Ag掺杂BiVO4光催化剂的制备及其性能

以硫化钠为模板剂,利用回流合成法制备Ag掺杂型光催化剂Ag/BiVO4;采用SEM、XRD、XPS、UVVis DRS对产物结构进行表征;以C.I.活性蓝19(RB-19)为降解物,研究其光催化性能和降解机理。结果表明:Ag/BiVO4较相同方法制备的BiVO4的光催化性能有较大的提升,在可见光条件下照射1 h,对25 mg/L的C.I.活性蓝RB-19的降解率即可达到86%。     

新型硅镁胶（MgO·2.4SiO2）对亚甲基蓝的吸附性能

文章合成出了一种新型硅镁胶(MgO·2.4SiO2)吸附材料并对其进行了比表面积和孔径分析,其比表面积和平均孔径分别为708.21 m2/g和7.59 nm。吸附实验结果表明:此种硅镁胶对亚甲基蓝有很强的吸附能力,25℃时,最大吸附量可达1 044.68 mg/g,远大于其他吸附剂对亚甲基蓝的吸附量。吸附过程符合Langmuir等温吸附方程和伪二级动力学方程。     

玉米芯生物炭对水中活性艳蓝的吸附特性

以玉米芯为原料制备生物炭,采用SEM及比表面积分析仪对其表面形貌及孔结构进行了表征,通过批次吸附试验,研究其对水中活性艳蓝的吸附行为。结果表明:玉米芯生物炭对活性艳蓝的吸附在120 min达到平衡,吸附过程符合准二级动力学方程;Langmuir吸附模型能够很好的模拟吸附等温线,最大饱和吸附量为80.01 mg/g。吸附热力学结果显示:玉米芯生物炭对活性艳蓝的吸附是自发的,升高温度有利于吸附。     

松子壳基活性炭对印染废水中活性艳蓝X-BR的吸附研究北大核心

用磷酸浸渍松子壳粉末制备活性炭,探究了该活性炭对活性艳蓝X-BR的吸附性能。结果表明,松子壳基活性炭的吸附能力比市售活性炭强,松子壳基活性炭最佳吸附条件:pH 2～5,25℃,60 min,松子壳基活性炭用量0.15 g,活性艳蓝X-BR初始质量浓度300 mg/L,在此条件下吸附率和吸附量分别为97.98%和196.46 mg/g;松子壳基活性炭对活性艳蓝X-BR的吸附符合Temkin等温模型,吸附过程符合准二级动力学方程。     

基于衰减全反射LED光谱的g-C3N4对亚甲基蓝表面的吸附

以SiO₂光导纤维为载体,通过溶胶-凝胶法将g-C₃N₄负载在SiO2光导纤维表面形成一层均匀的薄膜,采用X射线衍射(XRD)、红外光谱(FT-IR)、扫描电镜(SEM)、瞬态荧光光谱(PL)、荧光电镜(LSCM)、Zeta电位等表征技术对样品进行表征。结果表明：g-C₃N₄均匀分布在SiO₂光导纤维表面,吸附亚甲基蓝分子后Zeta电位由-45.35 mV升高到-28.72 mV;FT-IR光谱中700 cm^-1处的吸收峰移动到667 cm^-1处,600 cm^-1处的吸收峰消失;PL光谱典型发射峰明显下降,这都说明了g-C₃N₄对亚甲基蓝分子有较好的吸附能力。利用SiO₂光导纤维对光全反射的特点并借助衰减全反射光谱原理,以红光LED为光源,光电倍增管为检测器,研究了g-C₃N₄对亚甲...     

钼酸铵改性膨润土的制备及其对碱性蓝染料的吸附

针对印染行业废水的污染现状,以钙基膨润土为原料,钼酸铵作为改性剂,制得一种新型水处理剂钼酸铵改性土,对碱性蓝染料印染废水进行处理。经过试验研究,确定了制备的最佳条件：膨润土悬浊液配比为1∶15、钼酸铵溶液质量分数为0.2%、浸泡时间为5min、加热时间为10min。由于钼酸铵聚合体的引入改变了膨润土在水中的分散状态,增强了其对污染物的吸附和离子交换能力。处理后印染废水的脱色率可达96.53%。在此基础上通过建立等温吸附曲线,确定改性膨润土等温吸附线为典型的L-型,属于表面配位吸附。     

微孔淀粉对次甲基蓝的吸附热力学与动力学研究

研究了微孔淀粉对次甲基蓝的吸附效果,考察了温度、pH、吸附时间等因素对吸附的影响,以及微孔淀粉吸附次甲基蓝的热力学及动力学特性。结果表明,在30℃、pH为5.0时,吸附1h后吸附率最佳。微孔淀粉的吸附符合Freundich等温方程,焓变ΔHθ=-44.4026kJ/mol,熵变ΔSθ=-0.1239kJ/mol·K,反应吉布斯自由能ΔGθ随温度升高向负方向增加。热力学参数表明吸附过程为放热和自发的。      

角蛋白/酚磺酸缩合物复合材料对亚甲基蓝的吸附研究

在皮革的生产加工过程中,角蛋白未能得到充分利用便被处置,造成了一定的资源浪费.通过溶液共混法制备了角蛋白/酚磺酸缩合物复合材料,并考察其对亚甲基蓝的吸附性能.研究结果表明:复合材料对亚甲基蓝的吸附量随pH值的上升而上升,对400 mg/L的亚甲基蓝最佳吸附条件是pH值为10,复合材料使用量为2.0 g/L,吸附温度50...     

改善膨润土对松香酸的吸附性能探索

将3种产地不同的膨润土进行了钠化改型及有机改性,形成钠基膨润土和有机物复合膨润土,研究了不同质地及不同改性方式膨润土对松香酸的吸附能力.     

提高膨润土吸附性能的研究

用制备的聚合物对膨润土进行改性加工,使无机膨润土与有机物结合.比较了使用聚合物、膨润土、聚合物改性膨润土以及聚合物与膨润土简单混合等几种物质对松香酸的吸附作用.结果表明,与聚合物结合能够提高膨润土吸附松香酸的能力.     

还原氧化石墨烯/粘胶基钒酸铋光催化材料的制备及其性能

针对钒酸铋(BiVO₄)光催化效率低、难回收的缺点,利用硅烷偶联剂KH-560和氧化石墨烯(GO)依次对粘胶非织造布改性,再利用搅拌水热法在其表面生长BiVO₄制备还原氧化石墨烯(RGO)/粘胶基BiVO₄光催化材料。采用扫描电子显微镜、X射线衍射、X射线光电子能谱和紫外-可见吸收光谱对材料进行了表征,并研究了RGO/粘胶基BiVO₄材料的光催化活性、重复使用性能和光催化机制。结果表明:BiVO₄成功负载在RGO/粘胶非织造布表面,得到了RGO/粘胶基BiVO₄光催化材料;在1 kW氙灯照射下,90 min内对活性黑5脱色率达到95%以上,重复5次后仍达到92%以上;自由基捕捉实验表明,光生空穴、超氧自由基和羟基自由基参与了光化学反应,其中羟基自由基的作用最大。     

聚氨酯泡沫固定化生物体系对活性蓝4的吸附脱色

为构建长效作用的生物脱色体系,采用聚氨酯泡沫(PUF)材料对生物吸附剂黄曲霉菌Aspergillus flavus A5p1进行固定化,以蒽醌染料活性蓝4(RB4)为模型底物,开展了生物吸附剂固定化前后的吸附动力学、不同RB4质量浓度和NaCl质量浓度对脱色的影响、重复使用脱色等实验的对比研究。结果表明：菌株经过固定化之后显著加快了对染料RB4的脱色,20 min时对200 mg/L染料RB4的吸附率达到77.8%,而未固定化的游离细胞90 min的吸附率为62.8%,脱色过程可采用颗粒内扩散动力学模型来描述;PUF-固定化细胞体系对2 000 mg/L染料RB4的吸附量约是游离细胞体系的2.5倍,并且能耐受NaCl质量浓度为50 g/L的高盐条件进行脱色;PUF-固定化细胞体系重复使用7次仍能保持89%的脱色率,而游离细胞体系则下降至74.3%,该PUF-固定化细胞体系展示出对提高RB4生物脱色的有效性及可靠性。     

Agave sisalana,a biosorbent for the adsorption of Reactive Red 120 from aqueous solution

The textile industry is one of the largest producers of dye effluent. Treatment of these effluents has to be cost effective hence a number of precursors have been studied as a viable alternative adsorbent. Sisal fibre was converted to activated carbon by chemical methods. Sisal fibre was activated with different activating agents such as H₃PO₄, HCl, HNO₃, NaOH and KOH. The adsorption of Reactive Red 120 (RR 120) dye onto sisal fibre activated carbon (SFAC) from aqueous solution was investigated. Adsorption experiments were carried out at different dye concentrations, initial solution pH and carbon dosage. Batch adsorption studies were carried out using activated carbon produced using phosphoric acid yielded better carbon as it good results in terms of Methylene Blue number and Iodine number. These carbons were used to study the batch adsorption studies. Methylene Blue number and Iodine number of SFAC were found to be 240 mg/g and 855 mg/g, respectively. The BET surface area of the carbon was 885 m²/g. The batch experiments adsorption isotherm studies fitted well to Langmuir isotherm and the adsorption capacity was found to be 110 mg/g. Adsorption kinetics data were tested using pseudo-first-order and pseudo-second-order models. Kinetic studies showed that the adsorption data followed a pseudo-second-order reaction.     

新型可见光催化剂BiVO4在环境治理中的研究进展

阐述了新型可见光催化剂BiVO4的光催化机理以及提高BiVO4光催化活性的方法(表面金属沉积、复合半导体、表面敏化、金属离子掺杂、催化剂固定化),介绍了BiVO4光催化剂在污水处理和室内环境治理中的应用情况,分析了目前存在的问题并提出了研究方向.     

改性棕榈纤维活性炭对活性染料的吸附性能

为了探究棕榈纤维在处理印染废水中的应用,将MgO通过共沉淀-灼烧氧化法负载于棕榈纤维活性炭,利用FE-SEM、FTIR、真密度测定法表明棕榈纤维活性炭孔道及表面存在MgO。通过静态吸附实验,研究了棕榈纤维活性炭改性前后对于活性艳红X-3B染料的吸附性能,考察了不同染料初始浓度下MgO改性棕榈纤维活性炭（MgO/PAC）对染料的吸附动力学,以及在不同pH下对染料的吸附性能。实验结果表明：MgO改性可显著提高吸附性;经镁与碳以摩尔比2.5:1改性的棕榈活性炭对染料活性艳红X-3B的吸附量提高约8倍;MgO改性棕榈纤维活性炭对活性艳红X-3B的吸附符合伪二级动力学模型,颗粒内扩散不是吸附过程的唯一速率控制步骤,整个吸附过程是由多种动力学吸附机理共同作用的结果。     

表面活性剂对C.I.活性蓝221的增溶作用

分别以NaCl、AEO9、AEO3、JFC、AES和L-64为添加剂,研究了它们对C.I.活性蓝221在25 ℃水中的溶解度的影响。实验结果表明,NaCl的加入会大幅降低染料的溶解度;而五种表面活性剂对染料都有增溶作用,增溶效果依次为：JFC（L-64）>AEO9>AEO3>AES。当JFC或L-64用量为80 g/L时,可使C.I.活性蓝221的溶解度由空白时的100 g/L提高至190 g/L。以JFC,L-64,AEO9为混合助溶剂时,当溶液中含有15 g/L JFC, 20 g/L L-64和5 g/L AEO9时,C.I.活性蓝221的溶解度可以提升至200 g/L,染料溶液稳定时间达20 h以上。     

大孔树脂对甘蔗糖蜜色素的吸附性能和动力学

探究了大孔树脂对糖蜜色素的吸附性能及动力学。本文采用静态法考察了5种树脂对甘蔗糖蜜的脱色及再生特性。结果表明,大孔离子交换树脂D750具有最高的脱色性能和较好的再生性能。单因素实验结果表明,D750对100 m L IU560约13500,锤度约12°Bx的糖浆脱色的最优工艺条件为树脂用量10 g、时间6 h、温度60℃和糖蜜p H7.04,此时脱色率为86.90%。进一步地吸附性能和动力学研究结果表明,D750对甘蔗糖蜜脱色过程符合Freundlich方程,脱色过程的吸附动力学符合颗粒扩散模型,扩散速率常数为0.09 min-1。      

膨润土对饲料中营养成分的吸附

本实验研究了膨润土对赖氨酸、蛋氨酸、维生素B2的吸附特点。结果表明，膨润土对赖氨酸、维生素B2在酸性条件下的吸附能力比在碱性条件下高；对蛋氨酸吸附性弱，甚至表现为负吸附。膨润土对赖氨酸吸附量大，而吸附解吸率低，配合饲料时应注意赖氨酸的补充平衡。     

BiVO4/膨润土负载型光催化剂的制备及其性能

采用溶液燃烧法制备了不同煅烧温度的BiVO4/膨润土负载型可见光催化剂,并以C.I.活性蓝19为目标降解物,研究其催化性能.采用X射线衍射(XRD)、场发射扫描电镜(FE-SEM)、比表面积(BET)、紫外-可见漫反射光谱(UV-vis DRS)等测试手段,对光催化剂的晶型、表面形貌、颗粒大小、光吸收范围等进行了表征.结果表明,300℃煅烧的BiV04/膨润土为单斜晶型,晶粒尺寸约为30nm,在可见光400～500 nm处有强吸收;其对活性蓝19的光催化性能较好,2h光照后的脱色率可达93.9％.