Tensile fracture of as-cast and hot rolled Mg-Zn-Y alloy with long-period stacking phase

An experimental Mg97Zn1Y2(molar fraction,%)alloy was produced by rolling the as-cast alloy.The microstructure of the alloy is composed of theα-Mg(also marked as 2H-Mg with reference to long-period stacking structure according to hexagonal close packed structure)and long-period stacking(LPS)phase.Tensile tests of Mg97Zn1Y2 alloy in comparison with pure Mg were conducted.The fracture morphologies of the tensile specimens were characterized and the microstructures near fracture surface were observed.The results show that the rolled Mg97Zn1Y2 alloy shows a mixed fracture mode including dimples indicating a ductile fracture pattern and a small fraction of cleavage planes indicating a brittle fracture pattern,which is different from the single brittle fracture of the as-cast alloy.In addition,the plastic deformation is mainly from dislocations induced strain with small strengthening effect during plastic deformation in the as-cast Mg97Zn1Y2 alloy,and the strain hardening rate is similar to that of the as-cast pure magnesium.The deformation mechanism of Mg97Zn1Y2 alloy is different from that of the pure magnesium according to a metallographical observation that whether twins are found or not.The strengthening effect hardly exists in the rolled Mg97Zn1Y2 alloy under the same dislocations induced strain,which is different from that of the as-cast alloy with moderate strengthening effect.     

Effects of Pb on microstructure,mechanical properties and corrosion resistance of as-cast Mg97Zn1Y2 alloys

In this present work, Pb was applied in the Mg97Zn1Y2 alloy to improve its microstructure and properties, using conventional casting methods. The microstructure and properties of the Mg97 Zn1 Y2 alloy and Mg97Zn1Y2-x Pb(x=0.6 wt.%, 1.2 wt.% and 1.8 wt.%) alloys were observed by optical microscopy, scanning electron microscopy method and analyzed by X-ray diffraction, hardness and strength measurement and electrochemical testing. After adding Pb to the Mg97Zn1Y2 alloy, a new particle phase Mg_2 Pb was identified along the grain boundaries, and dendrites were refined. In addtion, the hardness of Mg97Zn1Y2-xPb(x=0.6 wt.%, 1.2 wt.% and 1.8 wt.%) alloys was higher than that of the Mg97 Zn1Y2 alloy; with the increase of Pb content, the hardness of the alloy increased first and then decreased, followed by a final slight increase, and reached a maximum of 89.1 HV when the Pb content was 0.6 wt.%. The strength of the alloy increased first and then decreased as the Pb content increased. Moreover, adding a small amount of Pb to the alloy can effectively inhibit corrosion, and Mg97Zn1Y2-0.6 wt.%Pb exhibits the best corrosion resistance ability.     

锆元素对Mg_(97)Y_2Zn_1镁合金微观组织和力学性能的影响(英文)

研究锆元素对Mg97Y2Zn1镁合金微观组织和力学性能的影响。锆元素的添加可以细化铸态Mg97Y2Zn1合金的组织。在挤压过程中,Mg97Y2Zn1镁合金在原始晶界和第二相周围优先形核。锆元素的添加促进合金的再结晶过程,这是因为锆元素的添加使合金形成更多的晶界,从而提高了再结晶的形核率。此外,锆元素的添加还能够提高合金的强度和伸长率等力学性能。     

Comparison of as-cast microstructure,tensile and creep properties for Mg-3Sn-1Ca and Mg-3Sn-2Ca magnesium alloys

The as-cast microstructure,tensile and creep properties of Mg-3Sn-1Ca and Mg-3Sn-2Ca magnesium alloys were investigated and compared by using optical microscopy and scanning electron microscopy,X-ray diffraction analysis and tensile tests. The results indicate that the as-cast microstructures of Mg-3Sn-1Ca and Mg-3Sn-2Ca alloys are different.The former is mainly composed ofα-Mg,eutectic CaMgSn and solid state precipitation of Mg 2 Sn,whereas the latter is mainly composed ofα-Mg, primary CaMgSn,eutectic CaMgSn and Mg2Ca phases.As a result,the two alloys obtain different tensile and creep properties. Mg-3Sn-1Ca alloy shows relatively higher ultimate tensile strength and elongation at room temperature and 150℃than Mg-3Sn-2Ca alloy,however,the yield strengths of Mg-3Sn-1Ca alloy at room temperature and 150℃are relatively low.In addition,the creep properties of Mg-3Sn-1Ca alloy at 150℃and 70 MPa for 100 h are obviously lower than those of the Mg-3Sn-2Ca alloy.     

Zn对铸态Mg-10Gd-3Sm-0.5Zr合金组织和力学性能的影响

采用熔炼铸造法制备了添加0~2%Zn(质量分数)的Mg-10Gd-3Sm-0.5Zr合金,通过X射线衍射、扫描电镜和拉伸性能测试等分析了Zn对铸态Mg-10Gd-3Sm-0.5Zr合金组织与性能的影响。结果表明:铸态Mg-10Gd-3Sm-0.5Zr合金由粗大枝晶α-Mg基体和晶界处半连续分布稀土相Mg41(Sm,Gd)5和Mg5Gd(Sm)组成,加入Zn元素后,在合金中产生了新相(Mg,Zn)3(Sm,Gd)1;铸态Mg-10Gd-3Sm-xZn-0.5Zr合金室温拉伸力学性能随着Zn元素含量的增加先升高后降低,当Zn的添加量为1%时,综合力学性能最好,其抗拉强度、屈服强度、伸长率分别为215 MPa、173 MPa和5.5%;合金的断裂方式主要为脆性断裂,加入Zn元素后有向韧性断裂转变的趋势。     

Zn、Y含量的变化对Mg-Zn-Y合金组织和性能的影响

以Mg6Zn2Y为基础研究了Zn、Y含量的变化对Mg-Zn-Y基合金组织和性能的影响.结果表明铸态下增加1%Zn的合金的组织变得粗大,抗拉强度降低约10%,伸长率降低25%;同时添加1%Zn和1%Y的合金组织明显细化,抗拉强度和伸长率分别提高11%和17%;挤压后由于Y的加入形成了高熔点的化合物相,合金受这些相抑制,没有发生动态再结晶,力学性能因挤压变形得到不同程度的提高,对比分析Mg7Zn3Y合金拥有抗拉强度355 MPa和伸长率4.5%较好的综合性能.     

Effect of long-period stacking ordered phase on mechanical properties of Mg97Zn1Y2 extruded alloy

The mechanical properties of Mg97Zn1Y2 extruded alloy, composed of Mg matrix phase and a long-period stacking ordered phase, the so-called LPSO phase, with a volume fraction of approximately 24%, were investigated using compression tests at room temperature. The microstructure was varied to a large degree by various heat treatments at high temperatures above 400 °C, and the relationship between the microstructure and mechanical properties was clarified. The plastic behavior of the Mg/LPSO two-phase alloy was compared with that of Mg99.2Zn0.2Y0.6 alloy, composed almost Mg-solid-solution phase, and the strengthening mechanisms at work in the Mg97Zn1Y2 extruded alloy are discussed. The existence of the LPSO phase strongly enhanced the refinement of Mg matrix grains during extrusion, which led to a large increase in yield stress through the Hall–Petch relationship. In addition, the LPSO phases, which were aligned along the direction of extrusion in the Mg97Zn1Y2 extruded alloy, acted as hardening phases, being roughly coordinated with the short-fiber reinforcement mechanism.     

Zn含量对Mg-Gd-Zn合金显微组织与力学性能的影响

研究了3种成分的Mg-11Gd-(1,1.5,2)Zn合金的显微组织和力学性能。结果表明,合金的铸态显微组织均由α-Mg基体、(Mg,Zn)3Gd共晶相和14H型LPSO相组成。铸态组织中(Mg,Zn)3Gd相的体积分数随Zn含量的增加而增大,且其热稳定性不断提高。同时,合金中LPSO相的体积分数也随Zn含量的增加而逐渐增大。合金在常温时的抗拉强度随着Zn含量的增加而降低,其中Zn含量较少的Mg-11Gd-1Zn合金在T6处理后呈现最高的强度和良好的塑性。当Zn含量较多时,合金T6处理的效果却远低于T5处理。随Zn含量的增加,合金在200℃高温下的抗蠕变性能也略有下降,但3种合金的抗蠕变性能都优于WE54合金。     

稀土钇对铸态Mg-8Li-3Al-3Zn合金显微组织和力学性能的影响

镁锂(Mg-Li)合金是现今最轻的金属结构材料,在航空航天及交通运输等领域具有重大的应用价值.但铸造镁锂合金绝对强度低限制了其发展和应用.在Mg-Li二元合金中添加铝(Al)、锌(Zn)和稀土元素钇(Y)三种强化元素制备Mg-Li-Al-Zn-Y五元铸态镁锂合金来提高镁锂合金的力学性能.利用X射线衍射仪(XRD)、扫描...     

Aging kinetics of 14H-LPSO precipitates in Mg-Zn-Y alloy

Alloys with long-period stacking ordered structures(LPSO)have good properties and are highly regarded.Mg-Zn-Y alloy containing LPSO phase was prepared by the traditional casting method,and the aging heat treatment was performed at different temperatures and times.The microstructure and phase constitutions of the alloy were observed by means of optical microscopy and scanning electron microscopy methods.Results show the microstructure of as-cast Mg95.5Zn1.5Y3 mainly consists ofα-Mg,W phases and LPSO phases.During the aging treatment,fine lamellar-shaped 14H-LPSO phase is formed at the grain boundaries and precipitates from the supersaturated magnesium matrix,and the volume fraction increases as the aging time increases.By controlling the aging time,Mg-Zn-Y alloys with different volume fractions of 14H-LPSO phase were prepared.The aging kinetics equation of the 14H-LPSO phase is summarized,that is f=1-exp(-0.2705 t 0.6368).The phase transformation mechanism of 14H-LPSO in Mg95.5Zn1.5Y3 alloy can be described as the change of dislocation energy.     

Ce、Y和Gd对Mg-3Sn-2Sr镁合金铸态组织和力学性能的影响(英文)

通过扫描电镜、X射线衍射、差热分析以及抗拉和蠕变性能测试等手段,调查和比较了Ce、Y和Gd对Mg-3Sn-2Sr镁合金铸态组织和力学性能的影响。结果表明:Mg-3Sn-2Sr三元合金主要由?-Mg、初生和共晶SrMgSn以及Mg2Sn相组成。当添加1.0%Ce、1.0%Y和1.0%Gd到Mg-3Sn-2Sr合金后,合金中分别形成了Mg12Ce、YMgSn、GdMgSn和/或Mg17Sr2相。同时,合金中初生SrMgSn相的形成被抑制,且呈针状的粗大初生SrMgSn相也被变质和细化。此外,添加1.0%Ce、1.0%Y和1.0%Gd均能同时改善Mg-3Sn-2Sr合金的抗拉性能和蠕变性能。在含Ce、Y和Gd合金中,含Ce合金的抗拉性能相对较含Y和含Gd合金的高。     

Mg94TM(Zn,Cu,Ni)2Y4合金的铸态组织及摩擦磨损性能

利用普通铸造法制备了Mg94TM(Zn,Cu,Ni)2Y4三种合金,并研究其铸态组织特征、物相组成及耐磨性能.Mg94Zn2Y4和Mg94Cu2Y4合金组织呈现[明显的树枝晶结构,而Mg94Ni2Y4以等轴晶为主;Mg94Cu2Y4和Mg94Ni2Y4两种合金的金属间化合物组成要比Mg94Zn2Y4合金复杂.三种合金材料中,Mg94Zn2Y4合金的硬度最低,耐磨性最差,其磨损机制均主要表现为犁沟磨损、粘着磨损和氧化磨损.     

Y对Mg-3Al-1Zn镁合金铸态组织的影响

研究Y对Mg-3Al-1Zn镁合金铸态组织的影响。结果表明,在Mg-3Al-1Zn合金中加入w(Y)=0.3%和w(Y)=0.6%对合金组织中合金相种类没有影响,但当w(Y)=0.9%时有Al3Y相存在。同时,加入微量Y使合金组织中Mg17Al12相基本上转变为断续状和颗粒状分布,且其分布具有一定方向性,同时其数量也逐渐减少。此外,研究结果还发现微量Y对Mg-3Al-1Zn合金的组织有一定的细化作用。     

Microstructures and Properties of Reciprocatingly Extruded Mg-6.4Zn-1.1Y Alloys

An icosahedral Mg3 YZn6 quasicrystalline phase can be produced in Mg-Zn- Y system alloys when a proper amount of Zn and Y is contained, and it is feasible to prepare the quasicrystal phase-reinforced low-density magnesium alloy. In this article, phase constituents and the effect of reciprocating extrusion on microstructures and properties of the as-cast Mg-6.4Zn-1.1 Y alloy are analyzed. The microstructure of the as-cast Mg-6.4Zn-1.1 Y alloy consists of the α-Mg solid solution, icosahedral Mg3YZn6 quasicrystal, and Mg3 Y2Zn3 and MgZn2 compounds. After the alloy was reciprocatingly extruded for four passes, grains were refined, Mg3 Y2 Zn3 and MgZn2 phases dissolved into the matrix, whereas, Mg3 YZn6 precipitated and distributed uniformly. The alloy possesses the best performance at this state; the tensile strength, yield strength, and elongation are 323.4 MPa, 258.2 MPa, and 19.7%, respectively. In comparison with that of the as-cast alloy, the tensile strength, yield strength, and elongation of the reciprocatingly extruded alloy increase by 258.3%, 397.5%, and 18 times, respectively. It is concluded that reciprocating extrusion can substantially improve the properties of the as-cast Mg-6.4Zn-1.1 Y alloy, particularly for elongation. The high performance of the Mg-6.4Zn-1.1 Y alloy after reciprocating extrusion can be attributed to dispersion strengthening and grain-refined microstructures.     

Microstructure and mechanical properties of ZA62 based magnesium alloys with calcium addition

As-cast microstructure and mechanical properties of Mg-6Zn-2Al-0.3Mn (ZA62) alloys with calcium addition were investigated.The as-cast microstructure of the base alloy ZA62 consists of the α-Mg matrix and eutectic phase Mg51Zn20.The Mg51Zn20 eutectic was gradually replaced by MgZn phase and Mg32(Al,Zn)49 phase when calcium is added into the base alloy.Further addition of calcium leads to the increase of grain boundary phases and formation of a new quaternary Mg-Zn-Al-Ca eutectic compound.In comparison with the base alloy,the increase of calcium addition to the base alloy results in the reduction of both strength and ductility at ambient temperature,but increase at elevated temperatures due to the thermal stability of Ca-containing phases.At elevated temperatures,the creep resistance of ZA62 based alloys containing calcium is significantly higher than that of AZ91 which is the most commonly used magnesium alloy.     

Microstructure,mechanical properties,and corrosion resistance of Mg–9Li–3Al–1.6Y alloy

Mg–9Li–3Al–1.6Y alloys were prepared through mixture method. The microstructure, mechanical properties, and corrosion resistance of the as-cast and asextruded alloys were studied by optical microscopy(OM),scanning electronic microscopy(SEM), X-ray diffraction(XRD), mechanical properties testing, and electrochemical measurement. The as-cast Mg–9Li–3Al–1.6Y alloy with the average grain size of 325 lm is composed of b-Li matrix, block a-Mg, and granule Al_2Y phases. After extrusion, the grain size of the as-cast alloy is obviously refined and reaches to 75 lm; the strength and elongation of the extruded alloy are enhanced by 17.20 % and49.45 %, respectively, owing to their fine microstructure and reduction of casting defects. The as-extruded alloy shows better corrosion resistance compared to the as-cast one, which may be related to the low stored energy and dislocation density in the extruded alloy, also the homogenization treatment before extrusion.     

MICROSTRUCTURES AND PROPERTIES OF RECIPROCATINGLY EXTRUDED Mg-6.4Zn-1.IY ALLOYS

An icosahedral Mg3 YZn6 quasicrystalline phase can be produced in Mg-Zn-Y system alloys when a proper amount of Zn and Y is contained, and it is feasible to prepare the quasicrystal phase-reinforced low-density magnesium alloy. In this article, phase constituents and the effect of reciprocating extrusion on microstructures and properties of the as-cast Mg-6.4Zn-1.1 Y alloy are analyzed. The microstructure of the as-cast Mg-6.4Zn-1.1 Y alloy consists of the a-Mg solid solution, icosahedral Mg3 YZn6 quasicrystal, and Mg3 Y2Zn3 and MgZn2 compounds. After the alloy was reciprocatingly extruded for four passes, grains were refined, Mg3 Y2 Zn3 and MgZn2 phases dissolved into the matrix, whereas, Mg3YZn6 precipitated and distributed uniformly. The alloy possesses the best performance at this state; the tensile strength, yield strength, and elongation are 323.4 MPa, 258.2 MPa, and 19.7%, respectively. In comparison with that of the as-cast alloy, the tensile strength, yield strength, and elongation of the reciprocatingly extruded alloy increase by 258.3%, 397.5%, and 18 times, respectively. It is concluded that reciprocating extrusion can substantially improve the properties of the as-cast Mg-6.4Zn-1.1 Y alloy, particularly for elongation. The high performance of the Mg-6.4Zn-1.1 Y alloy after reciprocating extrusion can be attributed to dispersion strengthening and grain-refined microstructures.     

Zn与Mg质量比对热挤压Al-Zn-Mg-Sc显微组织及力学性能的影响

制备了Al-2Mg-0.4Sc、Al-5Mg-0.4Sc、Al-5Mg-2Zn-0.4Sc和Al-5Zn-2Mg-0.4Sc等4种合金并在350℃进行热挤压,通过光学显微镜(OM),X射线衍射(XRD),扫描电子显微镜(SEM)、室温拉伸测试,研究了Zn/Mg比对于Al-Zn-Mg-Sc合金组织与力学性能的影响。结果表明,Zn/Mg比的提高对于铸态晶粒具有细化作用,挤压后发生动态再结晶,晶粒尺寸显著减小,但挤压态晶粒尺寸并未随Zn/Mg比的提高而减小。另一方面,Zn/Mg比的提高使Mg32(Al,Zn)49第二相数量增加,且呈现更明显的网状结构。挤压态Al-Zn-Mg-Sc合金屈服强度随Zn/Mg比的提高而提升,主要由于大量Al3Sc粒子与碎化的第二相呈网状分布于晶界,使第二相强化起到主导作用。     

Plastic deformation behavior of Mg97Zn1Y2 extruded alloys

The mechanical properties of the Mg97ZnlY2 extruded alloy containing the long-period stacking ordered phase, the so-called LPSO-phase, with a volume fraction of 24%-25%, were examined by compression tests and cyclic tension-compression deformation tests. The plastic behavior of the extruded alloys with compositions of Mg99.2Zn0.2Y0.6 and Mg89Zn4Y7 （molar fraction, %）, which were almost the same compositions of Mg matrix phase and LPSO phase in Mg97Zn1Y2 Mg/LPSO two-phase alloy, respectively, were also prepared. By comparing their mechanical properties, the strengthening mechanisms operating in the Mg97Zn1 Y2 extruded alloy were discussed. Existence of the LPSO-phase strongly enhanced the refinement of Mg matrix grain size during extrusion, which led to a large increment of the strength of alloy. In addition, the LPSO-phases, which were aligned along the extrusion direction in Mg97Zn1Y2 extruded alloy, acted as hardening phases, just like reinforced fibers.     

Effect of Cu addition on microstructure and properties of Mg-10Zn-5Al-0.1Sb high zinc magnesium alloy

To improve the strength,hardness and heat resistance of Mg-Zn based alloys,the effects of Cu addition on the as-cast microstructure and mechanical properties of Mg-10Zn-5Al-0.1Sb high zinc magnesium alloy were investigated by means of Brinell hardness measurement,scanning electron microscopy (SEM),energy dispersive spectroscopy (EDS),XRD and tensile tests at room and elevated temperatures.The results show that the microstructure of as-cast Mg-10Zn-5Al-0.1Sb alloy is composed of α-Mg,t-Mg32(Al,Zn)49,φ-Al2Mg5Zn2 and Mg3Sb2 phases.The morphologies of these phases in the Cu-containing alloys change from semi-continuous long strip to black herringbone as well as particle-like shapes with increasing Cu content.When the addition of Cu is over 1.0wt.%,the formation of a new thermally-stable Mg2Cu phase can be observed.The Brinell hardness,room temperature and elevated temperature strengths firstly increase and then decrease as the Cu content increases.Among the Cu-containing alloys,the alloy with the addition of 2.0wt.% Cu exhibits the optimum mechanical properties.Its hardness and strengths at room and elevated temperatures are 79.35 HB,190MPa and 160MPa,which are increased by 9.65%,21.1% and 14.3%,respectively compared with those of the Cu-free one.After T6 heat treatment,the strengths at room and elevated temperatures are improved by 20% and 10%,respectively compared with those of the as-cast alloy.This research results provide a new way for strengthening of magnesium alloys at room and elevated temperatures,and a method of producing thermally-stable Mg-10Zn-5Al based high zinc magnesium alloys.