The influence of antimony-additions on the creep behaviour of a 25wt% Cr-20wt% Ni austenitic stainless steel

The effect of antimony on the creep behaviour (dislocation creep) of a 25 wt% Cr-20 wt% Ni stainless steel with ~ 0.005 wt% C was studied with a view to assessing the segregation effect. The antimony content of the steel was varied up to 4000 ppm. The test temperature range was 1153 to 1193 K, the stress range, 9.8 to 49.0 MPa, and the grain-size range, 40 to 600m. The steady state creep rate, , decreases with increasing antimony content, especially in the range of intermediate grain sizes (100 to 300m). Stress drop tests were performed in the secondary creep stages and the results indicate that antimony causes dislocations in the substructure to be immobile, probably by segregating to them, reducing the driving stress for creep.Nomenclature _a Creep stress in a constant load creep test without stress-drop - _A Initial applied stress in stress-drop tests - Stress decrement - ( _A-) Applied stress after a stress decrement, - t _i Incubation time after stress drop (by the positive creep) - _C Strain-arrest stress - _i Internal stress - _{s s}-component (= _i- _c) - Steady state creep rate (average value) in a constant load creep test - Strain rate at time,t, in a constant load creep test - New steady state creep rate (average value) after stress drop from _A to ( _A-) - Strain rate at time,t, after stress drop.     

Steady-state creep in a 25 wt % Cr-20 wt % Ni austenitic stainless steel

Steady-state creep behaviour of a 25 wt % Cr-20 wt % Ni stainless steel without precipitates was studied in the stress range 9.8 to 39.2 MPa at temperatures between 1133 and 1193 K. The results of stress-drop tests indicate that, in the steady-state creep region, diffusion-controlled recovery creep is dominant. Such recovery creep can be accounted for in terms of the composition of the internal stress, _i=_s+_c, except in the case of fine-grained specimens where d<80 m, whered is the mean grain diameter, _s is possible to reduce easily and is comparable to the driving stress for creep, and _c is the persistent stress field due to metastable substructure. In the fine-grained specimens, it is suggested that the steady-state creep is dominantly controlled by grain boundaries.     

A study of the Bailey-Orowan equation of creep

A new method was developed to study the Bailey-Orowan equation of creep, _c=r/h, where _c is the creep rate,r is the recovery rate andh is the work-hardening coefficient. The method was to vary the strain rate,, around the creep rate, _c, and to measure the corresponding stress rate,. In a plot of stress rate against strain rate, a straight line was obtained. The slope of the straight line was equal toh, and the intersection of the straight line with the stress axis was equal to –r, as in the equation=–r+h. The creep test under a constant stress is a special case of this equation when the stress rate,, is zero. The above measurement was carried out within a very small stress variation, less than 1% of the total stress, so that the values ofr andh were not disturbed. The creep test was performed on Type 316 stainless steel. The creep rate was shown to be equal to the ratior/h, but the value ofh was approximately equal to Young's modulus at the testing temperature, rather than, as is commonly believed, to the work-hardening coefficient.     

On internal stress and activation volume in polymers

The two-site model is developed for the analysis of stress relaxation data. It is shown that the product of d In (– )/d and (- _i) is constant where is the applied stress, _i is the (deformation-induced) internal stress and = d/dt. The quantity d In ( )/d is often presented in the literature as the (experimental) activation volume, and there are many examples in which the above relationship with (- _i) holds true. This is in apparent contradiction to the arguments that lead to the association of the quantity d In (– )/d with the activation volume, since these normally start with the premise that the activation volume is independent of stress. In the modified theory presented here the source of this anomaly is apparent. Similar anomalies arise in the estimation of activation volume from creep or constant strain rate tests and these are also examined from the standpoint of the site model theory. In the derivation presented here full account is taken of the site population distribution and this is the major difference compared to most other analyses. The predicted behaviour is identical to that obtained with the standard linear solid. Consideration is also given to the orientation-dependence of stress-aided activation.     

Distribution characteristics of mechanical properties and correlation between the respective properties on S35C carbon steel

Mechanical properties of tensile strength, , upper yield stress, _SU, lower yield stress, _SL elongation, , area reduction, , Vickers hardness, H _v, and impact absorbed energy, E, were examined using 50 specimens of S35C carbon steel, which were machined from two bars supplied from the same charged and heat-treated material. Distribution characteristics of these properties are discussed, and the correlation between each pair of them is investigated from a statistical viewpoint. The main conclusions obtained are summarized as follows; distribution characteristics of _B, _SL, , , H _v and E are well approximated by a normal distribution, but those of asu are not approximated as well by this type of distribution. In the latter case, a Weibull distribution is preferable to represent the distribution pattern. No significant correlation was observed between each pair of the above mechanical properties. Consequently, individual properties have the inherent distribution characteristics independent of the other properties.     

Optimal design of a thick-walled pipeline cross-section against creep rupture

Summary Cylinder under combined loadings (pressure, bending, axial force) is subject to non-linear creep described by Norton-Odqvist creep law. In view of bending a circularly-symmetric cross-section is no longer optimal in this case. Hence we optimize the shape of the cross-section; minimal area being the design objective under the constraint of creep rupture. Kachanov-Sdobyrev hypothesis of brittle creep rupture is applied. The solution is based on the perturbation method (expansions into double series of small parameters), adjusted to optimization problems.Notation A cross-sectional area - C, , creep rupture constants - K, n, _C , _C creep constants - F dimensionless creep modulus - M bending moment - N axial force - a(),b() internal and external radii of the cross-section - j creep modulus - p internal pressure - r, ,z cylindrical coordinates - s _r ,s ,s _z ,t _r dimensionless stresses - t _R time to rupture - stress function - , () dimensionless internal and external radii - _e effective strain rate - _kl strain rates - rate of curvature - rate of elongation of the central axis - dimensionless radius - _e effective stress - _I maximal principal stress - _S Sdobyrev's reduced stress - _r , , _z , _r components of the stress tensor - measure of material continuity - measure of deterioration With 7 Figures     

Absence of Phase-Fluctuation Contribution to the Low-Frequency Optical Conductivity in d-Wave Superconductors at Zero Temperature

The behavior of the low-frequency optical conductivity _reg() in superconducting cuprates is, at the present, an open and interesting issue. In particular, since the zero-temperature and zero-frequency limit of _reg() attains a value much larger than the universal value expected within a self-consistent T-matrix calculation, an intriguing possibility is that the collective mode can also contribute to _reg(). By taking into account the effect of dissipation on the collective mode in a d-wave superconductor, we evaluate the phase-fluctuation contribution to _reg(0) within the formalism of the phase-only action. We show that even though the collective mode contributes to _reg() at finite frequencies, approaching the zero-temperature and zero-frequency regime the corrections at _reg() due to phase fluctuations vanish.     

The stress dependence of the crack growth rate during creep

An equation is derived for the crack growth rate under creep conditions. In the model, the propagation of a grain boundary crack is controlled by the plastic growth of cavities located in the grain boundaries ahead of the crack. It is assumed that the cavities grow by power law creep in the elastic crack tip stress field. Hence, the stress dependence of the crack velocity is provided through the elastic stress intensity factor, i.e., dC/dt=BK _I ^p .The cavity spacing, , appears as an important factor in the coefficient,B ^–(p–2)/2. At large values of , corresponding to less severe creep damage in the grain boundaries, the above equation would predict very low values for the crack velocity. Under such conditions, we suggest that another mechanism, whose stress dependence is provided through the net section stress, becomes active, i.e., dC/dt=B _net ^p . Since increases with decreasing applied stress, one should observe the _net correlation at low stresses. The results of recent creep crack growth experiments which tend to support this hypothesis are presented.

---

Résumé On dérive une équation décrivant la vitesse de propagation d'une fissure dans les conditions de fluage. Dans ce modèle, la propagation d'une fissure aux frontières de grains est contrôlée par la croissance dans le domaine plastique de cavités situées aux frontières de grains en avant de la fissure.On suppose que les cavités s'étendent dans le champ de contraintes élastiques situées à l'extrémité de la fissure en suivant une loi de fluage parabolique. Dès lors, la dépendance de la vitesse de la fissuration en fonction de la contrainte est fournie par un facteur d'intensité de contrainte élastique, c'est-à-dire dC/dt=BK _I ^p .L'espace entre les cavités, , apparaît être un facteur important dans les coefficientsB. Pour de grandes valeurs de , qui correspondent à un dommage moins sévère par fluage aux frontières des grains, l'équation ci-dessus permettrait de prédire des valeurs très faibles de la vitesse de fissuration.Sous ces conditions, il est suggèré qu'un autre mécanisme, dont la dépendance de la contrainte est fournie par la contrainte agissant sur la section droite, devient plus actif; on a alors dC/dt=B _nette ^p .Comme augmente lorsque la contrainte appliquée diminue, on devrait observer une corrélation de nette à basses contraintes.Les résultats d'essais de croissance de fissure sous des conditions de fluage effectués récemment tendent à supporter cette hypothèse et sont présentés.

     

Crack-tip damaged zones in rubber-toughened amorphous polymers: a micromechanical model

The various stages of crack propagation in rubber-toughened amorphous polymers (onset and arrest, stable and unstable growth) are governed by the rate of energy dissipation in the cracktip damaged zone; hence the relationship between the applied stress intensity factorK ₁ and the damaged zone size is of utmost importance. The size of the crack-tip damaged zone has been related toK ₁ via a parameter which is characteristic of the material in given conditions: this factor is proportional to the threshold stress for damage initiation in a triaxial stress field, and has been denoted by ^*. Theoretical values of ^* have been calculated by means of a micromechanical model involving the derivation of the stresses near the particles and the application of damage initiation criteria. The morphology, average size and volume fraction of the rubbery particles have been taken into account together with the nature of the matrix. The calculated values of ^* have been successfully compared with the experimental ones, for a wide set of high-impact polystyrenes (HIPS) and rubber-toughened poly(methyl methacrylate) (RTPMMA).Nomenclature PS; HIPS polystyrene; high-impact polystyrene - PMMA; RTPMMA poly(methyl methacrylate); rubber-toughened PMMA - MI; CS/H; CS/R particle morphologies (multiple inclusion; hard core - rubber shell; rubber core - rigid shell) - K _r;K _g bulk moduli of rubber and glassy materials - G _r;G _g shear moduli of the same materials - v _p particle volume fraction - L mean centre-to-centre distance between neighbouring particles - B; H; W standard names for the dimensions of the compact tension specimen - R _y size of the crack-tip plastic zone in a homogeneous material - h half thickness of the crack-tip damaged zone - r; polar coordinates around the crack tip (Fig. 1) - r;r _p distance from particle centre; particle radius - p normalized distance from the particle (Equation 5) - K ₁;K _1c;K _1p stress intensity factor; critical values ofK ₁ at the onset of and during crack growth - G _1c plane strain energy release rate - _y yield stress in uniaxial tension - _th macroscopic threshold stress for the onset of local damage initiation in a composite material - ^* characteristic parameter (Equation 3) - ⁰; ₁ ⁰ ; ₂ ⁰ ; ₃ ⁰ applied stress tensor and its three principal stresses - ⁰ uniaxial applied stress - ; ₁; ₂; ₃ local stress tensor and its three principal stresses - A tensor which elements are the ratios of those of over those of ⁰ (Equation 4) - v Poisson's coefficient of the matrix - g triaxiality factor of the crack-tip stress field - _e; _p Mises equivalent stress; dilatational stress (negative pressure) - I ₁;I ₂ invariants of the stress tensor - U ₁;U ₂ material parameters for argon and Hannoosh's craze initiation criterion (Equation 12)     

Effect of magnesium content on the stress exponent and effective stress in the steady state creep of Al-Mg alloys

The stress exponent of steady state creep,n, and the internal ( _i) and effective stresses ( _e) have been determined using the strain transient dip test for a series of polycrystalline Al-Mg alloys creep tested at 300° C and compared with previously published data. The internal or dislocation back stress, _i, varied with applied stress,, but was insensitive to magnesium content of the alloy, being represented by the empirical equation _i=1.084 ^1.802. Such an applied stress dependence of _i can be explained by using an equation for _i of the form _i (dislocation density)^1/2 and published values for the stress dependence of dislocation density. Values of the friction stress, _f, derived using the equation _e/=(1–c) (1– _f/), indicate that _f is not dependent on the magnesium content. A constant value of _f can best be rationalized by postulating that the creep dislocation structure is relatively insensitive to the magnesium content of the alloy.On leave from Engineering Materials Department, University of Windsor, Windsor, Ontario N9B 3P4, Canada.     

Electrical conductivity,thermoelectric power and dielectric constant of NiWO4

The a.c. electrical conductivity ( _ac), thermoelectric power () and dielectric constant () of antiferromagnetic NiWO₄ are presented. _ac and have been measured in the temperature range 300 to 1000 K and in the temperature range 600 to 1000 K. Conductivity data are interpreted in the light of band theory of solids. The compound obeys the exponential law of conductivity = ₀ exp (–W/kT). Activation energy has been estimated as 0.75eV. The conductivity result is summarized in the following equation =2.86 exp (–0.75 eV/kT)^–1 cm^–1 in the intrinsic region. The material is p-type below 660 K and above 950 K, and is n-type between 660 and 950 K.     

Investigation of the creep and micropolar creep of various materials under static and dynamic loads

Creep is investigated under a uniform stress state with allowance for the micropolar creep of the following materials: lignostone (T=293°K), steel ON2M (T=773° K), and an AIMgSi aluminum alloy (T= 293° K) understate and cyclic tension, i.e., atA = ^a/^m = 0, 0.25, and 0.5. It is established that for lignostone, the microstrains I₁₁ are two orders lower than 2₁₂ in torsion, and the values of 2l₁₂ are only a half order lower than ₁₁ in tension. The creep strain of lignostone is described using nonlinear theory of viscoelasticity. For alloys and metals under static creep, the value of I_ij is two or three orders lower than _ij A qualitative change in microipolar creep occurs in the case of dynamic loading: whenA = 0.5,the ratio of values of fatigue creep rate 21₁₂/₁₂ = 0.2.A subject investigated in 1990 with funding provided by the Ministry of National Education.Translated from Problemy Prochnosti, No. 12, pp. 18–23, December, 1993.     

On the measurement and physical meaning of the cleavage fracture stress in steel

Elastic-plastic two-dimensional (2D) and three-dimensional (3D) finite element models (FEM) are used to analyze the stress distributions ahead of notches of four-point bending (4PB) and three-point bending (3PB) specimens with various sizes of a C-Mn steel. By accurately measuring the location of the cleavage initiation sites, the local cleavage fracture stress _f and the macroscopic cleavage fracture stress _F is accurately measured. The _f and _F measured by 2D FEM are higher than that by 3D FEM. _f values are lower than the _F, and the _f values could be predicted by _f=(0.8––1.0)_F. With increasing specimen sizes (W,B and a) and specimen widths (B) and changing loading methods (4PB and 3PB), the fracture load P _f changes considerably, but the _F and _f remain nearly constant. The stable lower boundary _F and _f values could be obtained by using notched specimens with sizes larger than the Griffiths–Owen specimen. The local cleavage fracture stress _f could be accurately used in the analysis of fracture micromechanism, and to characterize intrinsic toughness of steel. The macroscopic cleavage fracture stress _F is suggested to be a potential engineering parameter which can be used to assess fracture toughness of steel and to design engineering structure.     

Notch tip stress distribution in strain hardening materials

Using the results of elastic-plastic stress analyses for notched bars, it is shown that a modified form of slip-line field solution can satisfactorily explain the variation of longitudinal stress ahead of notch tips in strain hardening materials.

---

Résumé En utilisant les résultats d'analyses de contrainte élastoplastique dans le cas de barres entaillées, on montre qu'il est possible d'utiliser une forme simplifiée de solution du champ des lignes de glissement pour expliquer de façon satisfaisante la variation des contraintes longitudinales en avant d'extrémités d'entaille dans des matériaux susceptibles d'un écrouissage.

---

Nomenclature _yy longitudinal tensile stress in the notch tip plastic zone - _xx transverse stress in the x-direction - _zz transverse stress in the z-direction - k yield stress in shear - ₀ yield stress in tension - ₀ ^* strain hardened yield stress (flow stress) - _{0/* c} flow stress at notch tip - _total total strain _pl plastic strain _l principal strain - _{1 c} maximum principal strain at notch tip - _1pl plastic strain in they-direction - _{1 cp1} E_{1 pl} at notch tip - _eff effective plastic strain - _{c eff eff} at notch tip - ₀ yield strainC Stress decay constant in the notch tip region - /e_pl linear strain hardening rate - n strain hardening exponent in power hardening law - 2 flank angle of notch - distance from notch tip - p notch tip radius - k _I applied stress intensity for Mode I loading - E Young's modulus - V _c crack tip opening displacement     

Charged defects-controlled conductivity in Ge-ln-Se glasses

The variation of the d.c. electrical conductivity, , with composition and temperature was investigated for glasses of the Ge-In-Se system. The results indicate a decrease in the activation energy for electrical conductivity, E, and an increase in on introduction of indium into Ge-Se glasses. The changes in E and with composition (selenium content in the glasses) are identical for the Ge_x In₅ Se_95–x and Ge_x In₈Se_92–x families. The results have been traced to the conduction controlled by charged defects in these chalcogenide glasses. The changes in E and have been explained by a shift in the Fermi level, being brought by the introduction of indium.     

Low endurance fatigue in metals and polymers

The fatigue behaviour of commercially pure aluminium and of nylon under sequentially varying strain amplitudes is compared with a damage law of the type suggested by Miner. Aluminium obeys such a law for both cyclic and uniaxial prestrains but the behaviour of nylon is significantly affected by microcracking, which produces a marked effect of loading sequence.Appendix N Number of strain cycles at a given time - N _f Value of N at failure - True tensile stress - True stress range for a strain cycled specimen - _h Value of at half the life of the specimen - True tensile strain - Total true strain range - _p True plastic strain range (= the breadth of the hysteresis loop at = 0) - _d True diametral strain range - E Young's modulus - Linear strain hardening rate when tested at a particular value of _p - D Damage due to cycling - D _p Damage due to prestrain - _p Prestrain. C, K, K₁, , are constants     

Statistical analysis of the Hertzian fracture of pyrex glass using the Weibull distribution function

Hertzian fracture tests were carried out on specimens of ground-and-polished Pyrex glass using polished Pyrex glass balls of 6 and 8 mm diameter. The results were analysed according to the theory of flaw statistics originally proposed by Weibull. The Weibull parameters m and ₀ were found to be independent of ball size; _u however decreased with increase in ball size. The parameters _u,₀ and m obtained from the Hertzian tests differed from those obtained from a four-point bend test. The predicted mean fracture stress and the mean fracture location for Hertzian fracture using the derived Weibull parameters agreed reasonably well with the experimental values.     

Frequency and temperature dependence of the millimeter wave conductivity of epitaxial YBa2Cu3O7 films

A millimeter wave spectrometer for frequencies between 100 and 350 GHz consisting of continuously tunable backward wave oscillators as sources and a quasioptical interferometer in the Mach-Zehnder configuration was used to measure the transmittivity in phase and amplitude of YBa₂Cu₃O₇ thin films on NdGaO₃ substrates. From the measured spectra we derived the real and imaginary part of the dynamic conductivity= ₁+i ₂ in the superconducting state as a function of temperature. The ₁(T) and ₂(T) values at 300 GHz were compared to corresponding values at 19 GHz determined by surface impedance measurements of the same films using a shielded dielectric resonator. Our observed frequency dependence of both ₁(T) and ₂(T) is consistent with a strong reduction of the quasiparticle scattering rate ^–1(T) with decreasing temperature belowT _c .     

Effective conductivity of a composite of poly-dispered spherical particles in a linear continuum

Rayleigh's method is used to find the electric potentials of a composite of poly-dispered spherical particles in a linear continuum in an external electric field. Based on the solutions of potentials, analytical formula for the effective electric conductivity is derived. Based on the formula, several factors, such as the number of spherical inclusions, the spatial distribution of the spheres, the contrast ratio _i / _h (where, _i and _h are the conductivities of the spherical inclusion and the host medium, respectively) and volume fraction of the inclusions, are discussed. Our results show that at high volume fraction, the effective conductivity is also affected by the spatial distribution of the inclusions.