Ultrafast Formation of Amorphous Bimetallic Hydroxide Films on 3D Conductive Sulfide Nanoarrays for Large‐Current‐Density Oxygen Evolution Electrocatalysis

Developing nonprecious oxygen evolution electrocatalysts that can work well at large current densities is of primary importance in a viable water‐splitting technology. Herein, a facile ultrafast (5 s) synthetic approach is reported that produces a novel, efficient, non‐noble metal oxygen‐evolution nano‐electrocatalyst that is composed of amorphous Ni–Fe bimetallic hydroxide film‐coated, nickel foam (NF)‐supported, Ni₃S₂ nanosheet arrays. The composite nanomaterial (denoted as Ni‐Fe‐OH@Ni₃S₂/NF) shows highly efficient electrocatalytic activity toward oxygen evolution reaction (OER) at large current densities, even in the order of 1000 mA cm^?2. Ni‐Fe‐OH@Ni₃S₂/NF also gives an excellent catalytic stability toward OER both in 1 m KOH solution and in 30 wt% KOH solution. Further experimental results indicate that the effective integration of high catalytic reactivity, high structural stability, and high electronic conductivity into a single material system makes Ni‐Fe‐OH@Ni₃S₂/NF a remarkable catalytic ability for OER at large current densities.     

ZIF衍生钴镍笼状双金属硫化物高效双功能电催化剂

锌-空气电池的阴极氧还原反应(ORR)动力迟缓,急需开发活性高、成本低的阴极催化剂。本文采用两次热解法合成了沸石咪唑酯骨架结构(ZIF)衍生的多孔碳负载Co、Ni双金属硫化物笼状纳米颗粒材料,通过SEM、XRD、Raman、N₂吸附比表面分析、电化学分析等对负载Co、Ni笼状双金属硫化物的多孔碳进行形貌、结构表征以及性能测试。结果表明,金属硫化物导电性能优异,且热解后的多孔碳结构会暴露更多活性位点,具有优异的电催化活性,ORR性能测试中,其半波电位可达0.89 V,优于商用Pt/C催化剂的0.85 V。OER性能在电流密度为10 mA/cm²时电位为1.79 V,与商用IrO₂(电位可达1.68 V)相当。本文制备的笼状双金属硫化物具有优异的性能,可作为锌-空气电池的优异双功能电催化剂。     

Atomic‐Level Fe‐N‐C Coupled with Fe3C‐Fe Nanocomposites in Carbon Matrixes as High‐Efficiency Bifunctional Oxygen Catalysts

Highly active and durable bifunctional oxygen electrocatalysts are of pivotal importance for clean and renewable energy conversion devices, but the lack of earth‐abundant electrocatalysts to improve the intrinsic sluggish kinetic process of oxygen reduction/evolution reactions (ORR/OER) is still a challenge. Fe‐N‐C catalysts with abundant natural merits are considered as promising alternatives to noble‐based catalysts, yet further improvements are urgently needed because of their poor stability and unclear catalytic mechanism. Here, an atomic‐level Fe‐N‐C electrocatalyst coupled with low crystalline Fe₃C‐Fe nanocomposite in 3D carbon matrix (Fe‐SAs/Fe₃C‐Fe@NC) is fabricated by a facile and scalable method. Versus atomically FeN_x species and crystallized Fe₃C‐Fe nanoparticles, Fe‐SAs/Fe₃C‐Fe@NC catalyst, abundant in vertical branched carbon nanotubes decorated on intertwined carbon nanofibers, exhibits high electrocatalytic activities and excellent stabilities both in ORR (E_1/2, 0.927 V) and OER (E_J=10, 1.57 V). This performance benefits from the strong synergistic effects of multicomponents and the unique structural advantages. In‐depth X‐ray absorption fine structure analysis and density functional theory calculation further demonstrate that more extra charges derived from modified Fe clusters decisively promote the ORR/OER performance for atomically FeN₄ configurations by enhanced oxygen adsorption energy. These insightful findings inspire new perspectives for the rational design and synthesis of economical–practical bifunctional oxygen electrocatalysts.     

Active Site Engineering in Porous Electrocatalysts

Electrocatalysis is at the center of many sustainable energy conversion technologies that are being developed to reduce the dependence on fossil fuels. The past decade has witnessed significant progresses in the exploitation of advanced electrocatalysts for diverse electrochemical reactions involved in electrolyzers and fuel cells, such as the hydrogen evolution reaction (HER), the oxygen reduction reaction (ORR), the CO₂ reduction reaction (CO₂RR), the nitrogen reduction reaction (NRR), and the oxygen evolution reaction (OER). Herein, the recent research advances made in porous electrocatalysts for these five important reactions are reviewed. In the discussions, an attempt is made to highlight the advantages of porous electrocatalysts in multiobjective optimization of surface active sites including not only their density and accessibility but also their intrinsic activity. First, the current knowledge about electrocatalytic active sites is briefly summarized. Then, the electrocatalytic mechanisms of the five above-mentioned reactions (HER, ORR, CO₂RR, NRR, and OER), the current challenges faced by these reactions, and the recent efforts to meet these challenges using porous electrocatalysts are examined. Finally, the future research directions on porous electrocatalysts including synthetic strategies leading to these materials, insights into their active sites, and the standardized tests and the performance requirements involved are discussed.     

Iridium‐Based Multimetallic Porous Hollow Nanocrystals for Efficient Overall‐Water‐Splitting Catalysis

The development of active and durable bifunctional electrocatalysts for overall water splitting is mandatory for renewable energy conversion. This study reports a general method for controllable synthesis of a class of IrM (M = Co, Ni, CoNi) multimetallic porous hollow nanocrystals (PHNCs), through etching Ir‐based, multimetallic, solid nanocrystals using Fe³⁺ ions, as catalysts for boosting overall water splitting. The Ir‐based multimetallic PHNCs show transition‐metal‐dependent bifunctional electrocatalytic activities for both the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) in acidic electrolyte, with IrCo and IrCoNi PHNCs being the best for HER and OER, respectively. First‐principles calculations reveal a ligand effect, induced by alloying Ir with 3d transition metals, can weaken the adsorption energy of oxygen intermediates, which is the key to realizing much‐enhanced OER activity. The IrCoNi PHNCs are highly efficient in overall‐water‐splitting catalysis by showing a low cell voltage of only 1.56 V at a current density of 2 mA cm^?2, and only 8 mV of polarization‐curve shift after a 1000‐cycle durability test in 0.5 m H₂SO₄ solution. This work highlights a potentially powerful strategy toward the general synthesis of novel, multimetallic, PHNCs as highly active and durable bifunctional electrocatalysts for high‐performance electrochemical overall‐water‐splitting devices.     

Atomic Layer Deposition‐Assisted Fabrication of Co‐Nanoparticle/N‐Doped Carbon Nanotube Hybrids as Efficient Electrocatalysts for the Oxygen Evolution Reaction

Transition metal (TM)‐based carbon hybrids have numerous applications in the field of regenerative electrochemical energy. The synergetic effects of high conductivity of carbon supports and abundant catalytic active sites in TMs make these hybrids promising oxygen evolution reaction (OER) electrocatalysts. However, strategies for modulating the catalytic active species in the above hybrids are limited despite being highly sought after. Furthermore, the exact roles of chemical species in the hybrids (e.g., N, C, or TM) mainly responsible for this high OER performance remain unknown. Herein, an innovative approach based on atomic layer deposition is developed to tune the true active species in Co nanoparticle/N‐doped carbon nanotube (Co/N‐CNT) hybrids. Specifically, the configuration predominantly promoting water oxidation in an alkaline medium is identified as pyridinic N–Co–C. Furthermore, a physicochemical intact interface between metallic Co nanoparticles and conductive N‐CNTs is demonstrated to induce synergetic effects for accelerating charge transfer and enhancing electrocatalytic activity as well as stability in the hybrid catalysts. The optimized hybrid catalyst is revealed to exhibit outstanding alkaline OER activity and stability, outperforming RuO₂, a benchmark novel OER electrocatalyst.     

Reduced Graphene Oxide‐Wrapped Co9–xFexS8/Co,Fe‐N‐C Composite as Bifunctional Electrocatalyst for Oxygen Reduction and Evolution

Searching for highly efficient bifunctional electrocatalysts for the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) using nonnoble metal‐based catalysts is essential for the development of many energy conversion systems, including rechargeable fuel cells and metal–air batteries. Here, Co_9–xFe_xS₈/Co,Fe‐N‐C hybrids wrapped by reduced graphene oxide (rGO) (abbreviated as S‐Co_9–xFe_xS₈@rGO) are synthesized through a semivulcanization and calcination method using graphene oxide (GO) wrapped bimetallic zeolite imidazolate framework (ZIF) Co,Fe‐ZIF (CoFe‐ZIF@GO) as precursors. Benefiting from the synergistic effect of OER active CoFeS and ORR active Co,Fe‐N‐C in a single component, as well as high dispersity and enhanced conductivity derived from rGO coating and Fe‐doping, the obtained S‐Co_9–xFe_xS₈@rGO‐10 catalyst shows an ultrasmall overpotential of ≈0.29 V at 10 mA cm^?2 in OER and a half‐wave potential of 0.84 V in ORR, combining a superior oxygen electrode activity of ≈0.68 V in 0.1 m KOH.     

Turning Waste into Treasure: Regulating the Oxygen Corrosion on Fe Foam for Efficient Electrocatalysis

Iron corrosion causes a great damage to the economy due to the function attenuation of iron‐based devices. However, the corrosion products can be used as active materials for some electrocatalytic reactions, such as oxygen evolution reaction (OER). Herein, the oxygen corrosion on Fe foams (FF) to synthesize effective self‐supporting electrocatalysts for OER, leading to “turning waste into treasure,” is regulated. A dual chloride aqueous system of “NaCl‐NiCl₂” is employed to tailor the structures and OER properties of corrosion layers. The corrosion behaviors identify that Cl^? anions serve as accelerators for oxygen corrosion, while Ni²⁺ cations guarantee the uniform growth of corrosion layers owing to the appeared chemical plating. The synergistic effect of “NaCl‐NiCl₂” generates one of the highest OER activities that only an overpotential of 212 mV is required to achieve 100 mA cm^?2 in 1.0 m KOH solution. The as‐prepared catalyst also exhibits excellent durability over 168 h (one week) at 100 mA cm^?2 and promising application for overall water splitting. Specially, a large self‐supporting electrode (9 × 10 cm²) is successfully synthesized via this cost‐effective and easily scale‐up approach. By combining with corrosion science, this work provides a significant stepping stone in exploring high‐performance OER electrocatalysts.     

Slower Removing Ligands of Metal Organic Frameworks Enables Higher Electrocatalytic Performance of Derived Nanomaterials

The widely used route of high‐temperature pyrolysis for transformation of Prussian blue analogs (PBAs) to functional nanomaterials leads to the fast removal of CN^? ligands, and thus the formation of large metal aggregates and the loss of porous structures inside PBAs. Here, a controllable pyrolysis route at low temperature is reported for retaining the confined effect of CN^? ligands to metal cations during the whole pyrolysis process, thereby preparing high‐surface‐area cubes comprising disordered bimetallic oxides (i.e., Co₃O₄ and Fe₂O₃) nanoparticles. The disordered structure of Co₃O₄ enables the exposure of abundant oxygen vacancies. Notably, for the first time, it is found that the in situ generated CoOOH during the oxygen evolution reaction (OER) can inherit the oxygen vacancies of pristine Co₃O₄ (i.e., before OER), and such CoOOH with abundant oxygen vacancies adsorbs two ^?OH in the following Co³⁺ to Co⁴⁺ for markedly promoting OER. However, during the similar step, the ordered Co₃O₄ with less oxygen vacancies only involves one ^?OH, resulting in the additional overpotentials for adsorbing ^?OH. Consequently, with high surface area and disordered Co₃O₄, the as‐synthesized electrocatalysts have a low potential of 237 mV at 10 mA cm^?2, surpassing most of reported electrocatalysts.     

Bifunctional Transition Metal Hydroxysulfides: Room‐Temperature Sulfurization and Their Applications in Zn–Air Batteries

Bifunctional electrocatalysis for oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) constitutes the bottleneck of various sustainable energy devices and systems like rechargeable metal–air batteries. Emerging catalyst materials are strongly requested toward superior electrocatalytic activities and practical applications. In this study, transition metal hydroxysulfides are presented as bifunctional OER/ORR electrocatalysts for Zn–air batteries. By simply immersing Co‐based hydroxide precursor into solution with high‐concentration S^2?, transition metal hydroxides convert to hydroxysulfides with excellent morphology preservation at room temperature. The as‐obtained Co‐based metal hydroxysulfides are with high intrinsic reactivity and electrical conductivity. The electron structure of the active sites is adjusted by anion modulation. The potential for 10 mA cm^?2 OER current density is 1.588 V versus reversible hydrogen electrode (RHE), and the ORR half‐wave potential is 0.721 V versus RHE, with a potential gap of 0.867 V for bifunctional oxygen electrocatalysis. The Co₃FeS_1.5(OH)₆ hydroxysulfides are employed in the air electrode for a rechargeable Zn–air battery with a small overpotential of 0.86 V at 20.0 mA cm^?2, a high specific capacity of 898 mAh g^?1, and a long cycling life, which is much better than Pt and Ir‐based electrocatalyst in Zn–air batteries.     

Promoting Oxygen Evolution Reaction of Co‐Based Catalysts (Co3O4, CoS,CoP, and CoN) through Photothermal Effect

The increase of reaction temperature of electrocatalysts is regarded as an efficient method to improve the oxygen evolution reaction (OER) activity. Herein, it is reported that the electrocatalytic performance of dual functional (i.e., electrocatalytic and photothermal functions) Co₃O₄ can be dramatically improved via its photothermal effect. The operating temperature of the Co₃O₄ electrode is elevated in situ under near infrared (NIR) light irradiation, resulting in enhanced oxygen evolution activity due to its accelerated electrical conductivity, reaction kinetics, and desorption rate of O₂ bubbles from the electrode. In addition, photothermal effect can also enhance the electrocatalytic reaction rates of metal‐doped Co₃O₄ electrodes, indicating that it is able to significantly improve the OER activities of electrodes together with other modification strategies. With the assistance of the photothermal effect, the obtained Ni‐doped Co₃O₄ catalyst requires an extremely low overpotential of 208 mV to achieve a benchmark of 10 mA cm^?2 with a small Tafel slope, superior to most reported Co‐based catalysts. Significantly, the electrocatalytic performance of other electrodes with photothermal effect, such as CoN, CoP, and CoS, are also boosted under NIR light irradiation, indicating opportunities for implementing photothermal enhancement in electrocatalytic water splitting.     

Construction of Defect‐Rich Ni‐Fe‐Doped K0.23MnO2 Cubic Nanoflowers via Etching Prussian Blue Analogue for Efficient Overall Water Splitting

Designing elaborate nanostructures and engineering defects have been promising approaches to fabricate cost‐efficient electrocatalysts toward overall water splitting. In this work, a controllable Prussian‐blue‐analogue‐sacrificed strategy followed by an annealing process to harvest defect‐rich Ni‐Fe‐doped K_0.23MnO₂ cubic nanoflowers (Ni‐Fe‐K_0.23MnO₂ CNFs‐300) as highly active bifunctional catalysts for oxygen and hydrogen evolution reactions (OER and HER) is reported. Benefiting from many merits, including unique morphology, abundant defects, and doping effect, Ni‐Fe‐K_0.23MnO₂ CNFs‐300 shows the best electrocatalytic performances among currently reported Mn oxide‐based electrocatalysts. This catalyst affords low overpotentials of 270 (320) mV at 10 (100) mA cm^?2 for OER with a small Tafel slope of 42.3 mV dec^?1, while requiring overpotentials of 116 and 243 mV to attain 10 and 100 mA cm^?2 for HER respectively. Moreover, Ni‐Fe‐K_0.23MnO₂ CNFs‐300 applied to overall water splitting exhibits a low cell voltage of 1.62 V at 10 mA cm^?2 and excellent durability, even superior to the Pt/C||IrO₂ cell at large current density. Density functional theory calculations further confirm that doping Ni and Fe into the crystal lattice of δ‐MnO₂ can not only reinforce the conductivity but also reduces the adsorption free‐energy barriers on the active sites during OER and HER.     

3D Nitrogen‐Anion‐Decorated Nickel Sulfides for Highly Efficient Overall Water Splitting

Developing non‐noble‐metal electrocatalysts with high activity and low cost for both the oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) is of paramount importance for improving the generation of H₂ fuel by electrocatalytic water‐splitting. This study puts forward a new N‐anion‐decorated Ni₃S₂ material synthesized by a simple one‐step calcination route, acting as a superior bifunctional electrocatalyst for the OER/HER for the first time. The introduction of N anions significantly modifies the morphology and electronic structure of Ni₃S₂, bringing high surface active sites exposure, enhanced electrical conductivity, optimal HER Gibbs free‐energy (ΔG_H*), and water adsorption energy change (ΔG_H2O*). Remarkably, the obtained N‐Ni₃S₂/NF 3D electrode exhibits extremely low overpotentials of 330 and 110 mV to reach a current density of 100 and 10 mA cm^?2 for the OER and HER in 1.0 m KOH, respectively. Moreover, an overall water‐splitting device comprising this electrode delivers a current density of 10 mA cm^?2 at a very low cell voltage of 1.48 V. Our finding introduces a new way to design advanced bifunctional catalysts for water splitting.     

Oxygen Vacancies Dominated NiS2/CoS2 Interface Porous Nanowires for Portable Zn–Air Batteries Driven Water Splitting Devices

The development of highly active and stable oxygen evolution reaction (OER) electrocatalysts is crucial for improving the efficiency of water splitting and metal–air battery devices. Herein, an efficient strategy is demonstrated for making the oxygen vacancies dominated cobalt–nickel sulfide interface porous nanowires (NiS₂/CoS₂–O NWs) for boosting OER catalysis through in situ electrochemical reaction of NiS₂/CoS₂ interface NWs. Because of the abundant oxygen vacancies and interface porous nanowires structure, they can catalyze the OER efficiently with a low overpotential of 235 mV at j = 10 mA cm^?2 and remarkable long‐term stability in 1.0 m KOH. The home‐made rechargeable portable Zn–air batteries by using NiS₂/CoS₂–O NWs as the air–cathode display a very high open‐circuit voltage of 1.49 V, which can maintain for more than 30 h. Most importantly, a highly efficient self‐driven water splitting device is designed with NiS₂/CoS₂–O NWs as both anode and cathode, powered by two‐series‐connected NiS₂/CoS₂–O NWs‐based portable Zn–air batteries. The present work opens a new way for designing oxygen vacancies dominated interface nanowires as highly efficient multifunctional electrocatalysts for electrochemical reactions and renewable energy devices.     

Enhanced Electrocatalytic Performance through Body Enrichment of Co‐Based Bimetallic Nanoparticles In Situ Embedded Porous N‐Doped Carbon Spheres

Extending available body space loading active species and controllably tailoring the d‐band center to Fermi level of catalysts are of paramount importance but extremely challenging for the enhancement of electrocatalytic performance. Herein, a melamine‐bridged self‐construction strategy is proposed to in situ embed Co‐based bimetallic nanoparticles in the body of N‐doped porous carbon spheres (CoM‐e‐PNC), and achieve the controllable tailoring of the d‐band center position by alloying of Co and another transition metal M (M = Ni, Fe, Mn, and Cu). The enrichment and exposure of the active sites in the body interior of porous carbon spheres, and the best balance between the adsorption of OH species and the desorption of O₂ induced by optimizing the d‐band center position, collectively enhance the oxygen evolution reaction (OER) performance. Meanwhile, the relationship of d‐band center position and OER activity is found to exhibit the volcano curve rule, where the CoNi‐e‐PNC catalyst shows optimal OER performance with an overpotential of 0.24 V at 10 mA cm^?2 in alkaline media, outperforming those of the ever‐reported CoNi‐based catalysts. Besides, CoNi‐e‐PNC catalyst also demonstrates high OER stability with slight current decrease after 100 h.     

Ultrathin Cobalt Oxide Layers as Electrocatalysts for High‐Performance Flexible Zn–Air Batteries

Synergistic improvements in the electrical conductivity and catalytic activity for the oxygen reduction reaction (ORR)/oxygen evolution reaction (OER) are of paramount importance for rechargeable metal–air batteries. In this study, one‐nanometer‐scale ultrathin cobalt oxide (CoO_x) layers are fabricated on a conducting substrate (i.e., a metallic Co/N‐doped graphene substrate) to achieve superior bifunctional activity in both the ORR and OER and ultrahigh output power for flexible Zn–air batteries. Specifically, at the atomic scale, the ultrathin CoO_x layers effectively accelerate electron conduction and provide abundant active sites. X‐ray absorption spectroscopy reveals that the metallic Co/N‐doped graphene substrate contributes to electron transfer toward the ultrathin CoO_x layer, which is beneficial for the electrocatalytic process. The as‐obtained electrocatalyst exhibits ultrahigh electrochemical activity with a positive half‐wave potential of 0.896 V for ORR and a low overpotential of 370 mV at 10 mA cm^?2 for OER. The flexible Zn–air battery built with this catalyst exhibits an ultrahigh specific power of 300 W g_cat ^?1, which is essential for portable devices. This work provides a new design pathway for electrocatalysts for high‐performance rechargeable metal–air battery systems.     

Synergistic Coupling of Ni Nanoparticles with Ni3C Nanosheets for Highly Efficient Overall Water Splitting

Exploring earth‐abundant bifunctional electrocatalysts with high efficiency for water electrolysis is extremely demanding and challenging. Herein, density functional theory (DFT) predictions reveal that coupling Ni with Ni₃C can not only facilitate the oxygen evolution reaction (OER) kinetics, but also optimize the hydrogen adsorption and water adsorption energies. Experimentally, a facile strategy is designed to in situ fabricate Ni₃C nanosheets on carbon cloth (CC), and simultaneously couple with Ni nanoparticles, resulting in the formation of an integrated heterostructure catalyst (Ni–Ni₃C/CC). Benefiting from the superior intrinsic activity as well as the abundant active sites, the Ni–Ni₃C/CC electrode demonstrates excellent bifunctional electrocatalytic activities toward the OER and hydrogen evolution reaction (HER), which are superior to all the documented Ni₃C‐based electrocatalysts in alkaline electrolytes. Specifically, the Ni–Ni₃C/CC catalyst exhibits the low overpotentials of only 299 mV at the current density of 20 mA cm^?2 for the OER and 98 mV at 10 mA cm^?2 for the HER in 1 m KOH. Furthermore, the bifunctional Ni–Ni₃C/CC catalyst can propel water electrolysis with excellent activity and nearly 100% faradic efficiency. This work highlights an easy approach for designing and constructing advanced nickel carbide‐based catalysts with high activity based on the theoretical predictions.     

Flexible Co–Mo–N/Au Electrodes with a Hierarchical Nanoporous Architecture as Highly Efficient Electrocatalysts for Oxygen Evolution Reaction

Designing highly active and robust electrocatalysts for oxygen evolution reaction (OER) is crucial for many renewable energy storage and conversion devices. Here, self-supported monolithic hybrid electrodes that are composed of bimetallic cobalt–molybdenum nitride nanosheets vertically aligned on 3D and bicontinuous nanoporous gold (NP Au/CoMoN_x) are reported as highly efficient electrocatalysts to boost the sluggish reaction kinetics of water oxidation in alkaline media. By virtue of the constituent CoMoN_x nanosheets having large accessible CoMoO_x surface with remarkably enhanced electrocatalytic activity and the nanoporous Au skeleton facilitating electron transfer and mass transport, the NP Au/CoMoN_x electrode exhibits superior OER electrocatalysis in 1 m KOH, with low onset overpotential (166 mV) and Tafel slope (46 mV dec⁻¹). It only takes a low overpotential of 370 mV to reach ultrahigh current density of 1156 mA cm⁻², ≈140-fold higher than free CoMoN_x nanosheets. The electrocatalytic performance makes it an attractive candidate as the OER catalyst in the water electrolysis.     

Morphology and Structure Engineering in Nanofiber Reactor: Tubular Hierarchical Integrated Networks Composed of Dual Phase Octahedral CoMn2O4/Carbon Nanofibers for Water Oxidation

1D hollow nanostructures combine the advantages of enhanced surface‐to‐volume ratio, short transport lengths, and efficient 1D electron transport, which can provide more design ideas for the preparation of highly active oxygen evolution (OER) electrocatalysts. A unique architecture of dual‐phase octahedral CoMn₂O₄/carbon hollow nanofibers has been prepared via a two‐step heat‐treatment process including preoxidation treatment and Ostwald ripening process. The hollow and porous structures provide interior void spaces, large exposed surfaces, and high contact areas between the nanofibers and electrolyte and the morphology can be engineered by adjusting the heating conditions. Due to the intimate electrical and chemical coupling between the oxide nanocrystals and integrated carbon, the dual‐phase octahedral CoMn₂O₄/carbon hollow nanofibers exhibit excellent OER activity with overpotentials of 337 mV at current density of 10 mA cm^?2 and Tafel slope of 82 mV dec^?1. This approach will lead to the new perception of design issue for the nanoarchitecture with fine morphology, structures, and excellent electrocatalytic activity.     

Co9S8 Nanoparticles‐Embedded N/S‐Codoped Carbon Nanofibers Derived from Metal–Organic Framework‐Wrapped CdS Nanowires for Efficient Oxygen Evolution Reaction

Metal–organic frameworks (MOFs) with tunable compositions and morphologies are recognized as efficient self‐sacrificial templates to achieve function‐oriented nanostructured materials. Moreover, it is urgently needed to develop highly efficient noble metal‐free oxygen evolution reaction (OER) electrocatalysts to accelerate the development of overall water splitting green energy conversion systems. Herein, a facile and cost‐efficient strategy to synthesize Co₉S₈ nanoparticles‐embedded N/S‐codoped carbon nanofibers (Co₉S₈/NSCNFs) as highly active OER catalyst is developed. The hybrid precursor of core–shell ZIF‐wrapped CdS nanowires is first prepared and then leads to the formation of uniformly dispersed Co₉S₈/N, S‐codoped carbon nanocomposites through a one‐step calcination reaction. The optimal Co₉S₈/NSCNFs‐850 is demonstrated to possess excellent electrocatalytic performance for OER in 1.0 m KOH solution, affording a low overpotential of 302 mV to reach the current density of 10 mA cm^?2, a small Tafel slope of 54 mV dec^?1, and superior long‐term stability for 1000 cyclic voltammetry cycles. The favorable results raise a concept of exploring more MOF‐based nanohybrids as precursors to induce the synthesis of novel porous nanomaterials as non‐noble‐metal electrocatalysts for sustainable energy conversion.