-Si and p-Si substrates for device applications.     

Water repellent ZnO nanowire arrays synthesized by simple solvothermal technique

The authors report on the water repellent properties of quasialigned zinc oxide (ZnO) nanowire arrays grown by low-temperature solvothermal technique. The uniform and dense ZnO nanowires of average diameter ∼ 75 nm have been found to have hexagonal wurtzite type structure. The as synthesized ZnO nanowire surfaces have hydrophilic nature with a water contact angle of 73° ± 3°. The superhydrophobic behavior with a water contact angle of 145° ± 3° of the nanowire arrays has been realized due to the reduction of surface free energy after being coated with an octadecyltrichlorosilane (OTS) monolayer. This work may be of huge importance from the viewpoint of both the understanding of the mechanisms involved and industrial applications.     

The growth of nanoscale ZnO films by pulsed-spray evaporation chemical vapor deposition and their structural, electric and optical properties

Great interest in nanoscale thin films (sub-100 nm) has been stimulated by the developing demands of functional devices. In this paper, nanoscale zinc oxide (ZnO) thin films were deposited on glass substrates at 300 °C by pulsed-spray evaporation chemical vapor deposition. Scanning electron micrographs indicate uniform surface morphologies composed of nanometer-sized spherical particles. The growth kinetics and growth mode are studied and the relationship between the film thickness and the electric properties with respect to the growth mode is interpreted. X-ray diffraction shows that all ZnO films grown by this process were crystallized in a hexagonal structure and highly oriented with their c-axes perpendicular to the plane of the substrate. Optical measurements show transparencies above 85% in the visible spectral range for all films. The absorbance in the UV spectral range respects well the Beer-Lambert law, enabling an accurate optical thickness measurement, and the absorption coefficient was measured for a selected wavelength. The measured band gap energies exhibit an almost constant value of 3.41 eV for all films with different thicknesses, which attributed to the thickness-independent crystallite size.     

Solution processed Al doped ZnO film fabrication through electrohydrodynamic atomization

In this study, highly transparent, 250 nm thick films of Aluminum doped Zinc-oxide (ZnO:Al) are achieved on glass substrates at ambient conditions through a solution processing technique called electrohydrodynamic atomization. A 10 wt.% monodispersed solution containing 6% ZnO:Al nanoparticles (ZnO/Al₂O₃) in ethanol has been synthesized first and then used in the deposition process as the working solution. Pure and uniform transparent films with an average transmittance of 93% have been deposited with crystal structure exhibiting both zincite and gahnite phases. Surface composition purity has been confirmed using X-ray photoelectron spectroscopy technique and the clear indication of Zn-2p and Al-2p peaks confirms surface integrity. Fourier Transform Infrared analysis further confirms the presence of aluminum in the samples. The electrical properties are studied by recording and analyzing the current-voltage (I-V) measurements and the resistivity has been estimated from the slope of the IV-curve which is approximately 25 mΩ.cm. The layer roughness has been characterized using atomic force microscopy.     

Deposition of Na–N dual acceptor doped p-type ZnO thin films and fabrication of p-ZnO:(Na,N)/n-ZnO:Eu homojunction

Sodium and nitrogen dual acceptor doped p-type ZnO (ZnO:(Na, N)) films have been prepared by spray pyrolysis technique at a substrate temperature of 623 K. The ZnO:(Na, N) films are grown at a fixed N doping concentration of 2 at.% and varying the nominal Na doping concentration from 0 to 8 at.%. The XRD results show that all the ZnO:(Na, N) films exhibited (0 0 2) preferential orientation. The EDX and elemental mapping analysis shows the presence and distribution of Zn, O, Na and N in the deposited films. The Hall measurement results demonstrate that the Na–N dual acceptor doped ZnO films show excellent p-type conduction. The p-type ZnO:(Na, N) films with comparatively low resistivity of 5.60 × 10⁻² Ω cm and relatively high carrier concentration of 3.15 × 10¹⁸ cm⁻³ are obtained at 6 at.%. ZnO based homojunction is fabricated by depositing n-type layer (Eu doped ZnO) grown over the p-type layer ZnO:(Na, N). The current–voltage (I–V) characteristics measured from the two-layer structure show typical rectifying characteristics of p-n junction with a low turn on voltage of about 1.69 V. The ZnO:(Na, N) films exhibit a high transmittance (about >90%) and the average reflectance is 8.9% in the visible region. PL measurement shows near-band-edge (NBE) emission and deep-level (DL) emission in the ZnO:(Na, N) thin films.     

The uniformity of Al distribution in aluminum-doped zinc oxide films grown by atomic layer deposition

We investigated the aluminum distribution in aluminum-doped zinc oxide films grown by atomic layer deposition. Surface morphology, structure, composition and electrical properties of obtained films were studied. For the aluminum content less than 2 at.%, a periodicity of Al distribution along the layer depth was observed. This periodicity diminished significantly after annealing the samples in nitrogen atmosphere at 300 °C. For the Al content higher than 2 at.%, its distribution in ZnO:Al films was uniform within the depth measurement accuracy of ∼5-10 nm.     

Microstructural and optical properties of Ga-doped ZnO semiconductor thin films prepared by sol-gel process

Transparent thin films of Ga-doped ZnO (GZO), with Ga dopant levels that varied from 0 to 7 at.%, were deposited onto alkali-free glass substrates by a sol-gel process. Each spin-coated film was preheated at 300 °C for 10 min, and then annealed at 500 °C for 1 h under air ambiance. The effects of Ga dopant concentrations on crystallinity levels, microstructures, optical properties, and electrical resistivities of these ZnO thin films were systematically investigated. Photoluminescence spectra of GZO thin films were examined at room temperature. XRD results revealed that the undoped ZnO thin films exhibited a preferred orientation along the (002) plane and that the ZnO thin films doped with Ga showed degraded crystallinity. Experimental results also showed that Ga doping of ZnO thin films could markedly decrease surface roughness, improve transparency in the visible range, and produce finer microstructures than those of undoped ZnO thin films. The most promising films for transparent thin film transistor (TTFT) application produced in this study, were the 3 and 5 at.% Ga-doped ZnO thin films, both of which exhibited an average transmittance of 90.6% and an RMS roughness value of about 2.0 nm.     

Growth and characterization of electrosynthesised zinc oxide thin films

Zinc oxide (ZnO) films have been electrodeposited from an aqueous solution containing 0.1 M zinc nitrate as the electrolyte with pH around 5±0.1. The deposition was carried out by galvanostatic reduction with an applied cathodic current density in the range between 5 and 20 mA cm⁻². The influence of bath composition on the preparation of ZnO films is studied. The effects of zinc nitrate concentration and cathodic current density on the deposition rate of ZnO films were also studied. An optimum current density of 10 mA cm⁻² is identified for the growth of ZnO film with improved crystallinity and optical transmittance. The crystalline structure of the deposits studied by X-ray diffraction reveals the possibility of growing hexagonal ZnO films under suitable electrochemical conditions. The surface morphological studies by scanning electron micrographs revealed the presence of nodular appearance for films deposited at 800 °C bath temperatures.     

Power and pressure effects upon magnetron sputtered aluminum doped ZnO films properties

In this work, polycrystalline aluminum doped zinc oxide (ZnO:Al) films with c-axis (002) orientation have been grown on glass and silicon substrates by RF (radio frequency) magnetron sputtering technique, at room temperature. A systematic study of the effect of sputtering deposition parameters (i.e. RF power and argon gas pressure) on the structural, optical and electrical properties of the films was carried out. We observed that, with increasing RF power the growth rate increased, while it decreased with increasing gas pressure. As mentioned above, the films were polycrystalline in nature with a strong preferred (002) orientation. The intrinsic compressive stress was found to decrease with both increasing RF power and gas pressure, and near stress-free film was obtained at 200 W RF power and 2 × 10^− 1 Pa gas pressure. The obtained ZnO:Al films, not only have an average transmittance greater than 90% in the visible region, but also have an optical band gap between 3.33 and 3.47 eV depending on the sputtering parameters. Moreover, a low value of the electrical resistivity (~ 1.25 × 10^− 3 Ω cm) was obtained for the film deposited at 200 W and 2 × 10^− 3 mbar.     

Dependence of the electrical and optical properties on the bias voltage for ZnO:Al films deposited by r.f. magnetron sputtering

Aluminum-doped zinc oxide (ZnO:Al) thin films were deposited on glass, polycarbonate (PC), and polyethylene terephthalate (PET) substrates by r.f. magnetron sputtering. The substrate dc bias voltage varied from 0 V to 50 V. Structural, electrical and optical properties of the films were investigated. The deposition rate of ZnO:Al films on glass substrate initially increased with the bias voltage, and then decreased with further increasing bias voltage. It was found that the best films on glass substrate with a low as 6.2 × 10^− 4 Ω cm and an average transmittance over 80% at the wavelength range of 500-900 nm can be obtained by applying the bias voltage of 30 V. The properties of the films deposited on polymer substrate, such as PC and PET, have a similar tendency, with slightly inferior values to those on glass substrate.     

Effect of precursor concentration on structural and optical properties of ZnO microrods by spray pyrolysis

ZnO films have been prepared by spray pyrolysis technique on glass substrate at 500 °C. Zinc Chloride has been used as a precursor. Effect of precursor concentration on structural and optical properties has been investigated. Homogenous films are obtained with precursor concentration rating between 0.1 M and 0.4 M. X-ray diffraction patterns show that ZnO films are polycrystalline with (002) plane as preferential orientation. Field emission scanning electron microscopy images show that ZnO films consist of microrods that their length increases with increasing precursor concentration and tallest microrods obtain by spraying precursor with 0.3 M concentration. The optical transmittance spectrum shows that transmittance increases with decreasing of the concentration and transmittance reaches to a maximum value of about 80% for the visible region ZnO films prepared with 0.1 M. Photoluminescence spectra at room temperature show an ultraviolet emission at 3.21 eV that can be related to band gap and two visible emissions at 2.88 eV and 2.38 eV.     

Characterizations of gallium-doped ZnO films on glass substrate prepared by atmospheric pressure metal-organic chemical vapor deposition

Ga-doped zinc oxide (ZnO:Ga) films were grown on glass substrate by atmospheric pressure metal-organic chemical vapor deposition (AP-MOCVD) using diethylzinc and water as reactant gases and triethyl gallium (TEG) as an n-type dopant gas. The structural, electrical and optical properties of ZnO:Ga films obtained at various flow rates of TEG ranging from 1.5 to 10 sccm were investigated. X-ray diffraction patterns and scanning electron microscopy images indicated that Ga-doping plays an important role in forming microstructures in ZnO films. A smooth surface with a predominant orientation of (101) was obtained for the ZnO:Ga film grown at a flow rate of TEG = 7.5 sccm. Moreover, a lowest resistivity of 3.6 × 10^− 4 Ω cm and a highest mobility of 30.4 cm² V^− 1 s^− 1 were presented by the same sample, as evaluated by Hall measurement. Otherwise, as the flow rate of TEG was increased, the average transmittance of ZnO:Ga films increased from 75% to more than 85% in the wavelength range of 400-800 nm, simultaneously with a blue-shift in the absorption edge. The results obtained suggest that low-resistivity and high-transparency ZnO films can be obtained by AP-MOCVD using Ga-doping sufficiently to make the films grow degenerate and effect the Burstein-Moss shift to raise the band-gap energy from 3.26 to 3.71 eV.     

ZnO thin films prepared by pulsed laser deposition

Zinc oxide (ZnO) thin films were deposited on soda lime glass substrates by pulsed laser deposition (PLD) in an oxygen-reactive atmosphere. The structural, optical, and electrical properties of the as-prepared thin films were studied in dependence of substrate temperature and oxygen pressure. High quality polycrystalline ZnO films with hexagonal wurtzite structure were deposited at substrate temperatures of 100 and 300 °C. The RMS roughness of the deposited oxide films was found to be in the range 2-9 nm and was only slightly dependent on substrate temperature and oxygen pressure. Electrical measurements indicated a decrease of film resistivity with the increase of substrate temperature and the decrease of oxygen pressure. The ZnO films exhibited high transmittance of 90% and their energy band gap and thickness were in the range 3.26-3.30 eV and 256-627 nm, respectively.     

Pulsed laser deposited ZnO:In as transparent conducting oxide

Zinc oxide (ZnO) and indium doped ZnO (IZO) thin films with different indium compositions were grown by pulsed laser deposition technique on corning glass substrate. The effect of indium concentration on the structural, morphological, optical and electrical properties of the film was studied. The films were oriented along c-direction with wurtzite structure and highly transparent with an average transmittance of more than 80% in the visible wavelength region. The energy band gap was found to decrease with increasing indium concentration. High transparency makes the films useful as optical windows while the high band gap values support the idea that the film could be a good candidate for optoelectronic devices. The value of resistivity observed to decrease initially with doping concentration and subsequently increases. IZO with 1% of indium showed the lowest resistivity of 2.41 × 10⁻² Ω cm and large transmittance in the visible wavelength region. Especially 1% IZO thin film was observed to be a suitable transparent conducting oxide material to potentially replace indium tin oxide.