团状模塑料/丁苯橡胶/甲基乙烯基硅橡胶绝缘复合材料的性能研究

制备玻璃纤维团状模塑料(DMC)/丁苯橡胶(SBR)/甲基乙烯基硅橡胶(MVQ)绝缘复合材料,并对其性能进行研究。结果表明:与采用顺丁橡胶、丁腈橡胶、丙烯酸酯橡胶和三元乙丙橡胶作相容剂相比,采用SBR作相容剂可以改善DMC和MVQ间的相容性,提高DMC/SBR/MVQ绝缘复合材料的性能,DMC/SBR/MVQ的最佳配比为60/25/75;DMC/SBR/MVQ绝缘复合材料最佳混炼工艺为分步法加入白炭黑、分批法加入DMC,分别将MVQ和SBR进行混炼,再将两种混炼胶共混均匀;最佳硫化条件为180℃/1.2 MPa×15 min。在此条件下制备的DMC/SBR/MVQ绝缘复合材料的电绝缘性能良好,阻燃性能达到电缆绝缘材料的要求。     

团状模塑料增强硅橡胶绝缘材料性能的影响因素

以甲基乙烯基硅橡胶(MVQ)为基质、团状模塑料(DMC)为增强剂、丁苯橡胶(SBR)为相容剂制备DMC/SBR/MVQ绝缘复合材料,考察了SBR和DMC用量对材料力学性能、相容性、绝缘性的影响,并对材料进行了动态热机械分析、傅里叶变换红外光谱分析。结果表明,SBR作为相容剂,可以改善DMC与MVQ的相容性,提高绝缘复合材料的力学性能,在DMC/SBR/MVQ(质量比)为60/25/75时,力学性能最佳。不同质量比下的DMC/SBR/MVQ绝缘复合材料的体积电阻率都在4.8×1012Ω·m以上,绝缘性能良好;当三者质量比为60/25/75时,材料的体积电阻率最高,绝缘性最好。DMC的加入提高了SBR/MVQ绝缘复合材料的耐热性能。     

DMC/白炭黑/MVQ复合材料的制备及性能研究

采用机械共混法制备团状模塑料(DMC)/白炭黑/甲基乙烯基硅橡胶(MVQ)复合材料,并对其性能进行研究.结果表明,DMC/白炭黑/MVQ复合材料具有良好的物理性能和耐热空气老化性能,其优化配方为MVQ 100,DMC 70,白炭黑 30,氧化锌 5,硬脂酸 2,防老剂D 1,三氧化二铁 2,硫化剂DCP 6,硫黄 1,促进剂M 1;适宜的硫化条件为170 ℃/10 MPa×30 min.偏光显微镜分析表明,DMC与MVQ的相容性良好.     

硅橡胶/丁苯橡胶并用胶的制备及表征

针对硅橡胶具有较高的耐热性,但力学性能差;丁苯橡胶(SBR)力学性能较好,但粘性较差;提出了将硅橡胶与SBR共混,制成共混材料;采用偏光显微镜、傅里叶变换红外光谱、差示扫描量热仪以及力学性能、热老化性能测试手段,研究了甲基乙烯基硅橡胶(MVQ)/SBR共混体系的并用比(质量比)、硫化工艺参数以及顺丁橡胶(BR)的加入对力学性能、耐热老化性能和相容性的影响。结果表明:MVQ与SBR最佳配比为30/70,白炭黑为45份;最佳硫化工艺参数为170℃×10 MPa×30 min。MVQ/SBR并用胶的玻璃化温度为-20℃,MVQ和SBR具有较好的相容性。     

碳纤维增强硅橡胶复合材料制备

由于硅橡胶具有较好的耐热性但力学性能比较差,本文用高性能的碳纤维作增强剂,硅橡胶（MVQ）作基相及偶联剂作为相容剂制备了碳纤维/硅橡胶复合材料。通过力学性能和热老化测试,确定碳纤维的用量。用偶联剂作相容剂研究了偶联剂对硅橡胶和碳纤维相容性影响;通过傅里叶变换红外光谱（FTIR)和扫描电镜(SEM)分析了碳纤维和硅橡胶交联结构和相容性。结果显示,制备了碳纤维/硅橡胶复合材料的最佳配方为硅橡胶 100份,碳纤维 12份,KH-550 2.5份。碳纤维增强硅橡胶的最佳硫化条件为：温度 175℃,压力为10MPa,时间为30min。由扫描电镜和红外光谱分析,进一步论证了用KH-550处理的比没有处理及用Si69处理的碳纤维与硅橡胶的混合相容性好。     

固相法改性淀粉／炭黑／丁苯橡胶复合材料的制备与性能研究

采用固相法制备了淀粉接枝马来酸酐（MAH）和丙烯酸丁酯（BA）的共聚物Starch-gMAH／BA（SMB）。采用机械共混法用15phr的改性淀粉（SMB）代替等量的炭黑（CB）,制备了改性淀粉／炭黑／丁苯橡胶复合材料（SMt3／CB／SBR）,研究了复合材料的力学性能、热氧老化性能、动态力学性能以及微观形态。结果表明,SMB／CB／SBR复合材料的力学性能优于未改性淀粉／CB／SBR复合材料,拉伸强度及扯断伸长率等性能优于SBR／CB复合材料;且SMB／CB／SBR复合材料具有更好的耐热氧老化性能;与SBR／CB复合材料相比,SMB／CB／SBR复合材料具有更低的滚动阻力;微观形态显示,淀粉经改性后粒子尺寸减小,在SBR基体中的分散性得到改善,与SBR基体的相容性得到提高。     

碳纤维/硅橡胶/氟橡胶复合材料制备及表征

以硅橡胶（MVQ）/氟橡胶（FKM）并用胶为基相、碳纤维（CF）为增强相制备CK/MVQ/FKM复合材料。最佳配方为：FKM混炼胶　90,MVQ混炼胶　10,白炭黑　20,硅烷偶联剂KH590　2.5,碳纤维（纤维长度为12 mm）　8;其中FKM混炼胶配方为FKM　100,氢氧化钙　6,氧化镁　3,3#硫化剂　3;MVQ混炼胶配方为硅橡胶　100,氧化锌　3,三氧化二铁　1,防老剂D　1,促进剂M　1.5,硫化剂DCP　5。最佳一段和二段硫化条件分别为170 ℃/10 MPa×30 min和200 ℃（常压）×2 h。     

隔热填料对硅橡胶性能的影响

以甲基乙烯基硅橡胶为基体(MVQ),二氧化硅气凝胶(Aerogels)、云母粉(Mica)和空心玻璃微珠(HGB)为隔热填料,制备了MVQ/Aerogels、MVQ/Mica、MVQ/HGB 3种硅橡胶复合材料,并研究了隔热填料对硅橡胶性能的影响。结果表明,复合材料的隔热效果为MVQ-Mica相似文献   

硅橡胶基高导电复合材料的制备及其性能研究

以导电炭黑、片状微米银、碳纳米管为填料制备甲基乙烯基硅橡胶（MVQ）基高导电复合材料并研究其性能。结果表明：导电炭黑在MVQ中的逾渗阈值为8～12份（体积分数3.33%～4.92%）,导电炭黑用量为12份时导电炭黑/MVQ复合材料的交联网络最稳定;在添加12份导电炭黑的基础上添加150份片状微米银时,导电炭黑/片状微米银/MVQ复合材料在50%应变后的导电网络恢复程度最大;导电炭黑/片状微米银/碳纳米管/MVQ复合材料在50%应变后的电导率为1.2×104 S·m-1,电导率变化率为18%。     

玄武岩短纤维/硅橡胶/氟橡胶复合材料制备及表征

以氟橡胶(FMK)和硅橡胶(MVQ)为基体,用玄武岩短纤维作增强相制备了玄武岩短纤维/MVQ/FMK复合材料,研究了MVQ/FMK的最佳并用比,玄武岩短纤维的长径比、用量及表面处理,二段硫化条件对复合材料力学性能的影响,用扫描电镜(SEM)和红外光谱(IR)分析表征了玄武岩短纤维和FMK/MVQ的相容性。结果表明,MVQ/FMK(质量比)为10/90时,并用胶的力学性能最好,使用长径比为1 800的玄武岩短纤维7份时,玄武岩短纤维/MVQ/FMK复合材料的力学性能最佳,最佳的二段硫化条件是200℃×6h。SEM和IR分析得出γ-巯丙基三甲基硅烷(KH-590)、双(γ-三乙氧基硅基丙基)四硫化物(Si69)在玄武岩短纤维表面发生了明显的化学反应,而且KH590处理的玄武岩短纤维与MVQ/FMK的相容性较好。     

Enhancement in electrical and thermal performance of high-temperature vulcanized silicone rubber composites for outdoor insulating applications

High-temperature vulcanized silicone rubber composites are highly desirable as outdoor insulating materials due to their immense thermal and electrical performance. The aim of this work is to study the role of co-combined fillers (modified fumed silica [MFS], titanium dioxide [TiO₂], with graphene [G]) on electrical and thermal properties of silicone rubber (S) composites. The dielectric response of S/MFS_10 phr and S/TiO₂_20 composites tailored with 2 phr G was characterized by broadband dielectric spectroscopy. The hybrid filler/composites were found to show higher thermal stability when 2 phr G was added. In addition, a low quantity of G filler was found to slightly increase the AC dielectric breakdown strength of the S/MFS_10 and S/TiO₂_20, where an improvement of 3 and 5% was found, respectively. Several steps were observed in the thermal decomposition of the S rubber composites by thermogravimetric analysis-Fourier-transform infrared spectroscopy. Our findings revealed great potentials for fabricating hybrid-filler/silicone rubber composites with enhanced electrical and thermal properties for outdoor insulating applications.     

Formulation and morphology of kaolin-filled rubber composites

In the present work the formulation and morphology of novel kaolin-filled rubber composites were investigated. The kaolin-filled rubber composites were obtained by filling rubbers such as natural rubber (NR), styrene–butadiene rubber (SBR), polybutadiene rubber (ER), nitrile butadiene rubber (NBR), ethylene propylene diene monomer (EPDM), chloroprene rubber (CR) and methyl vinyl silicon rubber (MVQ). The best formulation of filled rubbers was determined by determining the mechanical and thermal properties of the composites. Structural characterization was carried out by using infrared spectroscopy (IR) and a polarizing light microscope (PLM). The kaolin/rubber composites have outstanding mechanical and thermal properties except elongation at break, and good compatibility. The best formulation of kaolin filled rubbers is respectively 40 parts per hundred rubber (phr), 40 phr, 50 phr, 40 phr, 50 phr, and 50 phr for NR, SBR, BR, NBR, EPDM and CR. Kaolin can replace silica in the specific rubber products, and is suitable to reinforce more steric rigid rubber.     

Effect of KH550 on the Preparation and Compatibility of Carbon Fibers Reinforced Silicone Rubber Composites

Silicone rubber has good heat resistance, but its mechanical properties are poor. To improve the mechanical properties of the silicone rubber, the carbon fiber / silicone rubber composites were prepared in this paper, in which the silicone rubber was used as the matrix, the high-performance carbon fiber (CF) treated with coupling agent is used as the reinforcement. The best composite formulation, the types and content of coupling agent are determined by testing mechanical properties of the composites. The morphology structures of the composites were observed by scanning electron microscope (SEM), the compatibility between carbon fiber and silicone rubber was studied by infrared spectrum analysis (IR), dynamic thermal mechanical analysis (DMA) and X-ray photoelectron spectroscopy (XPS). The results show that the best composite formulation is silicone rubber of 100 phr, carbon fiber of 12 phr, coupling agent KH550 of 2.5 phr. The best first curing conditions are at 175 ^°C under 10 MPa for 30 min, the postcuring conditions are at 200 ^°C for 2h. The compatibility between carbon fiber treated with KH550 and silicon rubber is the best by SEM, IR, DMA and XPS analysis, and confirm that the coupling agent KH550 plays a compatilizer role in the preparation process of the carbon fiber/silicone rubber composites.     

硅橡胶/有机改性蒙脱土纳米复合材料的性能研究

用熔体插层法制备甲基乙烯基硅橡胶(MVQ)/有机改性蒙脱土(OMMT)纳米复合材料并研究其微观结构和性能。结果表明:OMMT改性剂疏水性从优到劣的顺序为I.44P,I.30P,Bengel434,I.44P和I.30P在MVQ中的分散性优于Bengel434;MVQ/OMMT纳米复合材料的物理性能和热稳定性从优到劣的顺序为MVQ/I.44P,MVQ/I.30P,MVQ/Bengel434纳米复合材料;添加40份I.44P的MVQ/I.44P纳米复合材料的100%定伸应力、拉伸强度和撕裂强度比纯胶有较大提高。     

气相白炭黑对氟橡胶／硅橡胶共混胶性能的影响

采用气相白炭黑补强氟橡胶／硅橡胶共混胶。研究了气相白炭黑的用量和比表面积对氟橡胶／硅橡胶共混胶的力学性能、耐热老化性能和耐油性能的影响,并采用SEM观察了共混硫化胶的拉伸断面形貌。研究表明,随着气相白炭黑的用量从0份增加到50份,气相白炭黑的比表面积从120m^2·g^-1增大到380m^2·g^-1,共混胶的力学性能和耐油性能提高,而耐热老化性能下降;当气相白炭黑用量为40份,且比表面积为220m^2·g^-1时,共混硫化胶具有较好的综合性能。SEM照片表明,随着气相白炭黑用量增大,其在氟橡胶／硅橡胶共混胶中的分散均匀性下降;当气相白炭黑比表面积为220m^2·g^-1时,气相白炭黑的分散性较好。     

丁苯橡胶接枝马来酸酐增容丁苯橡胶/蛭石复合材料的制备

通过力化学接枝反应制得丁苯橡胶接枝马来酸酐,用傅里叶变换衰减全反射红外光谱对接枝物进行了定性表征。将所制备的丁苯橡胶接枝马来酸酐应用于丁苯橡胶/蛭石复合材料体系中,研究了膨胀蛭石和接枝单体马来酸酐的用量对复合材料性能的影响,并通过电子扫描显微镜观察了复合材料内部的微观结构。实验结果表明:当接枝单体用量为6phr、膨胀蛭石用量为15phr时,复合材料综合性能较好。适量丁苯橡胶接枝马来酸酐的生成,有利于改善丁苯橡胶与膨胀蛭石两相间的界面结合。     

SMC晶须在丁苯橡胶中的应用

对硅镁钙晶须（SMC晶须）在丁苯橡胶（SBR）中的应用进行了研究,考察了晶须用量（0～50phr）对胶料的硫化特性和硫化胶的力学性能的影响,并与常用的填料白炭黑（WCB）和碳酸钙（CaCO3）进行了比较。实验结果表明：SMC晶须对SBR有促进硫化作用;SMC晶须对SBR具有一定的补强作用,拉伸强度随着晶须用量的增加而增大;用量相同时,SMC晶须填充的复合材料硬度和撕裂强度与WCB填充的相当,300%定伸应力比WCB填充的高,拉伸永久变形比WCB小得多;SMC晶须补强效果远优于CaCO3。     

酚醛树脂对淀粉/SBR复合材料结构和性能的影响

将自制的间苯二酚甲醛树脂（RF）用于改性淀粉糊，制备了原位改性的淀粉／SBR复合材料．考察了RF用量对复合材料微观结构及各项性能的影响。研究表明，添加少量（0．3份）RF可对复合材料的性能产生较明显的影响；随着RF用量的增加，复合材料的定伸应力、拉伸强度、撕裂强度进一步提高．且当用量在1．2份左右时．其综合增强效应可达到最佳效果。     

高岭土填充橡胶共混物的性能及表征

以一种高岭土为增强相,分别填充天然橡胶、丁苯橡胶、顺丁橡胶、丁腈橡胶、三元乙丙橡胶、氯丁橡胶和硅橡胶,制备高岭土/橡胶复合材料,通过力学和热老化性能测试、红外光谱和偏光显微镜测试分析,确定了高岭土在各种橡胶中填充的最佳配比,研究高岭土的用量对橡胶力学性能、热老化性能和相容性上的影响,并与白炭黑填充橡胶进行比较。实验表明,除扯断伸长率外,高岭土/橡胶具有优异的力学和耐热性能,高岭土与橡胶有较好的相容性,且适合刚性橡胶的补强。