Crystallographic and dielectric properties of barium-substituted Pb(Mg1/3Ta2/3)O3 ceramics

Ceramic powders of (Ba,Pb)Pb(Mg_1/3Ta_2/3)O₃ were prepared via a B-site precursor route. Crystal symmetries and lattice parameters were determined. Monophasic perovskite was developed after the two-step reaction process, in which the lattice parameters showed linear changes in the entire composition range. Dielectric responses of the ceramics with compositional and frequency changes were investigated. The results were also compared with the (Ba,Pb)(Zn_1/3Ta_2/3)O₃ data.     

Effect of Pb(Fe1/2Nb1/2)O3 modification on dielectric and piezoelectric properties of Pb(Mg1/3Nb2/3)O3-PbZr0.52Ti0.48O3 ceramics

10 mol% Pb(Fe_1/2Nb_1/2)O₃ (PFN) modified Pb(Mg_1/3Nb_2/3)O₃-PbZr_0.52Ti_0.48O₃ (PMN-PZT) relaxor ferroelectric ceramics with compositions of (0.9 − x)PMN-0.1PFN-xPZT (x = 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8 and 0.9) were prepared. X-ray diffraction investigations indicated that as-prepared ceramics were of pure perovskite phase and the sample with composition of x = 0.8 was close to morphotropic phase boundary (MPB) between rhombohedral and tetragonal phase. Dielectric properties of the as-prepared ceramics were measured, and the Curie temperature (T_c) increased sharply with increasing PZT content and could be higher than 300 °C around morphotropic phase boundary (MPB) area. At 1 kHz, the sample with composition of x = 0.1 had the largest room temperature dielectric constant ?_r = 3519 and maximum dielectric constant ?_m = 20,475 at T_m, while the sample with composition of x = 0.3 possessed the maximum dielectric relaxor factor of γ = 1.94. The largest d₃₃ = 318 pC/N could be obtained from as-prepared ceramics at x = 0.9. The maximum remnant polarization (P_r = 28.3 μC/cm²) was obtained from as-prepared ceramics at x = 0.4.     

Electrical properties of Pb(Mg1/3Nb2/3)O3-PbTiO3 ceramics modified with WO3

Ferroelectrics 0.67Pb (Mg_1/3Nb_2/3)O₃-0.33PbTiO₃ (PMN-PT) + x mol% WO₃ (x=0.1, 0.5, 1, 2) were prepared by columbite precursor method. Electrical properties of WO₃-modified ferroelectrics were investigated. X-ray diffraction (XRD) was used to identify crystal structure, and pyrochlore phase were observed in 0.67Pb (Mg_1/3Nb_2/3)O₃-0.33PbTiO₃+2 mol% WO₃. Dielectric peak temperature decreased with WO₃ doping, indicating that W⁶⁺ incorporated into PMN-PT lattice. Lattice constant, pyrochlore phase and grain size contribute to the variation of K_max. Both piezoelectric constant (d₃₃) and electromechanical coupling factors (k_p) were enhanced by doping 0.1 mol% WO₃, which results from the introduction of “soft” characteristics into PMN-PT, while further WO₃ addition was detrimental. We consider that the two factors, introduction of “soft” characteristics and the formation of pyrochlore phase, appear to act together to cause the variation of piezoelectric properties of 0.67PMN-0.33PT ceramics doping with WO₃.     

Comparative investigation of structure and dielectric properties of Pb(Mg1/3Nb2/3)O3-PbTiO3 (65/35) and 10% PbZrO3-doped Pb(Mg1/3Nb2/3)O3-PbTiO3 (65/35) ceramics prepared by a modified precursor method

Relaxor ferroelectric Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ (65/35) and 10% PbZrO₃-doped Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ (65/35) ceramics were both prepared by a modified precursor method, which was based on the high-temperature synthesis of an oxide precursor that contained all the B-site cations for the consideration of B-site homogeneity. The dielectric properties of Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ (65/35) ceramic was more of normal ferroelectric behavior, but the high dielectric constant (?_m = 34,200 at 1 kHz) and piezoelectric constant (d₃₃ = 709 pC/N) were observed for this composition close to the morphotropic phase boundary. Comparatively, introduction of 10% PbZrO₃ into Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃ (65/35) ceramics enhanced the diffuse phase transition as well as the rhombohedral to tetragonal phase transition temperature, while it also kept the high dielectric constant (?_m = 29,600 at 1 kHz) and piezoelectric constant (d₃₃ = 511 pC/N).     

Development of perovskite in Fe-substituted Pb(Zn1/3Ta2/3)O3 and dielectric characteristics

Pb(Zn_1/3Ta_2/3)O₃ ceramics, compositionally modified by the incorporation of Fe to the octahedral lattice sites, were prepared and characterized in terms of perovskite development, dielectric properties, as well as microstructure evolution. The powders of the B-site precursor compositions were synthesized separately and reacted with PbO to form Pb[(Zn_1/3Ta_2/3),(Fe_1/2Ta_1/2)]O₃. The perovskite contents increased continuously with the Fe concentration. The maximum dielectric constant values of the ceramics increased tremendously with the fraction of Fe, whereas the dielectric maximum temperatures were rather insensitive to the compositional change.     

Investigation of BiFeO3 modified PbTiO3-Bi(MgZr)O3-based complex perovskite ceramics

Bismuth containing crystalline solutions of (1 − x)Bi(MgZr)_0.5O₃-xPbTiO₃ (BMZ-PT) and [(BiFeO₃)_y − (BiMg_0.5Zr_0.5)_1−y]_x − [PbTiO₃]_1−x (BMZ-BF-PT) have been developed using conventional ceramic technology. X-ray diffraction analysis reveals that both the systems possess a perovskite structure, in which tetragonal to rhombohedral phase transformation appears for x = 0.55 in BMZ-PT and y = 0.20 in BMZ-BF-PT systems. SEM photographs reveal a uniform grain size distribution in the solid solution matrix with the presence of ferroelectric domains in few of the compositions. Ferroelectric hysteresis (polarization-electric field, P-E) loops reveal that increase in BiFeO₃ in BMZ-PT systems results in a decrease in residual polarization of the system with change and distortion in the shape of the (P-E) loops.     

Growth and electrical performance of Pb(Mg1/3Nb2/3)O3-PbTiO3-Pb(Fe1/2Nb1/2)O3 single crystals

For the first time, we have grown ferroelectric single crystals Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃-Pb(Fe_1/2Nb_1/2)O₃ (PMN-PT-PFN) from the melt by the simple slow cooling process. The chemical composition of the single crystals PMN-PT-PFN (0.59/0.31/0.10) is near the morphotropic phase boundary (MPB). X-ray diffraction (XRD) was used to study phase structure of the as-grown crystals, energy dispersive X-ray spectrometer (EDS) and electron probe micro-analyzer (EPMA) were employed to confirm the chemical composition and element distribution of the as-grown crystals, respectively. The ferroelectric, dielectric and piezoelectric properties of the as-grown PMN-PT-PFN (0.59/0.31/0.10) single crystal oriented along the (0 0 1) axis were measured, which showed that the remnant polarization (P_r), coercive electric fields (E_c), the Curie temperature (T_c) and the piezoelectric coefficient (d₃₃) were 50.2 μC/cm², 13.9 kV/cm, 158 °C and about 1800 pC/N, respectively. All the results indicated that the PMN-PT-PFN (0.59/0.31/0.10) single crystals are promising for applying to field of high frequency.     

Microwave dielectric properties of (Pb1−3x/2Lax)(Mg1/2W1/2)O3

La modified Pb(Mg_1/2W_1/2)O₃ were prepared by solid-state reaction process, and the sintering behavior, microstructure and microwave dielectric properties were investigated by X-ray powder diffraction (XRD), Raman scattering and HP network analyzer in this paper. A series of single phase perovskite type solid solutions with A-site vacancies (Pb_1−3x/2La_x(Mg_1/2W_1/2)O₃ (0 ≤ x ≤ 2/3)) were formed. The solid solution took cubic perovskite type structure (Fm3m) with random distribution of A-site vacancies when 0 < x < 0.5, and tetragonal or orthorhombic structure with the ordering of A-site vacancies when 0.5 ≤ x ≤ 2/3. The dielectric constant and temperature coefficient of resonant frequency decrease with increasing La content. Relatively good combination microwave dielectric properties were obtained for x = 0.56: ?_r = 28.7; Q × f = 18098; and τ_f = −5.8 ppm/°C.     

Diffuse transition and piezoelectric properties of Pb[(Zr1−xTix)0.74(Mg1/3Nb2/3)0.20(Zn1/3Nb2/3)0.06]O3 Ceramics

In this work, the piezoelectric ceramic system of Pb[(Zr_1−xTi_x)_0.74(Mg_1/3Nb_2/3)_0.20(Zn_1/3Nb_2/3)_0.06]O₃, 0.47≤x≤0.57, with composition close to the morphotropic phase boundary, was studied. From the results of X-ray diffraction and piezoelectric measurement, ceramics near x=0.51 were found at the morphotropic phase boundary (MPB) between the tetragonal and pseudocubic perovskite. The planar coupling factor (k_p=0.72) is high at compositions near the MPB, but the mechanical quality factor (Q_m=75) is low. The calculation of the diffuseness of phase transition shows that the region of phase coexistence of this system is broader than that of the ternary system.     

Microstructure and microwave dielectric characteristics of (1 − x)Ba(Zn1/3Ta2/3)O3-xBaTi4O9 ceramics

(1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ (0.1 ≤ x ≤ 0.85) composites are prepared by mixing 1150 °C-calcined BaTi₄O₉ with 1150 °C-calcined Ba(Zn_1/3Ta_2/3)O₃ powders. The crystal structure, microwave dielectric properties and sinterabilites of the (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics have been investigated. X-ray diffraction patterns reveal that BaTi₄O₉, ordered and disordered Ba(Zn_1/3Ta_2/3)O₃ phases exist independently over the whole compositional range. The sintering temperatures of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics are about 1240 - 1320 °C and obviously lower than those of Ba(Zn_1/3Ta_2/3)O₃ ceramics. The dielectric constants (?_r) and the temperature coefficient of resonant frequency (τ_f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of BaTi₄O₉ content. Nevertheless, the bulk densities and the quality values (Q × f) of (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramics increase with the increase of Ba(Zn_1/3Ta_2/3)O₃ content. The results are attributed to the higher density and quality value of Ba(Zn_1/3Ta_2/3)O₃ ceramics, the better grain growth, and the densification of sintered specimens added a small BaTi₄O₉ content. The (1 − x)Ba(Zn_1/3Ta_2/3)O₃-xBaTi₄O₉ ceramic with x = 0.1 sintered at 1320 °C exhibits a ?_r value of 31.5, a maximum Q × f value of 68500 GHz and a minimum τ_f value of 4.1 ppm/°C.     

Synthesis and characterization of 0.65Pb(Mg1/3Nb2/3)O3-0.35PbTiO3 fibers with Pt core

This paper reports the synthesis and electromechanical characterization of 0.65Pb(Mg_1/3Nb_2/3)O₃-0.35PbTiO₃ (PMN-35PT) ceramics and fibers. To prevent the lead loss during the sintering of the fibers, lead-atmosphere was used during the sintering process. As a consequence, it was possible to ensure a good densification of the fiber and a pure perovskite phase. The electromechanical coupling factor and piezoelectric coefficient of the piezoelectric fiber were found to be k₃₁ = 0.20 and d₃₁ = −130 pC/N, respectively. These results are lower than ceramic sample properties (k₃₁ = 0.32 and d₃₁ = −234 pC/N). In order to determine reasons for these lower results in fiber shape sample, density and poling studies were performed. It is shown that fiber shape samples cannot be poled correctly because of the ratio between core and ceramic diameters.     

Crystallographic and dielectric aspects of Pb[(Mg,Zn)1/3Ta2/3]O3 system with 40 at.% Nb substitution

A total of 40 at.% Nb was substituted for Ta in the Pb[(Mg,Zn)_1/3Ta_2/3]O₃ system in order to enhance perovskite development. System powders were prepared by a B-site precursor method. Perovskite formation yields and lattice parameters of the pyrochlore/perovskite structures were determined from X-ray diffraction results. Weak-field low-frequency dielectric responses of the system ceramics were investigated as functions of temperature, composition, and frequency. Phase transition modes reflected in the dielectric constant spectra were further analyzed in terms of diffuseness parameters.     

Improved microwave dielectric properties of B2O3-doped Nd(Co1/2Ti1/2)O3 ceramics with near zero temperature coefficient of resonant frequency

The microwave dielectric properties and the microstructures of Nd(Co_1/2Ti_1/2)O₃ ceramics prepared by conventional solid-state route have been studied. The prepared Nd(Co_1/2Ti_1/2)O₃ exhibited a mixture of Co and Ti showing 1:1 order in the B-site. It is found that low-level doping of B₂O₃ (up to 0.75 wt.%) can significantly improve the density and dielectric properties of Nd(Co_1/2Ti_1/2)O₃ ceramics. Nd(Co_1/2Ti_1/2)O₃ ceramics with additives could be sintered to a theoretical density higher than 98.5% at 1320 °C. Second phases were not observed at the level of 0.25-0.75 wt.% B₂O₃ addition. The temperature coefficient of resonant frequency (τ_f) was not significantly affected, while the dielectric constants (?_r) and the unloaded quality factors Q were effectively promoted by B₂O₃ addition. At 1320 °C/4 h, Nd(Co_1/2Ti_1/2)O₃ ceramics with 0.75 wt.% B₂O₃ addition possesses a dielectric constant (?_r) of 27.2, a Q × f value of 153,000 GHz (at 9 GHz) and a temperature coefficient of resonant frequency (τ_f) of 0 ppm/°C. The B₂O₃-doped Nd(Co_1/2Ti_1/2)O₃ ceramics can find applications in microwave devices requiring low sintering temperature.     

(5 − x)BaO-xMgO-2Nb2O5 ceramics prepared using a reaction-sintering process

(5 − x)BaO-xMgO-2Nb₂O₅ (x = 0.5 and 1; 5MBN and 10MBN) microwave ceramics prepared using a reaction-sintering process were investigated. Without any calcinations involved, the mixture of BaCO₃, MgO, and Nb₂O₅ was pressed and sintered directly. MBN ceramics were produced after 2-6 h of sintering at 1350-1500 °C. The formation of (BaMg)₅Nb₄O₁₅ was a major phase in producing 5MBN ceramics, and the formation of Ba(Mg_1/3Nb_2/3)O₃ was a major phase in producing 10MBN ceramics. As CuO (1 wt%) was added, the sintering temperature dropped by more than 150 °C. We produced 5MBN ceramics with these dielectric properties: ?_r = 36.69, Qf = 20,097 GHz, and τ_f = 61.1 ppm/°C, and 10MBN ceramics with these dielectric properties: ?_r = 39.2, Qf = 43,878 GHz, and τ_f = 37.6 ppm/°C. The reaction-sintering process is a simple and effective method for producing (5 − x)BaO-xMgO-2Nb₂O₅ ceramics for applications in microwave dielectric resonators.     

Synthesis of La(Mg0.5Ti0.5)O3 ceramics for microwave applications

La(Mg_0.5Ti_0.5)O₃ ceramics were prepared by a non-conventional chemical route, which was based on the Pechini method. For the synthesis of La(Mg_0.5Ti_0.5)O₃ powders, special attention was paid to calcination and milling conditions. Powder morphology and composition were evaluated. Fine La(Mg_0.5Ti_0.5)O₃ powders were obtained at lower temperatures than by conventional methods. Sintering under different conditions was also tested. Dense La(Mg_0.5Ti_0.5)O₃ ceramics were obtained at lower temperatures showing a single phase composition and a homogeneous microstructure. Preliminary dielectric characterization at microwave frequencies was also performed.     

Effects of Mn doping on the structure and electrical properties of high-temperature BiScO3-PbTiO3-Pb(Zn1/3Nb2/3)O3 piezoelectric ceramics

The effects of Mn addition on the structure, ferroelectric, and piezoelectric properties of the 0.35BiScO₃-0.60PbTiO₃-0.05Pb(Zn_1/3Nb_2/3)O₃ ceramics were studied. The results demonstrate that the addition of small amounts of Mn did not cause a remarkable change in crystal structure, but resulted in an evident evolution in microstructure and ferro-piezoelctric properties. The addition of Mn can induce combinatory “hard” and “soft” piezoelectric characteristics due to aliovalent substitutions. The optimal electrical properties are obtained in the 0.25 mol% Mn-doped composition with a high Curie temperature, indicating that Mn doping contributes to the electrical properties of the ceramics. It can be expected that the improved piezoelectric material can be a promising candidate for high-temperature piezoelectric applications.     

Dielectric properties of (1−x)(Mg0.95Co0.05)TiO3-xCaTiO3 ceramic system at microwave frequency

The microwave dielectric properties and the microstructures of the (1−x)MgTiO₃-xCaTiO₃ ceramic system were investigated. With partial replacement of Mg by Co, dielectric properties of the (1−x)(Mg_0.95Co_0.05)TiO₃-xCaTiO₃ ceramics can be promoted. The microwave dielectric properties are strongly correlated with the sintering temperature. At 1275°C, the 0.95(Mg_0.95Co_0.05)TiO₃-0.05CaTiO₃ ceramics possesses excellent microwave dielectric properties: a dielectric constant ε_r of 20.3, a Q×f value of 107 000 ( at 7 GHz) and a τ_f value of −22.8 ppm/°C. By appropriately adjusting the x value in the (1−x)(Mg_0.95Co_0.05)TiO₃-xCaTiO₃ ceramic system, zero τ_f value can be achieved. With x=0.07, a dielectric constant ε_γ of 21.6, a Q×f value of 92 000 (at 7 GHz) and a τ_f value of −1.8 ppm/°C was obtained for 0.93(Mg_0.95Co_0.05)TiO₃-0.07CaTiO₃ ceramics sintered at 1275°C for 4 h.     

Dielectric relaxation in complex perovskite oxide In(Ni1/2Zr1/2)O3

The dielectric study of indium nickel zirconate, In(Ni_1/2Zr_1/2)O₃ (INZ) synthesized by solid state reaction technique is performed in a frequency range from 500 Hz to 1 MHz and in a temperature range from 303 to 493 K. The X-ray diffraction analysis shows that the compound is monoclinic. A relaxation is observed in the entire temperature range as a gradual decrease in ?′(ω) and as a broad peak in ?″(ω) in the frequency dependent real and imaginary parts of dielectric constant, respectively. The frequency dependent electrical data are analyzed in the framework of conductivity and electric modulus formalisms. The frequencies corresponding to the maxima of the imaginary electric modulus at various temperatures are found to obey an Arrhenius law with activation energy of 0.66 eV. The Cole-Cole model is used to study the dielectric relaxation of INZ. The scaling behaviour of imaginary part of electric modulus suggests that the relaxation describes the same mechanism at various temperatures. The frequency dependent conductivity spectra follow the universal power law.     

Solid state and solution synthesis of Ba(Mg1/3Ta2/3)O3: A comparative study

Ba(Mg_1/3Ta_2/3)O₃ [BMT] dielectric ceramics are prepared by solid state (one step, two step and molten salt synthesis) and wet chemical methods (precipitation, citrate gel and sol-gel). The formation mechanism of BMT in each synthesis technique is discussed. The formation temperature and particle size of the formed BMT were found to be much lesser (in nanometer range) for solution synthesized powders. It is found that synthesis by sol-gel method resulted in the formation of ultra pure nanopowders of BMT at about 600 °C with average crystallite size of about 18 nm where as in solid state synthesis the formation of BMT was formed at about 1100 °C with average crystallite size of 220 nm. On sintering these powders, densification and grain growth of the chemically derived powders were found to be lower than that of solid state synthesized BMT powder. This has resulted in a slight decrease in density and microwave dielectric properties of the solution synthesized BMT samples. It is found that the microwave dielectric properties improved with increase in the average grain diameter of the sintered BMT ceramics.