Thermoelectric Properties of Sb-Doped Mg<Subscript>2</Subscript>Si<Subscript>0.3</Subscript>Sn<Subscript>0.7</Subscript>

Mg₂(Si_0.3Sn_0.7)_1−y Sb _y (0 ≤ y ≤ 0.04) solid solutions were prepared by a two-step solid-state reaction method combined with the spark plasma sintering technique. Investigations indicate that the Sb doping amount has a significant impact on the thermoelectric properties of Mg₂(Si_0.3Sn_0.7)_1−y Sb _y compounds. As the Sb fraction y increases, the electron concentration and electrical conductivity of Mg₂(Si_0.3Sn_0.7)_1−y Sb _y first increase and then decrease, and both reach their highest value at y = 0.025. The sample with y = 0.025, possessing the highest electrical conductivity and one of the higher Seebeck coefficient values among all the samples, has the highest power factor, being 3.45 mW m⁻¹ K⁻² to 3.69 mW m⁻¹ K⁻² in the temperature range of 300 K to 660 K. Meanwhile, Sb doping can significantly reduce the lattice thermal conductivity (κ _ph) of Mg₂(Si_0.3Sn_0.7)_1−y Sb _y due to increased point defect scattering, and κ _ph for Sb-doped samples is 10% to 20% lower than that of the nondoped sample for 300 K < T < 400 K. Mg₂(Si_0.3Sn_0.7)_0.975Sb_0.025 possesses the highest power factor and one of the lower κ _ph values among all the samples, and reaches the highest ZT value: 1.0 at 640 K.     

Thermal Stability of Barium and Indium Double-Filled Skutterudite Ba<Subscript>0.3</Subscript>In<Subscript>0.2</Subscript>Co<Subscript>3.95</Subscript>Ni<Subscript>0.05</Subscript>Sb<Subscript>12</Subscript> Coated by SiO<Subscript>2</Subscript> Nanoparticles

Filled skutterudite thermoelectric (TE) materials have been extensively studied to search for better TE materials in the past decade. However, there is no detailed investigation about the thermal stability of filled skutterudite TE materials. The evolution of microstructure and TE properties of nanostructured skutterudite materials fabricated with Ba_0.3In_0.2Co_3.95Ni_0.05Sb₁₂/SiO₂ core–shell composite particles with 3 nm thickness shell was investigated during periodic thermal cycling from room temperature to 723 K in this work. Scanning electronic microscopy and electron probe microscopy analysis were used to investigate the microstructure and chemical composition of the nanostructured skutterudite materials. TE properties of the nanostructured skutterudite materials were measured after every 200 cycles of quenching in the temperature range from 300 K to 800 K. The results show that the microstructure and composition of Ba_0.3In_0.2Co_3.95Ni_0.05Sb₁₂/SiO₂ nanostructured skutterudite materials were more stable than those of single-phase Ba_0.3In_0.2Co_3.95Ni_0.05Sb₁₂ bulk materials. The evolution of TE properties indicates that the electrical and thermal conductivity decrease along with an increase in the Seebeck coefficient with increasing quenching up to 2000 cycles. As a result, the dimensionless TE figure of merit (ZT) of the nanostructured skutterudite materials remains almost constant. It can be concluded that these nanostructured skutterudite materials have good thermal stability and are suitable for use in solar power generation systems.     

High Power Factor of HPHT-Sintered GeTe-AgSbTe<Subscript>2</Subscript> Alloys

The thermopower and electrical resistivity of alloys of GeTe and AgSbTe₂ (TAGS) sintered at high pressure (up to 4.5 GPa) and high temperature (HPHT) have been studied from 300 K to 750 K. An apparatus for measuring thermopower and electrical resistivity at temperatures >300 K is described. The linear temperature dependence of thermopower and electrical conductivity indicates that these materials are likely to be degenerate semiconductors. At a sintering pressure of 4.0 GPa, the calculated power factor shows a steady progression, reaching a maximum at a sintering temperature of 800°C, with a subsequent decrease at the highest sintering temperature of 850°C. The maximum power factor of 4.32 × 10⁻³ W m⁻¹ K⁻² at ~675 K is ~25% higher than reported values. These results illustrate that HPHT processing is a feasible and controllable way of tuning the properties of thermoelectric materials.     

High-Performance (Ag<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>SbTe<Subscript><Emphasis Type="Italic">x</Emphasis>/2+1.5</Subscript>)<Subscript>15</Subscript>(GeTe)<Subscript>85</Subscript> Thermoelectric Materials Prepared by Melt Spinning

A new preparation process combining melt spinning and hot pressing has been developed for the (Ag _x SbTe _x/2+1.5)₁₅(GeTe)₈₅ (TAGS-85) system. Compared with samples prepared by the traditional air-quenching and hot-pressing method, electrical conductivity and thermal conductivity are lowered. The thermoelectric performance of the TAGS-85 samples varied with changing Ag content and reached the highest ZT of 1.48 when x was 0.8 for the melt-spun sample, compared with the maximum ZT of 1.36 for the air-quenched sample. The Seebeck coefficient of the melt-spun TAGS-85 alloys was improved, while both the electrical conductivity and thermal conductivity were decreased. The net result of this process is to effectively enlarge the temperature span of ZT > 1, which will benefit industrial application.     

Electrical and Thermal Conductivity and Conduction Mechanism of Ge<Subscript>2</Subscript>Sb<Subscript>2</Subscript>Te<Subscript>5</Subscript> Alloy

Ge₂Sb₂Te₅ alloy has drawn much attention due to its application in phase-change random-access memory and potential as a thermoelectric material. Electrical and thermal conductivity are important material properties in both applications. The aim of this work is to investigate the temperature dependence of the electrical and thermal conductivity of Ge₂Sb₂Te₅ alloy and discuss the thermal conduction mechanism. The electrical resistivity and thermal conductivity of Ge₂Sb₂Te₅ alloy were measured from room temperature to 823 K by four-terminal and hot-strip method, respectively. With increasing temperature, the electrical resistivity increased while the thermal conductivity first decreased up to about 600 K then increased. The electronic component of the thermal conductivity was calculated from the Wiedemann–Franz law using the resistivity results. At room temperature, Ge₂Sb₂Te₅ alloy has large electronic thermal conductivity and low lattice thermal conductivity. Bipolar diffusion contributes more to the thermal conductivity with increasing temperature. The special crystallographic structure of Ge₂Sb₂Te₅ alloy accounts for the thermal conduction mechanism.     

Thermal Conductivity of Bi<Subscript>0.5</Subscript>Sb<Subscript>1.5</Subscript>Te<Subscript>3</Subscript> Affected by Grain Size and Pores

A fine measurement system for measuring thermal conductivity was constructed. An accuracy of 1% was determined for the reference quartz with a value of 1.411 W/m K. Bi_0.5Sb_1.5Te₃ samples were prepared by mechanical alloying followed by hot-pressing. Grain sizes were varied in the range from 1 μm to 10 μm by controlling the sintering temperature in the temperature range from 623 K to 773 K. The thermal conductivity was 0.89 W/m K for the sample sintered at 623 K, while a grain size of 1.75 μm was measured by optical microscopy and scanning electron microscopy. The thermal conductivity increased on the sample sintered at 673 K because of grain growth and decreased on those sintered at the temperatures from 673 K to 773 K because the increase of pore size caused to decrease thermal conductivity. The increase of thermal conductivity for the samples sintered at temperatures above 773 K was affected by the increase of carrier concentration.     

Effects of SiC Nanodispersion on the Thermoelectric Properties of <Emphasis Type="Italic">p</Emphasis>-Type and <Emphasis Type="Italic">n</Emphasis>-Type Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Based Alloys

Polycrystalline p-type Bi_0.5Sb_1.5Te₃ and n-type Bi₂Te_2.7Se_0.3 thermoelectric (TE) alloys containing a small amount (vol.% ≤5) of SiC nanoparticles were fabricated by mechanical alloying and spark plasma sintering. It was revealed that the effects of SiC addition on TE properties can be different between p-type and n-type Bi₂Te₃-based alloys. SiC addition slightly increased the power factor of the p-type materials by decreasing both the electrical resistivity (ρ) and Seebeck coefficient (α), but decreased the power factor of n-type materials by increasing both ρ and α. Regardless of the conductivity type, the thermal conductivity was reduced by dispersing SiC nanoparticles in the Bi₂Te₃-based alloy matrix. As a result, a small amount (0.1 vol.%) of SiC addition increased the maximum dimensionless figure of merit (ZT _max) of the p-type Bi_0.5Sb_1.5Te₃ alloys from 0.88 for the SiC-free sample to 0.97 at 323 K, though no improvement in TE performance was obtained in the case of n-type Bi₂Te_2.7Se_0.3 alloys. Importantly, the SiC-dispersed alloys showed better mechanical properties, which can improve material machinability and device reliability.     

Solid-State Synthesis of Te-Doped Mg<Subscript>2</Subscript>Si

Te-doped Mg₂Si (Mg₂Si:Te _m , m = 0, 0.01, 0.02, 0.03, 0.05) alloys were synthesized by a solid-state reaction and mechanical alloying. The electronic transport properties (Hall coefficient, carrier concentration, and mobility) and thermoelectric properties (Seebeck coefficient, electrical conductivity, thermal conductivity, and figure of merit) were examined. Mg₂Si was synthesized successfully by a solid-state reaction at 673 K for 6 h, and Te-doped Mg₂Si powders were obtained by mechanical alloying for 24 h. The alloys were fully consolidated by hot-pressing at 1073 K for 1 h. All the Mg₂Si:Te _m samples showed n-type conduction, indicating that the electrical conduction is due mainly to electrons. The electrical conductivity increased and the absolute value of the Seebeck coefficient decreased with increasing Te content, because Te doping increased the electron concentration considerably from 10¹⁶ cm⁻³ to 10¹⁸ cm⁻³. The thermal conductivity did not change significantly on Te doping, due to the much larger contribution of lattice thermal conductivity over the electronic thermal conductivity. Thermal conduction in Te-doped Mg₂Si was due primarily to lattice vibrations (phonons). The thermoelectric figure of merit of intrinsic Mg₂Si was improved by Te doping.     

Effects of Ball-Milling Atmosphere on the Thermoelectric Properties of TAGS-85 Compounds

Inspired by the high ZT value lately attained in Ar-protected ball-milled nanocrystalline p-BiSbTe bulk alloy, we report herein an investigation of the effects of ball-milling atmosphere on the thermoelectric (TE) properties of the traditional TE material (GeTe)₈₅(AgSbTe₂)₁₅ (TAGS-85). TAGS-85 samples were prepared via a melting–quenching–annealing process, and then ball-milled in different atmospheres and subsequently densified using a spark plasma sintering technique. The Seebeck coefficient, electrical conductivity, thermal conductivity, and Hall coefficient were measured as a function of temperature from 10 K to 310 K. It was found that different ball-milling atmospheres, i.e., air, liquid N₂ (LN₂), and Ar, profoundly affected the TE properties. A state-of-the-art figure of merit ZT ≈ 0.30 was attained at 310 K in the Ar-ball milled sample. The results are discussed in terms of the carrier concentration, mobility, crystallinity, and the grain boundary scattering.     

Thermoelectric Properties of Mo<Subscript>3</Subscript>Sb<Subscript>5.4</Subscript>Te<Subscript>1.6</Subscript> and Ni<Subscript>0.06</Subscript>Mo<Subscript>3</Subscript>Sb<Subscript>5.4</Subscript>Te<Subscript>1.6</Subscript>

Mo₃Sb₇, crystallizing in the Ir₃Ge₇ type structure, has poor thermoelectric (TE) properties due to its metallic behavior. However, by a partial Sb-Te exchange, it becomes semiconducting without noticeable structure changes and so achieves a significant enhancement in the thermopower with the composition of Mo₃Sb₅Te₂. Meanwhile, large cubic voids in the Mo₃Sb₅Te₂ crystal structure provide the possibility of filling the voids with small cations to decrease the thermal conductivity by the so-called rattling effect. As part of the effort to verify this idea, we report herein the growth as well as measurements of the thermal and electrical transport properties of Mo₃Sb_5.4Te_1.6 and Ni_0.06Mo₃Sb_5.4Te_1.6.     

Thermal Stability of Ge<Subscript>2</Subscript>Sb<Subscript>2</Subscript>Te<Subscript>5</Subscript> in Contact with Ti and TiN

The thermal stability of a Ge₂Sb₂Te₅ chalcogenide layer in contact with titanium and titanium nitride metallic thin films has been investigated mainly using x-ray diffraction and elastic nuclear backscattering techniques. Without breaking vacuum, Ti and TiN have been deposited on Ge₂Sb₂Te₅ material using magnetron sputtering. Thermal treatments have been performed in a 10⁻⁷ mbar vacuum furnace. On annealing up to 450°C, the TiN metallic film does not interact with the chalcogenide film, but at the same time adhesion problems and instabilities in contact resistance arise. To improve the adhesion and eventually stabilize the contact resistance, an interfacial Ti layer has been considered. At 300°C, a TiTe₂ compound is formed by interacting with Te segregated from the Ge₂Sb₂Te₅ layer. At higher temperatures, the Ti layer decomposes the chalcogenide film, forming several compounds tentatively identified as GeTe, Ge₃Ti₅, Ge₅Ti₆, TiTe_2,, and Sb₂Te₃. It has been found that the properties of the Ge₂Sb₂Te₅ film can be retained by controlling the decomposition rate of the chalcogenide layer, which is achieved by providing a limited supply of Ti and/or by depositing a Te-rich Ge₂Sb₂Te₅ film.     

Low-Temperature Thermoelectric Properties of Co<Subscript>0.9</Subscript>Fe<Subscript>0.1</Subscript>Sb<Subscript>3</Subscript>-Based Skutterudite Nanocomposites with FeSb<Subscript>2</Subscript> Nanoinclusions

Bulk thermoelectric nanocomposite materials have great potential to exhibit higher ZT due to effects arising from their nanostructure. Herein, we report low-temperature thermoelectric properties of Co_0.9Fe_0.1Sb₃-based skutterudite nanocomposites containing FeSb₂ nanoinclusions. These nanocomposites can be easily synthesized by melting and rapid water quenching. The nanoscale FeSb₂ precipitates are well dispersed in the skutterudite matrix and reduce the lattice thermal conductivity due to additional phonon scattering from nanoscopic interfaces. Moreover, the nanocomposite samples also exhibit enhanced Seebeck coefficients relative to regular iron-substituted skutterudite samples. As a result, our best nanocomposite sample boasts a ZT = 0.041 at 300 K, which is nearly three times as large as that for Co_0.9Fe_0.1Sb₃ previously reported.     

Thermoelectric Characteristics of <Emphasis Type="Italic">p</Emphasis>-Type (Bi,Sb)<Subscript>2</Subscript>Te<Subscript>3</Subscript>/(Pb,Sn)Te Functional Gradient Materials with Variation of the Segment Ratio

The p-type (Bi,Sb)₂Te₃/(Pb,Sn)Te functional gradient materials (FGMs) were fabricated by hot-pressing mechanically alloyed (Bi_0.2Sb_0.8)₂Te₃ and 0.5 at.% Na₂Te-doped (Pb_0.7Sn_0.3)Te powders together at 500°C for 1 h in vacuum. Segment ratios of (Bi,Sb)₂Te₃ to (Pb,Sn)Te were varied as 3:1, 1.3:1, and 1:1.6. A reaction layer of about 350-μm thickness was formed at the (Bi,Sb)₂Te₃/(Pb,Sn)Te FGM interface. Under temperature differences larger than 340°C applied across a specimen, superior figures of merit were predicted for the (Bi,Sb)₂Te₃/(Pb,Sn)Te FGMs to those of (Bi_0.2Sb_0.8)₂Te₃ and (Pb_0.7Sn_0.3)Te. With a temperature difference of 320°C applied across a specimen, the (Bi,Sb)₂Te₃/(Pb,Sn)Te FGMs with segment ratios of 3:1 and 1.3:1 exhibited the maximum output powers of 72.1 mW and 72.6 mW, respectively, larger than the 63.9 mW of (Bi_0.2Sb_0.8)₂Te₃ and the 26 mW of 0.5 at.% Na₂Te-doped (Pb_0.7Sn_0.3)Te.     

Thermoelectric Properties of Co<Subscript>4</Subscript>Sb<Subscript>12</Subscript> Skutterudite Materials with Partial In Filling and Excess In Additions

The properties of Co₄Sb₁₂ with various In additions were studied. X-ray diffraction revealed the presence of the pure δ-phase of In_0.16Co₄Sb₁₂, whereas impurity phases (γ-CoSb₂ and InSb) appeared for x = 0.25, 0.40, 0.80, and 1.20. The homogeneity and morphology of the samples were observed by Seebeck microprobe and scanning electron microscopy, respectively. All the quenched ingots from which the studied samples were cut were inhomogeneous in the axial direction. The temperature dependence of the Seebeck coefficient (S), electrical conductivity (σ), and thermal conductivity (κ) was measured from room temperature up to 673 K. The Seebeck coefficient of all In-added Co₄Sb₁₂ materials was negative. When the filler concentration increases, the Seebeck coefficient decreases. The samples with In additions above the filling limit (x = 0.22) show an even lower Seebeck coefficient due to the formation of secondary phases: InSb and CoSb₂. The temperature variation of the electrical conductivity is semiconductor-like. The thermal conductivity of all the samples decreases with temperature. The central region of the In_0.4Co₄Sb₁₂ ingot shows the lowest thermal conductivity, probably due to the combined effect of (a) rattling due to maximum filling and (b) the presence of a small amount of fine-dispersed secondary phases at the grain boundaries. Thus, regardless of the non-single-phase morphology, a promising ZT (S ² σT/κ) value of 0.96 at 673 K has been obtained with an In addition above the filling limit.     

Synthesis and Thermoelectric Properties of the Double-Filled Skutterudite Yb<Subscript>0.2</Subscript>In<Subscript><Emphasis Type="Italic">y</Emphasis></Subscript>Co<Subscript>4</Subscript>Sb<Subscript>12</Subscript>

Filled skutterudites have long been singled out as one of the prime examples of phonon glass electron crystal materials. Recently the double-filling approach in these materials has been attracting increased attention. In this study, Yb_0.2In _y Co₄Sb₁₂ (y = 0.0 to 0.2) samples have been prepared by a simple melting method and their thermoelectric properties have been investigated. The power factor is increased dramatically when increasing the In content, while the lattice thermal conductivity is lowered considerably, leading to a large increase of the ZT value. A state-of-the-art ZT value of 1.0 is attained in Yb_0.2In_0.2Co₄Sb₁₂ at 750 K.     

Thermoelectric Properties of In<Subscript>0.3</Subscript>Ga<Subscript>0.7</Subscript>N Alloys

We report on the experimental investigation of the potential of InGaN alloys as thermoelectric (TE) materials. We have grown undoped and Si-doped In_0.3Ga_0.7N alloys by metalorganic chemical vapor deposition and measured the Seebeck coefficient and electrical conductivity of the grown films with the aim of maximizing the power factor (P). It was found that P decreases as electron concentration (n) increases. The maximum value for P was found to be 7.3 × 10⁻⁴ W/m K² at 750 K in an undoped sample with corresponding values of Seebeck coefficient and electrical conductivity of 280 μV/K and 93␣(Ω cm)⁻¹, respectively. Further enhancement in P is expected by improving the InGaN material quality and conductivity control by reducing background electron concentration.     

Thermoelectric Properties of Co<Subscript>4</Subscript>Sn<Subscript>6</Subscript>Se<Subscript>6</Subscript> Ternary Skutterudites

A ternary ordered variant of the skutterudite structure, the Co₄Sn₆Se₆ compound, was prepared. Polycrystalline samples were prepared by a modified ceramic method. The electrical conductivity, the Seebeck coefficient and the thermal conductivity were measured over a temperature range of 300–800 K. The undoped Co₄Sn₆Se₆ compound was of p-type electrical conductivity and had a band gap E _g of approximately 0.6 eV. The influence of transition metal (Ni and Ru) doping on the thermoelectric properties was studied. While the thermal conductivity was significantly lowered both for the undoped Co₄Sn₆Se₆ compound and for the doped compounds, as compared with the Co₄Sb₁₂ binary skutterudite, the calculated ZT values were improved only slightly.     

Impact of <Emphasis Type="Italic">In Situ</Emphasis> Generated Ag<Subscript>2</Subscript>Te Nanoparticles on the Microstructure and Thermoelectric Properties of AgSbTe<Subscript>2</Subscript> Compounds

A series of ternary (Ag₂Te) _x (Sb₂Te₃)_100−x (x = 44 to 54) bulk materials with in situ generated Ag₂Te nanoparticles were prepared from high-purity elements by combining the melt-quench technique with the spark plasma sintering technique. The influence of the Ag₂Te nanoparticles on the thermoelectric transport properties, and the mechanism of nanoparticle formation were investigated. With increasing x, the concentration of the Ag₂Te nanoparticles increased monotonically, but their diameter remained nearly unchanged. Due to the possible carrier energy filtering effect caused by the Ag₂Te nanoparticle inclusions, the Seebeck coefficient of the sample with x = 50 was two times higher than that of the sample prepared by the melting method. Moreover, notable scattering of mid-to-long wavelength phonons arising from the evenly distributed Ag₂Te nanoparticles led to a large reduction of the lattice thermal conductivity. All these effects led to the enhancement of the ZT value of the x = 50 sample (AgSbTe₂) compared with the single-phase sample (x = 44).     

Thermoelectric Properties of Zintl Compound YbZn<Subscript>2</Subscript>Sb<Subscript>2</Subscript> with Mn Substitution in Anionic Framework

The thermoelectric properties of the Zintl compound YbZn₂Sb₂ with isoelectronic substitution of Zn by Mn in the anionic (Zn₂Sb₂)²⁻ framework have been studied. The p-type YbZn_2−x Mn _x Sb₂ (0.0 ≤ x ≤ 0.4) samples were prepared via melting followed by annealing and hot-pressing. Thermoelectric property measurement showed that the Mn substitution effectively lowered the thermal conductivity for all the samples, while it significantly increased the Seebeck coefficient for x < 0.2. As a result, a dimensionless figure of merit ZT of approximately 0.61 to 0.65 was attained at 726 K for x = 0.05 to 0.15, compared with the ZT of ~0.48 in the unsubstituted YbZn₂Sb₂.     

Improvement of Thermoelectric Power Factor of Hydrothermally Prepared Bi<Subscript>0.5</Subscript>Sb<Subscript>1.5</Subscript>Te<Subscript>3</Subscript> Compared with its Solvothermally Prepared Counterpart

We report on the successful hydrothermal synthesis of Bi_0.5Sb_1.5Te₃, using water as the solvent. The products of the hydrothermally prepared Bi_0.5 Sb_1.5Te₃ were hexagonal platelets with edges of 200–1500 nm and thicknesses of 30–50 nm. Both the Seebeck coefficient and electrical conductivity of the hydrothermally prepared Bi_0.5Sb_1.5Te₃ were larger than those of the solvothermally prepared counterpart. Hall measurements of Bi_0.5Sb_1.5Te₃ at room temperature indicated that the charge carrier was p-type, with a carrier concentration of 9.47 × 10¹⁸ cm⁻³ and 1.42 × 10¹⁹ cm⁻³ for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively. The thermoelectric power factor at 290 K was 10.4 μW/cm K² and 2.9 μW/cm K² for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively.