CdS/CNT-TiO2光催化剂的合成及其对亚甲基蓝的光催化降解（英文）

采用多壁碳纳米管(MWCNTs)为载体,分别以醋酸镉((CH3COO)2Cd.2H2O)和硫化钠(Na2S.5H2O)为镉源和硫源,经简单逐滴滴入途径制备了CdS/CNT复合材料。再以四丁氧基钛(TNB)为钛源,苯为溶剂,成功地将二氧化钛(TiO2)纳米粒子沉积在CdS修饰的MWCNTs表面而得到CdS/CNT-TiO2光催化剂。利用N2吸附等温线、扫描电子显微镜、X射线衍射、能量分散性X射线分析以及透射电子显微镜对所制CdS/CNT-TiO2光催化剂进行表征。CdS/CNT-TiO2复合材料呈多孔结构,MWCNTs均匀分散在材料中,且未出现明显的TiO2和CdS纳米颗粒团聚体。该材料在紫外和可见光照射下对亚甲基蓝具有优异的降解活性。这不仅归因于TiO2对自由基的反应和MWCNTs吸附能力,且归因于引入窄带隙半导体CdS,使粒子在MWCNTs表面的电子转移速率得到提高。     

碳纳米管负载纳米TiO2复合材料的制备及组织结构表征

采用溶胶-凝胶法,以钛酸四丁酯为原料,以碳纳米管为载体,在碳纳米管表面上负载纳米TiO2粉体,制备出CNT-TiO2复合材料.通过X射线衍射(XRD),透射电子显微镜(TEM)等手段研究了复合材料颗粒的组织结构及包覆情况,通过UV-vis漫反射谱分析比较了纯TiO2、纯CNTs和CNT-TiO2的吸光性能.结果表明,纳米TiO2均匀的包覆在CNTs表面上,且包覆均匀致密.CNT-TiO2复合材料经450℃热处理后,纳米TiO2颗粒以鋭钛矿相存在,其平均粒径约为7.3nm.CNTs-TiO2复合材料兼具载体碳纳米管和外层纳米TiO2对光的吸收性能,在紫外光区域和可见光区域对光都有非常好的吸收性能.     

炭表面改性对负载型TiO_2/活性炭复合光催化剂性能的影响

采用HNO3、H2O2和O3对商品活性炭进行表面改性处理,考察了改性处理对活性炭表面基团、负载TiO2以及所形成的TiO2/活性炭复合光催化剂性能的影响。利用傅里叶红外光谱(IR)、X射线光电子能谱(XPS)、扫描电镜(SEM)及氮气吸附等手段对材料进行了表征。结果表明,3种改性方法均可有效提高活性炭载体表面的含氧官能团数量,但是对活性炭的比表面积和孔容影响不大;H2O2和O3对活性炭载体改性后可以提高对钛前驱体的吸附性能,HNO3改性有利于TiO2颗粒在活性炭表面的分散。使用改性后的活性炭作为载体制备的TiO2/活性炭光催化降解甲基橙的性能均高于未改性的TiO2/活性炭催化剂,其中以HNO3改性后的TiO2/活性炭活性最高。     

活性炭负载TiO2复合光催化剂的光催化活性研究

采用水热法将TiO2负载在不同活性炭上形成复合光催化剂,通过SEM和XRD对所得复合催化剂进行表征,并对亚甲基蓝(MB)进行光催化降解。结果表明:复合光催化剂具有很高的光催化降解率,其中椰壳活性炭载体优于煤质活性炭载体。负载的TiO2均为锐钛矿晶型,晶粒发育较完善、粒径小、分布均匀。TiO2负载量的提高未能改变光催化活性,反而降低了复合光催化剂的吸附能力。煅烧处理可以进一步提高光催化活性。     

TiO2/活性炭复合体的制备及其表征

以活性炭(AC)为载体,采用溶胶-凝胶法制备纳米TiO2/AC复合型催化剂.利用SEM,TG-DTA,XRD,等手段对其组成、结构、尺寸等进行分析和表征,结果表明,该复合材料由碳、钛、氧等3种元素组成,其中TiO2纳米粒子尺寸在2O-50nm之间,比本体TiO2纳米粒子尺寸小;在该纳米复合材料中,活性炭作为载体与TiO2结合牢固,存在着某种化学键,TiO2纳米颗粒间不发生团聚,并且活性炭载体的比表面积变化不大.     

聚氨酯TiO2纳米管复合材料的制备与光催化特性研究

为了解决水体中光催化剂的分离和回收问题,对纳米TiO2的改性和固载化及其光催化特性进行了研究。首先以纳米TiO2为原料,采用水热合成法制备TiO2纳米管;再对TiO2纳米管硅烷化,改善其表面性质;然后以聚氨酯(PU)膜片为载体负载TiO2纳米管,制成了负载型PU/TiO2薄膜的光催化材料。采用X射线衍射(XRD)、傅里叶变换红外光谱(FTIR)、衰减全反射傅里叶变换红外光谱(ATR-FTIR)和扫描电子显微镜(SEM)等手段对催化剂进行了表征,结果表明硅烷化后的TiO2纳米管能很好地接枝在PU薄膜表面。以300 W高压汞灯为光源,萘普生为目标降解物,研究了负载PU/TiO2薄膜的光催化活性和稳定性,结果表明其对目标物的降解具有较高活性,用乙醇冲洗即可多次重复使用,其催化活性能较长时间保持稳定。     

静电纺丝制备Fe2O3-TiO2纳米纤维及光催化性能研究

采用静电纺丝法制备了Fe2O3掺杂纳米TiO2的有机无机PVP/Fe2O3-TiO2纤维,经高温焙烧得到Fe2O3-TiO2纳米纤维。利用差动-热重(DSC-TGA)、傅里叶红外光谱(FT-IR)、扫描电镜(SEM)、XRD和比表面积分析仪等对样品进行了表征。以10mg/L亚甲基蓝溶液为底物,研究了Fe2O3掺杂量和焙烧温度等对亚甲基蓝太阳光催化降解效果的影响。结果表明,掺杂量为0.08%、焙烧温度为500℃得到的Fe2O3-TiO2纳米纤维光降解效果最好,达到96.3%,重复使用7次降解率仍在90%以上。     

活性炭负载Co0.8Zn0.2Fe2O4铁氧体的制备及电磁性能研究

采用溶胶-凝胶法制备活性炭负载纳米钴锌铁氧体复合吸波材料研究。以柠檬酸为络合剂制备Co0.8Zn0.2Fe2O4铁氧体溶胶,加入活性炭于溶胶中,经浓缩制得活性炭/钴锌铁氧体凝胶,再经过低温煅烧,制备出形态和结构理想的活性炭负载钴锌铁氧体复合材料;详细地考察烧结温度、煅烧时间及活性炭与铁氧体的配比等工艺参数对复合材料的形态和结构的影响;分别采用X射线衍射(XRD)、扫描电镜(SEM)和能量散射X射线荧光光谱(EDX)对制备出的复合材料进行形貌、结构及组成表征分析。采用波导法在8.2～12.4GHz波段对活性炭负载纳米钴锌铁氧体复合材料进行电磁参数测试分析,结果表明所制备活性炭负载纳米钴锌铁氧体复合材料具有较高的电、磁损耗角正切值,其吸波性能较好。     

磷酸处理HZSM-5负载TiO2光催化降解活性艳红X-3B

以磷酸改性的HZSM-5分子筛为载体,采用溶胶-凝胶法制备TiO2/HZSM-5光催化剂,通过XRD,SEM,BET,FT-IR和XPS进行表征。结果表明:TiO2均匀地分散在HZSM-5表面,没有发生TiO2颗粒的聚集。负载后的TiO2保持了锐钛矿晶体结构,TiO2的晶粒尺寸在负载后有所减小。TiO2/0.5HZSM-5的比表面积和对活性艳红X-3B的吸附量都随HZSM-5含量的增加而增加。负载后的TiO2光催化活性均高于纯TiO2,50%(质量分数)TiO2/0.5HZSM-5具有最高的活性,经紫外光照射2h可使活性艳红X-3B降解93.4%,而染料在纯TiO2上的降解率只有61.0%。     

银负载TiO_2纳米线/石墨烯的制备及光催化应用

采用二步水热法和光照还原法制备了银负载TiO2纳米线/石墨烯(GR/TiO2NW/Ag)复合材料,并对其进行了表征,结果表明:Ag纳米颗粒修饰的TiO2NW分布于石墨烯表面,TiO2NW为锐钛矿晶型,光生电子和空穴复合效率降低。并研究了GR/TiO2NW/Ag复合材料在紫外光下降解双酚A废水的光催化性能,实验结果表明,GR/TiO2NW/Ag对双酚A的降解效果明显优于TiO2。40min内,GR/TiO2NW/Ag在紫外光照下对双酚A降解率达到100%。     

Elastic and Electronic Properties of Superconducting CaPd 2 As 2 and SrPd 2 As 2 vs. Non-superconducting BaPd 2 As 2

The first-principles calculations were performed to predict the elastic and electronic properties of the superconducting ThCr₂Si₂-type phases CaPd₂As₂ and SrPd₂As₂ in comparison with the non-superconducting CeMg₂Si₂-type phase BaPd₂As₂. Besides, the same properties were compared for CeMg₂Si₂- and ThCr₂Si₂-type polymorphs of BaPd₂As₂. We found that all these phases are mechanically stable and belong to soft materials with low hardness. The near-Fermi region is formed by the valence states of the blocks [Pd₂As₂] with decisive contributions of Pd 4d states. The values of N(E _F) increase in the sequence: CaPd₂As₂ < SrPd₂As₂ < BaPd₂As₂, i.e. in the reverse sequence relative to the transition temperatures T _C. Thus, the change in T _C cannot be explained by the electronic factor, i.e. by the simple correlation T _C～N(E _F). Most likely the decrease in T _C in the sequence CaPd₂As₂ → SrPd₂As₂ and the absence of a superconducting transition in BaPd₂As₂ are related to the structural factors and the peculiarities of the electron–phonon coupling mechanism.     

Preparation of ZrO2-CeO2 and HfO2-CeO2 nanopowders

We prepared weakly agglomerated powders of ZrO₂-CeO₂ and HfO₂-CeO₂ solid solutions 5–8 nm in particle size, consisting of monoclinic and tetragonal phases. After heat treatment at 1200°C, the crystallite size was 30 and 14 nm, respectively. We also examined the effect of precipitate freeze drying on the crystallization of hafnia-based solid solutions containing up to 20 mol % CeO₂.     

VLE data for CO2-CF2Cl2, N2-CO2, N2-CF2Cl2 and N2-CO2-CF2Cl

Knowledge about vapour-liquid (VLE) is required as a basis of reliable calculations for separation processes. Correlations available for the prediction of T, p, x, y data are less accurate for mixtures at high pressures and mixtures containing supercritical components. The results of VLE experiments are reported and compared with data calculated with equations of state.     

Thermal diffusion in binary mixtures H2-CCl2F2 and H2-CHClF2

Thermal diffusion coefficients were measured in two gaseous mixtures, in which one component was close to the critical temperature, in the pressure range (19.6–127.4)·10⁴ N/m² and at a freon concentration of 0.25–0.8.     

SiO2—TiO2—ZrO2系涂层的制备及其特性

用溶胶－凝胶法（sol-gel method）在不锈钢表面制备了SiO2-TiO2-ZrO2系无机氧化膜（STZ）。用DTA／TG、IR、XRD和SEM等手段研究了涂层制备时由凝胶向玻璃态的转变以及涂层薄膜的显微结构特点，考察了涂层对基体的保护效果。试验结果表明，在溶胶至凝胶最终转变为无机氧化物的过程中形成了无机网络，Si^4 和Zr^4 充当了网络骨架的形成离子。涂层为无定型玻璃态，其间混有石英、锐钛矿或金红石等微晶。     

SiO2-TiO2-ZrO2涂层的制备及其特性

用溶胶-凝胶法(sol-gel method)在不锈钢表面制备了 SiO\-2-TiO\-2-ZrO\-2系无机氧化膜(STZ).用DTA/TG、IR、XRD和SEM等手段研究了涂层制备时由凝胶向玻璃态的转变以及涂层薄膜的显微结构特点,考察了涂层对基体的保护效果. 试验结果表明,在溶胶至凝胶最终转变为无机氧化物的过程中形成了无机网络,Si4+ 和Zr4+充当了网络骨架的形成离子.涂层为无定型玻璃态,其间混有石英、锐钛矿或金红石等微晶.     

晶态骨架介孔CeO2和CeO2-ZrO2的合成与结构表征

以乙酸铈、乙酸锆为无机源,嵌段共聚物P123为模版剂,采用溶胶-凝胶法合成了介孔CeO2及CeO2-ZrO2复合体,用XRD、氮气吸附脱附、TEM、HRTEM、SAED等对材料进行了表征.结果表明,所得介孔CeO2具有规则的晶态孔道结构,孔径约在10nm左右,特别是其孔壁晶粒高度定向排列且平行于孔道方向.原位高温TEM观测表明,该介孔CeO2在800℃仍具有很高的孔道完整性.掺杂ZrO2后发现,在ZrO2摩尔含量低于30%时仍具备高度定向排列结构,高于30%时骨架晶粒取向逐渐趋向无序化.     

Strain engineering in single-, bi- and tri-layer MoS2, MoSe2, WS2 and WSe2

Nano Research - Strain is a powerful tool to modify the optical properties of semiconducting transition metal dichalcogenides like MoS2, MoSe2, WS2 and WSe2. In this work we provide a thorough...