Phase-transition temperatures and piezoelectric properties of (Bi1/2Na1/2)TiO3-(Bi1/2Li1/2)TiO3-(Bi1/2K1/2)TiO3 lead-free ferroelectric ceramics.

The phase-transition temperatures and piezoelectric properties of x(Bi(1/2)Na(1/2))TiO3-y(Bi(1/2)Li(1/2))TiO3-z(Bi(1/2)K(1/2))TiO3 [x + y + z = 1] (abbreviated as BNLKT100(y)-100(z)) ceramics were investigated. These ceramics were prepared using a conventional ceramic fabrication process. The phase-transition temperatures such as depolarization temperatures T(d), rhombohedraltetragonal phase transition temperature T(R-T), and dielectric-maximum temperature T(m) were determined using electrical measurements such as dielectric and piezoelectric properties. The X-ray powder diffraction patterns of BNLKT100(y)-100(z)) show the morphotropic phase boundary (MPB) between rhombohedral and tetragonal at approximately z = 0.20, and the piezoelectric properties show the maximum at the MPB. The electromechanical coupling factor k(33), piezoelectric constant d(33) and T(d) of BNLKT4-20 and BNLKT8-20 were 0.603, 176 pC/N, and 171 degrees C, and 0.590, 190 pC/N, and 115 degrees C, respectively. In addition, the relationship between d33 and Td of tetragonal side and rhombohedral side for BNLKT4-100z and BNLKT8-100z were presented. Considering both high Td and high d(33), the tetragonal side of BNLKT4-100z is thought to be the superior composition. The d(33) and T(d) of BNLKT4-28 were 135 pC/N and 218 degrees C, respectively. Moreover, this study revealed that the variation of T(d) is related to the variation of lattice distortion such as rhombohedrality 90-alpha and tetragonality c/a.     

Piezoelectric properties in (K0.5Bi0.5)TiO 3-(Na0.5Bi0.5)TiO3-BaTiO 3 lead-free ceramics

Lead-free piezoelectric ceramics with compositions around the morphotropic phase boundary (MPB) x(Na_0.5Bi_0.5)TiO _3-y(K_0.5Bi_0.5)TiO₃-zBaTiO ₃ [x + y + z = 1; y:z = 2:1] were synthesized using conventional, solid-state processing. Dielectric maximum temperatures of 280degC and 262degC were found for tetragonal 0.79(Na_0.5Bi_0.5)TiO₃-0.14(K_0.5 Bi_0.5)TiO₃-0.07BaTiO$ d3 (BNBK79) and MPB composition 0.88(Na_0.5Bi_0.5)TiO₃-0.08(K _0.5Bi_0.5)TiO₃-0.04BaTiO$ d3 (BNBK88), with depolarization temperatures of 224degC and 162degC, respectively. Piezoelectric coefficients d₃₃ were found to be 135 pC/N and 170 pC/N for BNBK79 and BNBK88, and the piezoelectric d₃₁ was determined to be -37 pC/N and -51 pC/N, demonstrating strong anisotropy. Coercive field values were found to be 37 kV/cm and 29 kV/cm for BNBK79 and BNBK88, respectively. The remanent polarization of BNBK88 (~40 muC/cm²) was larger than that of BNBK79 (~29 muC/cm²). The piezoelectric, electromechanical, and high-field strain behaviors also were studied as a function of temperature and discussed     

Preparation and characterization of yBiGaO/sub 3/-(1-x-y)BiScOs/sub 3-x/PbTiO/sub 3/ piezoelectric ceramics

The ternary system of j/BiGaO₃-(1-x-y) BiScO₃-xPbTiO₃ (BGS-PT) ceramics was prepared by using conventional mixing oxide processing. X-ray diffraction analysis revealed that the BGS-PT ceramics showed the perovskite structure. The Curie temperature (T_C) of BGS-PT ceramics was found to increase with increasing BiGaO₃ content. However, a larger BiGaO₃ content led to sharply decreased piezoelectric properties, and the secondary phase was formed in the BGS-PT system. BGS-PT ceramics with x = 0.56, y = 0.19 showed a high Curie temperature T_C and a large piezoelectric constant d₃₃ of 501degC and 152 pC/N, respectively. The high T_C of BGS-PT ceramics with usable piezoelectric properties suggests future high-temperature applications.     

Fabrication of Lead-Free Piezoelectric (Na/sub 0.5/K/sub 0.5/)NbO/sub 3/Ceramics by a Modified Solid-State Reaction Method

Sodium potassium niobate, (Na_0.5K_0.5)NbO₃, fine powder has been successfully synthesized at the low temperature of 550degC through a modified solid-state reaction method, in which urea [CO(NH₂)₂] plays an important role. High-density (Na_0.5K_0.5)NbO₃ ceramics could be obtained by conventional sintering of the synthesized (Na_0.5K_0.5)NbO₃ fine powder with the addition of 0.03 mol% Co₃O₄ as a sintering additive. The crystal structure, microstructure, and dielectric and piezoelectric properties were characterized. The (Na_0.5K_0.5)NbO₃ ceramic showed a comparatively saturated P-E hysteresis loop. The (Na_0.5K_0.5)NbO₃ ceramic also displayed piezoelectricity with a piezoelectric constant d₃₃ of 126 pC/N and a planar electromechanical coupling factor k_p of 33%.     

Structure and ferroelectric properties of Bi(Zn1/2Ti1/2)O3-(Bi1/2K1/2)TiO3 perovskite solid solutions

Lead-free piezoelectric ceramics based on χBi(Zn_1/2Ti_1/2)O₃-(1-χ)(Bi_1/2K_1/2)TiO₃ were obtained via solid state processing techniques. A single perovskite phase with tetragonal symmetry was obtained for Bi(Zn_1/2Ti_1/2)O₃ (BZT) substitutions up to 20 mol%. The maximum density was 97.1% at the composition of χ = 0.1. The dielectric measurement indicated that the transition temperature decreased linearly with increasing BZT content. The P-E loops revealed an increase in remanent polarization (P_r) with the addition of BZT. The maximum planar coupling coefficient, κ_r, for the χ = 0.1 composition was 21.6 and the piezoelectric coefficient, d₃₃, for χ = 0, χ = 0.05, and χ = 0.1 was 108, 185, and 235 pm/V, respectively. Overall, the dielectric and piezoelectric properties showed significant improvement when BZT was added.     

Piezoelectric properties in (K0.5Bi0.5)TiO3-(Na0.5Bi0.5)TiO3-BaTiO3 lead-free ceramics.

Lead-free piezoelectric ceramics with compositions around the morphotropic phase boundary (MPB) x(Na0.5Bi0.5)TiO3-y(K0.5Bi0.5)TiO3-zBaTiO3 [x + y + z = 1; y:z = 2:1] were synthesized using conventional, solid-state processing. Dielectric maximum temperatures of 280 degrees C and 262 degrees C were found for tetragonal 0.79(Na0.5Bi0.5)TiO3-0.14(K0.5Bi0.5)TiO3-0.07BaTiO3 (BNBK79) and MPB composition 0.88(Na0.5Bi0.5)TiO3-0.08(K0.5Bi0.5)TiO3-0.04BaTiO3 (BNBK88), with depolarization temperatures of 224 degrees C and 162 degrees C, respectively. Piezoelectric coefficients d33 were found to be 135 pC/N and 170 pC/N for BNBK79 and BNBK88, and the piezoelectric d31 was determined to be -37 pC/N and -51 pC/N, demonstrating strong anisotropy. Coercive field values were found to be 37 kV/cm and 29 kV/cm for BNBK79 and BNBK88, respectively. The remanent polarization of BNBK88 (approximately 40 microC/cm2) was larger than that of BNBK79 (approximately 29 microC/cm2). The piezoelectric, electromechanical, and high-field strain behaviors also were studied as a function of temperature and discussed.     

0.94Na1/2Bi1/2TiO3-0.06BaTiO3:TiO2无铅复合陶瓷的结构及退极化温度研究

采用固相法将纳米TiO₂引入0.94Na_1/2Bi_1/2TiO₃-0.06BaTiO₃ (简称NBT-6BT)钙钛矿结构压电陶瓷晶界中, 成功制备出NBT-6BT: xTiO₂ (x=0, 0.05, 0.1, 0.2, 0.3) 0-3型复合结构陶瓷, 并系统地研究了掺杂TiO₂对陶瓷的结构及压电性能的影响。实验结果表明, 部分TiO₂进入晶格内部造成陶瓷单斜相Cc含量减少, 晶体对称性提高; 随着TiO₂的掺杂量的增加, 明显提高了NBT-6BT陶瓷的退极化温度。对NBT-6BT:0.1TiO₂样品, 在保持一定压电常数(69 pC/N)的前提下, 陶瓷的退极化温度相比纯NBT-6BT提升约88%, 此时介电损耗tanδ=0.044, 表明该材料是一种适用于更高温区间的新型无铅压电材料。     

A High Temperature Piezoelectric Ceramic: (1-x)(Bi0.9La0.1)FeO3-xPbTiO3 Crystalline Solutions

(1-x)(Bi_0.9La_0.1)FeO_3-xPbTiO₃ (BLF-PT) crystalline solutions for x = 0.35, 0.37, 0.4, 0.43 and 0.45 have been prepared by the solid-state reaction method. The X-ray diffraction analysis shows that BLF-PT has a single perovskite phase with mixed tetragonal and rhombohedral phases between x = 0.4 and 0.43. The Curie temperature of BLF-PT for x = 0.4 attains 460degC, which is about 80degC higher than that of hard Pb(Zr,Ti)O₃ ceramics. The remnant polarization and piezoelectric constant of BLF-PT for x = 0.4 reach 38 muC/cm² and 112 pC/N, respectively. The planar coupling factor k_p of BLF-PT for x = 0.4 remains stable at temperature increases of up to 360degC. The impedance spectroscopy study reveals that the high temperature conduction of BLF-PT may be attributed to the motion of oxygen vacancies within the material. Our results indicate that BLF-PT is a promising candidate for high temperature applications.     

三元陶瓷Pb(In1/2Nb1/2)O3-Pb(Ni1/3Nb2/3)O3-PbTiO3准同型相界附近组分的介电、铁电和压电性能

铅基复合钙钛矿铁电材料广泛应用于机电传感器、致动器和换能器。二元铁电固溶体Pb(Ni_1/3Nb_2/3)O₃- PbTiO₃(PNN-PT)由于其在准同型相界(MPB)区域具有优异的压电、介电性能而备受关注。然而较大的介电损耗和较低的居里温度限制了其在高温高功率器件方面的应用。本研究通过引入Pb(In_1/2Nb_1/2)O₃ (PIN)作为第三组元改善PNN-PT的电学性能, 提高其居里温度; 通过两步法合成了MPB区域的三元铁电陶瓷Pb(In_1/2Nb_1/2)O₃- Pb(Ni_1/3Nb_2/3)O₃-PbTiO₃ (PIN-PNN-PT), 研究了其结构、介电、铁电和压电性能。制备的所有组分陶瓷具有纯的钙钛矿结构。随着PT含量的增加, 陶瓷结构从三方相转变为四方相。通过XRD分析得到了室温下PIN-PNN-PT体系的MPB相图。体系的居里温度由于PIN的加入得到了很大的提高, 更重要的是PIN的引入降低了PNN-PT体系的介电损耗和电导。MPB处的组分展现出了优异的电学性能, 室温下, 性能最优组分为0.30PIN-0.33PNN-0.37PT: d₃₃=417 pC/N, T_C=200 ℃, ε′= 3206, tanδ=0.033, P_r=33.5 μC/cm², E_C=14.1 kV/cm。引入PNN-PT的PIN第三组元使得体系的居里温度和压电性得到提高的同时降低了的介电损耗和电导率, 因此, PIN-PNN-PT三元铁电陶瓷在高温高功率换能器等方面具备一定的应用潜力。     

Enhancement of Q/sub m/by Co-Doping of Li and Cu to Potassium Sodium Niobate Lead-Free Ceramics

Lead-free piezoelectric ceramics KNN modified by Li-substitution and CuO addition have been synthesized, and the piezoelectric and dielectric properties were measured. A morphotropic phase boundary (MPB) between orthorhombic and tetragonal phases was formed with Li-substitution. The co-doping of Li and Cu markedly enhanced the mechanical quality factor (Q_m) in comparison with the sole doping of Li and Cu. Anomalous anti-ferroelectric-like hysteresis curves were observed in 2 mol% CuO-doped ceramics. The anti-ferroelectric-like curves were changed to that of normal ferroelectrics following poling. A model based on the formation of the internal bias field (Ei) due to the movements of space charges was proposed to explain these phenomena. It was considered that the Ei stabilized the spontaneous polarization (Pa) and suppressed the domain wall motion to enhance the Q_m. The highest Q_m obtained in this study was 742. The [(Na_0.5K_0.5)_0.96Li_0.04] NbO₃ + 0.45 mol% CuO ceramics showed a high Q_m value of 414 with a high piezoelectric constant d₃₃ of 100 pC/N.     

Depolarization temperature and piezoelectric properties of Na1/2Bi1/2TiO3-Na1/2Bi1/2(Zn1/3Nb2/3)O3 ceramics by two-stage calcination method

A new group of NBT-based lead-free piezoelectric ceramics, Na_1/2Bi_1/2TiO₃-Na_1/2Bi_1/2(Zn_1/3Nb_2/3)O₃, was synthesized using the two-stage calcination method and depolarization temperatures and piezoelectric properties were also investigated. The XRD analysis showed that the ceramics system had a morphotropic phase boundary (MPB) between the rhombohedral and the tetragonal structure. The highest piezoelectric properties of d ₃₃ = 97 pC/N and k _t = 0·46 were obtained near MPB compositions. Furthermore, the depolarization temperatures near MPB compositions were slightly decreased and the lowest T _d was maintained at 210°C.     

Piezoceramics Properties as a Function of the Structure in the System (K,Na,Li)(Nb,Ta,Sb)O3

The influence of the sintering conditions and stoichiometry on the crystalline symmetry and electrical properties of the system (K_0.44+xNa_0.52Li_0.04)(Nb_0.86Ta_0.10Sb_0.04)O_3+x/2, with x = -0.06, 0.00, and 0.04, has been evaluated. By lowering the concentration of K cations, a faster stabilization of the tetragonal phase is reached. Increasing the sintering time also leads to the stabilization of the tetragonal phase at room temperature, as evidenced by Raman spectroscopy, thus improving the piezoelectric properties of these materials. The Raman spectra versus temperature showed 2 anomalies at temperatures of ~70 and ~270 to 330degC, associated with polymorphism and the ferro-paraelectric phase transitions, respectively. Active Raman scattering modes are observed above Curie temperature, indicating that the symmetry is not cubic but pseudocubic. This pseudocubic phase is associated with relaxor diffuseness, attributed to composition fluctuations. In addition, the piezoelectric properties were correlated with the tetragonality of the system, showing a linear dependence between the piezoelectric properties and the tetragonality ratio. The ceramics with c/a = 1.011 ratio exhibit enhanced electrical properties, d₃₃ ~255 pC/N and k_p ~0.47.     

Dielectric and ferroelectric properties of Bi(Zn1/2Ti1/2)O3-PbTiO3-PbZrO3 ternary ceramics

Ceramics of a new ternary solid solution system, xBi(Zn(1/2)Ti(1/2))O(3-yPbTiO(3)z)PbZrO(3) (xBZT-yPT-zPZ), with compositions along the solubility limit curve are prepared by solid-state reaction and sintering technique. Two morphotropic phase boundaries (MPBs) separating the orthorhombic and tetragonal (MPB(O-T)) phases and the tetragonal and rhombohedral (MPB(T-R)) phases, respectively, are observed with increasing z (0.10 ≤ x ≤ 0.21; 0 ≤ y ≤ 0.49). It is found that the transition from the ferroelectric to paraelectric phase becomes more diffuse with the addition of BZT into the PZT solid solution. Enhanced dielectric and ferroelectric properties appear at MPB(R-T), which exists over a wide composition region (0.45 ≤ z ≤ 0.6), as revealed by X-ray diffraction and dielectric measurements. The dielectric constant reaches a maximum value (ε' = 1250) on the tetragonal majority side of the MPB. The highest remnant polarization (P(r) = 34.2 μC/cm(2)) is found in the composition at the center of the MPB, where the rhombohedral and tetragonal phases coexist in almost equal quantities.     

新型铁电晶体铌镥酸铅-钛酸铅的生长与性能

采用顶部籽晶法生长了一系列不同组分的高居里温度铌镥酸铅-钛酸铅[(1-x)Pb(Lu_1/2Nb_1/2)O₃-xPbTiO₃ (PLN-xPT)]铁电晶体。该晶体在三方相区域表现出典型的介电弛豫特性, 不同组分的晶体表现出了较高的居里温度; 基于介电和结构测试结果, 得到了该体系的低温二元体系相图, 在相图中存在一个准同型相界区域(MPB), 其组分位于x = 0.49~0.51; 利用偏光显微镜分析晶体电畴结构得到和X射线粉末衍射测试结果吻合的相结构; 电学性能测试结果表明不同组分的晶体性能差异较大。组分位于MPB附近的晶体表现出优异的压电性能, 如x = 0.49时, 居里温度T_c = 360℃, 压电常数d₃₃ > 1600 pC/N。处于MPB附近的晶体存在较大的矫顽E_c >10kV/cm, 一些组分晶体的三方–四方相变温度T_RT > 200℃。结果表明高的居里温度及优异的压电性能使二元铌镥酸铅-钛酸铅晶体具有更大的温度应用范围及更广阔的应用前景。     

铌镁酸铋-钛酸铅压电陶瓷准同型相界附近的性能和相变温度研究

利用传统固相烧结法制备了Bi(Mg_2/3Nb_1/3)O₃-PbTiO₃(BMN-PT)压电陶瓷, 分析了不同PbTiO₃含量对BMN-PT压电陶瓷的晶体结构、介电、压电及铁电性能的影响. XRD结果表明: 合成的BMN-PT陶瓷具有纯钙钛矿结构, 并且在PbTiO₃含量为x=0.60时, 其组分的XRD图谱在衍射角2θ=45°出现明显的分峰, 说明该组分相结构中存在三方和四方相的共存. 压电铁电性能显示, BMN-0.60PT有最大的压电常数d₃₃(~170pC/N)和平面机电耦合系数k_p(0.35), 最小的矫顽场E_c(29.4 kV/cm)及最大的剩余极化P_r(31.4 μC/cm²). 确定了BMN-PT压电陶瓷的准同型相界(MPB)为PbTiO₃含量x=0.60的组分. 介电系数温谱表明介电系数峰值温度(Tm)随着PbTiO₃含量的增大而升高, MPB组分的Tm约为276℃.     

BaZrO3掺杂对(K0.49Na0.51)0.98Li0.02(Nb0.77Ta0.18Sb0.05)O3无铅压电陶瓷的结构与电性能的影响

采用固相反应法制备了(K_0.49Na_0.51)_0.98Li_0.02(Nb_0.77Ta_0.18Sb_0.05)O₃-xBaZrO₃ (NKNLST-xBZ, x = 0~0.020 mol)无铅压电陶瓷, 系统研究了BaZrO₃的掺杂量对陶瓷的压电、介电、机电和铁电性能的影响。结果表明: 随着BaZrO₃掺杂量x的增加, 陶瓷的晶体结构由正交相向四方相转变, 在x=0.005~0.008区间出现正交相与四方相两相共存的区域, 在此区域内陶瓷的晶粒变得细小且均匀, 介电损耗tanδ大幅降低, 压电常数d₃₃和平面机电耦合系数k_p增加。该体系陶瓷的介电常数ε T 33 /ε0则随着BaZrO₃的增加持续增加, 相变温度则向低温方向移动。当x=0.005时, 该组成陶瓷具有最佳的综合性能: 压电常数d33=372 pC/N, 平面机电耦合系数kp=47.2%, 介电损耗tanδ=3.1%, 以及较高的介电常数ε^T₃₃ /ε₀=1470和居里温度T_c=208℃。     

简易合成Bi/Bi2MoO6/TiO2复合纳米纤维及其增强的可见光催化性能

以电纺TiO₂ 纳米纤维为基质, 葡萄糖为还原剂, 采用简单一步溶剂热法制备了等离子体Bi/Bi₂MoO₆/TiO₂复合纳米纤维。利用X射线衍射、场发射扫描电镜、透射电子显微镜、X射线光电子能谱、紫外-可见漫反射光谱和光致发光谱等对样品进行表征。以RhB和4-CP为模拟有机污染物, 评价材料的光催化性能。结果表明: 部分Bi ³⁺被葡萄糖还原成金属Bi纳米粒子, 原位沉积在Bi₂MoO₆纳米片上, 同时构筑在TiO₂纳米纤维表面。金属Bi的等离子体共振效应, 有效提高了样品的光催化活性。可见光照50 min, 样品对RhB的降解率为95.8%, 五次循环后仍保持在92%以上; 可见光照180 min, 样品对4-CP的降解率达68.8%。证实该材料具有良好的可见光催化活性和稳定性。     

Fabrication and Optical Properties of Pb(Mg/sub 1/3/Nb/sub 2/3/)O/sub 3/-PbTiO/sub 3/Thin Films on Si Substrates Using the PLD Method

Epitaxial 0.67Pb(Mg_1/3Nb_2/3)O₃-0.33PbTiO₃ (PMN-PT) thin films with electro-optic effects were fabricated on (La_0.5Sr_0.5)CoO₃(LSCO)/CeO₂/YSZ-buffered Si(001) substrates using double-pulse excitation pulsed laser deposition (PLD) method with a mask placed between the target and the substrate. Epitaxial growth of PMN-PT thin films was undertaken using the two-step growth method of PMN-PT film. The PMN-PT seed layer was deposited at 500degC on the LSCO/CeO₂/YSZ/Si, which temperature was the same as that used for LSCO deposition. The PMN-PT thin films were deposited on the PMN-PT seed layer at 600degC, which enables growth of high-crystallinity PMN-PT films with smooth surfaces. We obtained optimum fabrication conditions of PMN-PT film with micrometer-order thickness. Resultant films showed high crystallinity with full width at half maximum (FWHM)=0.73 deg and 1.6 mum thickness. Electro-optic properties and the refractive index value were measured at 633 nm wavelength using the prism coupling method. The obtained refractive index was 2.59. The electro-optic coefficients r₁₃ and r₃₃ were determined by applying the electrical field between a semitransparent, thin top electrode of Pt and a bottom LSCO electrode. The electro-optic coefficient was r₁₃=17 pm/V at transverse electric field (TE) mode and r₃₃=55 pm/V at transverse magnetic field (TM) mode.     

(Bi0.5Na0.5)TiO3:Sm3+无铅压电陶瓷的红光发射特性

采用传统的固相反应烧结方法制备了稀土Sm³⁺掺杂的(Bi_0.5Na_0.5)TiO₃无铅压电陶瓷。系统分析了掺杂浓度、烧结温度和离子补偿对发光特性的影响。稀土Sm³⁺离子的加入实现了(Bi_0.5Na_0.5)TiO₃陶瓷的红绿光发射, 其激发光波段位于400~500 nm范围内, 与已经成熟的蓝光LED芯片的发射光谱充分匹配。当烧结温度为1100℃, Sm³⁺离子的掺杂浓度为0.015 mol时, 陶瓷样品呈现最强的发光强度。同时, 通过Li⁺、Na⁺、K⁺离子进行电荷补偿, 有效提高了陶瓷样品的发光性能, 发光强度随离子半径增大而增强。可见, Sm³⁺掺杂的(Bi_0.5Na_0.5)TiO₃材料在光电集成器件中具有很好的应用前景。     

Dielectric and piezoelectric properties of (0.97-x) Bi1/2Na1/2TiO3-xBi1/2K1/2TiO3-0.03NaNbO3 ceramics

Ceramics of the series (0.97-x)Bi_1/2Na_1/2TiO₃-xBi_1/2K_1/2TiO₃-0.03NaNbO₃ (x = 0, 0.02, 0.06, 0.10, 0.16, 0.20, 0.30) were prepared by the conventional mixed oxide method. Influence of Bi_1/2K_1/2TiO₃ content on the crystal structure, microstructure, dielectric and piezoelectric properties were studied. All compositions showed single perovskite phase and the morphotropic phase boundary (MPB) between rhombohedral and tetragonal phase existed at the point of x = 0.16. Temperature dependences of permittivity and dissipation factor of unpoled samples revealed that permittivity increased with Bi_1/2K_1/2TiO₃ content and it reached maximum value near the MPB. At the same time, the peak value of dissipation factor increased with the addition of Bi_1/2K_1/2TiO₃. All the samples experienced two phase transitions: from ferroelectric to antiferroelectric at the first transition temperature (T_d) and from antiferroelectric to paraelectric at the temperature (T_m) corresponding to maximum value of permittivity. The phase transition from ferroelectric to antiferroelectric had relaxor characteristic and T_d shifted to lower temperature while increasing Bi_1/2K_1/2TiO₃ content. The best piezoelectric properties were obtained in 0.81Bi_1/2Na_1/2TiO₃-0.16Bi_1/2K_1/2TiO₃-0.03NaNbO₃ ceramic with a piezoelectric constant (d₃₃) of 146pC/N, planar electromechanical coupling factor (k_p) of 30.3% and thickness electromechanical coupling factor (k_t) of 53.2%. Abnormal piezoelectric properties were observed in the sample (x = 0.20), which was attributed to the co-existence of ferroelectric and antiferroelectric phases in it.