AZ31镁合金的热挤压组织与力学性能分析

对常用变形镁合金AZ31进行了热挤压试验,制备出了四种规格的挤压材;观察了挤压前后镁合金的组织变化,并对挤压板材、棒材的力学性能进行了测试。研究结果表明:经过热挤压后,镁合金的晶粒得以细化,同时力学性能得到较大的提高,屈服强度达到200 N/mm2-270 N/mm2,抗拉强度达到300 N/mm2,伸长率在18%左右。     

变形态Mg-Nd合金的组织转变和拉伸性能特征

研究不同变形条件对Mg-2.2Nd-0.5Zn-0.5Zr合金室温拉伸性能和组织的影响.经过不同条件的热挤压变形后,该合金的强度和延性都有不同程度的增加,屈强比从0.58提高到0.87左右.固定变形温度时,强度随变形速率增大而降低,延性反之.固定变形速率时,升高变形温度则强度降低,延性增加.弥散于晶界的Mg9Nd化合物细化了晶粒.变形态Mg-Nd合金的高温超塑拉伸研究发现,375℃是该合金的最佳超塑变形温度,应变速率在1×10-2s-1时,延伸率达到329%;当变形速率提高到2×10-2s-1时,该合金的延伸率仍可达到213%.分析不同真应变下的组织发现,在变形初期发生动态再结晶,晶粒得到破碎而变得细小,随着变形程度的增加,晶粒长大程度较小.在变形后的断口形貌中发现,Mg-Nd合金的超塑变形机制为晶界滑移控制下的孔洞连接协调机制.     

挤压速度和电磁铸造锭坯对AZ31镁合金板材组织和性能影响

文章研究挤压条件下挤压速度和电磁铸造锭坯对挤压态AZ31镁合金板材组织和性能的影响。研究结果发现,挤压速度比较低时,板材晶粒尺寸小,板材的表面质量比较好;随着挤压速度的降低,抗拉强度、屈服强度和延伸率都有一定的提高。由于镁合金是HCP的晶体结构,同时对挤压速度非常敏感,对变形均匀性影响比较大,因此造成挤压板材的内外晶粒大小不均。在电磁场的作用下,溶质在晶内的固溶度增大,同时晶粒大小也比常规铸造的细小,因此电磁铸造的锭坯经挤压机挤压后,挤压板材的晶粒尺寸比较细小,且强度和塑性都有所提高。     

Microstructure and tensile properties of magnesium alloy modified by Si/Ca based refiner

Microstructure and mechanical properties of pure magnesium and AZ31 alloy with Ca/Si based refiner addition were investigated. The results indicate that addition of Ca/Si based refiners to pure magnesium and AZ31 alloy results in remarkable microstructure refinement. With proper amount of refiner addition, the grain size in as cast ingots can be one order of magnitude lower than that without refiner addition. Small amount of refiner addition to AZ31 alloy increases both ultimate strength and yield strength significantly,while the ductility of the alloy with refiner addition is similar to that without refiner addition. Addition of refiner improves the deformability of AZ31 alloy and extruded or hot rolled specimens （rods or sheets） with refiner addition exhibit higher surface quality and mechanical properties than those without refiner addition.     

热挤压工艺对AZ31镁合金组织与力学性能的影响

在不同挤压条件下对AZ31镁合金进行了热挤压试验,并对挤压前后材料组织与力学性能的变化进行了分析.研究结果表明,AZ31镁合金热挤压时发生了动态再结晶,材料组织比铸态时细化,力学性能大幅度提高;AZ31镁合金挤压后的组织及力学性能受挤压温度及冷却方式影响,在本试验范围内,AZ31镁合金在623 K挤压后空冷得到的组织均匀细小,力学性能良好.     

连铸AZ31镁合金的热挤压变形组织与性能(英文)

文章研究了电磁连铸AZ31镁合金经热挤压变形后的微观组织和力学性能。结果表明,挤压过程中的动态再结晶能够显著细化晶粒,局部细晶区的平均晶粒为2μm。与铸态合金相比,挤压后的AZ31镁合金具有更细小的晶粒和更均匀的微观组织。挤压变形后产生强烈的基面织构;挤压后材料的力学性能显著提高。屈服强度、抗拉强度和断面收缩率随着挤压比的增大而增大。挤压比为25时,屈服强度、抗拉强度和断面收缩率分别为259MPa,357MPa和30.5%,比铸态合金分别提高了86.33%,64.52%和67.40%。随着挤压比的增大,晶粒细化效果更为明显,微观组织更均匀。断口形貌分析表明,挤压变形后材料由韧脆混合型断裂,转变为韧性断裂。     

Microstructure and Mechanical Properties of AZ31 Mg Alloy Fabricated by Pre-compression and Frustum Shearing Extrusion

The AZ31 Mg alloys were processed by 6% pre-compression and frustum shearing extrusion at various temperatures, and the microstructure, texture and mechanical properties of the resulting alloys are systematically investigated. The results show that the grain size monotonically increases from 6.4 to 12.6 lm and the texture intensity increases from 6.7 to 9.6with the increase in the extrusion temperature. The combining effect of the pre-twinning and the frustum shearing deformation is found to contribute to the development of the weak basal texture in Mg alloys. The Mg alloy sheet produced at the extrusion temperature of 563 K exhibits excellent mechanical properties. The yield strength, ultimate tensile strength and elongation for the extruded alloys are 189.6 MPa, 288.4 MPa and 24.9%, respectively. Such improved mechanical properties are comparable or even superior to those of the alloys subjected to other deformation techniques, rendering the pre-compression and frustum shearing extrusion a promising way for further tailoring properties of Mg alloys.     

Effects of die angle on microstructures and mechanical properties of AZ31 magnesium alloy processed by equal channel angular pressing

1　INTRODUCTIONMagnesiumalloysarethelightestmetallicstruc turalmaterialsandhencetheyprovidegreatpotentialintheweightsavingofautomotiveandaerospacecomponents ,materialhandlingequipment ,portabletoolsandevensportinggoods[1,2 ] .Duetotheirhexago nalclose packed (HCP)crystalstructure ,magnesiumalloysperform poorformabilityandlimitedductilityatroomtemperature ,thustheirproductsaremainlyfabricatedbycasting ,inparticular ,die casting ,andtheapplicationsofwroughtmagnesiumalloysarelim ited .Nowit…     

Microstructure and properties of AZ80 magnesium alloy prepared by hot extrusion from recycled machined chips

1　ＩＮＴＲＯＤＵＣＴＩＯＮＭａｇｎｅｓｉｕｍａｌｌｏｙｓｈａｖｅｍａｎｙａｄｖａｎｔａｇｅｓｓｕｃｈａｓｌｏｗｄｅｎｓｉｔｙ ,ｈｉｇｈｓｐｅｃｉｆｉｃｓｔｒｅｎｇｔｈ ,ｇｏｏｄｅｌｅｃｔｒｏｍａｇ ｎｅｔｉｃｓｈｉｅｌｄｉｎｇｃｈａｒａｃｔｅｒｉｓｔｉｃｓ ,ｅｘｃｅｌｌｅｎｔｃａｓｔａｂｉｌｉｔｙａｎｄｍａｃｈｉｎａｂｉｌｉｔｙｅｔｃ .Ｍａｇｎｅｓｉｕｍｉｓａｎａｂｕｎｄａｎｔｅｌｅ ｍｅｎｔｓｉｎｃｅａｂｏｕｔ 1.93% (ｍａｓｓｆｒａｃｔｉｏｎ)ｏｆｅａｒｔｈｃｒｕｓｔｃｏｎｓｉｓｔｏｆｍａｇｎｅ…     

Paint-bake response of AZ80 and AZ31 Mg alloys

Aging behaviors of extruded and rolled AZ80 and AZ31 Mg alloys were investigated under conditions similar to the paint-bake cycle currently used in automotive industry.Artificial aging at 170℃ from 0.5 to 12 h was conducted on solution-treated specimens to study the effects of aging on mechanical properties.SEM observations and EDS data show thatβ-phase of Al12Mg17 precipitates continuously or discontinuously fromα-Mg matrix and distributes along grain boundaries of the AZ80 alloy during artificial aging.Data of tensile tests and Vickers hardness tests show that an optimum mechanical property is achieved after baking at 170℃ for 6-8 h when Vickers hardness,tensile strength,and elongation are increased by 6.35%,15.30%,and 7.88%,respectively, while the AZ31 alloy does not exhibit significant hardening behavior over the aging period.     

Microstructure and properties of hot extruded AZ31-0.25%Sb Mg-alloy

The effects of hot extrusion treatment on the microstructure and mechanical properties of AZ31-0.25%Sb Mg alloy were investigated by means of mechanical properties measurement and microstructure observation.The results show that the microstructure of AZ31-0.25%Sb Mg alloys consists ofα-Ms matrix,Mg_(17)Al_(12) and Mg_3Sb_2 phases.The ultimate tensile strength (UTS) and yield tensile strength(YTS) of the alloy are obviously enhanced by hot extrusion treatment,and the enhanced extent of UTS and YTS increas...     

Corrosion and mechanical properties of hot-extruded AZ31 magnesium alloys

AZ31 magnesium alloys were hot-extruded at 573 K and 623 K with extrusion ratio(λ) of 20,35 and 50.The corrosion and mechanical behavior of hot-extruded AZ31 were studied by galvanic tests and tensile tests.The microstructures of the studied AZ31 alloys were also investigated with optical microscope.The results show that,compared with the as-cast AZ31 alloy,the corrosion potentials of all hot-extruded AZ31 alloys are increased by 60 mV.Moreover,at the extrusion temperature of 623 K,the galvanic current o...     

Influence of Ca Content on Microstructure and Mechanical Properties of Extruded Mg-Al-Ca-Mn Alloys

Herein, the effects of Ca content on microstructure, texture and mechanical properties of extruded Mg-3Al-0.4Mn-xCa (x = 0.4, 0.8 and 1.2 wt%) rods are systematically investigated. The results reveal that the alloy, with Ca content of 0.8 wt%, exhibits the highest strength and ductility, possessing an ultimate tensile strength of 267.57 MPa and elongation (EL) of 16%. This is mainly due to the gradual transformation of typical fiber texture into a texture with a [10-11] component parallel to the extrusion direction (ED), which increases the Schmid factor of pyramidal slip and enhances the activation rate of pyramidal ⟨c + a⟩ slip. Simultaneously, the as-formed spherical phases and segregation of Ca at grain boundaries render a significant influence on the strength and ductility of the alloy.     

SiC_p/AZ91镁基复合材料的热挤压

采用搅拌铸造法制备SiC体积分数为5%、10%和15%的颗粒增强AZ91镁基复合材料（SiCp/AZ91）。复合材料经过T4处理后,于350°C以固定挤压比12：1进行热挤压。在铸态复合材料中,颗粒在晶间微观区域发生偏聚。热挤压基本上消除了这种偏聚并有效地改善颗粒分布。另外,热挤压有效地细化基体的晶粒。结果表明：热挤压明显提高复合材料的力学性能。在挤压态复合材料中,随着SiC颗粒含量的升高,基体的晶粒尺寸减小,强度和弹性模量升高,但是伸长率降低。     

喷射沉积Mg-12.55Al-3.33Zn-0.58Ca-1.0Nd合金组织与力学性能研究

利用XRD、OM、SEM、TEM研究了喷射沉积Mg-12.55Al-3.33Zn-0.58Ca-1.0Nd合金挤压态的显微组织和合金的力学性能。结果表明:喷射沉积挤压态镁合金主要包含基体α-Mg和Al2Ca相,基体组织为等轴晶,平均晶粒尺寸为3μm;Al2Ca颗粒主要沿镁基体晶界分布,颗粒尺寸在1.0μm左右,并在Al2Ca相中存在孪晶结构;合金的σb、σ0.2、δ分别为450、325MPa,5%。在拉伸断口上存在大量石块状的Al2Ca相,表明合金的断裂方式为沿晶断裂;与经热挤压的铸造AZ91镁合金对比,该合金强度明显提高,但合金塑性降低;合金强度的提高主要来源于合金的细晶强化和Al、Zn对合金的固溶强化,而伸长率降低是由于合金中存在的大量Al2Ca颗粒是沿镁基体晶界分布,导致合金的塑性降低。     

AZ31和AZ91镁合金等温挤压及挤压后的微观组织变化

通过等温挤压和金相观察,研究了AZ31和AZ91镁合金不同变形条件下的挤压性能和变形后的微观组织变化。结果表明,AZ31镁合金的挤压变形性能较好,而AZ91镁合金在挤压比为4∶1、挤压温度为400℃,以及在挤压比为9∶1、挤压温度为350℃和400℃时,挤压后的试件表面均出现了裂纹;AZ31镁合金的最佳成形温度为300℃～400℃,AZ91镁合金的最佳成形温度为300℃～350℃;镁合金在热挤压过程中发生了动态再结晶,挤压之后合金的晶粒显著细化。     

高精度AZ31镁合金薄壁管件等温挤压后的组织与性能

研究了不同条件下AZ3l镁合金管材的等温挤压情况,并对挤压前后材料组织与力学性能的变化进行了分析.研究结果表明,AZ31镁合金热挤压时发生了动态再结晶,材料组织比铸态时细化,力学性能大幅度提高;在(653±10)K挤压温度范围内金属流动均匀,挤出管材尺寸精度较高,力学性能良好;从综合性能看,AZ31镁合金挤压产品的合适退火工艺为573 K × 2 h;此时管材的机械拉伸强度为260 MPa,伸长率为23%.     

退火温度对大变形热轧AZ31镁合金板材力学性能的影响

采用热挤压态AZ31变形镁合金板坯,研究了退火温度对大变形热轧AZ31变形镁合金板材力学性能的影响.结果表明:随着退火温度的升高,变形镁合金板材的抗拉强度和屈服强度减小,伸长率呈线性增加趋势,硬度和杯突值均降低.变形镁合金板材的力学性能与其晶粒尺寸和组织均匀性密切相关.     

Microstructure and mechanical properties of Mg–Zn–(Nd)–Zr alloys with different extrusion processes

The effect of Nd addition and the in?uence of extrusion processes on the microstructure and mechanical properties of Mg–6Zn–0.5Zr(ZK60) and Mg–6Zn–1.5Nd–0.5Zr(ZKNd602) alloys were investigated. Nd element can obviously re?ne the microstructure of both as-cast and asextruded Mg–Zn–Nd–Zr alloy. All of the extruded alloys exhibit a bimodal grain structure composed of equiaxed?ne recrystallized(DRXed) grains and elongated coarse un DRXed grains. It is necessary to achieve high strength,particularly the yield strength, for ZKNd602 alloy, when it is extruded with a lower extrusion temperature, a suitable extrusion ratio and a relatively lower extrusion ram speed. In this study, the ultimate tensile strength(UTS),yield strength(YS) and elongation(El) of the extruded ZKNd602 alloy were 421 MPa, 402 MPa and 6.7 %,respectively, with extrusion temperature of 290 °C, extrusion ratio of 18:1 and a ram speed of approximate0.4 mm·s~(-1). Meanwhile, the extrusion process has obvious effects on the room-temperature properties but weak effects on the high-temperature properties.     

挤压高强度AZ91D镁合金管材的研究

针对挤压变形得到的高强度AZ91D合金管材进行了组织分析,探讨了其强化机制。实验得出,在温度为430℃、应变速率为0.033s-1、挤压比为12时AZ91D镁合金挤压管材(T6)的抗拉强度可达417.2MPa,远远高于压铸镁合金及AZ31等常用变形镁合金;除细晶强化外,第二相强化、亚晶界析出强化和堆垛结构强化为其主要强化机制。