锂离子电池LiNi1/3Co1/3Mn1/3O2正极材料的性能研究(Ⅰ)

采用共沉淀法和高温固相烧结相结合,合成了锂离子电池层状LiNi1/3Co1/3Mn1/3O2正极材料。采用ICP-AES元素分析方法、XRD和SEM对LiNi1/3Co1/3Mn1/3O2正极材料的成分、结构和形貌进行了表征。SEM测试结果表明,LiNi1/3Co1/3Mn1/3O2的形貌近似为球形,且颗粒分布均匀。并对其进行了充放电性能测试,结果表明:LiNi1/3Co1/3Mn1/3O2在25℃、2.5～4.6 V、0.1 C倍率下,首次放电容量达189.32 mAh.g-1(锂为负极),C/LiNi1/3Co1/3Mn1/3O2在1 C、2.75～4.2 V下,初始放电比容量为145.5 mAh/g,循环100次后,容量保持率为98.41%。是一种有发展前景的锂离子电池正极材料。     

不同铝源对LiNi1/3Co1/3Mn1/3O2材料的包覆改性研究

分别以纳米氧化铝、氢氧化铝及异丙醇铝为原料,采用液相浸渍法对LiNi1/3Co1/3Mn1/3O2材料进行氧化铝包覆,考察不同包覆源在LiNi1/3Co1/3Mn1/3O2材料表面进行氧化铝包覆后对材料电化学性能的影响。SEM及XRD结果显示,产物为层状α-NaFeO2结构,氧化铝均匀包覆在LiNi1/3Co1/3Mn1/3O2材料表面。充放电性能测试结果表明,在3种铝源中,以异丙醇铝为包覆源的材料性能最佳：在3.0~4.6 V的电压下,0.1 C倍率下首次放电比容量为196.1 mA·h/g, 1 C下循环50周后容量保持率为95.6%。     

层状结构LiNi1/3Co1/3Mn1/3O2正极材料制备过程与电化学性能

采用固相自引发基团置换法结合高温焙烧制备了亚μm级的LiNi1/3Co1/3Mn1/3O2正极材料。研究了热处理气氛、烧结时间对材料结构及性能的影响。研究结果表明在空气氛围下900℃焙烧20 h制备的LiNi1/3Co1/3Mn1/3O2正极材料具有最佳的电化学性能。     

锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2研究进展

层状结构材料LiNi1/3Co1/3Mn1/3O2具有高比容量、高循环性能、低成本和环保等优点,有望取代LiCoO2成为新一代锂离子电池正极材料。在介绍LiNi1/3Co1/3Mn1/3O2的结构特点和电化学反应特性的基础上,对其主要合成方法进行了详细评述,总结了该正极材料的阴阳离子掺杂、复合离子掺杂以及表面包覆改性等技术,指出国内外目前锂离子电池材料研究中存在的问题和未来的发展方向。     

MgF2包覆对正极材料LiNi1/3Co1/3Mn1/3O2性能的影响

通过浸渍法在正极材料LiNi1/3Co1/3Mn1/3O2的表面包覆MgF2,通过XRD、SEM、交流阻抗（EIS）分析、充放电测试研究了不同量MgF2包覆对LiNi1/3Co1/3Mn1/3O2正极材料的结构与电化学性能的影响。结果表明,MgF2以非晶态形式包覆于LiNi1/3Co1/3Mn1/3O2材料颗粒的表面,当包覆量为3%（物质的量分数,下同）时,三元正极材料具有优良的电化学性能,在3.0~4.6 V充放电范围内0.1C充放电倍率下,首次放电比容量为196.3 mA·h/g,1C循环50次后容量保持率为95.7%,55 ℃高温下1C循环50次后容量保持率为93.3%。     

层状Li[Ni_（1/3）Co_（1/3）Mn_（1/3）]O_2锂离子电池正极材料制备方法的研究进展

层状结构Li[Ni1/3Co1/3Mn1/3]O2是目前国内外锂电池正极材料的研究热点。制备这种三元系材料的方法是热点中的重点。本文主要综述了不同的制备方法以及这些方法的简单对比,并探讨了Li[Ni1/3Co1/3Mn1/3]O2的应用前景。     

Al2O3包覆LiNi1/3Co1/3Mn1/3O2锂离子电池正极材料

综述了Al2O3包覆LiNi(1/3)Co(1/3)Mn(1/3)O2锂离子电池正极材料的研究现状与进展,并评述了其制备方法和包覆改性;讨论了包覆改善该正极材料性能的机理;提出了这种正极材料的研发过程中的一些问题并对其未来的发展前景作了展望。     

A12O3包覆LiNi（1/3）Co（1／3）Mn（1／3）O2

综述了A1203包覆LiNi（1/3）Cows）Mn（1/3）O2锂离子电池正极材料的研究现状与进展,并评述了其制备方法和包覆改性：讨论了包覆改善该正极材料性能的机理：提出了这种正极材料的研发过程中的一些问题并对其未来的发展前景作了展望。     

Li[Ni1/3Co1/3Mn1/3]O2合成工艺对其结构和性能的影响

采用碳酸盐共沉淀法制备Li[Ni1/3Co1/3Mn1/3]O2。研究了前驱体合成温度、时间和焙烧温度、焙烧时间对材料结构和电化学性能的影响。测试结果表明,合成温度为40℃,时间30 h所得前驱体的振实密度和电化学性能较好。XRD测试结果表明,不同焙烧温度下得到的Li[Ni1/3Co1/3Mn1/3]O2均具有α-NaFeO2型层状结构。其中800℃下焙烧15 h得到的样品具有较好的层状结构和较低的阳离子混排程度。样品在2.8～4.3 V电压范围内,0.2 C放电倍率下的首次放电比容量最高可达159.1 mAh·g-1,循环50次后容量保持率为95.7%。     

锂离子电池三元电极材料LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2的制备方法及其改性研究进展

三元正极材料(LiNi1/3Co1/3Mn1/3O2)具有较好的安全性能和循环性能,兼顾了其它二元电极材料的诸多优点,成为目前高性能锂离子电池正极材料的研究重点之一,其市场占有率已经超过40%。详细的叙述了近年来国内外对三元正极材料的制备和改性所做的研究,着重介绍了其高温固相法、共沉淀法、溶胶-凝胶法等制备方法及掺杂、包覆改性方法对LiNi1/3Co1/3Mn1/3O2电化学性能影响,以及这些改性方法存在的问题。     

High tap density of Ni3(PO4)2 coated LiNi1/3Co1/3Mn1/3O2 with enhanced cycling performance at high cut-off voltage

The LiNi1/3Co1/3Mn1/3O2 is first obtained by the control ed crystallization method and then coated with Ni3(PO4)2 particles. The effects of the coating on rate capability and cycle life at high cut-off voltage are investigated by elec-trochemical impedance spectroscopy and galvanostatic measurements. The element ratio of Ni:Mn:Co is tested by inductively-coupled plasma spectrometer (ICP) analysis and it testified to be 1:1:1. It is indicated that Ni3(PO4)2-coated LiNi1/3Co1/3Mn1/3O2 has an outstanding capacity retention, where 99%capacity retention is maintained after 10 cycles at 5C discharge rate between 2.7 V and 4.6 V. The electrochemical impedance spectroscopy (EIS) results show that the current exchange density i0 of the coated sample is higher than that of LiNi1/3Co1/3Mn1/3O2, which is beneficial to its electrochemical performances. All the conclusions show that the Ni3(PO4)2 coating can prominently enhance the high rate performance of the LiNi1/3Co1/3Mn1/3O2, especially at high cut-off voltage.     

pH对三元材料前驱体物理性能的影响

在不同pH下共沉淀制备了正极材料LiNi_1/3Mn_1/3Co_1/3O₂的前驱体Ni_1/3Mn_1/3Co_1/3（OH）₂。通过对前驱体产物进行粒径分布分析、振实密度分析及扫描电镜照片分析,比较了pH对合成前驱体材料性能的影响。结果表明,在pH等于11.0条件下,合成的前驱体粒径分布均匀,振实密度高,形貌规则。将该条件下的前驱体与氢氧化锂混合煅烧制备得到LiNi_1/3Mn_1/3Co_1/3O₂。经电化学性能测定,发现其电化学性能优异,在0.2 C和1.0 C下首次放电容量可达 160.0 mA·h/g和129.9 mA·h/g;在1.0 C下循环20次后,容量保持率高达94%。     

锂镍钴锰氧正极材料的热聚合法制备及性能表征研究

经过几十年的发展,锂离子电池由于其在能量密度、循环寿命等方面的优势,在小心电子产品上获得了广泛的应用。在目前的商业化锂离子电池产业中,应用最广泛的正极材料是由Good enough等开发的LiCoO2材料,但是其有毒、热稳定性差等特点,导致其难以得到进一步的应用。因此,通过开发他们的复合材料成为了锂离子电池正极材料开发的主要研究方向之一。论文主要对LiNi1/3Co1/3Mn1/3O2材料的热聚合法制备及性能表征进行了一定的研究。     

共沉淀法制备Li[Ni1/3Co1/3Mn1/3]O2及电化学性能研究

采用NH3-NaOH共沉淀法合成了L[Ni1/3Co1/3Mn1/3]O2正极材料,通过改变NH3·H2O浓度及加料方式研究材料的电化学性能.采用XRD、SEM对晶体的结构和形貌作表征.将正极材料Li[Ni1/3Co1/3Mn1/3]O2制成电极极片,组装成电池进行测试.分析测试结果表明,合成的极材料Li[Ni1/3Co1/3Mn1/3]O2具有典型的α-NaFeO2结构,粒径分布较好,呈类球形.     

溶剂热法合成锂离子电池正极材料-纳米LiFe1/3Mn1/3Co1/3PO4/C

首次报道了溶剂热法合成一种新型锂离子电池正极材料LiFe1/3Mn1/3Co1/3PO4,并对其结构和电化学性能进行了研究。合成的LiFe1/3Mn1/3Co1/3PO4属正交晶系结构,扫描电镜照片显示合成的材料是长度300～400nm,宽度200．250nm,厚度约100nm的板状结构。以碳包覆后的LiFe1/3Mn1/3Co1/3PO4作为正极材料组装电池进行充放电测试,在3．5V,4．1V,4．6V出现了三个平台,分别对应Fe^3＋／Fe^2＋,Mn^3＋／Mn^2＋,Co^3＋／Co^2＋氧化还原电对,0．2C时首次放电容量达到142．2mAh／g,经过50次循环后可逆容量仍保持在92．6mAh／g。     

锂离子正极材料Li（Ni_（1/3）Co_（1/3）Mn_（1/3））O_（2-x）F_x的合成与电化学性能

采用沉淀法合成一系列Li（Ni1/3Co1/3Mn1/3）O2-xFx正极材料（0≤x≤0.5）;用X射线衍射仪和扫描电镜仪分析了合成产物的晶体结构及表面形貌;利用充放电仪测定产物的电化学性能,结果表明Li（Ni1/3Co1/3Mn1/3）O1.7F0.3的电化学性能最佳,首次充放电比容量分别达181.9、174.0 mA.h/g,材料的结构在循环过程中保持稳定,倍率性能变好,电化学阻抗明显降低。