锻造方式对7075铝合金锻件动态再结晶的影响

利用金相(OM)、透射电镜(TEM)对7075铝合金热变形显微组织进行了观察。实验表明：在热锻条件下，7075铝合金完全可以发生动态再结晶并通过动态再结晶产生细小的再结晶晶粒。动态再结晶的方式为不连续动态再结晶，形核机制为亚晶转动、聚合形核；其临界应变值和加工道次有关，道次越多，临界值越低。在相同Z值下，再结晶晶粒尺寸随着应变的增加而减小。弥散的第二相粒子在动态再结晶过程中起了重要作用。     

铍对工业7475铝合金的再结晶动力学及时效行为的影响

通过对工业生产的7475铝合金加入不同含量的铍，研究了铍对合金的再结晶动力学及时效行为的影响。实验结果表明：加入0．023％Be能有效地提高7475铝合金的再结晶温度，降低再结晶速度，使合金的晶粒得到细化，且硬度值仍高于不含铍的合金；铍含量为0．7％时，上述影响减弱。铍能有效地降低7475铝合金的时效硬化时所需时间，同时提高了合金的硬度值，HB最高可达1400MPa。借助电子衍射分析，观察并讨论了合金中的析出相η′相、β相与基体间的位相关系的变化和差异。     

Recrystallization Behavior of Re-aged Cu-Ni-Si Alloy

The interaction between precipitation and recrystallization and its effect on the properties of the re-aged Cu-Ni-Si alloy are discussed. The results indicate that the pre-aging process for Cu-Ni-Si alloy was responsible to the significant strengthening effect in re-aging process, and the re-aging strengthening effect with pre-aging at 450“C for 8h was even more remarkable, Upon aging, a phenomenon of simultaneous in situ and discontinuous recrystallization was observed in the treatment of pre-aging and deformed Cu-Ni-Si alloy. On the formation and growth of recrystallization, the precipitated phases are coarsed or dissolved in the front of grain boundaries following a re-precipitation in the recrystallization area.     

超声滚压对6061铝合金晶间腐蚀行为的影响

目的 研究不同静压力条件下形变诱导梯度变形层对6061铝合金晶间腐蚀行为的影响。方法 使用超声滚压技术(USRP,Ultrasonic surface rolling processing)强化6061铝合金表层,采用激光共聚焦、X射线衍射等方法研究酸化Na Cl溶液体系下3种静压力条件对6061铝合金晶间腐蚀行为的影响。结果 随着静压力的增大,6061铝合金表层组织呈梯度变化,且形变层深度可延伸至近300μm。在酸化NaCl溶液腐蚀加速条件下,在相同时间内滚压后试样沿晶腐蚀的路径大幅缩短,向下扩展的深度降低了50%,使得6061铝合金的抗晶间腐蚀性能显著提高。表征结果表明,晶间腐蚀扩展路径与表面粗糙度无相关性,它主要与第二相(AlFeSi相)在形变层中的弥散分布有关。未经USRP处理的6061铝合金在沿晶界连续分布的AlFeSi相促进下发生了明显的沿晶腐蚀。相比之下,经USRP处理后,AlFeSi相会因晶粒形变而呈断续分布,减弱了它在晶界区域对铝合金基体的电偶腐蚀作用,降低了腐蚀通道的连通性,从而阻碍了腐蚀路径的扩展。结论 USRP可提高6061铝合金的抗晶间腐蚀性能,其表面粗糙度并非是提高晶间腐蚀抗性的主要因素,经USRP细化和分散后的AlFeSi相是阻断沿晶腐蚀路径的关键因素。     

变形量对Al-5Mg合金再结晶激活能的影响

根据公式G＝G0exp^(—Q／RT)计算了Al—5Mg合金再结晶激活能(Q)，并探讨了变形量对其再结晶激活能的影响。结果表明，Al—5Mg合金再结晶激活能随其变形量的增加而减小。     

Relating Initial Texture to Deformation Behavior During Cold Rolling and Static Recrystallization Upon Subsequent Annealing of an Extruded WE43 Alloy

Deformation behaviors during cold rolling and static recrystallization behaviors upon subsequent annealing of an extruded WE43 alloys with different initial textures were investigated in this study. Three types of differently textured WE43 initial alloys were labeled as samples Ⅰ, Ⅱ and Ⅲ. The results showed that multiple twinning modes and basal slip dominated the deformation of samples during cold rolling. Cold-rolled sample Ⅰ activated the larger number of double twins with high strain energy...     

GH738合金冷变形及中间退火再结晶行为研究

通过光学显微镜、扫描电镜、电子背散射衍射、显微硬度计等手段,系统研究了GH738合金不同冷轧变形量后中间退火组织演变规律。研究表明:变形量是影响加工硬化的主要因素;经过不同冷轧变形后,1000℃退火奥氏体未发生再结晶;在1040～1080℃进行退火处理,可得到均匀细小的等轴晶。建立了GH738合金冷加工本构方程和再结晶晶粒长大方程。     

热轧状态Al—0.328%Sc合金的动态再结晶

采用等温热压缩方法研究了一种热轧状态Al-Sc合金动态再结晶,并对试样的动态再结晶组织做了说明。     

Ti-5553合金高温变形时动态再结晶行为

采用热压缩试验方法,对Ti-5553钛合金的动态再结晶行为进行研究。结果表明,在温度800～860℃、应变速率0.01～10s-1的范围内,Ti-5553合金在高温、低应变速率变形时,晶界弓出形核是其主要的动态再结晶形核机制;在低温、高应变速率、大变形量变形时,位错塞积形核是主要的动态再结晶形核机制。在非均匀变形的条件下材料产生绝热剪切现象,其形核主要以亚晶吞并长大形核机制进行。     

变形量对CuCrZr合金再结晶的影响

研究了变形量对CuCrZr合金再结晶的影响,根据公式G=G0exp^（-Q/RT）计算出再结晶激活能（Q）。结果表明,CuCrZr合金再结晶随变形量的增加而加快,主要是由于再结晶激活能的减小所致。     

CuCrSnZnY合金的动态再结晶行为

在Gleeble-1500D热模拟试验机上,对Cu-Cr0.5-Sn0.31-Zn0.15-Y0.054合金进行高温等温压缩试验。变形条件是应变速率0.01、0.1、1、5 s-1,变形温度600、700、800℃,最大变形程度为真实应变0.6。结果表明:随变形温度升高,合金的流变应力下降,随应变速率提高,流变应力增大;在变形温度为700、800℃并且应变速率较低时,合金热压缩流变应力出现了明显的峰值;从流变应力、应变速率和温度的相关性,求得了热变形激活能(Q)和流变应力方程;合金动态再结晶的显微组织强烈受到变形条件的影响;变形条件对冷却后合金的硬度和导电率产生了明显的影响。     

Recrystallization and Precipitation Behavior of Cu-Cr-Zr Alloy

Recrystallization and precipitation behaviors after cold rolling and aging are investigated for Cu-0.7Cr-0.13Zr alloy. The processed alloy was characterized using the measurement of Vickers hardness, scanning electron microscopy, and transmission electron microscopy. The resultant complex microstructures are interpreted in terms of the interactions between precipitation and recrystallization. Upon aging at 500 °C for 1 h, the 45% rolled alloy exhibits a retarded recrystallization process and therefore an efficient hardening response, which are attributed to the pinning effect of fine dispersed precipitates on the dislocation. When heavily deformed and aged at high temperature, the alloy shows an accelerated process of recrystallization, and precipitates are found to coarsen.     

Recrystallization behavior of rolled ingots of 6061 and 6069 aluminum alloys

The purpose of this study was to investigate the recrystallization characteristics of rolled, as-cast, annealed, and homogenized ingots of “Air-Slip”™ Direct Chill (ASDC) 6061 and 6069 aluminum alloys. The % R_x for annealed and homogenized 6061 and 6069 ingots is higher than that of as-cast 6061 and 6069 ingots at a given % CW and heat-treatment temperature. There is no significant difference in % R_x between annealed ingots and homogenized ingots of the same composition at a given % CW and heat-treatment temperature. The % R_x for 6069-AC ingot is higher than that of 6061-AC ingot at a given % CW and heat-treatment temperature, especially at low heat-treatment temperatures. The % R_x of annealed 6069 ingot (6069-A) and homogenized 6069 ingot (6069-H) is slightly higher than that of corresponding 6061 ingots at a given fraction % CW and heat-treatment temperature. The difference in the recrystallization behavior may be related to the increased alloy additions, in excess of the solubility, leading to relatively large second-phase particles, particularly MgSi₂. This can lead to particle-stimulated recrystallization.     

Mg-3Y合金大应变量轧制过程中的孪生辅助动态再结晶及组织演变

采用预挤压加单道次大应变量热轧制的方法制备了Mg-3Y（质量分数,%）合金板材。并研究了大应变量轧制过程中不同孪晶类型对合金动态再结晶（DRX）及组织演变的影响。结果表明,在挤压比为8:1的预挤压过程中,合金内部发生了几乎完全的动态再结晶。而在接下来的大应变量热轧制过程中,孪生变形尤其是■压缩孪晶及■双孪晶在协调合金的塑性应变中发挥了重要作用。此外,大量动态再结晶在压缩孪晶及双孪晶内部发生,并扩展到非孪晶区域,有效缓解了轧制过程中的内应力集中。上述2个过程对提高合金在大应变量轧制中的成形性均起到了促进作用。     

Recrystallization model for hot-rolling of 5182 aluminum alloy

1　ＩＮＴＲＯＤＵＣＴＩＯＮＤｕｒｉｎｇｈｏｔ ｒｏｌｌｉｎｇ ,ａｌｌｏｙｓａｒｅｄｅｆｏｒｍｅｄｆｏｒｖａｒｉ ｏｕｓｐａｓｓｅｓａｔｄｉｆｆｅｒｅｎｔｔｅｍｐｅｒａｔｕｒｅ .Ｒｅｃｒｙｓｔａｌｌｉｚａｔｉｏｎｏｃｕｒｒｅｄａｔｅｖｅｒｙｐａｓｓｃａｎｉｎｆｌｕｅｎｃｅｍａｎｙｐｒｏｐｅｒｔｉｅｓｏｆａｌｌｏｙｓｓｕｃｈａｓｔｈｅｏｃｃｕｒｒｅｎｃｅｏｆｐｒｅｃｉｐｉｔａｔｉｏｎ ,ｐｒｅ ｆｅｒｒｅｄｏｒｉｅｎｔａｔｉｏｎａｎｄｇｒａｉｎｓｉｚｅ[1,2 ] .Ｕｓｕａｌｌｙ ,ｔｈｅｓｔａｔｉｃｒｅｃｒｙ…     

Effect of Deformation Conditions on the Dynamic Recrystallization of GH690 Alloy

采用Gleeble-3500热模拟试验机进行高温等温压缩实验,研究了变形条件对GH690合金高温变形动态再结晶的影响。结果表明:GH690合金动态再结晶过程是一个受变形温度和应变速率控制的过程,在应变速率为0.001～1s-1的实验条件下,GH690合金获得完全动态再结晶组织所需的温度随变形速率的增大而升高;动态再结晶晶粒尺寸随变形温度升高而增大。采用力学方法直接从流变曲线确定了GH690合金发生动态再结晶的临界应变量,并回归出临界应变量与Z参数的关系式:εc=1.135×10-3Z0.14233。GH690合金的主要动态再结晶机制是原始晶界凸起形核的不连续动态再结晶机制(DDRX),而新晶粒通过亚晶逐渐转动而形成的连续动态再结晶机制(CDRX)则起辅助作用。     

690合金高温变形行为与动态再结晶模型

利用物理模拟实验方法对690合金进行恒温恒速压缩实验,变形温度范围为1050～1250℃,应变速率分别为0.1,1、5,10s-1,获得了合金的流变应力数据,并对合金变形后的组织特征进行了分析。建立了690合金高温热变形的本构方程和动态再结晶模型。结果表明:690合金高温变形时的流变行为可用Zener-Hollomon参数的双曲正弦函数来描述,所建立流变应力本构模型的预测值与实验值吻合较好,建立了690合金的动态再结晶模型,为热挤压过程中的组织控制提供理论依据。     

含微量Zr的Al-6%Mg合金再结晶行为及其超塑性

研究了含微量元素Zr的Al-6%Mg合金大的冷变形后的板材和旋压管材在不同条件下退火时的再结晶行为及其后续的超塑性变形行为。制备了Al-6%Mg和Al-6%Mg-Zr试验合金,合金1、2经过73%的冷变形后获得2mm厚板材;合金3采用Al-6%Mg-Zr合金锭坯,经50%旋压变形后获得2.4mm厚旋压管材。观察对比了3种合金试样经250～525℃退火1h后的显微组织。然后分别在480℃、500℃和520℃,以1×10-4～1.6×10-3s-1的应变速率进行拉伸试验。结果表明:Zr在合金中形成的Al3Zr化合物能明显细化Al-6%Mg合金的铸态组织,抑制合金退火过程中再结晶晶粒的长大,合金再结晶后的晶粒尺寸达1.62μm,轴比为1.04。含Zr的Al-Mg合金在520℃时以应变速率8×10-4s-1的速率拉伸,其伸长率可达到600%。Al3Zr质点还可在退火时和超塑拉伸时抑制晶粒长大,使合金获得细小等轴晶粒,这是Al-Mg-Zr合金获得超塑性的主要原因。     

应变速率和固溶处理对7075铝合金锻件动态再结晶的影响

通过对不同状态的7075铝合金以不同的应变速率和不同的应变锻造，并利用了光镜(OM)、透射电镜(TEM)对热变形显微组织进行观察。实验表明：对于7075铝合金，较高的应变速率有利于出现动态再结晶，动态再结晶的方式为不连续动态再结晶，当应变速率较低时，只出现动态回复。弥散的第二相粒予在动态再结晶过程中起了重要作用。     

Hastelloy C-276合金热变形动态再结晶模型研究

采用Gleeble-3500热模拟试验机研究了Hastelloy C-276镍基合金在不同变形条件下的热压缩流变应力曲线,热变形过程中发生了动态再结晶行为。利用加工硬化率-应力关系曲线确定了动态再结晶临界条件,采用Johnson-Mehl-Avrami(JMA)方程计算再结晶体积分数实验值,建立了C-276合金动态再结晶体积分数和晶粒尺寸预测模型。结果表明:C-276合金动态再结晶体积分数随着应变量的增加,呈现典型的"S型"曲线;获得临界应变条件表达式:lnε_c=0.144lnZ-7.173;动态再结晶体积分数表达式X_(drx)=1-exp{-1.4034[(ε-ε_c)/ε_(0.5)]~(2.58384)},预测值和实验值的平均误差为2.16%;晶粒长大表达式d_(drx)=6.58×10~3Z~(-0.168),预测值和实验值的平均误差为6.63%。