Preparation and Upeonversion Lumineseenee ofNanoerystailine Gd2O3： Er^3＋, Yb^3＋

Nanocrystalline Gd1.77Yb0.2Er0.03O3 samples were prepared by combustion and precipitation methods. Structures and upconversion luminescence properties of samples were studied. The results of XRD show that all samples are cubic structure, the average crystallite size could be calculated as 23 nm and 39 nm, respectively. The lattice constants were obtained. The FT-IR spectra were measured to investigate the vibrational feature of the samples. Upconversion luminescence spectra of samples under 980 nm laser excitation were investigated. The strong red emission of samples were observed, and attributed to 4F9/2→4I152 transitions of Er^3＋ ions, the emission intensity for sample synthesized by precipitation method is stronger compared to that of combustion method. The possible upconversion luminescence mechanisms in nanocrystalline Gd1.77Yb0.2Er0.03O3 were discussed.     

Upeonversion Luminescence of Er3＋, Tin3＋ and Yb3＋ Co-doped Gd3Ga5O12 Nanocrystals

A series of Er3+,Tm3+ and Yb3+ doped Gd3Ga5O12 nanocrystals were prepared by a combustion method.The X-ray diffraction(XRD),field emission scanning electron microscope(FESEM)and upconversion(UC)emission spectra were used to characterize the samples.The results of XRD indicate that Gd3Ga5O12:Er3+,Tm3+,Yb3+ nanocrystals with cubic phase can be obtained.Under the excitation of a 980 nm laser,the different rare earth ions doped Gd3Ga5O12 nanocrystals show upconversion luminescence involving the green emission attributed to the 2H11/2→4I15/2,4S3/2→4I15/2 transitions of Er3+ ions,respectively,the red emissions assigned to the 4F9/2→4I15/2 transitions of Er3+ ions and the 1G4→3F4 as well as 3F2,3→3H6 transitions of Tm3+ ions,respectively,the blue emission attributed to 1G4→3H6 transitions of Tm3+ions,and the near-infrared assigned to the 3H4→3H6 transitions of Tm3+ ions.The CIE coordinates for the samples are calculated.The dependence of their upconversion luminescence properties on Yb3+ ion concentration is investigated.     

Combustion synthesis and luminescent properties of CaO: Eu<Superscript>3+</Superscript>, M<Superscript>+</Superscript> (M=Li,Na, K) phosphor

Li⁺, Na⁺, or K⁺ co-doped CaO: Eu³⁺ phosphors were prepared by the combustion synthesis method and characterized by X-ray diffraction (XRD), photoluminescence and photoluminescence excitation (PL-PLE) spectra. The experimental results show that, upon excitation with 250 nm xenon light, the emission spectrum of the CaO: Eu³⁺ consists of 4f-4f emission transitions from the ⁵ D ₀ excited level to the ⁷ F _J (J=1, 2, 3) levels with the mainly electric dipole transition ⁵ D ₀→⁷ F ₂ of Eu³⁺, indicating that the Eu³⁺ occupies a low symmetry. The charge-transfer band (CTB) shows somewhat red shift with the decreasing ionic radii of co-doped alkali metal ions. The PL and PLE intensities are significantly enhanced, especially the strongest intensity of luminescent is CaO: Eu³⁺, Li⁺ phosphor, when alkali metal ions are incorporated. The strongest peak of emission is slightly shifted from 614 to 593 nm, indicating that the Eu³⁺ ion locates in a symmetric position (O _h ) when alkali metal ions are incorporated.     

The effect of OH~- groups on the spectroscopic properties of erbium-doped tellurite glasses

With the rapid development of computer networks and other data-transmitting ser-vices, the demand for the increase of transmission capacity of the long distance trans-mission system is urgent. However, the conventional SiO2-based EDFA is limited for its small bandwidth. The Er3+-doped tellurite glass exhibits a larger stimulated-emission cross section and a broader emission bandwidth at the third communication window (1.55 μm) than that of silicate, phosphate, and germanate glasses, which c…     

Crystallization and luminescence properties of Sm<Superscript>3+</Superscript>-doped SrO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> glass-ceramics

The Sm³⁺-doped SrO-Al₂O₃-SiO₂ (SAS) glass-ceramics with excellent luminescence properties were prepared by batch melting and heat treatment. The crystallization behavior and luminescent properties of the glass-ceramics were investigated by DTA, XRD, SEM and luminescence spectroscopy. The results indicate that the crystal phase precipitated in this system is monocelsian (SrAl₂Si₂O₈) and with the increase of nucleation/crystallization temperature, the crystallite increases from 66 % to 79 %. The Sm³⁺-doped SAS glass-ceramics emit green, orange and red lights centered at 565, 605, 650 and 715 nm under the excitation of 475 nm blue light which can be assigned to the ⁴G_5/2→⁶ H _j/2 (j=5, 7, 9, 11) transitions of Sm³⁺, respectively. Besides, by increasing the crystallization temperature or the concentration of Sm³⁺, the emission lights of the samples located at 565, 605 and 650 nm are intensified significantly. The present results demonstrate that the Sm³⁺-doped SAS glass-ceramics are promising luminescence materials for white LED devices by fine controlling and combining of these three green, orange and red lights in appropriate proportion.     

Luminescence Characterization and Synthesis of γ-LiAlO_2:Eu~(3+) by Gel Combustion

γ-LiAlO2:Eu3+(Eu3+:LAO) phosphor was obtained by gel combustion method using LiNO3,Al(NO3)3·9H2O,Eu(NO3)3·6H2O and citric acid as raw materials.The structure,morphology and luminescence were characterized by means of X-ray diffraction (XRD),scanning electron microscopy (SEM),photoluminescence (PL).The results demonstrated that the phosphor was pure-phase of flaky tetragonal crystal system with a mean size of around 1 μm.The strongest excitation peak was at 254 nm,belonging to the broadband excitation and the maximum emission peak was at 613 nm,corresponding to the 5D0→7F2 transition of Eu3+.Luminous intensity is closely related to the calcination temperature and doping concentration of Eu3+.     

Phase structure and electrical properties of La<Subscript>2</Subscript>O<Subscript>3</Subscript>-doped BiInO<Subscript>3</Subscript>-PbTiO<Subscript>3</Subscript> ceramics with high curie temperature

The phase structure and electrical properties of pure and La2O3-doped Bi-InO3-PbTiO3 （BI-PT） ceramics were studied respectively. In （1 -x）BI-xPT （x=0.72-0.80） ceramics, the stability of tetragonal phase increased with increasing x, and pure perovskite structure was obtained for x=-0.80 ceramics. The phase transition temperature range was between 575 ℃ and 600 ℃ for x=0.72-0.80 ceramics, higher than that of PT （-490 ℃）. The c/a ratio almost linearly decreased with increasing La2O3 content in x-0.80 ceramics. It is believed that Pb^2＋ vacancies were formed by La^3＋ substituting Pb^2＋ in La2O3-doped BI-PT ceramics. Tc shifted to lower temperature by 30 ℃/mol% La2O3. The maximum dielectric constant 8557 around 559 ℃ was exhibited in 0.5mol%-doped BI-0.80PT ceramics. La2O3-doped ceramics could be poled resulting from decreasing of c/a ratio and improving of dielectric loss and resistivity. The maximum piezoelectric coefficient d33 was 12 pC/N for 2mol%-doped BI-0.80PT ceramics.     

Fluorescence detection for H<Subscript>2</Subscript>PO<Subscript>4</Subscript><Superscript>-</Superscript> based on carbon dots/Fe<Superscript>3+</Superscript> composite

A novel fluorescent probe for H₂PO₄ ^- was designed and fabricated based on the carbon dots/Fe³⁺ composite. The carbon dots were synthesized by an established one-pot hydrothermal method and characterized by transmission electron microscope, X-ray diffractometer, UV-Vis absorption spectrometer and fluorescence spectrophotometer. The carbon dots/Fe³⁺ composite was obtained by aqueous mixing of carbon dots and FeCl₃, and its fluorescence property was characterized by fluorescence spectrophotometer. The fluorescence of carbon dots was quenched by aqueous Fe³⁺ cations, resulting in the low fluorescence intensity of the carbon dots/Fe³⁺ composite. On the other hand, H₂PO₄ ^- reduced the concentration of Fe³⁺ by chemical reaction and enhanced the fluorescence of the carbon dots/Fe³⁺ composite. The Stern-Volmer equation was introduced to describe the relation between the relative fluorescence intensity of the carbon dots/Fe³⁺ composite and the concentration of H₂PO₄ ^-, and a fine linearity (R ²=0.997) was found in the range of H₂PO₄ ^- concentration of 0.4-12 mM.     

Sensitization and intra-molecular energy transfer of Eu<Superscript>3+</Superscript> by Tb<Superscript>3+</Superscript> in Eu-Tb binuclear complexes/PMMA

A series of Eu0.5Tb0.5(TTA)3Phen/PMMA (TTA=thenoyltrifluoroacetone,Phen=phenanthroline) and Eu0.5Tb0.5(TTA)3Dipy/PMMA (Dipy=2,2’-dipyridyl) were prepared by in-situ polymerization.The structures of the composites were characterized by IR spectra and electron spectrum.Photoluminescence properties were investigated by UV-Vis spectra and fluorescence spectra.Meanwhile,the energy transfer models were set up.The results indicated that polymer parts were attached with the rare-earth molecular parts in the composi...     

Synthesis and luminescence properties of red phosphor CaO: Eu3+

Ca(NO₃)₂·4H₂O, Eu(NO₃)₃ and H₂C₂O₄·2H₂O were adopted to synthesize CaO: Eu³⁺ with the chemical co-precipitation method, and the effects of the calcination temperature and Eu³⁺ doping concentration on the phosphor structure and its luminescent properties were investigated by TG-SDTA, XRD, and PL-PLE. The results confirm that the Eu³⁺ ions as luminescent centers substitutes Ca²⁺ sites without changing the crystal structure of cubic CaO. The optimum calcination temperature and the optimum concentration of Eu³⁺ are 1 100 ° and 1 mol%, respectively, under which the best crystallinity and highest PL intensity appeared. The maximum emission wavelength is 592 nm (⁵D₀→⁷F₁) which is excited by xenon lamp with the wavelength of 200–280 nm, indicating that the Eu³⁺ ion mainly locates in the symmetric position (O_h) in the crystal lattice of CaO. Funded by the Science and Technology Bureau of Sichun Province(No. 2006J13-059) and Education Bureau of Sichun Province (No. 2006A094)     

Synthesis and luminescence of nano fluorescent powder of Y<Subscript>4</Subscript>Al<Subscript>2</Subscript>O<Subscript>9</Subscript>: Eu<Superscript>3+</Superscript>

Nano fluorescent powder of Y₄Al₂O₉: Eu³⁺ was synthesized by sol-gel method. The XRD shows that the product prepared at 900°C is pure-phase Y₄Al₂O₉: Eu³⁺. The Y₄Al₂O₉ powder is nano-size crystal testified by BF and ED analysis of TEM. The grain diameter of Y₄Al₂O₉ is in the range between 20 and 50nm, and its average is 30 nm. The luminescent spectra show that Eu³⁺ ious occupy two kinds of sites in Y₄Al₂O₉ crystal lattice. One is in the strict inversion center, and the other is in off lying inversion center. When excited with UV light (λ=254nm), Y₄Al₂O₉: Eu³⁺ exhibits an orange emission bond at λ=590 nm due to the⁵D_o→⁷F₁ transition and a red emission band at λ=610 nm due to⁵D_o→⁷F₂ transition. YUAN Xi-ming: Born in 1951 Funded by Key Scientific and Technological Project of Hubei Province (2001 AA102A03)     

Microstructures and fatigue-free properties of the La<Superscript>3+</Superscript> and Nd<Superscript>3+</Superscript> doped Bi<Subscript>4</Subscript>Ti<Subscript>3</Subscript>O<Subscript>12</Subscript> thin films prepared by modified sol-gel technique

Ferroelectric Bi_3.25La_0.75Ti₃O₁₂ (BLT) and Bi_3.15Nd_0.85Ti₃O₁₂ (BNT) thin films were fabricated on Pt/TiO₂/SiO₂/Si (100) substrates by a modified sol-gel technique. X-ray diffraction indicated that these films were of single phase with random polycrystalline orientations. The surface morphologies of the films were observed by scanning electron microscope, showing uniform, dense films with grain size of 50–100 nm. Well-saturated hysteresis loops of the films were obtained in metal-ferroelectric-metal type capacitors with Cu top electrodes at an applied voltage of 400 kV/cm, giving the remanent polarization (2P _r) and coercive field (2E _c) values of the films of 25.1 μC/cm² and 203 kV/cm for BLT, and 44.2 μC/cm² and 296 kV/cm for BNT, respectively. Moreover, these capacitors did not show fatigue behaviors after up to 1.75×10¹⁰ switching cycles at the test frequency of 1 MHz, suggesting a fatigue-free character. The influences of the La³⁺ and Nd³⁺ doping on the properties of the films were comparatively discussed. Supported by the National Key Basic Research and Development Program of China (Grant No. 2006CB932305) and the Natural Science Foundation of Hubei Province, China (Grant No. 2004ABA082)     

Synthesis and electrochemical properties of Cr-doped Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> cathode materials for lithium-ion batteries

Cr-doped Li₃V₂(PO₄)₃ cathode materials Li₃V_2−x Cr _x (PO₄)₃ were prepared by a carbothermal reduction(CTR) process. The properties of the Cr-doped Li₃V₂(PO₄)₃ were investigated by X-ray diffraction (XRD), scanning electron microscopic (SEM), and electrochemical measurements. Results show that the Cr-doped Li₃V₂(PO₄)₃ has the same monoclinic structure as the undoped Li₃V₂(PO₄)₃, and the particle size of Cr-doped Li₃V₂(PO₄)₃ is smaller than that of the undoped Li₃V₂(PO₄)₃ and the smallest particle size is only about 1 μm. The Cr-doped Li₃V₂(PO₄)₃ samples were investigated on the Li extraction/insertion performances through charge/discharge, cyclic voltammogram (CV), and electrochemical impedance spectra(EIS). The optimal doping content of Cr was that x=0.04 in the Li₃V_2−x Cr _x (PO₄)₃ samples to achieve high discharge capacity and good cyclic stability. The electrode reaction reversibility was enhanced, and the charge transfer resistance was decreased through the Cr-doping. The improved electrochemical performances of the Cr-doped Li₃V₂(PO₄)₃ cathode materials are attributed to the addition of Cr³⁺ ion by stabilizing the monoclinic structure. Funded by the Guangxi Natural Science Foundation(No. 0832259) and the National Basic Research Program of China (No. 2007CB613607)     

Influence of rare earth co-dopant on the photocatalytic property of TiO<Subscript>2</Subscript> nano-particles

A series of nanometer TiO2 photocatalysts co-doped respectively with rare earth Er3+-Ce3+ and La3+-Fe3+ were prepared by sol-gel method,and the photocatalytic activity under ultra-violet light was evaluated by photocatalytic degradation of methyl blue.The crystallographic forms,particles size,and morphology were characterized by XRD and TEM.The results showed that the optimum heat temperature of co-doped TiO2 was 550 ℃,and the co-doped TiO2 kept anatase.The anatase crystal had the average size of 20 nm.The ...     

Structure and dielectric properties of ZnO and Nb<Subscript>2</Subscript>O<Subscript>5</Subscript> doped BaO-TiO<Subscript>2</Subscript> system microwave ceramics

The microwave dielectric properties and microstructure of BaTi4.3ZnyO9.6＋y ＋0.02 mol% SnO2＋0.01 mol% MnCO3＋x mol% Nb2O5（x=0-0.05, y=0-0.08） system ceramics were studied as a function of the amount of ZnO and Nb2O5 doped. Addition of （y=0-0.05） ZnO and （x=0-0.025） Nb2O5 enhanced the reactivity and decreased the sintering temperature effectively. It also increased the dielectric constant ε r and quality factor Q（=1/tan 8） of the system due to the substitution of Ti^4＋ ions with incorporating Zn^2＋and Nb^5＋ ions, which was analyzed by the reaction ZnO＋Nb2O5＋ 3 TiTxTi →ZnTi＋ 2NbTi＋3TiO2. When the system doped with （y=0.05） ZnO and （x=0.025） Nb205 were sintered at 1 160 ℃ for 6 h, the εr. Qf0 value and rfwere 36.5, 42 000 GHz, and＋1.8 ppm/℃, respectively, at 5 GHz.     

Energy transfer mechanism of GdPO4: RE3+ (RE = Tb, Tm) under VUV-UV excitation

Polycrystal of GdPO₄:RE³⁺ (RE=Tb, Tm) phosphors were prepared by solid-state method. Vacuum ultraviolet excitation and emission spectrum and the energy transfer mechanism between the host and dopants of Tb³⁺ and Tm³⁺ were investigated respectively. The emission of Gd³⁺ at 313 nm was enhanced by the strong absorption of CTS of Tm³⁺ at 180 nm in GdPO₄: Tm. It has also been concluded that the excitation of Gd³⁺ is transferred to Tb³⁺ and then emission peaks of ⁵D_J→⁷F_J of Tb³⁺ were observed.     

Nanostructure and formation mechanism of Pt-WO<Subscript>3</Subscript>/C nanocatalyst by ethylene glycol method

Pt-WO3 nanoparticles uniformly dispersed on Vulcan XC-72R carbon black were prepared by an ethylene glycol method.The morphology,composition,nanostructure,electrochemical characteristics and electrocatalytic activity were characterized,and the formation mechanism was investigated.The average particle size was 2.3 nm,the same as that of Pt/C catalyst.The W/Pt atomic ratio was 1/20,much lower than the design of 1/3.The deposition of WO3·xH2O nanoparticles on Vulcan XC-72R carbon black was found to be very difficult by TEM.From XPS and XRD,the Pt nanoparticles were formed in the colloidal solution of Na2WO4,the EG insoluble Na2WO4 resulted in the decreased relative crystallinity and increased crystalline lattice constant compared with those of Pt/C catalyst and,subsequently,the higher specific electrocatalytic activity as determined by CV.The Pt-mass and Pt-electrochemically-active-specific-surface-area based anodic peak current densities for ethanol oxidation were 422.2 mA·mg-1Pt and 0.43 mA·cm-2Pt,1.2 and 1.1 times higher than those of Pt/C catalyst,respectively.     

Roles of Eu^2＋, Dy^3＋ Ions in Persistent Luminescence of Strontium Aluminates Phosphors

The polycrystalline Eu^2＋ and Dy ^3＋ co-doped strontium aluminates SrAl2O4： Eu^2＋, Dy^3＋ with different compositions were prepared by solid state reactions. The UV-excited photoluminescence, persistent luminescence and thermo-luminescence were studied and compared. Results show that the doped Eu^2＋ ion in SrAl2O4： Eu^2＋, Dy^3＋ phosphors works as not only the UV-excited luminescent center but also the persistent luminescent center. The doped Dy^3＋ ion can hardly yield any luminescence under UV-excitation, but effectively enhance the persistent luminescence and thermo-luminescence of SrAl2O4： Eu^2＋. Dy^3＋ co-doping can help form electron traps with appropriate depth due to its suitable electro-negativity, and increase the density and depth of electron traps. Based on above observations, a persistent luminescence mechanism, electron transfer model, is proposed and illustrated.     

Effect of Pb substitution on the microstructure and ferroelectric properties of Ba<Subscript>0.7</Subscript>Sr<Subscript>0.3</Subscript>TiO<Subscript>3</Subscript> ceramic

Ferroelectric Ba0.7Sr0.3TiO3（BST） and partially Pb^2＋ substituted for Ba^2＋ ceramics （Ba0.7-xPbx）Sr0.3TiO3 （x=0.1-0.4, BPST） were prepared by using conventional solid-reaction method. XRD analysis shows that the samples microstructure changes from cubic phase to tetragonal one with the Pb^2＋ content increasing. ESEM analysis shows that the Pb^2＋ substituted samples have a denser and more uniform surface morphology than that of pure BST. Measured electrical properties suggest that the Pb^2＋ substitution for Ba^2＋ in the BST system enhances the ferroelectric performance obviously when x=0.2. In addition, the substitution increases the samples Curie temperature （To） r （Ba0.5Pb0.2）Sr0.3TiO3 ceramic has good ferroelectric properties measured at a maximal electric field of 30 kV/cm under the condition of room temperature. The corresponding saturated polarization （Ps）, remnant polarization （Pr） and coercive field （Ec） is respectively 15.687 μC/cm^2, 8.100 μ C/cm^2 and 6.611 kV/cm. The measured Tc of （Ba0.5Pb0.2）Sr0.3TiO3 is 117 ℃.     

Preparation and optical properties of Er<Superscript>3+</Superscript>: Na<Subscript>2</Subscript>O-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> transparent glass-ceramics

Na₂O-Al₂O₃-SiO₂ glass-ceramics doped with Er³⁺ ions were synthesized by the conventional melt quenching technique at a low melting temperature. The samples were characterized by differential scanning calorimetry (DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-vis-NIR scanning spectrophotometry, and fluorescence spectrometry. The results show that the main crystalline phase of glass-ceramics is nepheline.The best heat-treatment process is at 520 °C for 2 h. Because the up-conversion luminescence and near infrared luminescence properties of glass doped with Eu³⁺ are studied in detail.