晶相可调TiO2多孔薄膜的低温制备及其性能

采用低温方法制备了金红石含量可调TiO2多孔薄膜,并用X射线衍射仪(XRD)、BET比表面积测量仪和透射电镜(TEM)对其进行了表征。以甲基橙(MO)为光催化反应的模型化合物,研究了TiO2多孔薄膜的光催化活性以及重复使用效果。结果表明:随金红石含量增加,TiO2薄膜的紫外光催化活性减小,而可见光催化活性增加;在金红石含量相近的条件下,水热合成TiO2薄膜的紫外和可见光催化活性均高于机械混合TiO2薄膜;TiO2薄膜的光催化重复使用性能良好。当其它实验条件相同时改变MO溶液的初始pH值,其最大降解效率发生在pH=3.00时。光电共同催化效果优于光催化。     

Pb掺杂TiO2薄膜的制备及光催化活性研究

以硝酸铅和钛酸丁酯[Ti(OBt)4]为前驱体，用溶胶—凝胶法在活性炭表面制成了Pb掺杂TiO2薄膜，并用X射线衍射(XRD)、紫外可见光谱(UV—VIS)、透射电镜(TEM)对制得的Pb掺杂TiO2薄膜进行了表征，分别用甲基橙水溶液的光催化脱色反应、有机磷农药—氧化乐果(omethoate)水溶液的光催化降解反应评价了不同Pb掺杂TiO2薄膜的光催化活性。结果表明，薄膜为金红石和锐钛矿的混合晶相，相对于未掺杂的TiO2薄膜，由于金红石含量的增加，不同Pb掺杂TiO2薄膜的吸收带发生了微小的红移，Pb掺杂使薄膜的光催化活性明显提高，当Pb／TiO2质量分数为1．7％时，薄膜显示出最高的光催化活性。TiO2薄膜中的Pb可能以Pb(Ⅳ)和Pb(Ⅱ)两种形态存在，在紫外光的辐射下，Pb(Ⅳ)和Pb(Ⅱ)可能通过浅势俘获TiO2的光生电子和空穴而发生相互转化，减少了光生电子和空穴的简单复合，从而提高了薄膜的光催化活性。     

Ce-TiO2光催化剂的制备与性能研究

采用溶胶-凝胶法制备了稀土Ce离子掺杂的纳米TiO2光催化剂(Ce-TiO2),通过XRD、FT-IR、UV-Vis、PL、Nano-sizer纳米粒度分析仪等对Ce-TiO2样品进行了表征和分析,并以亚甲基蓝(MB)作为目标降解物,考察了不同掺杂浓度及经不同温度热处理后的Ce-TiO2样品对MB的光催化降解效果,结果表明所制备样品的晶型均为锐钛矿相和金红石相的混晶相,Ce离子的掺杂拓展了TiO2在可见光区的光谱响应范围,提高了TiO2光催化活性。当pH值为1.5,Ce的掺杂量为n(Ce)∶n(TiO2)=1∶300,热处理温度为600℃条件下制备的样品其催化活性显著高于Degussa P25。     

镁掺杂对二氧化钛晶化行为的影响

采用溶胶-凝胶法在较低的热处理温度下制备了镁掺杂的TiO2。通过差热分析（DTA）并经过计算，发现在TiO2溶胶中加入Mg（NO3）2，可以让TiO2从无定型到锐钛矿相和锐钛矿相到金红石相的晶型转变活化能分别从137．7和163．7kJ／mol降低到70．5和108．4kJ／mol；采用X射线衍射分析（XRD），确定了在600℃热处理，获得了具有锐钛矿相和金红石相混晶的镁掺杂TiO2；通过紫外光催化降解甲基橙水溶液实验，证明了镁掺杂的TiO2薄膜的光催化活性高于未掺杂TiO2薄膜。     

Pb2+改性TiO2薄膜性能的研究

以玻璃为载体,采用溶凝胶胶法制备Pb2 -TiO2薄膜.采用AFM、XRD等技术,考察Pb2 掺杂后对TiO 2晶型结构和光催化活性的影响,结果表明,在相同制备条件下掺杂后使TiO2晶型由锐钛型向金红石型转变温度降低,经AFM分析,掺杂后使TiO2粒径增大,苯酚水溶液的光催化氧化分解反应结果表明,掺杂后TiO2的光催化活性有所提高.     

Fe、S共掺杂纳米TiO2的制备及性能研究

采用溶胶-凝胶法,以硫脲和三氯化铁为掺杂剂,制备了Fe-TiO2、S-TiO2和S-Fe-TiO2纳米光催化剂.通过XRD、SEM等方法对掺杂纳米TiO2进行了表征,以甲基橙为模型化合物对纳米TiO2粉体的光催化活性进行了评价.结果表明;纯TiO2、掺Fe-TiO2粉体全部为锐钛矿相,S-TiO2粉体中金红石相占8.1%,S-Fe-TiO2粉体中金红石相占26.9%.S和Fe、S共掺杂引起金红石相变温度的降低.掺Fe的纳米TiO2粉体粒子团聚少,分散要均匀,掺S和Fe、S共掺的TiO2粉体颗粒团聚现象较严重.S-TiO2和Fe-TiO2光催化荆在紫外光和日光灯下光催化活性都较好,而Fe-S-TiO2光催化活性没有提高.     

双微乳液法制备掺杂Fe~(3+)的纳米TiO_2及其光催化性能

为了研究双微乳液法在制备纳米级光催化剂的应用,以TiCl4和NH3.H2O为原料,采用十六烷基三甲基溴化铵-正丁醇-环己烷-水微乳体系制备Fe3+掺杂纳米TiO2,对粉末的晶体结构进行X射线衍射表征,并以其对p-甲酚的降解考察其光催化活性。结果表明,在较小的掺杂量时,Fe3+掺杂量的提高可以提高TiO2的光催化活性,进一步提高掺杂量将引起光催化活性的降低;掺杂Fe3+可导致纳米TiO2的粒径减小;Fe3+的半径较小以及Fe2O3的熔点较低均有利于TiO2从锐钛矿向金红石的相变;当Fe3+掺杂摩尔分数为0.06%,煅烧温度为550℃时,纳米TiO2的光催化活性最高,此时形成TiO2的锐钛矿和金红石相的混晶;乳液中含水量也会影响晶相的组成和粒径大小,随着含水量增加产物中出现了一定比例的金红石相。     

混晶结构纳米TiO2粉的光催化活性

以钛酸四丁酯为钛源制备混晶结构纳米TiO2粉,研究了纳米TiO2的光催化活性与颗粒晶相结构之间的关系．结果表明,当金红石相的质量分数少于18．53％,光催化活性随着金红石相的增多而降低;当金红石相的质量分数为18．53％-28．2％时,随着金红石相的增多,光催化活性逐渐增强,在28．2％附近具有最高的光催化活性,与纯锐钛矿结构纳米TiO2粉的光催化活性相当;金红石相含量继续增加,则光催化活性逐渐降低．适量金红石相的存在有利于锐钛矿相中的电荷分离,使光催化活性提高．     

N、Fe双掺杂的纳米TiO2制备及其性能研究

采用溶胶-凝胶法制备了N、Fe双掺杂的纳米TiO2光催化材料.借助XRD、XPS对制备的光催化材料进行表征,并通过晶粒尺寸、晶粒比表面积和晶格畸变率等的分析,研究了N、Fe双掺杂对TiO2性能的影响.研究结果表明,N、Fe双掺杂抑制了TiO2由锐钛矿向金红石的转变,明显延缓了TiO2相的转移;N、Fe双掺杂可明显减小晶...     

TiO2-SiO2双组分膜结构与光催化性能的研究

采用溶胶-凝胶法制备了不同Si／Ti比的TiO2-SiO2双组分膜．用紫外光照射亚甲基蓝的分解实验比较薄膜的光催化性能．通过XRD、FTIR、HRTEM、FE—SEM、AFM以及UV—VS—NIR分光光度计等分析手段对薄膜的结构和光学性能进行了表征．结果表明：适量SiO2的引入，显著提高了TiO2薄膜的光催化活性，Si／Ti比为0．2时薄膜的光催化活性为最佳．SiO2引入TiO2薄膜后，生成了Ti—O—Si玻璃相和无定形SiO2，这两种物相聚集在TiO2晶界周围，有效地阻止了TiO2的晶粒长大，提高了锐钛矿相向金红石相的转变温度，使复合薄膜经过500℃热处理后，只有锐钛矿相存在，有利于薄膜的光催化活性的提高．     

铁、铬离子掺杂对TiO_2薄膜光催化活性的影响

采用溶胶－凝胶法在釉面砖表面制备了均匀的ＴｉＯ２薄膜,并研究了铁、铬离子掺杂对ＴｉＯ２光催化性能影响．对罗丹明Ｂ的光降解实验表明,适量的铁、铬离子掺杂均可提高ＴｉＯ２薄膜的光催化活性,铁离子的掺杂效果明显高于铬离子,而铬离子的掺杂方式影响ＴｉＯ２薄膜的光催化活性,这主要基于它们不同的掺杂机理     

Ag-Si Co-doped TiO2 photocatalyst synthesized via a nonaqueous method

Ag-Si/TiO2 photocatalysts were synthesized in a nonaqueous system at 140 degrees C, and then annealed at different temperatures. The obtained photocatalysts were characterized by XRD, TEM, BET, TG-DTA, XPS, as well as UV-vis DRS. The results showed that All Ag-Si/TiO2 held an anatase phase and high thermal stability and the phase transformation from anatase to rutile was retarded to about 900 degrees C. The Ag-Si/TiO2 particles were highly mono-dispersed and the particles size became smaller compared to TiO2. Additionally, UV-vis light absorption shifted to visible region after Ag doping. Si weaved into the matrix of TiO2, while Ag dispersed on the surface of TiO2 particles. The visible light photocatalytic activity was evaluated by Rhodamine B (RhB) degradation in an aqueous solution under visible light irradiation. It was found that the photccatalytic activities of the obtained Ag-Si/TiO2 samples were all higher than those of pure TiO2 and Ag/TiO2, reaching the maximum at the Ag and Si content of 0.5 mol% and 20.0 mol%, respectively. The enhanced visible photocatalytic activity may be attributed to the simultaneous effects of silver and silicon co-doping.     

Microstructures and Photocatalytic Properties of S Doped Nanocrystalline TiO2 Films

The nanocrystalline S doped titanium dioxide films were successfully prepared by the improved sol-gel process. Here TiO(C₄H₉O)₄ and CS(NH₂)₂ were used as precursors of titania and sulfur, respectively. The as-prepared specimens were characterized using x-ray diffraction (XRD), x-ray energy dispersive spectroscopy (EDS), high-resolution field emission scanning electron microscopy (FE-SEM), Brunauer-Emmett-Teller (BET) surface area, and ultraviolet-visible diffuse reflectance spectroscopy. The photocatalytic activities of the films were evaluated by degradation of organic dyes in aqueous solution. The results of XRD, FE-SEM, and BET analyses indicated that the TiO₂ films were composed of nanoparticles. S doping could obviously not only suppress the formation of brookite phase but also inhibit the transformation of anatase to rutile at high temperature. Compared with pure TiO₂ film, S doped TiO₂ film exhibited excellent photocatalytic activity. It is believed that the surface microstructure of the modified films is responsible for improving the photocatalytic activity.     

Sb对直流反应磁控溅射制备TiO2薄膜的影响

用直流磁控溅射方法在Si(100)面及载玻片上制备了Sb掺杂TiO2薄膜.利用XRD光谱研究了Sb对其薄膜结晶情况的影响,用AFM观察其表面形貌,利用分光光度计测量了TiO2薄膜的光学特性及其对亚甲基蓝的分解活性,通过测量和计算表面对水的接触角来衡量光致亲水性.研究结果表明纯TiO2薄膜为锐钛矿型,适量Sb的掺杂能使TiO2薄膜的结晶有显著改善,并出现Ti2O3和金红石相TiO2,薄膜的光催化活性和光致亲水性明显改善.随着掺杂量的增加,TiO2薄膜的吸收边逐渐红移.但Sb掺杂过量时,破坏了二氧化钛原有的晶格结构,光催化活性和光致亲水性也相应降低.     

镍掺杂TiO2光催化剂的制备及光催化性能

采用溶胶-凝胶法制备镍掺杂纳米TiO2光催化剂。通过XRD、XPS、FT-IR、UV-Vis、PL等对Ni-TiO2样品进行表征和分析,并以亚甲基蓝(MB)作为目标降解物,考察经不同热处理温度及不同掺镍量Ni-TiO2样品对MB的降解效果。结果表明所制备的Ni-TiO2样品的晶型为锐钛矿相与金红石相的混晶相,镍掺杂抑制了晶粒的生长和晶型的转变,样品的吸收阈值波长向可见光红移约55nm,提高了TiO2的光催化活性。在普通日光灯下,经500℃热处理、掺镍量与TiO2摩尔比为1∶100条件下制备的催化剂其光催化活性明显高于Degussa P25。     

磷掺杂解决玻璃基TiO2光催化薄膜的钠扩散问题

采用溶胶-凝胶法在钠钙硅玻璃上制备了纯的和掺磷的TiO2薄膜,分别用AFM、XRD分析了薄膜的表面形貌和晶相组成.磷的掺入降低了TiO2锐钛矿相的结晶度,并且可以与从钠钙硅玻璃基片中扩散至薄膜的钠离子形成磷和钠的化合物,从而降低热处理过程中钠离子扩散对TiO2薄膜光催化活性产生的不利影响.利用罗丹明B作为光催化降解物质来表征TiO2薄膜的光催化活性,在相同的实验条件下,纯的TiO2薄膜的降解率为24.3%,掺磷5%的TiO2薄膜的降解率为50.3%.     

铁、铬离子掺杂对TiO2薄膜光催化活性的影响

采用溶胶-凝胶法在釉面砖表面制备了均匀的TiO2薄膜,并研究了铁、铬离子掺杂对TiO2光催化性能影响。对罗丹明B的光降解实验表明,适量的铁、铬离子掺杂均可提高TiO2薄膜的光催化活性,铁离子的掺杂效果明显高于铬离子,而铬离子的掺杂方式影响TiO2薄膜的光催化活性,这主要基于它们不同的掺杂机理。