Effect of substrate temperature on the optical parameters of thermally evaporated Ge-Se-Te thin films

Thin films of Ge₁₀Se_90 − xTe_x (x = 0, 10, 20, 30, 40, 50) glassy alloys were deposited at three substrate temperatures (303 K, 363 K and 423 K) using conventional thermal evaporation technique at base pressure of ~ 10^− 4 Pa. X-ray diffraction results show that films deposited at 303 K are of amorphous nature while films deposited at 363 K and 423 K are of polycrystalline nature. The optical parameters, refractive index and optical gap have been derived from the transmission spectra (using UV-Vis-NIR spectrophotometer) of the thin films in the spectral region 400-1500 nm. This has been observed that refractive index values remain almost constant while the optical gap is found to decrease considerably with the increase of substrate temperature. The decrease in optical gap is explained on the basis of change in nature of films, from amorphous to polycrystalline state, with the increase of substrate temperature. The optical gap has also been observed to decrease with the increase of Te content.     

Study of flash evaporated CuIn1 − xGaxTe2 (x = 0, 0.5 and 1) thin films

CuIn_1 − xGa_xTe₂ thin films with x = 0, 0.5 and 1, have been prepared by flash evaporation technique. These semiconducting layers present a chalcopyrite structure. The optical measurements have been carried out in the wavelength range 200-3000 nm. The linear dependence of the lattice parameters as a function of Ga content obeying Vegard's law was observed. The films have high absorption coefficients (4 · 10⁴ cm^− 1) and optical band gaps ranging from 1.06 eV for CuInTe₂ to 1.21 eV for CuGaTe₂. The fundamental transition energies of the CuIn_1 − xGa_xTe₂ thin films can be fitted by a parabolic equation namely E_g1(x) = 1.06 + 0.237x − 0.082x². The second transition energies of the CuInTe₂ and CuGaTe₂ films were estimated to be: E_g2 = 1.21 eV and E_g2 = 1.39 eV respectively. This variation of the energy gap with x has allowed the achievement of absorber layers with large gaps.     

Fabrication and characterization of n-CdSe0.7Te0.3/p-CdSe0.15Te0.85 solar cell

Hot wall deposited CdSe_xTe_1−x where 0 ≤ x ≤ 1 thin films for solar cell applications have been prepared from a compound synthesized by direct reaction of high purity Cd, Se and Te elements. Crystal structure and composition of the films were analyzed by X-ray diffraction, scanning electron microscope and EDAX. X-ray diffraction studies carried out on pseudo-binary system revealed that the films are polycrystalline in nature with CdSe_0.7Te_0.3 film exhibiting hexagonal structure and CdSe_0.15Te_0.85 film exhibiting cubic zinc blende structure. The type of conduction was determined by Hall studies. A novel solar cell with structure n-CdSe_0.7Te_0.3/p-CdSe_0.15Te_0.85 has been fabricated and the efficiency was found to be 3.13%.     

Structural, electrical and optical properties of Bi2Se3 and Bi2Se(3−x)Tex thin films

Thin films of Bi₂Se₃, Bi₂Se_2.9Te_0.1, Bi₂Se_2.7Te_0.3 and Bi₂Se_2.6Te_0.4 are prepared by compound evaporation. Micro structural, optical and electrical measurements are carried out on these films. X-ray diffraction pattern indicates that the as-prepared films are polycrystalline in nature with exact matching of standard pattern. The composition and morphology are determined using energy dispersive X-ray analysis and scanning electron microscopy (SEM). The optical band gap, which is direct allowed, is 0.67 eV for Bi₂Se₃ thin films and the activation energy is 53 meV. Tellurium doped thin films also show strong optical absorption corresponding to a band gap of 0.70-0.78 eV. Absolute value of electrical conductivity in the case of tellurium doped thin film shows a decreasing trend with respect to parent structure.     

Thermoelectric properties of the tetradymite-type Bi2Te2S-Sb2Te2S solid solution

The thermoelectric properties of the tetradymite-type Bi_2−xSb_xTe₂S solid solution (0 ≤ x ≤ 2) are reported for the temperature range 5-300 K. The properties of non-stoichiometric, Cl and Sn doped n- and p-type variants are reported as well. The Seebeck coefficients for these materials range from −170 to +270 μV K⁻¹ while the resistivities range from those of semimetals, 2 mΩ cm, to semiconductors, >1000 mΩ cm. Thermal conductivities were low for most compositions, typically 1.5 W m⁻¹ K⁻¹. Nominally undoped Bi₂Te₂S shows the highest thermoelectric efficiency amongst the tested materials with a ZT = 0.26 at 300 K that decreased to 0.04 at 100 K. The crystal structure of Sb₂Te₂S, a novel tetradymite-type material, is also reported.     

Laser-induced amorphization and crystallization on Se80Te20−xPbx thin films

Thin films of glassy alloys of a-Se₈₀Te_20−xPb_x (x=2, 6 and 10) was crystallized in a specially designed sample holder under a vacuum of 10⁻² Pa. The amorphous and crystallized films were induced by pulse laser (wavelength: 337.1 nm, frequency: 10 Hz, pulse duration: 4 ns and pulse energy: 0.963 mJ). After laser irradiation on amorphous and crystalline films: optical band gaps were measured. Crystallization and amorphization of chalcogenide films is accompanied by the change in the optical band gap. The change in optical energy gap could be determined by identification of the transformed phase. This change in the optical band gap may be due to the increase in the grain size and the reduction in the disorder of the system.     

Optical characterization of vacuum evaporated a-Se80Te20−xCux thin films

Thin films of a-Se₈₀Te_20−xCu_x (where x=2, 6, 8 and 10) were deposited on glass substrates by vacuum evaporation technique. The absorbance, reflectance and transmittance of as-deposited thin films were measured in the wavelength region 400-1000 nm. The optical band gap and optical constants of amorphous thin films have been studied as a function of photon energy. The optical band gap increases on incorporation of copper in Se₈₀Te_20−xCu_x system. The value of refractive index (n) decreases while the value of the extinction coefficient (k) increases with increasing photon energy. The results are interpreted in terms of concentration of localized states.     

Band alignment of Cd(1 − x)ZnxS produced by spray pyrolysis method

Cd_(1 − x)Zn_xS thin films have been grown on glass substrates by the spray pyrolysis method using CdCl₂ (0.05 M), ZnCl₂ (0.05 M) and H₂NCSNH₂ (0.05 M) solutions and a substrate temperature of 260 °C. The energy band gap, which depends on the mole fraction × in the spray solution used for preparing the Cd_(1 − x)Zn_xS thin films, was determined. The energy band gaps of CdS and ZnS were determined from absorbance measurements in the visible range as 2.445 eV and 3.75 eV, respectively, using Tauc theory. On the other hand, the values calculated using Elliott-Toyozawa theory were 2.486 eV and 3.87 eV, respectively. The exciton binding energies of Cd_0.8Zn_0.2S and ZnS determined using Elliott-Toyozawa theory were 38 meV and 40 meV, respectively. X-ray diffraction results showed that the Cd_(1 − x)Zn_xS thin films formed were polycrystalline with hexagonal grain structure. Atomic force microscopy studies showed that the surface roughness of the Cd_(1 − x)Zn_xS thin films was about 50 nm. Grain sizes of the Cd_(1 − x)Zn_xS thin films varied between 100 and 760 nm.     

Optical, electrical and thermal studies on (As2Se3)3−x(As2Te3)x glasses

Optical properties and conductivity of glassy (As₂Se₃)_3−x(As₂Te₃)_x were studied for 0 ≤ x ≤ 3. The films of the above mentioned compound were prepared by thermal evaporation with thickness of about 250 nm. The optical-absorption edge is described and calculated using the non-direct transition model and the optical band gap is found to be in the range of 0.92 to 1.84 eV. While, the width of the band gap tail exhibits opposite behaviour and is found to be in the range of 0.157 to 0.061 eV, this behaviour is believed to be associated with cohesive energy and average coordination number. The conductivity measurement on the thin films is reported in the temperature range from 280 to 190 K. The conduction that occurs in this low-temperature range is due to variable range hopping in the band tails of localized states, which is in reasonable agreement with Mott's condition of variable range hopping conduction. Some parameters such as coordination number, molar volume and theoretical glass transition temperature were calculated and discussed in the light of the topological bonding structure.     

Calorimetric and optical study of amorphous Se85 − xTe15Bix glassy alloy

Bulk samples of Se_85 − xTe₁₅Bi_x (where x = 0, 1, 2, 3, 4, 5) glassy alloys are obtained by melt quenching technique. Differential scanning calorimetric (DSC) technique has been applied to determine the thermal properties of Se-rich Se_85 − xTe₁₅Bi_x glassy alloys in the glass transition and crystallization regions at four heating rates (5, 10, 15, 20 K min^− 1). The glass transition temperature (T_g) and peak crystallization temperature(T_p) are found to shift to a higher temperature with increasing heating rate. With Bi addition, the value of (T_g)increases. (T_p) is found to increase as Bi is introduced to the Se-Te host, however further increase in Bi concentration is responsible for the reduction of. Thin film of bulk samples are deposited on glass substrate using thermal evaporation technique under vacuum for optical characterization. Optical band gap is estimated using Tauc's extrapolation and is found to decrease from 1.46 to 1.24 eV with the Bi addition.     

Crystallization mechanisms of (In15Sb85)100−xBix phase change recording thin film

The (In₁₅Sb₈₅)_100−xBi_x films (x = 0–18.3) were deposited on nature oxidized Si wafer and glass substrate at room temperature by magnetron co-sputtering of Sb target and InBi composite target. The optical and thermal properties of the films were examined by reflectivity thermal analyzer. Microstructures of the films were analyzed by X-ray diffraction and transmission electron microscope. The crystallization activation energy of the (In₁₅Sb₈₅)_100−xBi_x film (x = 0–18.3) was decreased with increasing Bi content, this indicated that the crystallization speed was improved by doping Bi. The structure of as-deposited (In₁₅Sb₈₅)_100−xBi_x films was amorphous and it would transform to Sb, InSb, Bi, and BiIn₂ coexisting phases after annealing at 250 °C for 30 min.     

The properties of transparent semiconductor Zn1 − xTixO thin films prepared by the sol-gel method

Transparent semiconductor thin films of Zn_1 − xTi_xO (0 ≦ x ≦ 0.12) were deposited on alkali-free glass substrates by the sol-gel method. The effects of Ti addition on the crystallization, microstructure, optical properties and resistivity of ZnO thin films were investigated. The as-coated films were preheated at 300 °C, and then annealed at 500 °C in air ambiance. X-ray diffraction results showed all polycrystalline Zn_1 − xTi_xO thin films with preferred orientation along the (002) plane. Ti incorporated within the ZnO thin films not only decreased surface roughness but also increased optical transmittance and electrical resistivity. In the present study, the Zn_0.88Ti_0.12O film exhibited the best properties, namely an average transmittance of 91.0% (an increase of ~ 12% over the pure ZnO film) and an RMS roughness value of 1.04 nm.     

Thin film preparation and characterization of wide band gap Cu3TaQ4 (Q = S or Se) p-type semiconductors

The structural, optical, and electronic properties of thin films of a family of wide band gap (E_g > 2.3 eV) p-type semiconductors Cu₃TaQ₄ (Q = S or Se) are presented. Thin films prepared by pulsed laser deposition of ceramic Cu₃TaQ₄ targets and ex-situ annealing of the as-deposited films in chalcogenide vapor exhibit mixed polycrystalline/[100]-directed growth on amorphous SiO₂ substrates and strong (100) preferential orientation on single-crystal yttria-stabilized zirconia substrates. Cu₃TaS₄ (E_g = 2.70 eV) thin films are transparent over the entire visible spectrum while Cu₃TaSe₄ (E_g = 2.35 eV) thin films show some absorption in the blue. Thin film solid solutions of Cu₃TaSe_4 − xS_x and Cu₃TaSe_4 − xTe_x can be prepared by annealing Cu₃TaSe₄ films in a mixed chalcogenide vapor. Powders and thin films of Cu₃TaS₄ exhibit visible photoluminescence when illuminated by UV light.     

Rietveld refinement of the semiconducting system Bi2−xFexTe3 from X-ray powder diffraction

The semiconducting system Bi_2−xFe_xTe₃ (x = 0.0, 0.02, 0.04 and 0.08) was synthesized at 1000 °C for 30 h. The scanning electron microscope (SEM) image reveals the tendency of the Bi_2−xFe_xTe₃ system to form a sheet structure with more pronounced alignment and to enhance the formation of some microstructure tubes. The structure of the system under study was refined on the basis of X-ray powder diffraction data using the Rietveld method. The analysis revealed the complete miscibility of Fe in the Bi₂Te₃ matrix and hence the formation of single phase. The system crystallizes in the space group R-3m [1 6 6]. The lattice parameters and the unit cell size slightly change by the incorporation of Fe. The refinement of instrumental and structural parameters led to reliable values for the R_B, R_F and Chi².     

Effect of tellurium addition on the optical and physical properties of germanium selenide glassy semiconductors

Thin films of the glasses Ge₁₀ Se_90−x Te_x (0 ≤ x ≥ 40) have been prepared by melt quenching technique; thin films were evaporated at a pressure of ≈10⁻⁴ Pa. The optical absorption behavior of these thin films was studied from the reflection and transmission spectrum in the spectral range 200-1200 nm. The optical constants i.e optical band gap (E_opt), absorption coefficient, refractive index (n) are calculated. The optical band gap has been estimated using Tauc extrapolation and found to decrease with Te content. The Dispersion of refractive index has been studied in terms of Wemple - Di Domenico model. The value of static refraction index has been found to increase with Te content. The distribution of the possible chemical bonds has been calculated. The obtained results were correlated with the character of the chemical bond for the prepared compositions through a study of parameters such as average heat of atomization (Hs), the cohesive energies of the bonds (CE), The mean bond energy <E> and average coordination number (m).     

Properties of transparent conducting oxides formed from CdO alloyed with In2O3

The structure, optical and electrical properties of transparent conducting oxide films depend greatly on the methods of preparation, heat treatment, type and level of dopant. Thin films of (CdO)_1−x(In₂O₃)_x have been grown by electron beam evaporation technique for different concentrations of In₂O₃ (x = 0, 0.05, 0.1, 0.15 and 0.2). Increase of doping led to increased carrier concentration as derived from optical data and hence to increased electrical conductivity, which degraded the transparency of the films. An improvement of the electrical and optical properties of Cadmium indium oxide (CdIn₂O₄) has been achieved by post-deposition annealing. A resistivity value of 7 × 10^− 5 Ω cm and transmittance of 92% in the near infrared region and 82% in the visible region have been obtained after annealing at 300 °C for 90 min in air.     

Microstructure and thermoelectric properties of Sn-doped Bi2Te2.7Se0.3 thin films deposited by flash evaporation method

(Bi_1 − xSn_x)₂Te_2.7Se_0.3 thermoelectric thin films with thickness of 800 nm have been deposited on glass substrates by flash evaporation method at 473 K. The structures, morphology of the thin films were analyzed by X-ray diffraction and field emission scanning electron microscopy respectively. Effects of Sn-doping concentration on thermoelectric properties of the annealed thin films were investigated by room-temperature measurement of Seebeck coefficient and electrical resistivity. The thermoelectric power factor was enhanced to 12.8 μW/cmK² (x = 0.003). From x = 0.004 to 0.01 Sn doping concentration, the Seebeck coefficients are positive and show p-type conduction. The Seebeck coefficient and electrical resistivity gradually decrease with increasing Sn doping concentration.     

Effect of the substrate on the electrodeposition of Bi2Te3−ySey thin films

The potentiostatic electrodeposition of n-type Bi₂Te_3−ySe_y thermoelectric films onto stainless steel and gold substrates from nitric acid aqueous solutions has been carried out at room temperature. The cathodic process during the electrodeposition of Bi₂Te_3−ySe_y films was investigated by cyclic voltammetric experiments. The structure and surface morphology of Bi₂Te_3−ySe_y films deposited on both substrates were characterized by X-ray diffraction (XRD) and environment scanning electron microscopy (ESEM) coupled with energy dispersive spectroscopy (EDS). Electrical and thermoelectric properties of as-deposited films were also measured at room temperature. The results show that the reduction process under the same depositing conditions on gold and stainless steel substrates is very different. On gold substrates, H₂SeO₃ in the electrolyte is firstly reduced to elemental Se, and then the deposited Se reacts with HTeO₂⁺ and Bi³⁺ to form Bi₂Te_3−ySe_y alloy. On stainless steel substrates, HTeO₂⁺ in the electrolyte is firstly replaced by elemental Fe to produce elemental Te, and subsequently the generated Te reacts with H₂SeO₃ and Bi³⁺ to form Bi₂Te_3−ySe_y alloy. Analysis of ESEM show that the surface morphology of the films electrodeposited on gold substrates is more compact than that on stainless steel substrates. The XRD patterns indicate that the films electrodeposited on both substrates exhibit preferential orientation along (1 1 0) plane, but the relative peak intensity of (0 1 5) and (2 0 5) planes on stainless steel substrates is stronger than that on gold substrates. The Seebeck coefficient and electrical resistivity of the films deposited on stainless steel substrates are higher than that on gold substrates.     

Electrical and optical investigations on Pb1 − 3x/2LaxZr0.2Ti0.8O3 thin films obtained by radiofrequency assisted pulsed laser deposition

Thin films of ferroelectric relaxor Pb_1 − 3x/2La_xZr_0.2Ti_0.8O₃, x = 0.22 have been integrated in an oxidic heterostructure for electro-optical investigations. The quadratic electro-optic behavior and optical properties have been studied by means of variable angle spectroscopic ellipsometry method in reflection mode. Birefringence values up to δΔ = 0.17° have been obtained for quadratic compositions at λ = 540 nm and 65° angle of incidence. Structural, chemical and morphologic properties of Pb_1-3x/2La_xZr_0.2Ti_0.8O₃ (x = 0.22) thin films have been investigated by x-ray diffraction and atomic force microscopy techniques. The dielectric and ferroelectric behavior has been investigated using dielectric spectroscopy and a ferroelectric test system.     

Influence of laser-irradiation on the optical constants Se75S25 − xCdx thin films

Amorphous thin films of glassy alloys of Se₇₅S_25 − xCd_x (x = 2, 4 and 6) were prepared by thermal evaporation onto chemically cleaned glass substrates. Optical absorption and reflection measurements were carried out on as-deposited and laser-irradiated thin films in the wavelength region of 500-1000 nm. Analysis of the optical absorption data shows that the rule of no-direct transitions predominates. The laser-irradiated Se₇₅S_25 − xCd_x films showed an increase in the optical band gap and absorption coefficient with increasing the time of laser-irradiation. The results are interpreted in terms of the change in concentration of localized states due to the shift in Fermi level. The value of refractive index increases decreases with increasing photon energy and also by increasing the time of laser-irradiation. With the large absorption coefficient and change in the optical band gap and refractive index by the influence of laser-irradiation, these materials may be suitable for optical disc application.