快干型聚四氟乙烯用复合胶黏剂的研制

将环氧树脂胶黏剂作为组分A、有机硅树脂胶黏剂作为组分B,两种组分复配后得到一种快干型复合胶黏剂,将其应用于聚四氟乙烯材质的黏结。对影响复合胶黏剂反应时间、力学性能、固化速率的因素进行探讨,并对该复合胶黏剂进行红外表征。结果表明:与单一型环氧树脂胶黏剂相比,复合胶黏剂的力学性能明显提高,固化速率也有一定程度提升。     

高性能环氧树脂胶黏剂研究概况

简要介绍了环氧树脂胶黏剂的分类(根据固化温度的高低、耐热性、用途、固化剂的类型不同等)、组分和固化机理。并对国内外几种高性能环氧树脂胶黏剂的研究成果进行了综述,如:耐热性环氧树脂胶黏剂、高韧性环氧树脂胶黏剂、耐湿性环氧树脂胶黏剂、室温固化环氧树脂胶黏剂及其它功能性环氧树脂胶黏剂。对其发展方向进行展望,环氧胶黏剂将向着高性能化和高功能化方向发展,开发环境友好型、低公害胶黏剂以及引进或开发新型固化剂必将成为研究的热点。     

碳纤维片材加固胶黏剂的工艺性能改进研究

碳纤维片材加固胶黏剂已广泛应用于混凝土结构加固及改造领域,但对其工艺性能的改进研究一直未能引起足够的重视。本文研究了改性胺类固化剂对环氧树脂类碳纤维片材加固胶黏剂适用期的影响,同时也对触变剂进行了探讨,并提出了判定胶黏剂浸润性的方法。采用自制的固化剂复配得到了适用于不同季节使用的冬夏配方,工艺性能良好。     

阻燃环氧树脂胶黏剂的研制

采用以KH-560硅烷偶联剂包覆三聚氰胺多聚磷酸酯（MPP）为阻燃剂,以环氧树脂E-44为基体,制备阻燃环氧树脂胶黏剂。通过对所制得胶黏剂进行剪切强度测试、热失重测试以及阻燃性能测试,研究了包覆阻燃剂对环氧树脂胶黏剂力学性能、热稳定性和阻燃性能的影响。结果表明,采用包覆处理MPP为阻燃剂制备的阻燃环氧树脂胶黏剂综合性能较好,其剪切强度为19．9MPa,氧指数为31．2。最佳配方为100份环氧树脂、30份阻燃剂、30份固化剂、温度为70℃。     

高性能环氧树脂胶黏剂的制备及应用研究进展

环氧树脂胶黏剂具有优异的附着力和力学性能,可以在各种条件下为不同类型的底材提供强大的粘接性,应用领域非常广泛.但环氧胶黏剂本身是脆性材料,由于其高度交联的结构,极易断裂,限制了其结构粘接性能.随着粘接技术的发展,胶黏剂需要适应更加严苛的环境.因此,急需高性能环氧树脂胶黏剂的研制.本文讨论了环氧树脂胶黏剂的固化机理,以及...     

新型增韧阻燃环氧树脂胶黏剂的研究

采用以聚氨酯（PU）增韧改性环氧树脂为基体,在其中添加两次包覆红磷作为阻燃剂,从而制备出一种新型增韧阻燃环氧树脂胶黏剂。通过对所制得胶黏剂进行力学性能测试、热失重测试（TG）以及阻燃性能测试,从而研究了聚氨酯和两次包覆红磷用量对改性环氧树脂胶黏剂性能的影响。结果表明,采用100份环氧树脂、30份聚酯型聚氨酯预聚体、15份阻燃剂,可制备出综合性能较好的增韧阻燃环氧树脂胶黏剂,剪切强度为23．2MPa,氧指数可达到30％。     

聚氨酯改性环氧树脂胶黏剂的研究与应用进展

简要介绍了环氧树脂胶黏剂的特性,指出聚氨酯改性环氧树脂的主要目的是提高其韧性。分别论述了几种常用的聚氨酯增韧改性环氧树脂胶黏剂的方法,包括端胺基／端羟基／端异氰酸酯基／端环氧基聚氨酯预聚体增韧改性环氧树脂,聚氨酯环氧树脂接枝共聚改性环氧树脂以及聚氨酯互穿聚合物网络增韧环氧树脂,其中详细介绍了聚氨酯互穿聚合物网络增韧环氧树脂技术。同时,对国内聚氨酯改性环氧树脂胶黏剂的主要应用进行了介绍,并指出了我国目前聚氨酯改性环氧树脂胶黏剂的不足和发展方向。     

亚胺改性环氧树脂胶黏剂的研究

采用端羧基亚胺中间体对环氧树脂进行改性,用芳香胺做固化剂,制备了亚胺改性环氧树脂胶黏剂.研究了端羧基亚胺中间体的种类及用量、固化剂种类及用量、固化条件等因素对胶黏剂性能的影响.结果表明,采用分子中含有砜基的亚胺中间体对环氧进行改性、用DDS做固化剂制得的胶黏剂的性能最好.亚胺中间体用量为60phr～70phr、固化剂用量控制在固化剂活泼-H/环氧基为0.6～0.7时,胶黏剂的综合性能较好.适合该胶黏剂的固化条件为200℃/2h 220℃/4h.     

环氧树脂在建筑胶黏剂领域中的应用

阐述了环氧树脂在建筑胶黏剂领域中的应用,包括港工混凝土潮差及水下部位修补胶、水利工程用潮湿面及水下修补胶、混凝土细裂缝灌浆补强胶、建筑结构胶黏剂等,同时对环氧树脂建筑胶黏剂的发展前景进行了展望,旨在为建筑用环氧树脂胶黏剂的应用提供技术支持。     

国内外近期有关胶黏剂文献的增注题录

07-039室温固化耐热环氧树脂胶黏剂的制备和性能研究[采用氨基聚硅氧烷和羧基终端的丁二烯-丙烯氰(CTBN)对环氧树脂进行改性,并且制备了室温固化耐热环氧树脂胶黏剂。讨论了CTBN和氨基聚硅氧烷的含量、环氧树脂的种类对胶黏剂性能的影响。当环氧树脂和CTBN、氨基聚硅氧烷反应改性,然后和F-44和E-51混合,表现出了良好的剪切强度]Liu,Pei-ran;Li,Shu-cai.Tianjin University of Science and Technology,Tianjin,Peop.Rep.China.Zhongguo Jiaonianji(2007),16(3),31-33.07-040使用各向异性导电胶黏剂粘结电子仪器组件制造电路板的…     

Dynamic mechanical properties and adhesive strengths of epoxy resins modified with liquid rubber. I. Modification with ATBN

The dynamic mechanical properties and the adhesive strengths of Epikote 828 and Epikote 828-ATBN blend systems were investigated. The ATBN blend systems were proved to be completely incompatible with the dynamic mechanical measurement and also fitted well with Takayanagi's model which was designed for completely incompatible two-phase systems. The epoxy resin had a nonreacted part when cured at room temperature. The blending of ATBN reduced the nonreacted part of the epoxy resin, and made contributions to the adhesive strengths. In the case of tensile test of crosslap specimens using aluminium as adherends, the adhesive strengths of ATBN blend systems were almost 1.5-fold of those of epoxy resin without blending of ATBN. As for wood adherends, the maximum of the adhesive strengths was found at 60°C for epoxy resin without blending of ATBN, and at 0°C for ATBN blend systems. The facts meant that there were mutual interactions between the adhesive strengths and the viscoelastic behavior of the adhesive polymers in the two-phase systems as observed in completely miscible polymer blends. There was not pronounced distinction between epoxy resins without blending of ATBN and ATBN blend system, as to the shear adhesive strengths.     

半互穿网络法增韧环氧树脂胶粘剂的研究

利用半互穿聚合物网络法(Semi-IPN)对环氧树脂胶粘剂的合成及改性作了研究。结果表明:改性胶粘剂的剪切强度达47.8MPa,增幅为44.8%,且环氧树脂(丙烯酸丁酯Semi-IPN体系的抗湿热老化性能较好,胶粘剂的力学性能没有发生很大变化。这种现象可能与增韧剂聚丙烯酸丁酯和环氧树脂之间的相容性有关。     

KH-550改性纳米SiO2对环氧胶黏剂性能的影响

制备了氨基硅烷偶联剂（KH-550）表面接枝改性纳米SiO2粒子,利用正交实验,讨论了改性剂用量、改性温度以及改性时间对活化指数的影响。并将KH-550硅烷偶联剂包覆纳米SiO2作为填料,以环氧树脂E-44为基体,制备环氧树脂胶黏剂,通过对胶黏剂进行剪切强度,扫描电镜和阻抗测试,研究了改性纳米SiO2对环氧胶黏剂粘结性能以及耐蚀性能的影响。结果表明：改性纳米SiO2填充的环氧胶黏剂的剪切强度得到提高,最大增幅达到2MPa,耐蚀性能也得到提高。     

低粘度双酚A型环氧树脂的合成制备及应用

环氧树脂是一种具有优良的物理机械性能,电绝缘性和粘接性能热固性树脂,被广泛应用于涂料、胶粘剂、复合材料、模压材料和浇铸材料等领域中。其中,双酚A型环氧树脂占到总体环氧树脂用量的90%左右,但常温下的高粘度限制了它的应用。目前,低粘度双酚A型环氧树脂的制备和研究已成为研究者们所关注的重点之一。本文着重介绍了低粘度双酚A型环氧树脂的合成方法及得到的树脂粘度性质。     

聚氨酯改性环氧树脂的研究

为提高环氧树脂的韧性和粘接强度,采用自制端异氰酸酯聚氨酯预聚体对环氧树脂进行了改性,利用傅里叶变换红外光谱(FT-IR)对聚氨酯预聚体、改性环氧树脂的结构进行了表征。采用示差扫描量热法(DSC)对改性环氧树脂的固化行为进行了分析,并测试了改性环氧的力学性能。结果表明:聚氨酯预聚体与环氧树脂发生了接枝反应,n(NCO)/n(OH)=0.75时,改性环氧树脂/双氰胺/2-甲基咪唑组成的胶膜的剥离强度(液晶显示器(LCD)玻璃与柔性印刷线路板(FPC)界面)达到15.8 N/cm,粘接力良好。     

纳米蒙脱土/环氧树脂胶粘剂最佳组分的优化选择

将有机化处理后的蒙脱土作为填料，通过插层复合的方法制备出纳米蒙脱土／环氧树脂胶粘剂，进行了拉伸强度、硬度及XRD测试，并与粉煤灰、未处理蒙脱土作填料的环氧胶粘剂进行了性能对比。，试验结果表明，当加入质量分数5％的有机蒙脱土时，环氧胶粘剂的剪切强度达到21．6MPa；X射线衍射结果表明，用该法制得的胶粘涂层内部蒙脱土片层已被剥离，属于纳米复合胶粘剂；通过对比力学性能及密度，加入有机蒙脱土的环氧树脂胶粘剂涂层综合性能要优于一般环氧树脂胶粘剂。     

环氧树脂建筑结构胶粘剂增韧改性研究

采用改性环氧树脂和添加增强填料等方法,提高胶粘剂的力学性能,增强其柔韧性。通过对比试验得出了玻璃纤维作为填充剂在胶粘剂中的合理含量,为其在粘接领域的应用提供了基础数据．     

端脂肪氨基聚醚改性环氧树脂的性能研究

用自制的一种既含聚醚柔性链段又含苯脂肪氨基刚性链段的端脂肪氨基聚醚(APPEG)作为固化剂对环氧树脂进行增韧改性。扫描电子显微镜和力学性能测试结果表明,固化剂对环氧树脂具有明显的增强、增韧效果,且改性的环氧树脂胶粘剂具有很好的填充性能,填充比高达50%。与羰基铁粉组成的涂层材料具有优异的力学性能和热稳定性能。