S355J2W+N钢焊接接头显微组织与力学性能

使用国产焊丝H08MnSiCuCrNiⅡ,利用焊接机器人对S355J2W+N钢用MAG焊的焊接方法进行了焊接,通过拉伸、硬度和金相检验试验方法对焊接接头显微组织和力学性能进行了分析研究。结果表明:焊接接头具有较好的力学强度,最大硬度值215.2HV出现在焊接热影响区。焊缝组织主要为先共析铁素体、板条铁素体及少量珠光体和粒状贝氏体,过热区主要为块状先共析铁素体、珠光体、粒状贝氏体,细晶区主要是细小的铁素体和珠光体。     

退火对BWELDY960QL焊接接头组织与性能的影响

为了研究退火处理对焊接接头显微组织与力学性能的影响,采用CO₂气体保护焊对高强调质钢BWELDY960QL进行了焊接.结果表明,BWELDY960QL钢焊接接头的焊缝区由针状铁素体加先共析铁素体及少量珠光体组成,晶粒细小且分布均匀; 退火处理使针状铁素体数量明显增加,但退火温度过高,会使铁素体组织长大,出现一定数量的魏氏铁素体; 母材与焊丝之间Cr含量存在较大的差异,退火使Cr由热影响区向焊缝迁移; 经过退火处理后,焊接接头的力学性能得到明显改善,其中经过550 ℃退火后,焊件的综合力学性能最好.     

Q345B大厚板双面双弧焊接头组织与力学性能

针对Q345B大厚板高强钢接头在机器人双面双弧焊中易出现焊不透、撞枪的问题,采用根部无预留间隙的焊接方法,通过增大焊接线能量、减小弧间距实现根部全熔透。依据《美国钢结构焊接规范》标准对接头进行力学性能试验和显微组织分析,结果表明:根部打底前焊道组织为针状铁素体和贝氏体,打底后焊道和填充焊组织为针状铁素体和少量的先共析铁素体;熔合区组织为针状铁素体和板条马氏体,粗晶区为板条束更粗大的板条马氏体。焊接接头平均抗拉强度达到536.47 MPa,焊缝强度高于母材。接头出现局部硬化,硬度最高值为281 HV,符合标准的要求。     

稀土对10SiMnNb钢显微组织的影响

冶炼低硫钢10SiMnNb 和10SiMnNbRE 钢。测定了10SiMnNbRE 钢中固溶0.035wt%RE。研究了稀土元素对先共析铁素体析出,珠光体转变,贝氏体转变和马氏体转变的影响。结果表明,固溶稀土增加了过冷奥氏体的稳定性,在相同的冷却速度下,添加稀土元素和无稀土元素比较,显微组织显然不同,先共析铁素体量减少,珠光体量增加,粒状贝氏体量增加,并细化了马氏体组织。     

07MnNiCrMoVDR钢焊缝组织与低温冲击韧性分析

采用SMAW焊接工艺焊接低合金高强度07MnNiCrMoVDR钢获得焊接接头,通过焊缝显微组织观察、冲击断口分析、焊缝低温冲击试验,研究了07MnNiCrMoVDR钢焊缝组织与低温冲击韧性。结果表明,焊缝组织由沿晶界分布的先共析铁素体、晶内的针状铁素体和粒状贝氏体构成,针状铁素体以微夹杂物为核心生长。温度为－40 ℃时,不同部位焊缝冲击吸收功随试样截取深度的增大而减小;与近表面处相比,1/2厚度处焊缝冲击吸收功损失约67%,在1/4厚度处,焊缝冲击吸收功随着温度的降低而降低;焊缝的低温冲击韧性符合要求。焊缝冲击断口的表面由凹凸不平变得比较平整,断口的微观形貌由韧窝花样变成解理河流花样。     

WELDOX 960 E高强钢焊接对比试验分析

为了研究WELDOX 960E高强钢焊接接头组织与力学性能的关系,采用MAG与SMAW法得到良好成形的焊接接头,进行了焊接裂纹试验(硬度、拉伸、弯曲、冲击)和金相显微分析对比.结果表明:两种焊接方法所得焊接接头的力学性能均较高;SMAW需提前预热,且热影响区有软化现象;二者焊接接头金相组织相似,焊缝组织为针状铁素体和粒状贝氏体;粗晶区组织粗大,为M-A组元和少量板条马氏体.     

X80管线钢焊接接头组织及性能的研究

通过硬度测试及SEM观察,分析X80管线钢焊接接头处硬度和显微组织变化规律.受焊接热循环的影响,热影响区粗晶区组织主要为粗大的粒状贝氏体和板条贝氏体,硬度较高.靠近热影响区的基体,由于M/A岛分解,硬度值减小.外焊焊缝的显微组织主要是晶内形核铁素体、粒状贝氏体和多边形铁素体.靠近外焊焊缝的内焊焊缝组织受二次热循环的影响较大,组织为粒状贝氏体和块状的铁素体.远离外焊焊缝的内焊焊缝组织受二次热循环影响较小,组织和外焊焊缝组织相差不大.内焊组织中析出物的数量远大于外焊焊缝组织,析出强化效果显著,使内焊的硬度大于外焊的硬度.     

07MnNCrMioVDR钢焊缝组织与低温冲击韧性分析

采用SMAW焊接工艺焊接低合金高强度07Mn NCr Mi o VDR钢获得焊接接头,通过焊缝显微组织观察、冲击断口分析、焊缝低温冲击试验,研究了07Mn NCr Mi o VDR钢焊缝组织与低温冲击韧性。结果表明,焊缝组织由沿晶界分布的先共析铁素体、晶内的针状铁素体和粒状贝氏体构成,针状铁素体以微夹杂物为核心生长。温度为-40℃时,不同部位焊缝冲击吸收功随试样截取深度的增大而减小;与近表面处相比,1/2厚度处焊缝冲击吸收功损失约67%,在1/4厚度处,焊缝冲击吸收功随着温度的降低而降低;焊缝的低温冲击韧性符合要求。焊缝冲击断口的表面由凹凸不平变得比较平整,断口的微观形貌由韧窝花样变成解理河流花样。     

15CrMoR钢材的焊接接头组织及其硬度分析

分别采用焊条R307和焊条A302在母材15CrMoR容器用钢上进行焊接试验。对焊缝金属和热影响区金属的显微组织进行了分析，并对焊接接头金属的硬度进行了测试。研究结果表明：15CrMoR钢采用焊条R307焊接，经焊后热处理的焊接接头的组织为铁素体、珠光体和碳化物，焊缝金属的硬度与母材的硬度相近。采用焊条A302焊接时，其焊缝组织为奥氏体和树枝状的δ铁素体，并存在枝晶偏析，在热影响区形成了贝氏体组织，是导致热影响区金属的硬度比焊缝区金属的硬度高得多的原因。     

顶锻压力对1045钢/5Cr5MoV模具钢摩擦焊组织与性能的影响

采用连续驱动摩擦焊实现了1045钢与5Cr5MoV模具钢异种钢材的优质高效连接,获得了成形以及力学性能良好的焊接接头。微观组织和力学分析表明:焊缝为马氏体、珠光体和铁素体的混合组织。随着顶锻压力增大,1045钢侧焊接热影响区晶粒度减小,5Cr5MoV模具钢侧焊接淬火区晶粒由粒状变为带状。焊缝处硬度最高,向母材两侧硬度逐步降低,且随着顶锻压力增大,模具钢侧高硬度区增宽,而1045钢侧高硬度区变窄。焊接接头整体抗拉强度随顶锻压力的增加呈现先增加而后趋于稳定,当压力过高时强度略有下降;当顶锻压力在170～210MPa时,焊接接头抗拉强度最大可达到698MPa。焊接接头拉伸断口呈现以解理断裂为主的脆性断裂特征。     

S690Q高强钢对接节点的焊后性能

通过试验研究了S690Q高强钢对接节点的焊后性能.利用手工电弧焊焊接了3个厚度为8 mm的S690Q高强钢对接节点,焊接过程中对3个节点分别采用不同的焊接热量.在微观层面上,用微观结构测试和微观硬度测试研究焊接对于节点的影响;在宏观层面上,通过拉伸试验研究焊接对于节点力学性能的影响.微观结构测试结果表明,S690Q高强...     

Effect of zirconium addition on the austenite grain coarsening behavior and mechanical properties of 900 MPa low carbon bainite steel

The ultra-free bainitic microstructure of a 900 MPa low carbon bainitic Cu-Ni-Mo-B steel was obtained by a newly developed relaxation precipitation control (RPC) phase transformation processing.In a pan-cake like prior-anstenite grain,the microstructure consisted of lath bainite,a little of abnormal granular bainite,and acicular ferrite.The effect of zirconium carbonitrides on the austenite grain coarsening behavior was studied by transmission electron microscopy (TEM).The results show that,the lath is narrower with increasing cooling rate.The ratio of all kinds of bainitic microstructure is proper with the intermediate cooling rate;and Zr-containing precipitates distribute uniformly,which restrains austenite grain growing in heat-affected welding zone.     

Microstructures and properties of 550 MPa grade high strength thin-walled H-beam steel

The microstructures and mechanical properties of 550 MPa grade lightweight high strength thin-walled H-beam steel were experimentally studied. The experimental results show that the microstructure of the air-cooled H-beam steel sample is consisted of ferrite, pearlite and a small amount of granular bainites as well as fine and dispersive V（C,N） precipitates. The microstructure of the water-cooled steel sample is consisted of ferrite and bainite as well as a small amount of fine pearlites. The microstructure of the water-cooled sample is finer than that of the air-cooled sample with the average intercept size of the surface grains reaching to 3.5 gna. The finish rolling temperature of the thin-walled high strength H-beam steel is in the range of 750 ~C-850 ~C. The lower the finish rolling temperature and the faster the cooling rate, the finer the ferrite grains, the volume fraction of bainite is increased through water cooling process. Grain refinement strengthening and precipitation strengthening are used as major strengthening means to develop 550 MPa grade lightweight high strength thin- walled H-beam steel. Vanadium partially soluted in the matrix and contributes to the solution strengthening. The 550 MPa grade high-strength thin-walled H-beam steel could be developed by direct air cooling after hot rolling to fully meet the requirements of the target properties.     

辙叉贝氏体焊条连接修复组织性能研究

针对现场焊补及修复不便问题,本文提供了一种铁路钢轨及组合辙叉专用贝氏体焊条,该堆焊焊条焊前不用预热,焊后不用热处理。通过对该焊条连接及修复的组织性能特征分析,结果表明,无论是堆焊修复还是连接其焊缝组织都是粒状贝氏体,堆焊层显微硬度与基体基本一致,连接焊缝的冲击强度达到70J/cm2,焊条的组织性能满足贝氏体辙叉钢修复要求。     

激光焊接650MPa相变诱发塑性钢的组织与性能

采用固体Nd:YAG激光器焊接拉伸强度级别为650MPa、厚度为1.2mm的相变诱发塑性钢(TRIP)薄板,利用光学显微镜和电子显微镜研究了其不同焊接速度下对接焊缝的形貌和组织特点。测试了接头的硬度和抗拉强度,借助杯凸试验对比研究了激光焊接接头和母材的成形能力,并分析了焊接速度对接头组织、性能的影响。研究表明:TRIP钢的相组成主要是大量铁素体、贝氏体和少量的残余奥氏体;激光焊缝金属则主要由马氏体构成。焊缝金属或焊接热影响区的近缝区具有最高的硬度。焊缝金属的屈服强度和抗拉强度在垂直于焊缝方向与母材基本相同,但在平行于焊缝方向明显高于母材。与母材相比,激光焊接TRIP钢薄板的冲压成型能力明显下降。     

纵向磁场对WQ960钢焊接接头组织和性能的影响

为了研究纵向磁场对焊接接头的显微组织、冲击韧性和抗拉强度的影响,利用纵向磁场辅助MAG焊焊接WQ960高强钢.纵向磁场的施加提高了焊接接头的抗拉强度、冲击吸收功和冲击韧性,改善了焊接接头的显微组织,且焊接接头的显微组织主要由细小的针状铁素体构成.结果表明,当励磁电流达到2.5 A且磁场频率为20 Hz时,焊接接头的抗拉强度和低温冲击功均可达到最大值,分别为839 MPa和72 J,且分别提高了17.01%和24.14%;先共析铁素体和侧板条铁素体数量相应减少,因而形成了更多的针状铁素体.     

新型高强韧性奥—贝组织低合金钢的研究

作者应用新的合金设计思想,研制了一类新型高碳低合金超高强度钢。经适当热处理,获得贝氏体铁素体板条与奥氏体薄膜交替排列的奥氏体-贝氏体双相组织。文中研究了钢的组织、力学性能及其与转变温度的关系。