不同生物质活性炭脱除烟气中SO_2/NO_x的实验研究

利用锯末、麦秸、麦秸掺10%煤3种生物质颗粒制取的活性炭,根据比表面积、孔径分布、孔容、微孔结构、碱金属含量等特征参数讨论了活性炭品质。利用立式固定床管式炉系统进行了活性炭颗粒的烟气脱硫脱氮实验,研究了不同的活性炭原材料、工作温度对联合脱硫脱氮性能的影响,对脱除机理进行了分析。通过综合比较分析表明:秸秆加煤材料的活性炭在较长的时间里维持脱硫效率95%以上和脱氮效率85%以上;其在工作温度较低(70℃)时以物理吸附为主,在较高的工作温度(130℃)以化学吸附为主,均具有良好的吸附性能。     

Fe2O3/CAC低温脱硝实验研究

采用浸渍法对焦炭负载Fe_2O_3,并对负载改性的活性焦进行柱状成型,研究不同负载量的Fe_2O_3/CAC(columnar activated coke,CAC)低温脱硝性能。结果表明:Fe_2O_3/CAC脱硝效率最佳时Fe的质量分数为6%,特别在140℃时其脱硝效率达75.6%;改变SO2含量,Fe_2O_3/CAC的脱硫效率基本稳定在90%,脱硝效率最低维持在59.2%;同时引入SO2和H2O对Fe_2O_3/CAC的脱硫脱硝效率影响较大,SO_2和H_2O的体积分数分别为0.04%和9.5%时,其脱硫脱硝效率分别稳定在60%和40%;最佳负载量下,Fe_2O_3/CAC的吸附-脱附曲线属于H4滞后环的Ⅱ型等温线;Fe_2O_3/CAC中氧化物SiO_2与Fe_2O_3含量较高,Fe主要以γ-Fe_2O_3形式存在,有利于提高Fe_2O_3/CAC的低温脱硝性能;不同负载量的柱状Fe_2O_3/CAC落下强度均在50%左右。     

三段炭层吸附床联合脱除烟气污染物的实验研究

利用秸秆活性炭颗粒在三段炭层的吸附床反应器中进行了燃煤烟气脱硫、脱氮、脱汞的联合脱除实验研究。首先对实验所用炭（包括新炭和再生后炭）进行了活性炭品质分析,并讨论了烟气流经3段炭层吸附床时,脱硫脱氮段工作温度对脱硫、脱氮和脱汞效率的影响特性。实验结果表明,在所选三种工作温度中,90℃时脱硫层内以物理吸附为主,脱氮层吸附还原NOx的同时具有脱硫副反应,总脱硫效率可达98％,脱氮效率可达60％;经过冷却的烟气达到脱汞炭层时温度降到50℃,由氯化锌浸泡处理的炭层内同时发生催化氧化脱汞及汞的物理吸附,下层炭工作温度在130℃时,总脱汞效率达55％。该结果可指导干法烟气污染物的防治。     

浅谈脱硫脱硝一体化

"十二五"以来,我国环保部门对烟气排放指标要求越来越严格,国内为烟气脱销技术主要是SCR/SNCR工艺。SCR/SNCR工艺脱硝技术虽然比较成熟,但氨逃逸与烟气中的SO_3反应生成NH_4HSO_4,在250℃温度下粘符在尾部设备上,阻碍了锅炉热交换,降低了锅炉热效率。分析次氯酸钙脱销机理,理论上次氯酸钙脱硫脱销一体化向正方向进行。通过实验模拟:次氯酸钙脱硝可达到70%,脱硫效率可达到100%,脱硝效率可以与SNCR相媲美。脱硫脱硝一体化不仅能满足目前国家烟气运行排放要求,投资少,而且脱去烟气硫、硝时,对锅炉热效率没有任何影响,伴随其技术的不断成熟,湿法脱硫脱硝一体化未来将有美好的前景。     

碳酸氢钠干法脱硫的实验研究

为了促进污染物协同控制和超低排放的实现,简化烟气脱硫除尘工艺,为选择性催化还原法(selective catalytic reduction,SCR)脱硝创造适宜的烟气条件,利用烟气干法脱硫除尘一体化装置,研究了碳酸氢钠干法脱硫的温度、钠硫比(stoichiometric ratio of sodium bicarbonate to sulfur,NSR)、入口SO₂质量浓度、Na HCO₃粒径和粉尘质量浓度等因素对脱硫效率的影响,对装置的脱硫性能做出评价,最佳脱硫效率达到95%以上.实验结果表明:温度、NSR为主要影响因素,在130～200℃温度范围内,脱硫效率随温度的升高呈先下降后保持稳定的趋势;随着NSR的增大,效率呈先增加后保持稳定的规律;入口SO₂的质量浓度为1 000～2 000 mg/m³,脱硫效率随入口质量浓度的增大而有所增加;粒径较小的NaHCO₃颗粒脱硫效率更好;烟气中的粉尘在一定程度上能够促进脱硫反应的进行.     

几种改性同时脱硫脱硝吸收剂的比较研究

利用模拟烟气,在固定床上对几种改性同时脱硫脱硝吸收剂的性能进行了比较实验研究。结果表明:EDTA合铁、H2O2、尿素、半胱氨酸合铁、锰系物M以及复合剂F(N/NaClO2)等添加剂改性后其脱硫效率提升并不明显,但脱硝效果差异较大,其中复合添加剂F改性后脱除效率最高,用量最少,成本最低。利用正交试验,确定了复合添加剂F改性后同时脱硫脱硝剂的最佳实验条件为添加剂含量为0.2%,反应温度为60℃,Ca/(S+N)为1.2。     

ClO2液相氧化协同氨法烟气脱硫脱硝研究

采用ClO2作为脱硝添加剂,在已有的氨法脱硫中实现工业锅炉同时脱硫脱硝。分别考察了ClO2质量浓度、初始pH值、温度和吸收液液气比等对脱硫脱硝的影响。结果表明:SO2和NO去除率随着ClO2质量浓度和液气比的增大而提高;初始pH对SO2和NO的去除有较大影响,脱硝效率随着pH升高而减小;温度对脱硫效率影响不大,但适当升温可以提高脱硝效率。在适宜试验条件下,脱硫效率可达到99.8%,脱硝效率可达93.2%。在不改变氨法脱硫工艺条件前提下探索投资少成本低的脱硝新思路。     

活性炭吸附脱除高压聚乙烯装置返回气中丙醛的研究

研究了活性炭吸附脱除高压聚乙烯装置返回气中的丙醛,考察了温度和原料气流速对脱醛率的影响和活性炭吸附丙醛的吸附穿透曲线,同时比较了活性炭在不同脱附方法脱附后再吸附丙醛的情况。实验结果表明,温度对活性炭的脱醛率有影响,30℃时脱醛率最高;在原料气流速为30mL/min时,丙醛的脱除率为70%~90%;活性炭吸附570min后,丙醛的脱除率下降到30%左右;采用120℃水蒸气脱附法,活性炭三次吸附的脱醛率都在95%以上,好于加热氮气吹扫脱附法和加热抽真空脱附法。     

团聚剂对NaClO/NaClO_2溶液脱硫脱硝反应速率影响研究

为了实现NaClO/NaClO_2溶液法脱硫脱硝脱除细微颗粒物的高效运行,本文以脱硫脱硝化学反应速率为研究对象,对比了发泡团聚剂(用于团聚细微颗粒物)的加入对二氧化氯生成和脱硫脱硝反应速率的影响特性,通过周期性的实验,确定维持高效脱硫脱硝效率所需的溶液浓度。实验结果表明,一方面团聚剂增大了溶液粘度,减缓了溶液反应速率,抑制二氧化氯的析出;另一方面团聚剂生成的泡沫增加了气液之间的接触面积,促进了脱硝反应。而且在有无团聚剂的两种情况下,复合溶液的反应速率遵循了相近的变化规律,溶液中二氧化氯摩尔浓度高于0.96 mmol/L左右时,脱硫脱硝速率达到最高并维持一段时间;当二氧化氯摩尔浓度低于一定值时,脱硝效率迅速降低。该实验结果可以为脱硫脱硝技术的中试和放大提供理论指导。     

生活垃圾焚烧厂SCR低温催化剂运行案例分析

以某生活垃圾焚烧厂实际运行的蜂窝状钒钨钛低温脱硝催化剂为研究对象,通过压损测试、活性测试和脱硝效率检测,研究了典型的选择性催化还原法(SCR)低温催化剂催化活性的影响因素。运行结果表明,蜂窝状催化剂在抗中毒能力上要强于颗粒状催化剂;SCR低温催化剂反应温度可降低到166~170℃,脱硝效率达到50%左右;为控制排烟中的氨逃逸量,氨氮当量比值不宜超过1.3。     

含锌粉尘脱锌处理的实验室研究

充分利用高炉含锌瓦斯泥中充足的碳源,将铁和锌还原出来,得到脱锌金属化球团矿,实现资源的回收利用和环境保护.通过研究不同粘结剂、碱度、还原温度和还原时间对熟球抗压强度、脱锌率的影响,找出最佳试验方案为A1B3C3D3,得到脱锌率和抗压强度较高的金属化球团.     

Study on stainless steelmaking dust agglomeration

A new direct recycling technology was developed to recover the valuable metals present in the stainless steelmaking dust and protect the environment. The agglomeration behavior of the dust was analyzed to ensure the requirements of the direct recycling. The main characteristics such as strength, leachability, structure and chemical composition of the pellets were investigated. SEM images show a significant amount of porosities affecting the strength of the pellets and the arrangement of particles in the pellets reveals that no recrystallization bonds are formed, resulting in the poor strength of the pellets. When lignosulfonate is applied as the binder for the agglomeration and the green pellets are dried at room temperature for 60 h, the strong pellets can be obtained without milling the dust. The result of leachability tests shows that the pellets agglomerated can not satisfy the regulations set by the environmental protection agency of US. And it will cause some environmental problems in the long storage of pellets.     

含铁尘泥高碱度内配碳球团自还原过程中脱硫和脱磷研究

在竖式碳管炉中进行含铁尘泥高碱度内配碳球团的还原试验,并通过改变温度、配碳比和碱度对含铁尘泥还原过程中的脱硫和脱磷进行研究。结果表明,高碱度内配碳球团在高温下快速还原制备金属铁粒的脱硫率高于97％,铁粒中硫含量最低达到0．007％,而脱磷率一般为25％～35％,最高达到38．52％。随着温度和配碳比的升高,铁粒的脱硫率和脱磷率均增加;而随着碱度的增加,铁粒的脱硫率和脱磷率均先增大后减小。     

Thermodynamics calculation on the oxidation and sulfur removal abilities of slag in EAF dust pellet reduction process

ＥＡＦｄｕｓｔｈａｓｂｅｅｎｃｌａｓｓｉｆｉｅｄａｓｈａｚａｒｄｏｕｓｗａｓｔｅ ,ａｎｄｉｔｉｓｈａｒｍｆｕｌｉｎｔｈｅｃｏｎｖｅｎｔｉｏｎａｌｌａｎｄ ｆａｌｌｄｕｅｔｏｃｏｎｔａｉｎｉｎｇｈｅａｖｙｍｅｔａｌｓ[1] .Ｍｏｓｔｒｅｃｙ ｃｌｉｎｇｍｅｔｈｏｄｓ[2 8] ｄｅｖｅｌｏｐｅｄｆｏｒｔｈｅｄｕｓｔｓａｒｅｏｎｌｙｆｏｒｔｈｅｒｅｃｏｖｅｒｙｏｆｌｅａｄ ,ｚｉｎｃａｎｄｃａｄｍｉｕｍ .ＴｈｅＥＡＦｄｕｓｔｆｒｏｍｓｔａｉｎｌｅｓｓｓｔｅｅｌｍａｋｉｎｇｍａｉｎｌｙｃｏｎ ｔａｉｎｓｎｉｃｋｅ…     

Thermodynamic calculation on the smelting slag of direct recycling of electric arc furnace stainless steelmaking dust

1　ＩＮＴＲＯＤＵＣＴＩＯＮＥｌｅｃｔｒｉｃａｒｃｆｕｒｎａｃｅ (ＥＡＦ)ｄｕｓｔｈａｓｂｅｅｎｃｌａｓｓｉｆｉｅｄａｓａｈａｚａｒｄｏｕｓｗａｓｔｅｄｕｅｔｏｉｔｓｈｉｇｈｃｏｎｔｅｎｔｏｆｓｏｍｅｈｅａｖｙｍｅｔａｌｓｌｅａｃｈａｂｉｌｉｔｉｅｓｓｕｃｈａｓｚｉｎｃ ,ｌｅａｄ ,ｃａｄｍｉｕｍａｎｄｃｈｒｏｍｉｕｍ ,ｓｏｉｔｈａｓｂｅｅｎｂａｎｎｅｄｆｒｏｍｌａｎｄｆｉｌｌｓｉｎｍａｎｙｃｏｕｎ ｔｒｉｅｓ .Ａｎｅｓｔｉｍａｔｅｄ 1 % 2 %ｍａｓｓｆｒａｃｔｉｏｎｏｆｔｈｅｓｃｒａｐｃｈａｒｇｅｄ…     

棉秆用磷酸法制取脱色粉状活性炭的初步研究

我国是产棉大国，大多棉秆没有得到进一步的开发利用．本实验以棉秆为原料，用磷酸法从棉秆中制取脱色活性炭，并对炭化、活化等工艺条件进行了研究，实验结果表明，产品的收率及脱色性能较稳定，且活化剂的消耗量较少，为把棉秆转变为活性炭，提供了比较理想的实验条件．     

载铜活性炭的制备及其处理印染废水的应用

以废木屑为原料制备载铜活性炭。采用单因素法确定硝酸铜用量,用Design-Expert7.0软件设计试验方案,建立响应面模型。通过对模型的分析,确定载铜活性炭的最优制备条件为：硝酸铜溶液（0.5 mol·L^-1）用量为15 mL,活化温度为690℃,活化时间为2.1 h和活化剂（质量分数为40%的磷酸）用量为56 mL。最优条件制备的载铜活性碳处理模拟印染废水,其色度和COD的去除率分别为99.80%和88.34%,处理后的废水的色度为32倍和COD值为75 mg·L^-1。     

Kinetics of Evaporation of Zn and Pb from Carbon-bearing Pellets Made of Dust Containing Zn-Pb-Fe Oxides

The influence of reduction temperature, size of coal powder and the carbon content on the evaporation rates of Zn and Pb in pellets made of ZnO-PbO-FeO bearing dust has been investigated between 1100-1300℃. The evaporation rate of Zn and Pb obtained from the experiments has been analyzed with kinetic models. The results show that the control step for evaporation of Zn is reduction reaction of ZnO by CO at the interface,and that the evaporation rate of Pb is controlled by the volatilization of reduction products, i.e. liquid lead. The overall apparent activation energies of Zn and Pb evaporation from the pellet are 79.42kJ/mol and 88.74kJ/mol respectively.