高流态超早强聚合物修补砂浆的性能研究

采用可再分散乳胶粉改性硫铝酸盐水泥制备修补砂浆,研究了乳胶粉掺量对修补砂浆力学性能和粘结性能的影响。结果表明:乳胶粉掺量从0增加到2%时,修补砂浆的抗压强度逐渐降低,而抗折强度和粘结强度却逐渐提高。当乳胶粉掺量为1.5%时,修补砂浆2 h、1 d和28 d抗压强度分别为27.3、42.3、57.0 MPa,拉伸粘结强度为1.8 MPa,界面弯拉强度为7.8 MPa,抗拉强度恢复率为73.4%。在乳胶粉和聚氧化乙烯(PEO)复掺条件下,砂浆的拉伸粘结强度进一步提高,当乳胶粉和PEO掺量分别为1.5%和0.5%时,拉伸粘结强度可达2.31 MPa。     

掺聚丙烯纤维聚合物改性砂浆的早期失水

研究了聚合物(乳胶粉、纤维素醚)掺量、砂浆厚度及砂子细度模数对掺聚丙烯纤维聚合物改性砂浆在最初300 min内失水的影响.结果表明:聚合物对砂浆早期失水的影响由聚合物保水作用和聚合物增加聚丙烯纤维表面亲水性从而增加失水效应而共同决定.随乳胶粉掺量的增加,砂浆失水率呈“降低—增加—降低”趋势.纤维素醚掺量过小(0.1％和...     

偏高岭土对外保温黏结砂浆性能影响的研究

采用偏高岭土取代部分水泥、纤维素醚和可再分散乳胶粉来降低外保温黏结砂浆的成本。首先,采用正交试验的方法研究水泥、可再分散乳胶粉、纤维素醚、偏高岭土用量对外保温黏结砂浆性能影响规律;重点研究了偏高岭土对外保温黏结砂浆黏结强度的影响。研究表明:在一定范围内,水泥掺量对黏结原强度影响最大,其次是纤维素醚和偏高岭土掺量,可再分散乳胶粉对黏结砂浆黏结原强度的影响最小。研究发现,固定黏结砂浆稠度在合适范围内,随着偏高岭土掺量的提高,砂浆用水量逐步增加。在水泥用量保持不变的条件下,适当添加偏高岭土可以提高黏结砂浆的黏结性能。当偏高岭土的掺量超过3%时,随着偏高岭土掺量的提高,黏结砂浆的黏结原强度有所降低。因此,偏高岭土的掺量不超过3%时,偏高岭土部分取代水泥、纤维素醚、可再分散乳胶粉,显著降低外保温黏结砂浆的成本。     

聚丙烯纤维与胶粉复掺对砂浆强度和韧性的影响

采用聚丙烯纤维与聚合物胶粉复掺的方法配制了胶粉改性砂浆,并应用正交试验和多点分布的纤维单因素试验研究了聚丙烯纤维与聚合物胶粉复掺对砂浆强度和韧性的影响。结果表明:随着纤维掺量的增加,砂浆折压比总体上呈增加趋势,长度为10mm的聚丙烯纤维增韧效应最优;当聚丙烯纤维复合胶粉改性砂浆的折压比在0.17⁰.21时,韧性显著提高;配制参数纤维掺量为0.2%、纤维长度为10mm、胶粉掺量为5%、硅粉掺量为5%的胶粉改性砂浆的综合强度和韧性最优,适合作为混凝土剥蚀面层的修复材料。     

加气混凝土专用抗裂抹面砂浆的研制

通过加入甲基纤维素醚、可再分散乳胶粉、聚丙烯纤维等聚合物,粉煤灰掺合料对砂浆进行改性,研制的加气混凝土专用抗裂抹面砂浆。本课题通过分析几种聚合物掺量对砂浆性能影响因素的大小,得出最佳掺量,找出砂浆最佳配比。经测试,研制的加气混凝土专用抗裂抹面砂浆可操作性好,便于施工,与加气混凝土粘结强度高,抗裂性能好。     

聚合物改性膨胀玻化微珠保温砂浆的研制及性能研究

本文通过添加可再分散聚合物乳胶粉,研究可再分散聚合物乳胶粉的掺量对性能影响的变化规律,对膨胀玻化微珠保温砂浆进行改性,得到性价比好的保温砂浆,并很好地改善了其粘结性能,能有效解决了这一质量通病。     

不同养护方式下可再分散乳胶粉改性砂浆的性能

研究了三种不同养护方式(60℃蒸汽养护、饱和石灰水浸泡养护、早期水中-后期空气中养护)对掺入不同剂量的乙烯-醋酸乙烯共聚物可再分散乳胶粉(EVA乳胶粉)改性砂浆性能的影响规律。结果表明:随着EVA乳胶粉掺量的增加,砂浆的流动度先增大后减小,吸水率先减小后增大,且EVA掺量为4%时,砂浆流动性最好,掺量为6%时砂浆吸水率最小;砂浆抗折强度先增大后减小,且在4%掺量时取得最大值,而抗压强度一直减小,砂浆的压折比呈现出先减小后保持基本不变,并在4%乳胶粉掺量时有较低值;蒸汽养护最有利于聚合物砂浆结构的致密及强度的发展,而饱和石灰水浸泡养护对其致密性和强度最不利。     

聚合物改性粉煤灰建筑砂浆粉

通过实验,探讨聚合物羧甲基纤维素钠、聚丙烯酰胺对大掺量粉煤灰建筑砂浆粉的改性效果,为干粉砂浆的开发应用提供技术途径.     

加气混凝土专用抹灰砂浆的研制

由于传统砂浆用于加气混凝土抹灰时,存在保水性差、粘结强度低、易开裂空鼓等缺陷,这严重阻碍了加气混凝土的广泛应用。针对这些缺陷,研制了一种和易性好、保水性好、粘结强度高、收缩率低,适合加气混凝土抹灰用的砂浆。研究了粉煤灰、保水剂、可再分散乳胶粉、减水剂等对砂浆性能的影响,并探讨各种外加剂对砂浆的改性机理。经研究确定加气混凝土专用抹灰砂浆的基本配比为:胶砂比1∶3,水胶比0.50,粉煤灰掺量40%,HEMC掺量0.2%,乳胶粉掺量2%,聚羧酸高效减水剂掺量1.2%。     

粉煤灰和纤维对聚合物改性砂浆性能的影响

文中研究了粉煤灰和纤维单掺、复掺对聚合物改性砂浆工作性能、力学性能的影响。结果表明,随着粉煤灰取代量的增加,聚合物改性砂浆稠度提高,保水率下降,抗压强度降低,压折比减小;随着纤维掺量的增加,聚合物改性砂浆的稠度下降,保水率提高,抗压强度降低,压折比减小。当粉煤灰取代量为15%、纤维掺量为0.3%时,聚合物改性砂浆的施工性能有所改善,7 d和28 d抗压强度下降,压折比明显降低。粉煤灰和纤维复掺,虽然对抗压强度并无改善,但砂浆抗折强度增益产生了较好的复合效应。     

复合掺合料对水泥胶砂流动度和长期强度的影响

采用粉煤灰(F)、矿渣粉(Sl)、硅灰(Si)和石灰石粉(L)复合组成5种复合矿物掺合料,研究了复合掺合料的组成和掺量对水泥胶砂流动度、长期抗压强度和抗折强度的影响。结果表明:掺粉煤灰和石灰石粉的FSlL和FL复合掺合料流动性较好,流动度比达到110%以上;掺硅灰的FSlSi和SlSiL复合掺合料流动性较差,流动度比在80%左右;5种复合掺合料在30%、40%、50%掺量下,胶砂试件720 d抗压强度和抗折强度均达到纯水泥试件的110%~120%;FSlSi、FSl和FL复合掺合料随着掺量的提高,长龄期胶砂抗压强度有所增加,抗折强度发展趋势与抗压强度相同;SlL和SlSiL复合掺合料随着掺量的提高,长龄期胶砂抗压和抗折强度均略有下降。     

Action of redispersible vinyl acetate and versatate copolymer powder in cement mortar

Redispersible polymer powder of vinyl acetate and versatate copolymer (VA/VeoVa) is applied to modify cement mortar. The effect of VA/VeoVa powder on physical and mechanical properties of cement mortar is investigated. VA/VeoVa powder exhibits excellent water-reduction and water-retention effects in cement mortar and improves mortar properties effectively. Due to the air-entrainment effect of VA/VeoVa powder, the air content of fresh mortar is increased and the bulk density is decreased. VA/VeoVa powder makes the compressive strength decrease, but not so significant the effect on the flexural strength is, which results in the ratio of compressive strength to flexural strength goes down sharply with the increase of VA/VeoVa powder, indicating the toughness of cement mortar is improved markedly. Furthermore, VA/VeoVa powder reduces the shrinkage rate and improves the hydrophobicity and water impermeability of cement mortar.     

不同粒径废玻璃粉对水泥胶砂力学性能的影响

采用3种粒径(20、200、2 000目)的废玻璃粉等体积取代水泥胶砂中的标准砂,体积取代率分别为5%、10%、15%、20%,研究玻璃粉粒径和掺量对水泥胶砂的抗压强度和抗折强度的影响,并对玻璃粉水泥胶砂强度随龄期的变化规律进行了分析讨论。结果表明:不同粒径玻璃粉水泥胶砂的强度随玻璃粉掺量的变化规律存在较大的差异;在玻璃粉掺量相同的情况下,掺入较大粒径玻璃粉的水泥胶砂强度明显降低,玻璃粉粒径越小,强度降低程度越小,当玻璃粉粒径达到微米级,水泥胶砂的抗压强度和抗折强度均显著提高;玻璃粉水泥胶砂的抗压强度随龄期增长,早期强度增加的较快,后期发育增速变缓,而抗折强度早期增长的幅度较大,后期发育比较平缓。     

聚合物抹面砂浆耐候性试验研究破坏机理分析

对外墙外保温体系用聚合物抹面砂浆在耐候性试验环境下的力学性能进行研究。试验结果表明:外墙外保温体系用聚合物抹面砂浆经历一定次数的热雨循环和热冷循环后,抗压强度、抗折强度及粘结强度均有不同程度的下降,压折比提高。同时对外墙外保温用聚合物砂浆耐候性破坏机理进行了研究分析。     

胶粉对砂浆抗折抗压性能的影响

探讨了废旧轮胎胶粉的细度和掺量对水泥砂浆抗折抗压强度的影响。研究结果表明：胶粉的掺入会降低水泥砂浆的抗折抗压强度并随胶粉掺量的加大而减小。在等掺量的条件下,胶粉越细,砂浆的抗折抗压强度越低。     

粉煤灰-矿渣基地聚合物胶砂性能研究

通过正交试验研究了粉煤灰与矿粉质量比(粉矿比)、水玻璃模数、水胶比3个因素对粉煤灰-矿粉基地聚合物胶砂性能的影响规律,并对样品的微观性能进行测试。结果表明:水胶比为最显著影响因素,粉矿比为显著影响因素,水玻璃模数的影响最小,当粉矿比为3∶7,水玻璃模数为1.6,水胶比为0.35时,地聚合物胶砂的28 d抗折和28 d抗压强度最高,分别为7.8、57.2 MPa。     

可再分散乳胶粉对钢渣砂砂浆性能的影响

通过试验,就可再分散乳胶粉(简称“乳胶粉”)掺量对钢渣砂砂浆的流动性、抗压强度、抗折强度、拉伸黏结强度和柔韧性的影响进行了研究.结果表明:随着乳胶粉掺量的增加,钢渣砂砂浆的流动性提高,抗压强度下降,早期抗折强度降低,28 d抗折强度提高,拉伸黏结强度大幅增加,柔韧性得到改善.由此可知,对于钢渣砂砂浆,可掺入一定量乳胶粉来提高其抗折强度,改善柔韧性,并大幅增加拉伸黏结强度.     

PVA纤维对水泥胶砂抗侵蚀性能的影响

研究了不同掺量PVA纤维水泥胶砂经浓度为10000 mg/L和30000 mg/L的硫酸钠溶液侵蚀后的抗压强度和抗折强度变化规律,并以抗折抗蚀系数为指标评价了碱环境下PVA纤维对水泥胶砂抗侵蚀性能的影响。结果表明:随PVA纤维体积掺量的增加,水泥胶砂拌和物的流动度逐渐减小;经硫酸钠溶液侵蚀后,各组试件的力学性能和抗折抗蚀系数均有不同程度降低,高浓度和长侵蚀龄期对水泥胶砂的抗侵蚀性能影响较显著;对比基准组,掺入PVA纤维可有效提高水泥胶砂的力学性能和抗折抗蚀系数,且PVA纤维体积掺量为0.2%时效果最好。     

粗集料强度对混凝土抗折强度的影响

试验研究了4种粗集料(碎石、钢集料、砂浆、页岩陶粒)与3种抗压强度等级水泥砂浆基体组合的混凝土的抗折强度及其发展规律.结果表明,粗集料与水泥砂浆基体的协调性对混凝土抗折强度影响十分显著.当粗集料强度和弹性模量与水泥砂浆基体相匹配时,增加粗集料强度可提高混凝土抗折强度,但粗集料强度和弹性模量过高反而会因较大的应力集中而降低混凝土抗折强度;当粗集料强度比水泥砂浆基体抗压强度低时,单纯通过增大水泥砂浆基体抗压强度来提高混凝土抗折强度的效果不明显;粗集料与水泥砂浆基体在抗压强度和弹性模量上的差异对混凝土抗折强度及其发展规律有很大影响.只有在两者相互协调的基础上,才能充分发挥粗集料和水泥砂浆基体的作用.