广角布的拉伸性能研究

研究广角布的拉伸性能。以相同经纬纱和经纬密的广角布和普通平纹织物为例,测试了广角布经向、纬向、经纬向交织角60°和120°对角线方向的拉伸性能,并与普通平纹织物的经向、纬向和经纬向交织角90°对角线方向的拉伸性能进行了对比分析。结果表明:与普通平纹织物相比,广角布在受到沿经纱方向的载荷时,织物的断裂强力大而断裂伸长率小;在受到沿纬纱方向的载荷时,广角布的断裂强力和断裂伸长率均较大。认为:广角布的力学性能优于普通平纹织物,应用前景广阔。     

全棉薄织物的高强力保留率免烫整理

全棉薄织物的基础强力绝对值低,单独使用免烫树脂对其进行抗皱整理会降低织物的强力,严重影响服用性能.将聚氨酯与免烫树脂复配,用于全棉薄织物抗皱整理.试验得到全棉薄织物免烫整理的优化工艺条件:免烫树脂整理剂LT质量浓度80 g/L,水溶性聚氨酯交联剂PU95质量浓度7.5 g/L,水溶性聚氨酯交联剂PU2F质量浓度20 g/L;焙烘温度140℃,焙烘时间2 min.整理后的织物缓弹折皱回复角190°,经纬向断裂强力保留率分别为64.46%和79.22%,经纬向撕破强力保留率分别为96.45%和91.98%.     

竹浆棉混纺织物性能研究

研究竹浆纤维含量对混纺织物断裂强力、断裂伸长率、撕破强力、耐磨性的影响规律.经过测试相同织物组织结构、相同经纬纱线密度、相同经密、不同纬密情况下不同混纺比织物的各项性能,认为当织物经纬密保持不变,随着纬纱中竹浆纤维含量的减少,织物的纬向断裂强力增加,而经向断裂强力减小;织物纬向断裂伸长率呈下降趋势,而经向断裂伸长率先下降而后上升再下降;织物的纬向撕破强力先下降而后上升,而经向撕破强力先上升后下降;织物的耐磨性呈现先增加再减小而后再增加的趋势.     

亚麻机织物增强热塑性复合材料的性能

利用聚丙烯纤维对亚麻纱线进行包缠,使用该纱线织造3种经纱密度相同,纬纱密度不同的平纹织物。利用热压机将5层织物复合,分别制成3种复合材料板材。对板材的拉伸性能进行测试和分析。测试结果表明:织物中纱线的密度对层合板的强力和断裂伸长率有重要影响;在条件一定的情况下,随着织物纬纱密度的减小,材料沿经向的拉伸强度呈上升的趋势,而经向断裂伸长率呈下降趋势。     

石墨烯黏胶纤维机织物的功能改性研究

制备同规格的普通黏胶纤维机织物、石墨烯黏胶纤维机织物及不同不锈钢丝质量分数的石墨烯黏胶纤维/不锈钢丝机织物,对比它们的导电、防电磁辐射、防紫外线、抗静电、力学(拉伸、弯曲、耐磨)及透气等性能。结果表明:普通黏胶纤维经石墨烯改进后,所制成的石墨烯黏胶纤维机织物的导电、防电磁辐射、防紫外线、抗静电、力学(拉伸、弯曲、耐磨)等性能都有所改善,其中防紫外线与耐磨性能提高显著,透气性能下降明显;石墨烯黏胶纤维/不锈钢丝机织物的导电、防电磁辐射、防紫外线和抗静电、经向拉伸断裂强力、纬向抗弯刚度、透气性能都优于石墨烯黏胶纤维机织物,纬向拉伸断裂强力、经纬向拉伸断裂伸长率、经向抗弯刚度及耐磨性能不及石墨烯黏胶纤维机织物;随着不锈钢丝质量分数在7.0%~20.0%范围内的增加,石墨烯黏胶纤维/不锈钢丝机织物的导电、防紫外线、抗静电、经向拉伸断裂强力、纬向抗弯刚度及透气性能增强,纬向拉伸断裂强力、经纬向拉伸断裂伸长率、经向抗弯刚度、耐磨性能减小,不锈钢丝质量分数变化对防电磁辐射性能影响较小。当不锈钢丝质量分数为7.0%时,石墨烯黏胶纤维/不锈钢丝机织物的综合性能最佳。     

竹浆纤维含量及纬密对棉/竹浆纤维交织物力学性能的影响

对15种不同规格的棉与棉/竹浆纤维交织物面料的拉伸断裂强度、断裂伸长率、撕破强度、磨损牢度等力学性能进行测试比较,研究竹浆纤维含量及纬密对其力学性能的影响。结果表明：随着竹浆纤维含量增加,织物的经纬向拉伸断裂强力之和下降,纬向断裂伸长率上升,经向断裂伸长率先上升而后下降再上升;纬向撕破强力先下降而后上升,经向撕破强力变化不大;织物的质量减少率快速增加,织物磨损牢度变差,竹浆纤维含量为30%时,织物的磨损牢度最好;竹浆纤维含量达到70%时,交织物的断裂伸长率、撕破强力、摩损牢度均为最低,在实际生产应用中应尽量避免选用。当经密保持不变,纬密增加时,织物的断裂强力增加,断裂伸长率逐渐增大,撕破强力减小,耐磨性能提高。     

棉织物等离子体/柠檬酸的抗皱整理初探

采用低温等离子体/柠檬酸处理方法,对棉织物进行抗皱整理.研究了等离子体处理在棉织物抗皱整理中的加工顺序对棉织物性能的影响.以整理后织物的拉伸断裂强力、强力保留率、折皱回复角和白度等指标进行测试比较,说明该方法能在一定程度上提高整理织物的拉伸断裂强力和强力保留率,得出低温等离子体/柠檬酸整理织物的最佳工序为:浸轧整理液→烘干→焙烘→等离子体处理→水洗→晾干→烘干.     

蚕丝/PHA长丝织物的性能研究

为了研究桑蚕丝与聚羟基脂肪酸酯(PHA)长丝交织物的性能,选用生丝作经线,PHA长丝或PHA长丝与桑蚕丝生丝交替作纬线,制成9种不同规格交织物坯布,进一步采用酶精练法脱胶制成成品,测试织物力学性能、抗皱性、起毛起球性、热学性能和通透性等服用性能。试验结果表明:蚕丝并捻后与PHA交织,织物的断裂强力、透气性、接触暖感和导热性均优于以单根蚕丝作经的织物,但抗皱性、透湿性和保温性下降。在织物纬向加入聚酯纤维,织物纬向断裂强力、断裂伸长、抗皱性、接触暖感和透气性增强,抗起毛起球性、导热性、保温性和透湿性下降。随着织物盖覆紧度的增加,织物拉伸性能、接触暖感和导热性均得到改善。总体而言,蚕丝/PHA织物经向拉伸断裂性能、抗皱性、保温性、通透性:斜纹平纹,导热性和接触冷感:平纹斜纹。     

气密性涂层织物的拉伸性能探讨

测试分析了4种涂层织物涂层前后拉伸性能的变化,结果表明,织物经涂层后其拉伸断裂强度和断裂伸长率都有不同程度的增长,且涂层对织物经、纬向拉伸性能的影响不同。对试验4种涂层织物而言,涂层增重率对织物经纬向拉伸性能的影响不同;在相似增重率条件下,涤纶基布涂层织物的经向拉伸变化率较锦／棉基布涂层织物的显著。     

涤纶机织物的吸湿快干性能测试

利用万用表测试9种织物经向、纬向和斜向织物润湿后干燥过程中电阻随时间变化的值.结果证明,织物电阻与时间成线性关系.织物经纬密度和方向对其吸湿件能影响较大,-般织物密度越小,吸湿性能越好;对同-织物,经向吸湿性能最好,斜向次之,纬向最差.织物干燥性能受织物经纬密度、组织和方向影响,-般缎纹干燥速率最好,斜纹次之,平纹最差;织物密度越小,织物干燥就越快;对同-织物而言,纬向干燥速率最大,斜向次之,经向最差.     

蜂巢棉织物力学性能的测试与分析

为使蜂巢组织类织物在增强复合材料中得到更合理的应用,采用相同的原料和经纬密度织制不同蜂巢类组织织物,并对织物的拉伸强度、撕裂强度和顶破强度进行测试,分析不同蜂巢组织对其织物力学性能的影响。结果表明:在织物原料和经纬密度相同的情况下,不同蜂巢组织的织物其力学性能有明显的不同;纱线的交织次数越多,蜂窝越小,织物的断裂强力越大;而织物断裂伸长率、撕裂强力和顶破强力随着蜂窝尺寸的变小,先增加后减少。     

组织结构对UHMWPE短纤纱织物防刺性能的影响

UHMWPE短纤纱具有优秀的抗切割性与较好的树脂浸润性,非常适用于制作防刺材料。文章试织了12种不同织物规格的试样,进行准静态穿刺实验,探究5种因素(组织、紧度、纱线线密度、经纬密和面密度)对织物防刺性能的影响,并比较不同穿刺角度下织物防刺性能的差异。结果表明:与方平织物与接结双层织物相比,平纹织物的防刺性能最好;同种经纬密或同紧度下,粗特纱织制的平纹织物防刺性能好;随着经密增加,紧度增加,面密度增加,防刺性能逐渐增加,但织物过于紧密时,防刺性能反而降低;平纹织物的穿刺性能具有各向异性,经纬向的防刺性能优于45°方向。     

Analysis and tensile characterization of flocked fabric after rubbing

In this study, the tensile properties of flocked fabric after rubbing were studied. A statistical method was used to analyze the generated data. For this purpose, woven fabric was used as a substrate and an acrylic adhesive was applied on this substrate to hold the polyamide flock fibers forming flocked fabrics. A rubbing test was applied in dry and wet forms to the flocked fabrics before and after washing. The tensile properties of these rubbed flocked fabrics were determined. The regression models developed in this study explain the relationship between rubbing and the tensile strength of the flocked fabrics. The results from this experiment could be used in the development of flocked fabric as seat covers for the automotive industry. The warp tensile strength of a flocked fabric is generally higher than its weft tensile strength due to its higher substrate density in the warp direction. Also, the weft tensile elongation of a flocked fabric is generally higher than its warp tensile elongation due to its higher crimp ratio in the weft direction. When the stroke number increases, the warp and weft directional tensile strength and the elongation of a flocked fabric generally decrease. In addition, the stroke number of a flocked fabric before and after washing is low in its wet form compared to the dry form. The main reason is that the acrylic adhesive has poor wet properties. Results from the regression models were compared with the measured values. It was concluded that the method used in this study could be a viable and reliable tool.     

纯棉纱线合股数对织物性能的影响

为研究纯棉纱线合股数对织物力学性能和保形性的影响,采用线密度相同的单纱、双股线、3股线、4股线4种股线类型,以适当的经、纬密分别织制成平纹、斜纹、缎纹组织的织物。对织物的拉伸性能、撕裂强力、拉伸弹性、折皱回复性、悬垂性、弯曲性进行测试与分析。结果表明:3股线织物的断裂强力和撕裂强力较大,4股线织物的断裂伸长率较大,双股线织物的拉伸弹性回复率较大;平纹织物仅有双股线织物的折皱回复性优于单股线织物,斜纹和缎纹织物的折皱回复性随合股数的增加均变差;双股线平纹织物悬垂性相对较好,但均没有斜纹和缎纹织物的悬垂性好;单纱织物的弯曲性能比股线织物好。     

广角机织物的织造工艺及其偏轴拉伸力学性能

为开发适用于不同应用领域的产业用纺织品,在对原有普通剑杆织机改进的基础上,探讨了广角机织物的织造工艺,织造了经纱和纬纱夹角为120°的涤/棉平纹广角机织物。借助万能材料试验机研究了普通涤/棉正交织物和广角机织物不同偏轴方向的拉伸力学性能,获得了其应力-应变曲线和特征值变化规律,并分析了其变形及失效模式。结果表明:对于普通正交机织物和广角机织物,其拉伸断裂强力均呈现出明显的极轴特性;在断裂强力相同的情况下,与普通正交机织物相比,广角机织物纬向的断裂伸长率提高了30%,经、纬向弹性模量分别提高了42%和79%,展现出优异的强度和变形特征。     

组织结构对针织物电磁屏蔽效能的影响

设计了几种代表性织物组织结构的不锈钢纤维混纺针织物,研究了织物组织结构对针织物电磁屏蔽效能的影响。织物组织结构选择充满系数较高的双罗纹组织、打鸡双面组织、添纱衬垫组织、衬纬组织和绕经组织,以降低织物厚度、密度、孔隙等因素对织物电磁屏蔽效能的影响。对所有织物进行了电磁屏蔽效能测试,结果显示:双罗纹织物、双面织物、添纱衬垫织物、衬纬织物的电磁屏蔽效能都很不理想,且远远低于含不锈钢纤维机织平纹布,但是绕经织物的电磁屏蔽效能要比其他组织的针织物的屏蔽效能高得多,基本能达到国标上对屏蔽服的屏蔽效能要求。绕经织物与其他几种针织物最大的不同就是在纵向多了一些连续的含不锈钢纤维的混纺纱。说明针织物组织结构是影响电磁屏蔽效能的关键因素,可通过在织物纵横向形成纵横交错的导通的金属网栅的方式来改善不锈钢纤维混纺针织物的屏蔽效能。     

蜂窝状三维织物及其加强复合材料的研制

以涤纶网络丝为经纱,涤棉混纺纱为纬纱,平纹组织为基础组织和接结组织,纱罗组织为边组织,在剑杆织机上织造多层蜂窝状三维织物,用手糊法对其进行复合,测试其性能。结果表明,用树脂对蜂窝状三维织物进行复合可得到性能明显加强的复合材料。     

经编针织物双向拉伸性能研究

测试了5种经编针织物的双向拉伸性能,考察了拉伸方向、拉伸速率及织物结构对拉伸性能的影响。当织物结构相同且一个方向固定、另一个方向拉伸时,横向拉伸的断裂强力与断裂伸长大于纵向拉伸的。随着拉伸速率提高,织物的断裂强力与断裂伸长先增大后减小。当织物组织结构与参数相近时,双向拉伸的各项指标相差不大。单梳经绒织物的断裂伸长比经绒平、经平绒、菱形及四角网孔4种双梳织物的大。     

影响网格状稀疏织物结构稳定性的因素分析

探讨影响网格状稀疏织物结构稳定性的因素。通过测试不同组织、不同纱线号数和不同经纬密的多种机织网格状稀疏织物的滑移阻力,并反复对比分析了组织、纱线号数、摩擦因数和经纬密对网格状稀疏织物滑移阻力的影响。结果表明:平纹组织织物的滑移阻力明显大于方平组织织物;在一定范围内,织物的滑移阻力随纱线号数和摩擦因数的增大而增大,随经纬密度的增大而增大。认为网格状稀疏织物的滑移阻力测试分析结果为建立织物滑移阻力预测模型提供了依据。