共查询到20条相似文献,搜索用时 15 毫秒
1.
Synergistic flame‐retardant effect of halloysite nanotubes on intumescent flame retardant in LDPE
下载免费PDF全文
![点击此处可从《应用聚合物科学杂志》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Synergistic flame‐retardant effect of halloysite nanotubes (HNTs) on an intumescent flame retardant (IFR) in low‐density polyethylene (LDPE) was investigated by limited oxygen index (LOI), vertical burning test (UL‐94), thermogravimetric analysis (TGA), cone calorimeter (CC) test, and scanning electronic microscopy (SEM). The results of LOI and UL‐94 tests indicated that the addition of HNTs could dramatically increase the LOI value of LDPE/IFR in the case that the mass ratio of HNTs to IFR was 2/28 at 30 wt % of total flame retardant. Moreover, in this case the prepared samples could pass the V‐0 rating in UL‐94 tests. CC tests results showed that, for LDPE/IFR, both the heat release rate and the total heat release significantly decreased because of the incorporation of 2 wt % of HNTs. SEM observations directly approved that HNTs could promote the formation of more continuous and compact intumescent char layer in LDPE/IFR. TGA results demonstrated that the residue of LDPE/IFR containing 2 wt % of HNTs was obviously more than that of LDPE/IFR at the same total flame retardant of 30 wt % at 700°C under an air atmosphere, and its maximum decomposing rate was also lower than that of LDPE/IFR, suggesting that HNTs facilitated the charring of LDPE/IFR and its thermal stability at high temperature in this case. Both TGA and SEM results interpreted the mechanism on the synergistic effect of HNTs on IFR in LDPE, which is that the migration of HNTs to the surface during the combustion process led to the formation of a more compact barrier, resulting in the promotion of flame retardancy of LDPE/IFR. In addition, the mechanical properties of LDPE/IFR/HNTs systems were studied, the results showed that the addition of 0.5–2 wt % of HNTs could increase the tensile strength and the elongation at break of LDPE/IFR simultaneously. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40065. 相似文献
2.
The synergistic effects of fumed silica on the thermal and flame‐retardant properties of intumescent flame retardant (IFR) polypropylene based on the NP phosphorus‐nitrogen compound have been studied by Fourier transfer infrared (FTIR) spectroscopy, cone calorimeter test (CCT), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), limiting oxygen index (LOI), and UL‐94 tests. The LOI and UL‐94 data show that when ≤1 wt % fumed silica substituted for the IFR additive NP can increase 2 to 4% LOI values of the PP blends and keep the V‐0 rating. The data obtained from the CCT tests indicate the heat release rates (HRR) reduce by about 23% for the PP/NP sample with 0.5 wt % fumed silica, whereas the mass loss rates (MLR) and total heat release (THR) values are much lower than those of the PP/NP samples without fume silica. The TGA data demonstrate that a suitable amount of fumed silica can increase the thermal stability and charred residue of the PP/IFR/SiO2 blends after 500°C. The morphological structures of charred residues observed by SEM give positive evidence that a suitable amount of fumed silica can promote the formation of compact intumescent charred layers and prevent the charred layers from cracking, which effectively protects the underlying polymer from burning. The dynamic FTIR spectra reveal that the synergistic flame‐retardant mechanism of a suitable amount of fumed silica with IFR additive is due to its physical process in the condensed phases. However, a high loading of fumed silica restricts the formation of charred layers with P? O? P and P? O? C complexes formed from burning of polymer materials and destroys the swelling behavior of intumescent charred layers, which deteriorates the flame retardant and thermal properties of the PP/IFR blends. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010 相似文献
3.
Mesoporous silica SBA‐15 synthesized from Pluronic P123 and tetraethoxysilane was used as a synergistic agent on the flame retardancy of polypropylene (PP)/intumescent flame‐retardant (IFR) system. Limiting oxygen index (LOI), UL‐94 rating and thermogravimetric analysis were used to evaluate the synergistic effect of SBA‐15 on PP/IFR system. It showed that PP/IFR system could reach V‐0 with loading of SBA‐15 ranging from 0.5 to 3 wt%, while without SBA‐15 it had no rating at UL‐94 test. The LOI value increased from 25.5 to 32.2 when the loading of SBA‐15 was 1 wt%. The thermal stability of PP/IFR was improved in the presence of SBA‐15 and the amount of the char residue at 600° C was increased from 8.96 to 16.42 wt% when loading of SBA‐15 varied from 0.5 to 5 wt%. Laser Raman spectroscopy (LRS) and scanning electron microscopy were employed to study the morphology of the char residue of PP/IFR system with and without SBA‐15. Copyright © 2010 John Wiley & Sons, Ltd. 相似文献
4.
The flammability of polypropylene (PP) composites containing intumescent flame‐retardant additives, i.e., melamine pyrophosphate (MPP) and 1‐oxo‐4‐hydroxymethyl‐2,6,7‐trioxa‐1‐phosphabicyclo[2.2.2]octane (PEPA) was characterized by limiting oxygen index (LOI), UL 94 test, and cone calorimeter. In addition, the thermal degradation of the composites was studied using thermogravimetric analysis (TG) and real‐time Fourier transform infrared (RTFTIR). It has been found that the PP composite only containing MPP (or PEPA) does not show good flame retardancy even at 30% additive level. Compared with the PP/MPP binary composite, the LOI values of the PP/MPP/PEPA ternary composites at the same additive loading are all increased, and UL 94 rating of the ternary composite (PP3) studied is raised to V‐0 rating from no rating (PP/MPP). The cone calorimeter results show that the heat release rate of some ternary composites decreases in comparison with the binary composite. It is noted from the TG data that initial decomposition temperatures of ternary composites are lower than that of the binary composites. The RTFTIR study indicates that the PP/MPP/PEPA composites have higher thermal oxidative stability than the pure PP. POLYM. ENG. SCI., 2010. © 2009 Society of Plastics Engineers 相似文献
5.
Xiuyun Li Tairong Yan Xiaoping Hu Ke Wang Qiang Fu 《Polymer Engineering and Science》2013,53(2):410-416
A novel flame‐retardant system of isotactic polypropylene (iPP) is prepared using polyethylene glycol (PEG) and ammonium polyphosphate (APP). The flammability of iPP/PEG/APP composites containing 20 wt% APP improves with the increase of PEG concentration in the range of 3–15 wt%. The limit oxygen index (LOI) of iPP/PEG/APP composites reaches up to 30% with 15 wt% PEG concentration in the composites. At the same time, the mechanical properties of iPP/PEG/APP composites demonstrate that PEG can enhance toughness of iPP/APP composites. The results of cone calorimetry prove the synergistic effects of PEG and APP on intumescent flame‐retardant iPP, and those of the thermogravimetric analysis(TGA) reveal that iPP/PEG/APP samples decompose faster than iPP/APP composites. Investigated by scanning electronic microscopy (SEM), the morphology and structures of residues generated during LOI tests confirm the formation of effective char layer, and that the improvement of the flame retardancy and the impact strength of the composites are thanks to the presence of PEG. POLYM. ENG. SCI., 2013. © 2012 Society of Plastics Engineers 相似文献
6.
G. Sanchez‐Olivares A. Sanchez‐Solis F. Calderas L. Medina‐Torres E.E. Herrera‐Valencia A. Rivera‐Gonzaga O. Manero 《Polymer Engineering and Science》2013,53(9):2018-2026
In this work, the effect of processing conditions on the production of an intumescent flame‐retardant system is studied in polypropylene‐based compounds. Two distinct procedures were used: ultrasonic assisted single screw (with a static mixer die) and twin screw extrusion. The flame‐retardant, thermal, mechanical, morphological, and rheological properties were measured. It was found that the flame‐retardant intumescent content can be diminished from 30 phr (as usually used) to 21 phr using the application of ultrasonic waves during extrusion and with the addition of chemically modified clay to obtain a V0 classification according to UL94‐V standards. In addition, the processed materials presented improvements in the mechanical properties such as impact resistance (Izod Notched), strain at break and tenacity upon ultrasound application. The online application of ultrasound through a die that produces extensional flows improved greatly the dispersion and distribution of the particles of the intumescent system and the chemically modified clay in the polymer matrix. POLYM. ENG. SCI., 2013. © 2013 Society of Plastics Engineers 相似文献
7.
Amino trimethylene phosphonic acid piperazine (ATPIP) salt, as a novel charring agent, is prepared via a simple ionic reaction in distilled water using amino trimethylene phosphate (ATMP) and piperazine as raw materials. The synergistic flame retardant effect of ATPIP and ammonium polyphosphate (APP) as an intumescent flame retardant (IFR) is investigated by various characterization and testing methods. The results show that the polypropylene (PP)/modified APP with piperazine (MAPP)/ATPIP ternary blend passes UL-94 V-0 rating and achieve a limiting oxygen index (LOI) of 30% at a loading level of 25 wt% IFR (MAPP:ATPIP = 3:1). Meanwhile, the total smoke production (TSP) value of IFR-PP samples is 3.3 m2, which decreases by 93.2% compared with that of pure PP, exhibiting excellent smoke suppression performance. Besides, the analysis of gaseous pyrolysis products and char residue indicates that the IFR-PP samples show a synergistic flame-retardant mechanism including the gas phase and the condensed phase. 相似文献
8.
The phosphoric acid‐pentaerythritol‐melamine copolymer, which is composed of three main components of intumescent flame retardant (IFR) and has optimal intumescent degree, was selected as IFR. The influence of meleated polypropylene (PP‐g‐MAH) on the properties and compatibility of IFR polypropylene (PP) composites were studied. The results obtained from mechanical tests, rheological behavior of composites, and scanning electron microscope showed that PP‐g‐MAH was a true coupling agent for IFR/PP blends and did not change the necessary flame retardancy. The cocrystallization between bulk PP and PP segments of PP‐g‐MAH was also proven by WAXD analysis. Flow test showed that the flow behaviors of composites in the melt are those of a pseudoplastic and it is very small for PP‐g‐MAH affecting rheological behavior of the PP/IFR composite. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 257–262, 2002 相似文献
9.
A novel charring agent (CNCA‐DA) containing triazine and benzene ring, using cyanuric chloride, aniline, and ethylenediamine as raw materials, was synthesized and characterized. The effects of CNCA‐DA on flame retardancy, thermal degradation, and flammability properties of polypropylene (PP) were investigated by limited oxygen index (LOI), vertical burning test (UL‐94), thermogravimetric analysis (TGA), and cone calorimeter test (CCT). The TGA results showed that CNCA‐DA had a good char forming ability, and a high initial temperature of thermal degradation; the char residue of CNCA‐DA reached 18.5% at 800°C; Ammonium polyphosphate (APP) could improve the char residue of APP/CNCA‐DA system, the char residue reached 31.6% at 800°C. The results from LOI and UL‐94 showed that the intumescent flame retardant (IFR) containing CNCA‐DA and APP was very effective in flame retardancy of PP. When the mass ratio of APP and CNCA‐DA was 2 : 1, and the IFR loading was 30%, the IFR showed the best effect; the LOI value reached 35.6%. It was also found that when the IFR loading was only 20%, the flame retardancy of PP/IFR can still pass V‐0 rating in UL‐94 tests, and its LOI value reached 27.1%. The CCT results demonstrated that IFR could clearly change the decomposition behavior of PP and form a char layer on the surface of the composites, consequently resulting in efficient reduction of the flammability parameters, such as heat release rate (HRR), total heat release (THR), smoke production rate (SPR), total smoke production (TSP), and mass loss (ML). © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012 相似文献
10.
Thermal degradation and combustion behavior of intumescent flame‐retardant polypropylene with novel phosphorus‐based flame retardants
下载免费PDF全文
![点击此处可从《应用聚合物科学杂志》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Lingang Lu Nan Guo Xiaodong Qian Shousheng Yang Xuebao Wang Jing Jin Gaosong Shao 《应用聚合物科学杂志》2018,135(10)
The objective of this study was to develop an environmentally friendly fire‐retardant polypropylene (PP) with significantly improved fire‐retardancy performance with a novel flame‐retardant (FR) system. The system was composed of ammonium polyphosphate (APP), melamine (MEL), and novel phosphorus‐based FRs. Because of the synergistic FR effects among the three FRs, the FR PP composites achieved a V‐0 classification, and the limiting oxygen index reached as high as 36.5%. In the cone calorimeter test, both the peak heat‐release rate (pHRR) and total heat release (THR) of the FR PP composites were remarkably reduced by the incorporation of the novel FR system. The FR mechanism of the MEL–APP–FR–PP composites was investigated through thermogravimetric analysis and char residue characterization, and the results reveal that the addition of MEL–APP–FRs promoted the formation of stable intumescent char layers. This led to the reduction of pHRR and THR and resulted in the improvement of the fire retardancy. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 45962. 相似文献
11.
Supported nickel catalyst (Ni‐Cat) was used as a catalyst to improve the flame retardancy of intumescent flame‐retardants (IFR) systems based on ammonium polyphosphate and pentaerythritol (PETOL) in polypropylene (PP) matrix. Limited oxygen index (LOI), UL‐94 rating, and thermogravimetric analysis were used to characterize the flame retardancy and thermal stability of the PP systems, and field emission scanning electron microscopy (FE‐SEM) and Fourier transformed infrared spectroscopy (FTIR) were used to analyze the microstructure and composition of the chars formed during measuring LOI value and after combustion at 800°C. The catalytic effect of Ni‐Cat was shown in an increase of LOI, a change in the char microstructure, and improvement of the thermal stability in the PP systems, which result from the synergistic effect of Ni‐Cat and IFR. The results from FE‐SEM and FTIR spectra of the char can explain how this synergistic effect happened. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 5988–5993, 2006 相似文献
12.
The synergistic mechanism of tetrabutyl titanate (TBT) in the intumescent flame‐retardant polypropylene (PP) composites was investigated in this work. The intumescent flame‐retardant was composed of pentaerythritol (PER) as a carbonizing agent ammonium polyphosphate (APP) as a dehydrating agent and blowing agent. Five different concentrations (1, 1.25, 1.5, 1.75, 2 wt %) of TBT were incorporated into flame retardant formulation to investigate the synergistic mechanism. The thermal degradation and flammability of composites were characterized by thermogravimetric analysis (TGA), limiting oxygen index (LOI), and UL‐94 tests. The morphology and chemical structure of char layer was characterized by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and energy dispersive spectrometer (EDS). The results showed that LOI was increased from 27.8 to 32.5%, with the increase of TBT content from 0 to 1.5 wt %. Results from SEM, and FTIR demonstrated that TBT could react with APP and PER to form the stable char layer. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 4255–4263, 2013 相似文献
13.
Synergistic effects of dual imidazolium polyoxometalates on intumescent flame retardant polypropylene
下载免费PDF全文
![点击此处可从《应用聚合物科学杂志》网站下载免费的PDF全文](/ch/ext_images/free.gif)
The role of dual imidazolium polyoxometalates (POMs) in the flame retardancy of polypropylene/intumescent flame retardant (PP/IFR) composites was studied. The results showed that the structures of dual imidazolium POMs have a great effect on the flame retardancy of PP composites. The dual imidazolium POMs based on an ethyl group (EMIPMA) obtain the best flame retardant efficiency. With 15.5 wt % IFR and 0.5 wt % EMIPMA, the PP composites reach a limiting oxygen index of 25.7 and the UL‐94 V‐0 standard. However, the dual imidazolium POMs containing a butyl (BMIPMA) or hexyl (HMIPMA) group cannot achieve the UL‐94 V‐0 standard at the same formulation. Dual imidazolium POMs not only promote the formation of good char, but also induce the formation of intumescent char with a hierarchical and microporous structure that helps to prevent gas and heat from transferring from the flame to the resin. Therefore, the flame retardancy of PP/IFR composites is improved. However, excessive combustible components produced by BMIPMA or HMIPMA deteriorate the flame retardancy of PP/IFR composites. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 45491. 相似文献
14.
The synergistic effects of some metal oxides on novel intumescent flame retardant (IFR)–thermoplastic polyurethane (TPU) composites were evaluated by limiting oxygen index (LOI), vertical burning test (UL‐94), thermogravimetric analysis (TGA), cone calorimetry, and scanning electron microscopy. The experimental data indicated that the metal oxides enhanced the LOI value and restricted the dropping of the composites. The IFR–TPU composites passed the UL‐94 V‐0 rating test (1.6 mm) in the presence of magnesium oxide (MgO) and ferric oxide (Fe2O3) at 35 wt % IFR loading, whereas only the MgO‐containing IFR–TPU composite reached a UL‐94 V‐0 rating at 30 wt % IFR loading. The TGA results show that the metal oxides had different effects on the process of thermal degradation of the IFR–TPU compositions. MgO easily reacted with polyphosphoric acid generated by the decomposition of ammonium polyphosphate (APP) to produce magnesium phosphate. MgO and Fe2O3 showed low flammability and smoke emission due to peak heat release rate, peak smoke production rate, total heat release, and total smoke production (TSP). However, zinc oxide brought an increase in the smoke production rate and TSP values. Among the metal oxides, MgO provided an impressive promotion on the LOI value. The alkaline metal oxide MgO more easily reacted with APP in IFRs. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011 相似文献
15.
A new intumescent flame retardant (IFR) system consisting of ammonium polyphosphate (APP) and charing‐foaming agent (CFA) and a little organic montmorillonite (OMMT) was used in low‐density polyethylene (LLDPE)/ethylene‐vinyl acetate (EVA) composite. According to limiting oxygen index (LOI) value and UL‐94 rating obtained from this work, the reasonable mass ratio of APP to CFA was 3 : 1, and OMMT could obviously enhance the flame retardancy of the composites. Cone calorimeter (CONE) and thermogravimetric analysis (TGA) were applied to evaluate the burning behavior and thermal stability of IFR‐LLDPE/EVA (LLDPE/EVA) composites. The results of cone calorimeter showed that heat release rate peak (HRR‐peak) and smoke production rate peak (SPR‐peak) and time to ignition (TTI) of IFR‐LLDPE/EVA composites decreased clearly compared with the pure blend. TGA data showed that IFR could enhance the thermal stability of the composites at high temperature and effectively increase the char residue. The morphological structures of the composites observed by scanning electron microscopy (SEM) and X‐ray diffraction (XRD) demonstrated that OMMT could well disperse in the composites without exfoliation, and obviously improve the compatibility of components of IFR in LLDPE/EVA blend. The morphological structures of char layer obtained from Cone indicated that OMMT make the char layer structure be more homogenous and more stable. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009 相似文献
16.
Nanocomposite of thermoplastic elastomer ethylene‐octene copolymer/maleated ethylene‐octene (POE/POE‐g‐MAH) with organo‐montmorillonite (OMMT, 11 wt %) as masterbatch have been obtained by melt blending and it has been characterized by transmission electron microscopy (TEM). Flame retardant POE/POE‐g‐MAH/OMMT/ammonium polyphosphate‐pentaerythritol (APP‐PER) (an intumescent flame retardant with 75 wt % ammonium polyphosphate and 25 wt % pentaerythritol) composites were prepared by using melting processing to study their structures, flame‐retardancy, thermal, and mechanical properties. TEM showed exfoliated structures throughout POE/POE‐g‐MAH/OMMT masterbatch and POE/POE‐g‐MAH/OMMT/APP‐PER nanocomposites. Synergistic effect was observed between OMMT and APP‐PER resulting in significant improvements on thermal stability, flame‐retardancy and mechanical properties in the POE/POE‐g‐MAH/OMMT/APP‐PER nanocomposites. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013 相似文献
17.
The ammonium polyphosphate (APP)–pentaerythritol (PT)–melamine (M) system was selected as an intumescent flame retardant (IFR). The influence of dichromic acid–etched polypropylene (EPP) on the properties and compatibility of IFR/polypropylene (PP) composites was studied. The results obtained from mechanical tests and SEM showed that EPP was a true coupling agent for IFR/PP blends, but without changing the necessary flame retardancy. The cocrystallization between bulk PP and PP segments of EPP was confirmed by WAXD analysis. Flow tests showed that the flow behavior of composites in the melt is that of a pseudoplastic liquid, which is significant for EPP's effect on the rheological behavior of IFR/PP composite. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 1388–1391, 2004 相似文献
18.
Study on effect of polydimethylsiloxane in intumescent flame retardant polypropylene 总被引:2,自引:0,他引:2
The effect of polydimethylsiloxane (PDMS) in intumescent flame retarded polypropylene (PP) containing melamine phosphate (MP)
was studied using limiting oxygen index (LOI), UL-94 test, thermogravimetric analysis (TG), real time Fourier transform infrared
(FTIR) and pyrolysis/gas chromatogram/mass spectrometry (Py–GC/MS). It was found that the addition of PDMS into the PP/MP
composites leads to a decrease in the LOI values of the PP/MP/PDMS composites, and the values increase gradually with the
increase of the PDMS content. The UL-94 test results indicate that the PP/MP/PDMS composite with 30% PDMS reaches the V-0
rating compared with no rating of the PP/MP composite at the same MP loading. The water resistance of the PP/MP/PDMS composites
was investigated, and the improved water leaching of MP was observed. The TG and RTFTIR results illustrate the thermal stability
of the PP/MP composites containing PDMS is improved. Moreover, the pyrolysis of the PP/MP/PDMS composites was studied by the
Py–GC/MS method. 相似文献
19.
A phosphoric acid–pentaerythritol–melamine copolymer was selected as an intumescent flame retardant (IFR). The influence of α‐methacrylic acid grafted polypropylene (PP‐g‐MAA) on the properties and compatibility of IFR/PP composites was studied. The results obtained from mechanical tests and scanning electron microscopy showed that PP‐g‐MAA was a true coupling agent for IFR/PP blends, but it did not change the necessary flame retardancy. The cocrystallization between bulk PP and PP segments of PP‐g‐MAA was proved by wide‐angle X‐ray diffraction analysis. A flow test showed that the flow behaviors of composites in the melt were those of a pseudoplastic liquid and it was very small for PP‐g‐MAA and affected the rheological behavior of the PP/IFR composite. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 3128–3132, 2002; DOI 10.1002/app.10099 相似文献
20.
Zaihang Zheng Songfeng Liu Bingnan Wang Ting Yang Xuejun Cui Hongyan Wang 《Polymer Composites》2015,36(9):1606-1619
A novel phosphorus‐ and nitrogen‐containing flame retardant (melamine phytate) was synthesized via the reaction between melamine and phytic acid. The chemical structure of melamine phytate (MPA) was confirmed by Fourier transform‐infrared spectra (FT‐IR) and elemental analysis. And the thermal behavior of MPA investigated by thermogravimetric analysis (TGA) demonstrates that MPA possesses a good char‐forming ability at high temperature. Besides, limiting oxygen index (LOI) and vertical burning tests (UL‐94) illustrate that polypropylene/melamine phytate/dipentaerythritol (PP/MPA/DPER) (70/22.5/7.5) can reach the LOI value of 28.5% and achieve V‐0 rating at the flame retardant loading of 30 wt%. Except that, the thermal weight loss of MPA and DPER in PP composites was investigated by TGA in detail. Moreover, the char residue of PP composite after combustion was systematically analyzed by FT‐IR, scanning electron microscope (SEM) and X‐ray photoelectron spectroscopy (XPS), which can further propose and confirm the flame retardant mechanism. POLYM. COMPOS., 36:1606–1619, 2015. © 2014 Society of Plastics Engineers 相似文献