MoS_2纳米材料的制备及其催化性能

采用水热合成法,利用钼酸钠和硫粉作为前驱体,在200℃下成功制备出二硫化钼纳米材料,采用XRD和SEM对其进行了结构与形貌表征,并通过光催化实验对产物的光催化性能进行了研究,结果发现,当催化剂用量为0.2 g时,甲基橙的降解率最高。     

纳米花状MoS_2的水热法合成及其电催化析氢性能

为了制备低成本、高性能的非铂析氢电催化剂,以四水合钼酸铵((NH_3)_6Mo_7O_(24)·4H_2O)和L-半胱氨酸(HSCH_2CH(NH_2)COOH,L-CYS)为原料,采用水热法于200℃下反应24h,制备出纳米花状MoS_2。采用X射线衍射(XRD)、扫描电子显微镜(SEM)、高分辨透射电子显微镜(HRTEM)及能谱仪(EDS)等手段对纳米花状MoS_2的微观结构、形貌、组成进行表征,同时,测试评价2种MoS_2催化剂在酸性条件下电催化析氢性能。结果表明,通过该方法本文制备的纳米花状MoS_2电催化剂表现出优于市购MoS_2的析氢电催化活性。纳米花状MoS_2电催化剂表现出更优析氢电催化活性可归因于其暴露出较多边角结构及高活性晶面。     

含有金纳米粒子的复合纳米纤维的制备和表征

以氯金酸(HAu Cl4)为原料,柠檬酸钠(C6H5Na3O7·4H2O)为还原剂,聚乙烯吡咯烷酮(PVP)为保护剂,乙醇为溶剂制备出含有金纳米粒子的溶胶溶液;采用高压静电纺丝技术制备了含有金纳米粒子的聚乙烯吡咯烷酮复合纳米纤维。通过紫外光谱研究了不同含量的金纳米粒子对纤维吸光度的影响;通过扫描电子显微镜和透射电子显微镜考察了含有金纳米粒子的聚乙烯吡咯烷酮复合纳米纤维的形貌。研究表明,随着金纳米粒子在纺丝溶液含量的增大,金纳米颗粒的特征吸收峰越来越明显,且有红移趋势;随着金纳米颗粒的增多,纤维逐渐变细,浓度过高时则不能生成纤维。     

建筑室内环境净化材料纳米纤维膜的制备与研究

本文关注建筑室内环境净化材料纳米纤维膜的制备与研究,通过实验得出了可以制备出性能优良的纳米纤维膜材料的静电纺丝工艺。通过调控纺丝原液、溶剂、电压、速度等条件,制备出了多种结构的聚乳酸(PLA)纤维。将纤维进行了扫描电子显微镜和透射电子显微镜表征,对其过滤效率及过滤寿命进行了性能测试。将表征与测试的结果进行了分析,得出了理想的制备工艺。     

YF_3:Er~(3+)纳米纤维的制备与上转换发光性能

采用静电纺丝技术制备了PVP/[Y(NO3)3+Er(NO3)3]复合纳米纤维,经过氧化焙烧得到Y2O3:Er3+纳米纤维,再通过双坩埚氟化法制得YF3:Er3+纳米纤维。通过XRD、SEM、EDS和荧光光谱分析对样品的形貌和性质进行了表征。结果表明所制得YF3:Er3+纳米纤维是纯正交相,带有空间群Pnma。YF3:Er3+纳米纤维的直径大约为(89±11)nm且分布均匀。上转换发射光谱分析显示,在980nm激发下,YF3:Er3+纳米纤维在526、543和653nm处发射出强的绿光和弱的红光,它们分别归属于Er3+的2 H11/2→4I15/2、4S3/2→4I15/2和4F9/2→4Il5/2能级跃迁;在532nm可见光激发下,YF3:Er3+纳米纤维能够在1.52μm处产生近红外发射。随着Er3+浓度的增加,YF3:Er3+纳米纤维发光强度逐渐增大。由色坐标(CIE)图可知,YF3:Er3+纳米纤维所发射的颜色位于色坐标的绿光区。此外,还提出了YF3:Er3+纳米纤维可能的形成机理。     

聚丙烯腈纳米纤维与环氧树脂复合涂层防腐性能的研究

利用静电纺丝技术在Q235钢表面制备聚丙烯腈(PAN)纳米纤维膜并在其中包覆缓蚀剂苯并三氮唑(BTA),然后在其表面涂覆环氧树脂(EP),得到复合涂层(PAN-NFs/BTA/EP)。通过电化学测试表征复合涂层的防腐性能,结果表明在树脂涂层中加入纤维后,防腐性能得到明显提高。     

二氧化锰/活性炭复合材料的制备及其电化学性能研究

本文以KMnO4为锰源,采用水热法在同一体系中通过控制KMnO4与活性炭的质量,制备了质量比不同的δ-MnO2∕活性炭复合电极材料。通过高分辨扫描电子显微镜(SEM)和X射线衍射(XRD)对其微观形貌和晶体结构进行了表征分析;将所得到的复合型电极材料制备成电极片,并组装成夹心式对称型超级电容器,采用循环伏安(CV)、恒电流充放电(GCD)、交流阻抗(EIS)等方法在两电极体系下对其进行电化学性能测试。结果表明:当δ-MnO2和活性炭的质量比为2∶1时,所得到的复合材料的电化学性能最好,其质量比电容可达251.92 F/g。     

PANI/SiCNP复合材料的制备及其光热蒸发性能

采用原位聚合法实现了聚苯胺(Polyaniline, PANI)对碳化硅纳米颗粒(Silicon Carbide Nanoparticles, SiCNP)的有效包覆,得到了聚苯胺/碳化硅纳米颗粒的复合材料(PANI/SiCNP)。使用扫描电镜(Scanning Electron Microscopy, SEM)对样品进行形貌结构分析,结果表明：PANI较为均匀地生长在SiCNP表面,PANI/SiCNP直径从SiCNP的20～100 nm增加到100～200 nm,而且随着在复合材料中SiCNP的增加导致有较多的团聚。而且与PANI相比,PANI/SiCNP的热稳定性得到了提升。界面水蒸发测试结果显示,PANI/SiCNP复合材料有着良好的水蒸发速率和水蒸发稳定性。     

改性纳米纤维素纤维增强水泥基复合材料制备与性能研究

本研究以水泥浆及C40混凝土为基体,纳米纤维素纤维（Cellulose nanofiber,CNF）为增强体,采用阳离子改性剂十六烷基三甲基溴化铵对CNF进行改性处理,制备改性CNF水泥基复合材料并对其进行了表征。通过水泥浆抗折试验、抗压试验,研究不同掺量改性剂对水泥基复合材料力学性能的影响。结果表明在水泥基体中掺入适量的改性CNF可以显著提升水泥及复合材料的抗折强度与抗压强度。混凝土干燥收缩及塑性收缩的结果显示CNF及改性CNF可以提高混凝土的抗裂性能。     

聚氨酯泡沫/木质纤维复合材料的制备及其性能初探

以聚醚多元醇、多次甲基多苯基异氰酸酯(MDI)及木质纤维为原料,采用一步法制备了木质纤维增强硬泡聚氨酯复合材料。研究了木质纤维的长径比、用量对复合材料的力学性能、导热系数和其他性能的影响。结果表明,当长径比为40:1、添加量为10%时,复合材料的拉伸强度、压缩强度分别为4.8、5.6 MPa,与未增强的材料相比分别提高了2.06、2.20倍。并且增强聚氨酯复合材料的导热系数比未增强材料的导热系数更低,为0.017 W/(m.K)。     

混凝土增粘剂的合成制备及性能探究

采用自由基聚合法合成混凝土增粘剂,探究增粘剂的最佳合成工艺,对不同羧基密度的混凝土增粘剂的性能进行测试。结果表明,羧基密度越高的聚合物在水泥颗粒上的吸附容量越高,但吸附容量过高的聚合物会和聚羧酸减水剂产生竞争吸附,降低水泥净浆的流动度;基于最优工艺制备的NC-ZN420增粘剂能有效降低混凝土的泌水量,增加混凝土的粘度,增粘剂的使用对混凝土的强度发展没有明显影响。     

开发生活资源,灵动记叙文写作

<正>记叙文是初中语文写作教育的基础内容也是重点内容,对于初中生来说,写作不仅是提高书面表达能力的重要途径,而且对促进初中生养成良好品德,形成健康的审美情趣,均起着其他教学手段无法代替的作用。根据义务教育阶段新课标的要求,初中语文写作要求必须"能够具体明确、文从字顺地表达自己的见闻、体验"和"想法","运用常见的表达方式写作""发展书面语言运用能力"。因此从新课标要求来看,这一阶段中记叙文写作是重中之重。表达见闻、体验、想法,都离不     

Water absorption of wood polypropylene composite sheet piles and its influence on mechanical properties

The water absorption behavior and durability of extruded wood polypropylene composite (WPC) material used in Z-section sheet piles was investigated. An experimental technique to determine percentage water absorption and its effect on mechanical properties was implemented. Water absorption tests were carried out on specimens cut from flanges and webs of the Z-section by immersion in tap water at 21, 45 and 70 °C. Freeze–thaw resistance of saturated composites was studied by cycling temperatures in the range of 21 to ?29 °C. The absorption behavior followed the kinetics of a Fickian diffusion process. This behavior was modeled using an analytical solution based on Fick’s second law of diffusion. Quasi-static bending tests were conducted periodically on specimens immersed in water to assess degradation in flexural properties. A significant decrease in mechanical properties of the water-saturated specimens compared to the dry control was observed. Degradation of flexural modulus was found to be a strong function of water absorption with initial decrement as percentage water absorption increased and finally stabilized as the absorption process approached saturation. However, freeze–thaw cycling did not have any significant effect on mechanical properties of saturated composites. A phenomenological model for moisture intrusion and its effect on mechanical properties was implemented and applied to explain the experimental findings.     

丙烯酸酯-水泥复合注浆材料制备及其性能研究

将丙烯酸酯注浆材料加入到水泥浆液中,对复合浆液的结实率、固结体的无侧限抗压强度以及抗水冲刷性进行了研究。结果表明:复合浆液结实率均高达95%以上;养护28 d,水灰比为2.0的复合浆液固结体抗压强度较纯水泥浆液提高了5.43 MPa,而水灰比为1.0的复合浆液固结体抗压强度较纯水泥浆液提高了9.95 MPa;当动水流速达到0.6 m/s时,复合浆液固结体残留率均大于65%,而纯水泥浆液残留率降至15%以下,最低仅为3.9%。     

粉煤灰地质聚合物轻质发泡材料的制备与性能研究

以粉煤灰地质聚合物为基体,加入发泡剂和稳泡剂,制备了轻质发泡材料.主要研究了温度、表面活性剂、碱用量、水量对材料性能的影响.结果表明,表面活性剂对样品的性能影响最大,加入表面活性剂后,样品的孔径从4～10mm降低到1～2mm以下,抗压强度最高达2.57 MPa(密度为0.76g/cm3),导热系数小于0.09 W/(m·K),使用温度高达800℃,是很好的耐高温、高强度多孔保温材料.     

气相法原位合成氧化铁/黄铁矿材料及其光电性能

通过水热法在Ti基底上制备氧化铁的前驱物FeOOH,将长有FeOOH的钛片与硫代硫酸钠放入石英坩埚内,以Ar气作为载气,利用硫代硫酸钠在高温分解得到气相硫单质参与化合反应,然后通过控制煅烧温度,制备氧化铁纳米棒阵列与黄铁矿的原位复合产物。利用X射线衍射仪、场发射扫描电子显微镜和拉曼光谱对复合产物的晶型、形貌、成分、物相等进行分析,以电化学工作站测试Fe_2O_3/FeS_2复合材料的线性扫描伏安曲线、光电流-时间曲线、交流阻抗谱曲线和莫特-肖特基曲线。结果表明,黄铁矿在Fe_2O_3纳米棒表面均匀生成,样品在500℃热处理下具有优异的光电化学性能,其光电流密度可以从0.32 mA/cm~2提高到3.68 mA/cm~2。     

Conditions for obtaining and electrochemical properties of thermochemical and magnetite anodes

We studied the conditions for the formation of a magnetite anode by thermal decomposition of iron nitrate. It has been found that the magnetite samples obtained from pure nitrate possess low stability in operation and electrocatalytic activity. Introduction into the composition of the active coating of alloying additions of copper, cobalt, manganese, and molybdenum makes it possible to improve electrochemical properties of magnetite anodes. It has been shown that in terms of stability and electrocatalytic activity thermochemical anodes surpass plasma-evaporated ones.     

石材蜂窝板及其应用

本文简要介绍了石材蜂窝板的品种、结构、特点、应用范围及工程实例,并针对石材蜂窝板在应用中普遍存在的疑虑心理和主要技术问题,如耐久性、板型凹凸、安装连接、弯曲强度和物理力学性能等,提出了相应的见解和注意事项。     

新型复合轻质墙板及期制备

介绍一种新型轻质墙板的制备过程及其材性试验.该墙板为复合材料夹层结构,由泡桐木、玻璃纤维、乙烯基树脂等粘接而成,墙板采用真空导入工艺一次成型,具有质量轻、强度高、保温隔热等优点,可作为临时或永久性建筑物的围护结构使用.     

混凝土叠合板研究综述--受力性能和设计方法

叠合板具有节约材料、方便施工和整体性好的优异性能,是装配整体式结构中常用的预制部品。开展叠合板的研究,可以进一步优化叠合板的使用性能,完善装配体系性能,推动其在各类建筑中推广应用,加速建筑工业化进程。简要的介绍近些年先后出现的几种常见的叠合板,对各叠合板按照不同受力性能进行归纳和对比分析,并总结研究了设计方法方面的研究成果,最后对叠合楼板发展现状和趋势进行分析。