低相变场细电滞回线(Pb,La)(Zr,Sn,Ti)O_3反铁电陶瓷的研究

对远离反铁电-铁电准同型相界的(Pb,La)(Zr,Sn,Ti)O3反铁电组分进行Ba2+掺杂,制备出了细电滞回线、低相变电场的反铁电陶瓷,反铁电-铁电相变电场仅为1.5kV/mm,电场回滞减小到0.2kV/mm,并且极化强度和应变量随电场增大几乎呈线性变化,可通过调节电场大小得到不同的应变量,有利于开辟这类材料新的应用领域。     

脉冲电场诱导的相变研究

反铁电陶瓷材料在电场诱导下发生反铁电-铁电相变.为了研究快速电场诱导相变,诱导电场选择高压脉冲电源产生的脉冲电场.反铁电陶瓷选用Pb(Zr,Sn,Ti)O3相图中位于反铁电-铁电相界附近,正向相变电场小于40kV/cm的锆锡钛酸铅.脉冲电源输出波形为2.7 μs电压脉冲,测量陶瓷样品两端的电压波形与所通过的电流波形,作出正向半周期的"脉冲电滞回线".可以看到反铁电陶瓷在脉冲电场诱导下发生了相变.     

掺铌Pb(Zr,Sn,Ti)O3反铁电-铁电转换电场的研究

研究了掺铌PZST反铁电陶瓷中组份和温度对诱导反铁电－铁电相变转换电场的影响,测定了Pb0.99Nb0.02((Zr0.80Sn0.20)1-yTiy)0.98O3系中正向转换电场EF与组份y(Ti)的关系和电极化前后的反铁电／铁电相界。实验测量结果显示,某组份y(Ti)的反映电－铁电转换强度大小取决于该组份与铁电／铁电相界组份的差距。在Pb0.99Nb0.02((Zr0.80Sn0.20)1-yTiy)0.98O3系中随着试样温度升高,反向转换电场EB保持不变,正向转换电场EF和电滞△E降低。这一现象表明温度有助于降低反铁电－铁电相变的应能使得电场诱导反铁电－铁电相变容易进行,因此可以采用加热电极化方法来降低极化电场强度。     

电场诱导PZST陶瓷反铁电-铁电相变

研究了ＰＺＳＴ陶瓷电场诱导反铁电－铁电相变。当外加电场大于相变临界参数ＥＡＦＥ－ＦＥ时,样品由反铁电态诱导为铁电态,并在宏观性能上产生突变：极化强度和纵向应变分别由零跃变到大约３０μＣ／ｃｍ＾２和０．３％,介电常数下降５０％。利用直流偏压原位Ｘ射线衍射表征为相变时晶格结构的变化,结果表明,伴随着相变的发生,晶格结构由反铁电四方相转变为铁电三方相。     

(Na0.8K0.2)0.5Bi0.5TiO3陶瓷的介电压电性能

研究了(Na0.8K0.2)0.5Bi0.5TiO3陶瓷的介电和压电性能,发现陶瓷从室温到500℃温度范围的介电谱中存在两个介电峰,电滞回线显示第一个介电峰由铁电-反铁电相变引起的,温度继续升高,反铁电相由宏畴变为微畴,微畴向顺电相转变导致了第二个介电峰,该峰对应的相变为弥散型相变.室温下陶瓷具有较高的剩余极化强度Pr=29.4μC/cm2和相对低的矫顽电场Ec=2.8kV/mm,极化后的陶瓷显示出较高的压电常数d33=120pC/N和机电耦合系数Kp=28.5%,以及高的频率常数Nφ=2916Hz.m,120℃具有最小的谐振频率温度系数.     

温度场和电场调控硅基反铁电厚膜相变电流特性研究

采用溶胶-凝胶技术,在Pt(111)/Ti/SiO2/Si衬底上制备了高(100)取向生长、表面平整且结构致密的(Pb,La)(Zr,Ti)O3反铁电厚膜,研究了温度场和电场对(Pb,La)(Zr,Ti)O3反铁电厚膜电学性能的影响。实验结果表明反铁电厚膜在温度场和电场作用下发生反铁电相、铁电相和顺电相的相互转变,随外加电场增加,反铁电-铁电相变温度逐渐减小,介电常数峰值由2410减小到662,相变电流密度值由2.21×10-7A/cm2增大到8.52×10-7 A/cm2;随外加温度场增加,反铁电-铁电相变电场强度逐渐减小,饱和极化强度由39μC/cm2减小到31μC/cm2,相变电流密度值由2.89×10-5 A/cm2减小到8.8×10-6 A/cm2,温度场和电场可实现对反铁电厚膜相变电流效应的有效调控。     

(Pb0.97La0.02)(Zr0.66Sn0.23Ti0.11)O3纳米粉及PLZST/PVDF复合材料的制备和性能

采用溶胶-水热法合成了PLZST反铁电陶瓷纳米粉,并采用XRD,SEM和SAXS对其相组成、形貌和粒度进行了分析.PLZST晶相单一,纯度高,分散时为纳米球形,团聚为微米六面体,具自组装倾向.用溶解-热压法制备了不同比例的PLZST/PVDF 0-3型压电复合材料.研究了组成、电极以及极化电压对其介电性能的影响.结果表明质量比31的PLZST/PVDF复合材料在110℃,极化电压为15kV/mm的条件下极化0.5h,可使其相对介电常数从47.7增大到56.0.用SEM观察其微观组织可知,PLZST陶瓷粒子在PVDF聚合物基体中分散很均匀,但存有少量气孔.     

PZT陶瓷的韧性和温度与相变和极化的关系

研究了ＰＺＴ压电陶瓷铁电相变前后的断裂韧性和强度。分析了极化电场与外应力的相对取向对力学性能的影响。探讨了力学性能与极化层导致的畴转向和显微结构变化之间的关系。结果表明，断裂韧性和强度都随着温度的升高而下降至居里点处的低限值，然后略有回升。由于铁电相的热、弹性各向异性引起的内应力和极化残余应力，以及表面应力等的存在，强度比韧性随温度变化的幅度更陡。     

Ba0.04Bi0.48Na0.48TiO3-SrTiO3陶瓷微结构和储能性能

采用传统固相反应法制备了一种无铅储能铁电陶瓷(1-x)Ba0.04Bi0.48Na0.48TiO3-xSrTiO3 (x=0.27、0.28、0.30、0.32、0.34、0.36),研究了该陶瓷体系的微观结构、铁电、介电和电导率特征.所有陶瓷均形成了钙钛矿结构固溶体,晶粒尺寸均匀且致密.各陶瓷所得铁电曲线趋于双电滞回线,呈现反铁电特征,剩余极化强度较小,击穿强度高.当x=0.34时,可获得0.977J/cm3的较优储能值,陶瓷弥散程度高,表现为典型的弛豫特性.此含量对应低频下陶瓷的离子电导率为2.4×10-8 S/cm,电子电导率为6.02×10-13 S/cm,表明离子电导居于主导地位.     

Na0.5 Bi0.5 TiO3-K0.5 Bi0.5 TiO3系铁电体的相变研究

研究了(Na1-xKx)0.5Bi0.5TiO3体系x分别为0、0.08、0.16和0.20时陶瓷不同频率下的介电温谱,发现材料为弛豫型铁电体,材料的介电谱在室温到500℃的温度范围内存在一个介电常数-温度"台阶",一个介电常数-温度峰和一个介电损耗-温度峰,通过分析陶瓷不同温度下的电滞回线验证陶瓷在升温过程中产生了铁电-反铁电-顺电相变,采用铁电体成分起伏理论和内电场理论解释了这类弛豫型铁电体相变的原因.     

Optical properties of the metals Al, Co, Cu, Au, Fe, Pb, Ni, Pd, Pt, Ag, Ti, and W in the infrared and far infrared

Infrared optical constants collected from the literature are tabulated. The data for the noble metals and Al, Pb, and W can be reasonably fit using the Drude model. It is shown that -epsilon1(omega) = epsilon2(omega) approximately omega(2)(p)/(2omega(2)(tau)) at the damping frequency omega = omega(tau). Also -epsilon1(omega(tau)) approximately - (1/2) epsilon1(0), where the plasma frequency is omega(p).     

p,V, T and derived thermodynamic data for toluene,trichloromethane, dichloromethane,acetonitrile, aniline,and n-dodecane

Experimentally determined p,V,T data are reported for toluene, trichloromethane, dichloromethane, acetonitrile, aniline, and n-dodecane at 278, 288, 298, 313, and 323 K, except for dichloromethane, for which the highest temperature was 298 K. At each temperature, measurements were done at pressures up to about 280 MPa or (for aniline and n-dodecane) at a lower pressure slightly below the freezing pressure at the temperature of measurement. Values of the isobaric expansivity isothermal compressibility and (for toluene, trichloromethane, dichloromethane, and acetonitrile) internal pressure, derived from the p,V,T data, are presented.     

微波消解-ICP-AES法测定茶叶中钾、钠、磷、硫、铁、锰、铜、锌、钙、镁方法研究

通过优化微波消解条件,并根据不同元素性质,调谐ICP-AES工作条件至最佳,实现了茶叶中K、Na、P、S以及Fe、Mn、Cu、Zn、Ca、Mg 10种元素的同时测定。10种元素测定结果 RSD%为0.67(Cu)～5.57(Na),回收率为84.0%(Na)～101.5%(Fe),检出限为0.001(Mn)～0.029(S)μg·g-1,表明该方法准确可靠,能够满足茶叶中K、Na、P、S、Fe、Mn、Cu、Zn、Ca、Mg分析要求。     

抓管理重服务求可靠要效益--记广西计量测试研究所国家实验室认可工作

我所2001年9月份顺利地通过了中国实验室认可委紧张而严格的评审,得到了权威机构认可,成为西南地区较早通过国家实验室认可的省级计量校准机构.在建立质量体系、运行质量体系走过了艰辛之路,我们将全所职工的艰辛之路介绍给大家,希望能给将要申请认可的实验室得以参考.     

标准·质量·认证·会议(英文)

Standards IGRS:First Complete International Standards System in 3C Collaboration Field After ISO and IEC released three international standards of Intelligent Grouping and Resource Sharing (IGRS) including Core Protocol,File Communication Framework and Device Validation,four standards of IGRS,Application Framework,Basic Application,Service Types and Devices Types,got approved with high passing rate in the voting of Final Draft International Standard (FDIS) and will be officially issued soon around the world. It symbolizes that all     

Dry Autoclaving for the Nanofabrication of Sulfides,Selenides, Borides,Phosphides, Nitrides,Carbides, and Oxides

This review compiles various nanostructures fabricated by a distinct “dry autoclaving” approach, where the chemical reactions are carried out without solvents; above the dissociation temperature of the chemical precursor(s) at elevated temperature in a closed reactor. The diversity to fabricate carbides (SiC, Mo₂C, WC), oxides (VOx‐C, ZnO, Eu₂O₃, Fe₃O₄, MoO₂), hexaborides (LaB₆, CeB₆, NdB₆, SmB₆, EuB₆, GdB₆), nitrides (TiN, NbN, TaN), phosphides (PtP₂, WP), sulfides (ZnS, FeS/C, SnS/C, WS₂, WS₂/C), and selenides (Zn_1‐xMn_xSe/C, Cd_1‐xMn_xSe/C), with various shapes and sizes is accounted with plausible applications. This unique single‐step, solvent‐free synthetic process opens up a new route in the growing nanomaterials science; owing to its considerable advantages on the existing approaches.