Sr3LaNb3O12: A New Low Loss and Temperature Stable A4B3O12-Type Microwave Dielectric Ceramic

The microwave dielectric properties of dense ceramics of a new A₄B₃O₁₂ type cation-deficient hexagonal perovskite Sr₃LaNb₃O₁₂ are reported. Single-phase powders can be obtained from the mixed-oxide route at 1320°C and dense ceramics (>96% of the theoretical X-ray density) with uniform microstructures (5–12 um) can be obtained by sintering in air at 1430°C. The ceramic exhibits a moderate dielectric constant ɛ_r∼36, a high quality factor Q × f ∼45 327 GHz, and a low temperature coefficient of resonant frequency τ _f of −9 ppm/°C.     

High-Temperature Structural Phase Transition in Ca0.7Ti0.7La0.3Al0.3O3: Investigation by Synchrotron X-Ray Diffraction

Mixed-oxide prepared Ca_0.7Ti_0.7La_0.3Al_0.3O₃ (CTLA) ceramics (≈96% dense), grain size 6–7 μm, with dielectric properties (at 4 GHz) of ɛ_r≈46, Q × f ≈38 000 GHz, and τ_f+13 ppm/°C, were studied at 25°–1300°C using synchrotron X-ray powder diffraction. At room temperature, CTLA exhibits a distorted orthorhombic structure, with two tilt systems: a =5.40383 (4) Å, b =5.41106 (6) Å, and c =7.64114 (7) Å with space group Pbnm . At 1050°±25°C, there is a transition from orthorhombic ( Pbnm ) to tetragonal ( I 4/ mcm ), with a simpler tilt arrangement. The lattice parameters at 1100°C were: a =5.44285 (4) Å and c =7.68913 (8) Å.     

Dielectric Characteristics of Nd(Zn1/2Ti1/2)O3 Ceramics at Microwave Frequencies

The microwave dielectric properties and the microstructures of Nd(Zn_1/2Ti_1/2)O₃ (NZT) ceramics prepared by the conventional solid-state route have been studied. The prepared NZT exhibited a mixture of Zn and Ti showing 1:1 order in the B-site. The dielectric constant values (ɛ_r) saturated at 29.1–31.6. The quality factor ( Q × f ) values of 56 700–170 000 (at 8.5 GHz) can be obtained when the sintering temperatures are in the range of 1300°–1420°C. The temperature coefficient of resonant frequency τ_f was not sensitive to the sintering temperature. The ɛ _r value of 31.6, the Q × f value of 170 000 (at 8.5 GHz), and the τ_f value of −42 ppm/°C were obtained for NZT ceramics sintering at 1330°C for 4 h. For applications of high selective microwave ceramic resonators, filters, and antennas, NZT is proposed as a suitable material candidate.     

Microwave Dielectric Properties of Hexagonal 12R-Ba3LaNb3O12 Ceramics

The dielectric properties of dense ceramics of the n =0 member of a newly identified homologous series Ba_{3+ n} LaNb₃Ti _n O_{12+3 n} , where n =0, 1, and 2, are reported. Single-phase powders can be obtained from the mixed-oxide route at 1350°C and dense ceramics (>97% of the theoretical X-ray density) with uniform microstructures (3–5 μm) can be obtained by sintering in air at 1500°C. The ceramics are excellent dc insulators with a band gap >2.6 eV that resonate at microwave frequencies with a relative permittivity, ɛ_r∼44, a quality factor, Q × f _r, of ∼9000 at f _r∼5.5 GHz and a temperature coefficient of resonant frequency, TC_f,∼−100 ppm/K.     

Low-Dielectric Loss Characteristics of Nd(Co1/2Ti1/2)O3 Ceramics at Microwave Frequencies

The microwave dielectric properties and the microstructures of Nd(Co_1/2Ti_1/2)O₃ (NCT) ceramics using starting powders of Nd₂O₃, CoO, and TiO₂ prepared by the conventional solid-state route have been researched. The dielectric constant values (ɛ_r) saturated at 24.8–27. Quality factor ( Q × f ) values of 37 900–140 000 (at 9 GHz) and the measured τ_f values ranging from −45 to −48 ppm/°C can be obtained when the sintering temperatures are in the range of 1410°–1500°C. The ɛ_r value of 27, the Q × f value of 140 000 (at 9 GHz) and the τ_f value of −46 ppm/°C were obtained for NCT ceramics sintered at 1440°C for 4 h. For applications of high selective microwave ceramic resonator, filter, and antenna, NCT is proposed as a suitable material candidate.     

Dielectric Properties of the "Twinned" 8H-Hexagonal Perovskite Ba8Nb4Ti3O24

The dielectric properties of dense ceramics of the "twinned" 8H-hexagonal perovskite Ba₈Nb₄Ti₃O₂₄ are reported. Single-phase powders were obtained from the mixed-oxide route at 1325°C and ceramics (>92% of the theoretical X-ray density) by sintering in air or flowing O₂ at 1400°–1450°C. The ceramics are dc insulators with a band gap >3.4 eV that resonate at microwave frequencies with relative permittivity, ɛ_r∼44–48, quality factor, Q × f _r∼21 000–23 500 GHz (at f _r∼5.5 GHz) and temperature coefficient of resonant frequency, TC _f,∼+115 ppm/K.     

Synthesis and Microwave Dielectric Properties of Re3Ga5O12 (Re: Nd, Sm, Eu, Dy, Yb, and Y) Ceramics

Re₃Ga₅O₁₂ (Re: Nd, Sm, Eu, Dy, Yb, and Y) garnet ceramics were synthesized and their microwave dielectric properties were investigated for advanced substrate materials in microwave integrated circuits. The Re₃Ga₅O₁₂ ceramics sintered at 1350°–1500°C had a high-quality factor ( Q × f ) ranging from 40 000 to 192 173 GHz and a low-dielectric constant (ɛ_r) of between 11.5 and 12.5. They also exhibited a relatively stable temperature coefficient of resonant frequency (τ_f) in the range of −33.7 to −12.4 ppm/°C. In particular, the Sm₃Ga₅O₁₂ ceramics sintered at 1450°C exhibited good microwave dielectric properties of ɛ_r=12.4, Q × f =192 173 GHz, and τ_f=−19.2 ppm/°C.     

Microwave Dielectric Properties of CaTiO3-CaAl1/2Nb1/2O3 Ceramics Doped with Li3NbO4

The microwave dielectric properties of CaTi_{1− x} (Al_1/2Nb_1/2) _x O₃ solid solutions (0.3 ≤ x ≤ 0.7) have been investigated. The sintered samples had perovskite structures similar to CaTiO₃. The substitution of Ti⁴⁺ by Al³⁺/Nb⁵⁺ improved the quality factor Q of the sintered specimens. A small addition of Li₃NbO₄ (about 1 wt%) was found to be very effective for lowering sintering temperature of ceramics from 1450–1500° to 1300°C. The composition with x = 0.5 sintered at 1300°C for 5 h revealed excellent dielectric properties, namely, a dielectric constant (ɛ_r) of 48, a Q × f value of 32 100 GHz, and a temperature coefficient of the resonant frequency (τ_f) of −2 ppm/K. Li₃NbO₄ as a sintering additive had no harmful influence on τ_f of ceramics.     

Structure and Microwave Dielectric Characteristics of Ca1+xNd1−xAl1−xTixO4 Ceramics

CaNdAlO₄ microwave dielectric ceramics were modified by Ca/Ti co-substitution, and their dielectric characteristics were evaluated along with their structure and microstructures. Ca_{1+ x} Nd_{1− x} Al_{1− x} Ti _x O₄ ( x =0, 0.025, 0.05, 0.10, 0.15, 0.20) ceramics with the relative density of over 95% theoretical density were obtained by sintering at 1400°–1450°C in air for 3 h, where the K₂NiF₄-type solid solution single phase was determined from the compositions of x <0.20, while a small amount of CaTiO₃ secondary phase was detected for x =0.20. With Ca/Ti co-substitution in CaNdAlO₄ ceramics, the dielectric constant (ɛ_r) increased with increasing x , and the temperature coefficient of resonant frequency (τ_f) was adjusted from negative to positive, while the Q × f ₀ value increased significantly at first and reached an extreme value at x =0.025 and the maximum at x =0.15. The best combination of microwave dielectric characteristics were achieved at x =0.15 (ɛ_r=19.5, Q × f ₀=93 400 GHz, τ_f=−2 ppm/°C). The improvement of the Q × f ₀ value primarily originated from the reduced interlayer polarization with Ca/Ti co-substitution, while the decreased tolerance factor, the subsequent increased interlayer stress, and the appearance of CaTiO₃ secondary phase brought negative effects upon the Q × f ₀ value.     

Origin of Microwave Dielectric Loss in ZnNb2O6-TiO2

(1− x )ZnNb₂O₆· x TiO₂ ceramics were prepared using both anatase and rutile forms of TiO₂. At a composition of x = 0.58, a mixture region of ixiolite (ZnTiNb₂O₈) and rutile was observed and the temperature coefficient of resonant frequency (τ_f) was ∼0 ppm/°C. We found that although ɛ_r and τ_f were comparable, the quality factor ( Q × f , Q ≈ 1/ tan δ, f = resonant frequency) of 0.42ZnNb₂O₆·0.58TiO₂ prepared from anatase and rutile was 6000 and 29 000, respectively. The origin of the difference in Q × f of both samples was investigated by measuring electrical conductivity and by analysis of the anatase–rutile phase transition. The anatase-derived sample had higher conductivity, which was related to the reduction of Ti⁴⁺. It is suggested that the increase of dielectric loss originates from an increase in Ti³⁺ and oxygen vacancies due to an anatase–rutile phase transition.     

Effects of Calcium Substitution on the Structural and Microwave Dielectric Characteristics of [(Pb1−xCax)1/2La1/2](Mg1/2Nb1/2)O3 Ceramics

The effects of calcium substitution on the structural and microwave dielectric characteristics of [(Pb_{1− x} Ca _x )_1/2La_1/2](Mg_1/2Nb_1/2)O₃ ceramics (with x = 0.01–0.5) were investigated. All the materials were observed to have an ordered A(B_1/2^'B_1/2^")O₃-type perovskite structure; however, the space group of the structure changed from Fm 3 m to Pa 3 as the calcium content increased to x = 0.1, and then from Pa 3 to R 3¯ at the x = 0.5 composition. During the structural evolution, the lattice parameter of the perovskite cell decreased linearly, and the dielectric constant ( k ) also decreased, from k = 80 to k = 38. However, the product of the quality factor and the resonant frequency ( Q × f ) increased from 50 000 GHz to 90 000 GHz as the calcium content increased. Also, the temperature coefficient of resonant frequency (τ_ƒ) gradually changed from 120 ppm/°C to −40 ppm/°C as the calcium content increased. At the x = 0.3 composition, a combination of properties— k ∼ 50, Q × f ∼ 86 000 GHz, and τ_ƒ∼ 0 ppm/°C—can be obtained.     

Microstructures and Microwave Dielectric Characteristics of Ca(Zn1/3Nb2/3)O3 Complex Perovskite Ceramics

Ca(Zn_1/3Nb_2/3)O₃ microwave dielectric ceramics were prepared using a solid-state reaction process, and their microwave dielectric properties were evaluated as functions of sintering and postdensification annealing conditions. The relationship between microwave dielectric properties and processing was interpreted through the variation of microstructures. The dielectric constant showed slight variation with sintering and annealing conditions, but the Q × f value increased at first and then decreased with increased sintering temperature, and annealing in oxygen indicated significant improvement in Q × f , especially for the specimens sintered at higher temperatures. The good microwave dielectric properties were obtained in the ceramics sintered at 1225°C in air for 3 h and annealed at 1100°C in oxygen for 8 h: ɛ= 34.1, Q × f = 15 890 GHz, τ_f=−48 ppm/°C.     

Sintering Behavior and Dielectric Properties of Bi3NbO7 Ceramics Prepared by Mixed Oxides and High-Energy Ball-Milling Methods

The sintering behavior and dielectric properties of Bi₃NbO₇ ceramics prepared by the high-energy ball milling (HEM) method and conventional mixed oxides method with V₂O₅ addition were investigated. All the samples were sintered between 840° and 960°C. For the ceramics prepared by the mixed oxides method, the pure tetragonal Bi₃NbO₇ phase formed without any cubic phase. With changing sintering temperature, the dielectric constant ɛ_r lies between 79 and 92, while the Q × f values are between 300 and 640 GHz. The samples sintered at 870°C have the best microwave dielectric properties with ɛ_r=79, Q × f =640 GHz, and the temperature coefficients of resonant frequency τ_f between 0 and −20 ppm/°C. For the ceramics prepared by the HEM, a pure cubic phase was obtained. The ɛ_r changes between 78 and 80 and Q × f were between 200 and 290 GHz.     

High-Q Microwave Dielectrics in the (Mg1−xCox)2TiO4 Ceramics

The microwave dielectric properties and the microstructures of (Mg_{1− x} Co _x )₂TiO₄ ceramics prepared by the conventional solid-state route were investigated. Lattice parameters were also measured for specimens with different x . The formation of solid solution (Mg_{1− x} Co _x )₂TiO₄ ( x =0.02–0.1) was confirmed by the X-ray diffraction patterns, energy dispersive X-ray analysis, and the lattice parameters measured. By increasing x from 0 to 0.05, the Q × f of the specimen can be tremendously boosted from 150 000 GHz to a maximum of 286 000 GHz. A fine combination of microwave dielectric properties (ɛ_r∼15.7, Q × f ∼286 000 GHz at 10.4 GHz, τ_f∼−52.5 ppm/°C) was achieved for (Mg_0.95Co_0.05)₂TiO₄ ceramics sintered at 1390°C for 4 h. Ilmenite-structured (Mg_0.95Co_0.05)TiO₃ was detected as a second phase. The presence of the second phase would cause no significant variation in the dielectric properties of the specimen because it possesses compatible properties compared with that of the main phase. In addition, only a small deviation in the dielectric properties was monitored for specimens with x =0.04–0.05 at 1360°–1420°C. It not only provides a wide process window but also ensures an extremely reliable material proposed as a very promising dielectric for low-loss microwave and millimeter wave applications.     

Glass-Free KxBa1−xGa2−xGe2+xO8 Ceramics for Low-Temperature Cofired Ceramics Technology: Synthesis, Phase Transitions, Sintering, and Microwave Dielectric Properties

K _x Ba_{1− x} Ga_{2− x} Ge_{2+ x} O₈ (0.6≤ x ≤1) polycrystalline ceramics are potential materials for glass-free low-temperature cofired ceramics (LTCC) substrates. We have made a comprehensive study of the kinetics of the monoclinic-to-monoclinic P 2₁/ a ⇔ C 2/ m phase transition. The low-temperature-stable P 2₁/ a phase with a high Q × f value was synthesized using a subsolidus method and was well sintered at the LTCC temperature with a H₃BO₃ additive. A good combination of low sintering temperature (910°–920°C), high Q × f values (96 700–104 500 GHz), low permittivities (5.6–6.0), and a small temperature coefficient of resonant frequency (∼−20 ppm/°C) was obtained for ceramics with x =0.67 and 0.9 and with 0.1 wt% of H₃BO₃.     

Characteristics of High-Q Microwave Dielectric Ceramics Nd(Co1/2Ti1/2)O3 With CuO Addition

We report the microwave dielectric properties and the microstructures of Nd(Co_1/2Ti_1/2)O₃ ceramics prepared by the conventional solid-state route. The prepared Nd(Co_1/2Ti_1/2)O₃ exhibits a mixture of Co and Ti showing a 1:1 order in the B site. Lowering the sintering temperature (as low as 1260°C) and promoting the densification of Nd(Co_1/2Ti_1/2)O₃ ceramics could be effectively achieved by adding CuO (up to 0.75 wt%). At 1350°C, Nd(Co_1/2Ti_1/2)O₃ ceramics with 0.5 wt% CuO addition possess a dielectric constant (ɛ_r) of 27.6, a Q × f value of 165 000 GHz (at 9 GHz), and a temperature coefficient of resonant frequency (τ_f) of −20 ppm/°C. By comparing with pure Nd(Co_1/2Ti_1/2)O₃ ceramics, incorporating additional CuO helps to render a dielectric material with a higher dielectric constant, a smaller τ_f value, and a 20% dielectric loss reduction, which makes it a very promising candidate for applications requiring low microwave dielectric loss.     

Microwave Dielectrics in the (La1/2Na1/2)TiO3–Ca(Fe1/2Nb1/2)O3 System

Dielectric properties of the system (1 − x)(La_1/2Na_1/2)TiO₃– _x Ca(Fe_1/2Nb_1/2)O₃, where 0.4 # x # 0.6, have been investigated at microwave frequencies. The temperature coefficient of resonant frequency (τ_f), nearly 0 ppm/°C, was realized at x = 0.58. These ceramics had perovskite structure and showed relatively low dielectric losses. A new dielectric material applicable to microwave devices having Q · f of 12000–14000 GHz and a dielectric constant (ε_r) of 59–60 has been obtained at 1300–1350°C for 5–15 h sintering.     

Glass-Free Zn2Te3O8 Microwave Ceramic for LTCC Applications

A Zn₂Te₃O₈ ceramic was investigated as a promising dielectric material for low-temperature co-fired ceramics (LTCC) applications. The Zn₂Te₃O₈ ceramic was synthesized using the solid-state reaction method by sintering in the temperature range 540°–600°C. The structure and microstructure of the compounds were investigated using X-ray diffraction (XRD) and scanning electron microscopy methods. The dielectric properties of the ceramics were studied in the frequency range 4–6 GHz. The Zn₂Te₃O₈ ceramic has a dielectric constant (ɛ_r) of 16.2, a quality factor ( Q _u× f ) of 66 000 at 4.97 GHz, and a temperature coefficient of resonant frequency (τ_f) of −60 ppm/°C, respectively. Addition of 4 wt% TiO₂ improved the τ_f to −8.7 ppm/°C with an ɛ_r of 19.3 and a Q _u× f of 27 000 at 5.14 GHz when sintered at 650°C. The chemical reactivity of the Zn₂Te₃O₈ ceramic with Ag and Al metal electrodes was also investigated.     

Dielectric Properties of (1−x)CaTiO3–xCa(Zn1/3Nb2/3)O3 Ceramic System at Microwave Frequency

The microwave dielectric properties of the (1− x )CaTiO₃– x Ca(Zn_1/3Nb_2/3)O₃ ceramic system have been investigated. The ceramic samples sintered at 1300°–1450°C for 4 h in air exhibit orthorhombic pervoskite and form a complete solid solution for different x value. When the x value increased from 0.2 to 0.8, the permittivity ɛ_r decreased from 115 to 42, the unloaded quality factor Q × f increased from 5030 to 13 030 GHz, and the temperature coefficient τ_f decreased from 336 to −28 ppm/°C. When x =0.7, the best combination of dielectric properties, a near zero temperature coefficient of resonant frequency of τ_f∼−6 ppm/°C, Q × f ∼10 860 GHz and ɛ_r∼51 is obtained.     

A Novel Temperature-Compensated Microwave Dielectric (1−x)(Mg0.95Ni0.05)TiO3−xCa0.6La0.8/3TiO3 Ceramics System

The microstructure and microwave dielectric properties of a (1− x )(Mg_0.95Ni_0.05)TiO₃− x Ca_0.6La_0.8/3TiO₃ ceramics system have been investigated. The system was prepared using a conventional solid-state ceramic route. In order to produce a temperature-stable material, Ca_0.6La_0.8/3TiO₃ was added for a near-zero temperature coefficient (τ_f). With partial replacement of Mg²⁺ by Ni²⁺, the dielectric properties of the (1− x )(Mg_0.95Ni_0.05)TiO₃− x Ca_0.6La_0.8/3TiO₃ ceramics can be promoted. The microwave dielectric properties are strongly correlated with the sintering temperature and the composition. An excellent Q × f value of 118,000 GHz can be obtained for the system with x =0.9 at 1325°C. For practical application, a dielectric constant (ɛ_r) of 24.61, a Q × f value of 102,000 GHz, and a temperature coefficient of resonant frequency (τ_f) of −3.6 ppm/°C for 0.85(Mg_0.95Ni_0.05)TiO₃−0.15Ca_0.6La_0.8/3TiO₃ at 1325°C are proposed. A parallel-coupled line band-pass filter is designed and simulated using the proposed dielectric to study its performance.