Ultrathin Al-doped transparent conducting zinc oxide films fabricated by pulsed laser deposition

Al-doped transparent conducting zinc oxide (AZO) films, approximately 20-110 nm-thick, were deposited on glass substrates at substrate temperatures between 200 and 300 °C by pulsed laser deposition (PLD) using an ArF excimer laser (λ = 193 nm). When fabricated at a substrate temperature of 260 °C, a 40-nm-thick AZO film showed a low resistivity of 2.61 × 10^− 4 Ω·cm, carrier concentration of 8.64 × 10²⁰ cm^− 3, and Hall mobility of 27.7 cm²/V·s. Furthermore, for an ultrathin 20-nm-thick film, a resistivity of 3.91 × 10^− 4 Ω·cm, carrier concentration of 7.14 × 10²⁰ cm^− 3, and Hall mobility of 22.4 cm²/V·s were obtained. X-ray diffraction (XRD) spectra, obtained by the θ-2θ method, of the AZO films grown at a substrate temperature of 260 °C showed that the diffraction peak of the ZnO (0002) plane increased as the film thickness increased from 20 to 110 nm. The full-width-at-half-maximum (FWHM) values were 0.5500°, 0.3845°, and 0.2979° for film thicknesses of 20, 40, and 110 nm, respectively. For these films, the values of the average transmittance in visible light wavelengths (400-700 nm) were 95.1%, 94.2%, and 96.6%, respectively. Field emission scanning electron microscopy (FE-SEM) and atomic force microscopy (AFM) observations showed that even the 20-nm-thick films did not show island structures. In addition, exfoliated areas or vacant and void spaces were not observed for any of the films.     

Al-doped ZnO films by pulsed laser deposition at room temperature

Polycrystalline Al-doped ZnO films with good photoluminescence property were successfully deposited on quartz glass substrates by pulsed laser deposition (PLD) at room temperature. The films were obtained by ablating a metallic target (Zn:Al 3 wt%) at various laser energy densities (1.0-2.1 J/cm²) in oxygen atmosphere (9 Pa). The structure of the films was characterized by XRD. Ultraviolet photoluminescence centered at 359-361 nm was observed in the room temperature PL spectra of the Al-doped ZnO films.     

ZnO thin films prepared by pulsed laser deposition

Zinc oxide (ZnO) thin films were deposited on soda lime glass substrates by pulsed laser deposition (PLD) in an oxygen-reactive atmosphere. The structural, optical, and electrical properties of the as-prepared thin films were studied in dependence of substrate temperature and oxygen pressure. High quality polycrystalline ZnO films with hexagonal wurtzite structure were deposited at substrate temperatures of 100 and 300 °C. The RMS roughness of the deposited oxide films was found to be in the range 2-9 nm and was only slightly dependent on substrate temperature and oxygen pressure. Electrical measurements indicated a decrease of film resistivity with the increase of substrate temperature and the decrease of oxygen pressure. The ZnO films exhibited high transmittance of 90% and their energy band gap and thickness were in the range 3.26-3.30 eV and 256-627 nm, respectively.     

Metal-semiconductor transition in Nb-doped ZnO thin films prepared by pulsed laser deposition

The structural, electrical and optical properties of Nb-doped ZnO films were investigated with different Nb contents (0, 0.15, 0.31, 0.46, 0.62, and 0.94 at.%) in this article. The film with 0.46 at.% Nb content showed the lowest resistivity of 8.95 × 10^− 4 Ω cm and high transmittance about 80% with high c-axis orientation. The undoped ZnO film showed a semiconducting behavior. And Nb-doped ZnO films showed a metal-semiconductor transition (MST), which was connected with localization of degenerate electrons. The films showed metallic conductivity at temperatures closer to the ambient temperature and semiconducting behavior at lower temperatures. It was noted that the NZO films with much lower Nb concentration of 0.15 at.% presented MST compared with other transparent conducting oxides films.     

Pulsed electron beam deposition of transparent conducting Al-doped ZnO films

Good quality transparent conducting Al-doped ZnO films were deposited on quartz substrates from a high purity target using pulsed electron deposition (PED). Two series of films were made, one deposited at room temperature but at four pressures, viz., 0.7, 1.3, 2.0 and 2.7 Pa of oxygen and one deposited at 1.3 Pa oxygen pressure but at the substrate temperature ranged from room temperature to 600 °C. In order to evaluate the effect of substrate temperature and oxygen pressure on the properties of obtained films, various characterization techniques were employed including X-ray diffraction, stylus profiler, scanning electron microscope, optical spectrophotometer and electrical resistivity. For the first series films, the optimal oxygen pressure of 1.3 Pa was found to bring about the appropriate energetic deposition atoms which results in the best crystallinity. For the second series films, the lowest resistivity was obtained in the film grown at 400 °C. An attempt was made to reduce the resistivity by lowering the oxygen pressure to 0.5 Pa which was the lower limit of working pressure of the PED system. The obtained results indicate that PED is a suitable technique for growing transparent conducting ZnO films.     

Structural investigations of InZnO films grown by pulsed laser deposition technique

Thin films of indium zinc oxide were grown from targets with In atomic concentration [In/(In + Zn)] of 2.8%, 4.3%, and 16.8%, respectively, by pulsed laser deposition technique (KrF laser, 10 Hz, 4 J/cm² fluence) on Si(001) and glass substrates that were heated at 500 °C. X-ray diffraction investigations showed that targets that had an atomic In concentration of 2.8% exhibited only the wurtzite-type ZnO lattice, while the targets that contained In concentrations of 4.3% and 16.8% consisted of a mixture of the wurtzite-type ZnO and the homologous compound Zn₇In₂O₁₀. All deposited films exhibited only the wurtzite-type ZnO lattice, being c-axis textured. The increase of the In concentration resulted in films less textured that also exhibited increased lattice parameters a and c. X-ray photoelectron spectroscopy investigations showed slight changes of the In 3d and Zn 2p binding energies for increased In content, consistent with an In doped ZnO lattice.     

Transparent conducting F-doped SnO2 thin films grown by pulsed laser deposition

Transparent conducting fluorine-doped tin oxide (SnO₂:F) films have been deposited on glass substrates by pulsed laser deposition. The structural, electrical and optical properties of the SnO₂:F films have been investigated as a function of F-doping level and substrate deposition temperature. The optimum target composition for high conductivity was found to be 10 wt.% SnF₂ + 90 wt.% SnO₂. Under optimized deposition conditions (T_s = 300 °C, and 7.33 Pa of O₂), electrical resistivity of 5 × 10^− 4 Ω-cm, sheet resistance of 12.5 Ω/□, average optical transmittance of 87% in the visible range, and optical band-gap of 4.25 eV were obtained for 400 nm thick SnO₂:F films. Atomic force microscopy measurements for these SnO₂:F films indicated that their root-mean-square surface roughness ( 6 Å) was superior to that of commercially available chemical vapor deposited SnO₂:F films ( 85 Å).     

Reversible wettability of ZnO nanostructured thin films prepared by pulsed laser deposition

This work reports on the photoinduced wettability changes of high quality nanostructured ZnO films grown on Si by pulsed laser deposition (PLD) under different growth parameters. The wetting behavior of the resulting films can be reversibly switched from hydrophobic to hydrophilic, through alternation of UV illumination and dark storage. The kinetics of this wetting transition are studied by monitoring the time evolution of the corresponding contact angles. Finally, the influence of the film properties over the observed wetting response is discussed.     

AFM surface analysis of ZnO layers prepared by pulsed laser deposition at different oxygen pressures

Polycrystalline thin films of zinc oxide were deposited by pulsed laser deposition onto silicon substrates at different oxygen partial pressures in the range of 1-35 Pa. For ablation of the sintered zinc oxide target a pulsed Nd:YAG laser was used. Other processing parameters such as laser pulse energy, pulse repetition rate, substrate temperature and deposition pressure were identical. The effect of oxygen pressure on the structural properties of the films was systematically studied by using atomic force microscopy. The surface morphology, average roughness S_a, root mean square S_q, and mean size of grains on selected places with 2 × 2 μm² area of prepared samples were evaluated. Detailed structural analysis confirmed that partial oxygen pressure leads to the modification of surface morphology. Mean grain size in height and lateral direction decreases with raising oxygen pressure from 1 to 5 Pa while the further increase of oxygen pressure from 5 to 35 Pa results in grain size enlargement. The zinc oxide film formed at oxygen partial pressure 5 Pa shows smallest values of evaluated parameters (S_a = 0.6 nm, S_q = 0.7 nm and mean size of grains 50 nm).     

Uniformity of gallium doped zinc oxide thin film prepared by pulsed laser deposition

Recently, transparent conducting oxide thin films have attracted attention for the application to transparent conducting electrodes. In this work, we evaluated the uniformity of electrical, optical and structural properties for gallium doped zinc oxide thin films prepared on the 10 × 10 cm² silica glass substrate by pulsed laser deposition. The resistivity, carrier concentration, mobility, bonding state and atomic composition of the film were uniform along in-plane and depth direction over the 10 × 10 cm² area of the substrate. The film showed the average transmittance of 81-87%, resistivity of 1.4 × 10^− 3 Ω cm, carrier concentration of 9.7 × 10²⁰/cm³ and mobility of 5 cm²/Vs in spite of the amorphous X-ray diffraction pattern. The gradual thickness distribution was found, however, the potential for large-area and low temperature deposition of transparent conducting oxide thin film using pulsed laser deposition method was confirmed.     

High quality amorphous indium zinc oxide thin films synthesized by pulsed laser deposition

Indium zinc oxide films were grown from targets with two different In atomic concentration [In/(In + Zn)] of 40% and 80% by the pulsed laser deposition technique on glass substrates from room temperature up to 100 °C. X-ray diffraction and reflectometry investigations showed that films were amorphous and dense. Thin films (thickness < 100 nm) exhibited higher optical transmittance and resistivities than thick films (thickness > 1000 nm), probably caused by a significant decrease of oxygen vacancies due to atmosphere exposure. Films deposited from the In rich target under an oxygen pressure of 1 Pa exhibited optical transmittance higher than 85%, resistivities around 5- 7 × 10^− 4 Ω cm and mobilities in the 47-54 cm²/V s range.     

ITO thin films deposited by advanced pulsed laser deposition

Indium tin oxide thin films were deposited by computer assisted advanced PLD method in order to obtain transparent, conductive and homogeneous films on a large area. The films were deposited on glass substrates. We studied the influence of the temperature (room temperature (RT)-180 °C), pressure (1-6 × 10^− 2 Torr), laser fluence (1-4 J/cm²) and wavelength (266-355 nm) on the film properties. The deposition rate, roughness, film structure, optical transmission, electrical conductivity measurements were done. We deposited uniform ITO thin films (thickness 100-600 nm, roughness 5-10 nm) between RT and 180 °C on a large area (5 × 5 cm²). The films have electrical resistivity of 8 × 10^− 4 Ω cm at RT, 5 × 10^− 4 Ω cm at 180 °C and an optical transmission in the visible range, around 89%.     

Structural and magnetic properties of Co-Ga co-doped ZnO thin films fabricated by pulsed laser deposition

Co-Ga co-doped ZnO films were fabricated by pulsed laser deposition on quartz substrates. The obtained films exhibited a wurtzite structure with c-axes growth preference. Optical measurements showed the presence of the cobalt ions in a tetrahedral crystal field, which proved that the Co ion substitution in the ZnO lattice, acting as magnetic cation. Hall measurements indicated that the films were n-type conductive with the electron concentrations of ~ 10²⁰/cm³. This value was much higher than that of the Co-doped films, suggesting the effective incorporation of Ga in the films. Room temperature ferromagnetism was observed for the Ga-Co co-doped thin films.     

Improvements of spatial resistivity distribution in transparent conducting Al-doped ZnO thin films deposited by DC magnetron sputtering

The relationship between two techniques developed for improving the resistivity distribution on the substrate surface in transparent conducting Al-doped ZnO (AZO) thin films prepared at a temperature of 200 °C by dc magnetron sputtering depositions (dc-MSD) using various sintered AZO targets has been investigated. One improvement method superimposes an rf component onto the dc-MSD (rf + dc-MSD). The other improvement method uses conventional dc-MSD with a low resistivity AZO target prepared under optimized conditions. An improvement of resistivity distribution resulted from a decrease in the resistivity of targets used in the preparation of AZO thin films by dc-MSD either with or without superimposing rf power. However, the resistivity distribution of AZO thin films resulting from depositions using rf-superimposed dc-MSD with lower-resistivity targets was not significantly improved over that of AZO thin films prepared by conventional dc-MSD using targets with the same low resistivities. The use of rf superimposition only resulted in improved resistivity distribution in thin films when the AZO targets had a resistivity higher than around 1 × 10^− 3 Ω cm. It should be noted that sintered AZO targets optimized for the preparation of AZO thin films with lower resistivity as well as more uniform resistivity distribution on the substrate surface tended to exhibit a lower resistivity.     

Physical properties of CuCrO2 films prepared by pulsed laser deposition

High-quality CuCrO₂ films were prepared by pulsed laser deposition (PLD). The film deposited with the pulse energy density (PED) of 2 mJ/cm² is highly c-axis oriented. The refractive index of the CuCrO₂ films is about 1.29 obtained by transmission spectra of the films, which implies that the CuCrO₂ film will be a potential antireflection coating in visible light. The films prepared with different PEDs show different conduction mechanism, which suggested the different band structure between these CuCrO₂ films.     

Deterioration and recovery in the resistivity of Al-doped ZnO films prepared by the plasma sputtering

A hot-cathode plasma sputtering technique was used for fabricating the highly transparent and conducting aluminum-doped zinc oxide (AZO) films on glass substrates from a disk-shaped AZO (Al₂O₃: 2 wt.%) target. Under particular conditions where the target voltage was V_T = −200 V and the plasma excitation pressure was P_S = 1.5 × 10⁻³ Torr, the lowest resistivity of 4.2 × 10⁻⁴ Ω cm was obtained at 400 nm, and this was associated with a carrier density of 8.7 × 10²⁰ cm⁻³ and a Hall mobility of 17 cm²/V s. From the annealing experiment of the AZO films in the oxygen and nitrogen gases of the atmospheric pressure it was revealed that both the oxygen vacancies and the grain boundaries in the polycrystalline AZO film played an important role in the electrical properties of the film.     

Transparent, conducting, and ferromagnetic multilayer films based on ZnO/Fe3O4 by pulsed laser deposition technique

Multilayer thin films based on zinc oxide (ZnO) and iron oxide (Fe₃O₄) are fabricated using pulsed laser deposition method. The structural, electrical, and magnetic properties of these multilayer films are studied. X-ray diffraction study shows that ZnO film is highly oriented along (002) direction, while Fe₃O₄ film has preferred orientation along (222) direction. These films are transparent, conducting, and ferromagnetic at room temperature. The temperature dependence of resistance measurement shows semiconducting nature and charge transportation in these films is due to tunneling. Negative magneto-resistance of 0.28% is observed at room temperature.     

Copper doped nickel oxide transparent p-type conductive thin films deposited by pulsed plasma deposition

Transparent p-type conductive Ni_0.9Cu_0.1O thin films were prepared by pulsed plasma deposition (PPD) method. The effects of substrate temperature and oxygen pressure on the structural, electrical and optical properties of the films were investigated respectively. The film deposited at room temperature exhibits the highest conductivity of 5.17 S cm⁻¹, with an average transmittance of 60% in the visible region. A transparent p-Ni_0.9Cu_0.1O/n-In₂O₃:W (IWO) hetero-junction diode was fabricated exhibiting rectifying current-voltage characteristics.     

Influence of the deposition atmosphere on the characteristics of Pd–Mg thin films prepared by pulsed laser deposition

Bilayered palladium (30 nm thick)–magnesium (350 nm thick) thin films were prepared using the pulsed laser deposition technique in the presence of various background gases (Ar, He and a mixture He + H₂) under different partial pressures (47 and 27 Pa). According to the deposition atmosphere, the Pd/Mg interface shows either a sharp or an extended transition. The electrochemical hydriding properties and the mechanical stability upon cycling of the Pd/Mg film are greatly improved when an extended «intermixing» zone between the Pd and Mg layers is present. The Pd–Mg films prepared under pure helium fulfill these conditions.