MgCO_3对AZ31镁合金晶粒的细化

研究了MgCO3对AZ31镁合金凝固组织的影响。结果表明:随着MgCO3的增加,合金中的β-Mg17Al12相由晶内分布变为晶间分布。在AZ31中添加0.6%的MgCO3,于760℃时保温10min,细化效果最佳。α-Mg晶粒的尺寸由基体合金的570μm降至100μm,降低幅度约为82.5%,抗拉强度提高了57.9%,延伸率约提高了11.1%。通过能谱分析,结合能计算及自由能计算证实,细化机理是MgCO3反应后生成的部分Al4C3质点作为异质核心细化晶粒。多余的Al4C3质点钉扎晶界阻碍晶粒长大。Al元素随固/液界面前沿被快速推至晶界,生成沿晶界生长的β-Mg17Al12相,起到进一步固定晶界的作用。合金元素的分布均有改变。     

Al-TiC对AZ91合金铸态组织的影响

利用EPMA、SEM和XRD等测试手段研究了铸造反应法制备的Al-10%TiC(质量分数,下同)中间合金对AZ91合金晶粒的细化作用。结果表明:晶粒尺寸随中间合金加入量的增加而减小,当加入量为0.5%时,-αMg晶粒的尺寸由基体合金的107μm降至48μm,降低幅度约为55%,而且β相由连续网状向断网状或粒状转变,弥散程度增加。α-Mg晶粒的细化机制可能为:原位TiCp可作为初生-αMg的异质晶核。此外,悬浮在熔体中的TiCp在结晶过程中被推移到固/液界面前沿的液相中,从而降低了初生-αMg相的生长速度,最终导致α晶粒的进一步细化。     

MgCO_3添加量及搅拌处理对ZM5合金微观组织的影响

研究MgCO3加入质量分数(0.25%至1.75%)和搅拌时间对ZM5合金晶粒尺寸的影响规律,结果表明:在ZM5中添加MgCO3质量分数为0.25%时,ZM5合金晶粒尺寸明显降低,MgCO3添加量继续增加,合金晶粒尺寸继续降低,当MgCO3加入质量分数为1.00%时,细化效果最好,晶粒尺寸为240μm;当MgCO3加入质量分数超过1.00%时,晶粒发生粗化现象,合金强度在此时也达到峰值.随着搅拌时间增加,合金晶粒尺寸显著降低,当MgCO3搅拌时间为20 min时,细化效果最好,晶粒尺寸为270μm;继续增加搅拌时间,晶粒不再细化.通过扫描电镜和能谱分析可知,ZM5合金由α-Mg和细小条状晶界相组成,α-Mg为含有Al的过饱和固溶体,晶界相为Al12Mg17.     

Al-5Ti-0.25C-8Sr对AM60B镁合金铸态显微组织及性能的影响

研究了Al-5Ti-0.25 C-8Sr对AM60B镁合金显微组织及性能的影响.结果表明:Al-5Ti-0.25 C-8Sr对AM60B具有良好的细化和变质效果.添加质量分数为0.1％的Al-5Ti-0.25C-8Sr时,α-Mg显著细化,β相由连续或半连续状转变为颗粒状,平均晶粒尺寸由265 μm降低到约78 μm;但当Al-5Ti-0.25C-8Sr加入量大于0.1％时,镁合金晶粒有粗化趋势;AM60B的抗拉强度和显微硬度随着Al-5Ti-0.25C-8Sr添加量的增加先升高后下降,当加入量为0.1％时具有最大值.     

磁场电流对AZ31镁合金组织与性能的影响

为了改善AZ31镁合金的综合性能并提高其利用价值,通过在AZ31镁合金整个凝固过程施加旋转磁场制备镁合金管坯.通过改变磁场电流对磁场与自然凝固条件下获得的AZ31镁合金铸锭的微观组织及力学性能进行了观察与测试,研究了磁场电流对AZ31镁合金显微组织和力学性能的影响.结果表明,随着磁场电流的增大,合金晶粒逐渐细化,晶粒内部出现较多的孪晶,且β-Mg17Al12相逐渐减少并细化.磁场电流越大,AZ31镁合金的力学性能越好.当磁场电流为150 A时,AZ31镁合金的抗拉强度为194 MPa,屈服强度为98 MPa,伸长率为14. 8%,与自然凝固状态相比分别提高了23. 6%、32. 4%和57. 4%.     

Gd对ZK60镁合金显微组织的影响

采用光学金相显微镜、扫描电镜、能谱分析等方法研究了ZK60-xGd(x=0,1.6,2.0)合金的铸态和热挤压态显微组织.研究发现,ZK60合金铸态组织主要由α-Mg枝晶和分布在其周围的半连续网状或不规则片状MgZn相和颗粒状MgZn_2相组成.加入Gd后,MgZn相变为细小均匀的颗粒状,并且随着Gd含量的增加,α-Mg枝晶细化程度和颗粒相分布均匀度提高.Gd在热挤压过程中诱发了合金动态再结晶的进行,显著地细化ZK60-xGd合金挤压态晶粒尺寸,细化程度随着Gd含量的增加而显著提高.结果表明Gd能够显著地细化ZK60铸态和挤压态晶粒,有利于形变镁合金ZK60的变形.     

铸态AZ31-xGd镁合金在半固态等温热处理中显微组织和富Gd相的演变

本文深入研究了铸态AZ31-xGd(x=0,1.5 wt％,2.0 wt％,2.5 wt％)镁合金在半固态等温热处理中显微组织和富Gd相的演变.结果表明,添加Gd的AZ31镁合金中的层状(Mg,Al)3Gd相在半固态等温热处理过程中转变为颗粒状Al2Gd相,导致形成更多的球状α-Mg晶粒.当Gd含量为2.0％(质量分数...     

Mg—Sr—Y中间合金对AZ31镁合金铸态组织的影响

采用光学金相显微镜、扫描电子显微镜、能谱仪、XRD等对Mg—Sr-Y中间合金、AZ31-0．5％Sr和AZ31-0．5％Sr－1．5％Y的组织、相结构进行研究。结果表明,Mg—Sr—Y中间合金的组织由基体α—Mg相、沿晶界分布的枝晶状的共晶组织（Mg17Sr2＋Mg11Y）组成,Sr、Y可以细化AZ31镁合金晶粒,其细化效果与Sr、Y含量有关。     

Mg—Sr—Y中间合金对AZ31镁合金铸态组织的影响

采用光学金相显微镜、扫描电子显微镜、能谱仪、XRD等对Mg—Sr-Y中间合金、AZ31-0．5％Sr和AZ31-0．5％Sr－1．5％Y的组织、相结构进行研究。结果表明,Mg—Sr—Y中间合金的组织由基体α—Mg相、沿晶界分布的枝晶状的共晶组织（Mg17Sr2＋Mg11Y）组成,Sr、Y可以细化AZ31镁合金晶粒,其细...     

ZA52-xY合金相图计算及在合金设计中的应用

以相图热力学计算为基础,计算了ZA52-xY镁合金的垂直截面图,设计了三种ZA52-xY镁合金(Y的质量百分含量分别为0%,0.5%和1.0%).采用光学显微镜、扫描电镜以及微机控制电子万能试验机,对添加不同Y含量的ZA52镁合金进行了显微组织观察和室温拉伸性能测试.结果表明,随着Y元素的加入,ZA52合金的晶粒组织细化,合金的抗拉强度和延伸率都得到提高.固溶时效处理的ZA52-xY合金的显微组织由α-Mg,Al2Y,Al3YMg17Al12和MgZn2组成.当ZA52合金中加入0.5%Y时,合金的抗拉强度达到251 MPa.     

Galvanic Corrosion of Magnesium Alloy and Aluminum Alloy by Kelvin Probe

Galvanic corrosion on samples of AZ91D magnesium alloy coupled with 2A12 aluminum alloy during neutral salt spray test was investigated.The variations of the surface potential were measured using scanning kelvin probe(SKP).The results showed that galvanic effect on the corrosion of AZ91D magnesium alloy is closely related to the potential difference between the anodic and cathodic materials.In the initial period,corrosion only occurred in a narrow area at the coupling interface because of the limited distance galvanic current.Then,the corrosion rate of 2A12 aluminum alloy was accelerated due to its poor stability in strong alkali environment,which was attributed to the strong alkalization caused by the corrosion of AZ91D magnesium alloy.With the increase of the potential of 2A12 aluminum alloy as a result of the continuous covering of corrosion products,the potential difference between the two materials was enlarged,which enhanced the galvanic corrosion.     

过共晶铝硅合金中锰含量对合金性能的影响

研究了在Al-22%Si合金中分别加入1%Fe、0.76%Mn和1%Fe、1.50Mn对合金有关性能的影响.用测定合金的冷却曲线的方法,了解和比较了Mn量对合金凝固温度区间大小的作用;测定了不同Mn量合金的线膨胀系数,了解了Mn量对线膨胀系数的影响.研究结果表明,加入Fe、Mn后以及提高锰量,合金的凝固温度区间变窄;线膨胀系数减小.     

复合中间合金对铝合金机械性能的影响

以工业纯铝（L2）为基础,添加不同百分含量的合金元素Re、Al-Ti-B与Al-X等,以及选择适当的热处理工艺措施,对其所引起的机械性能、导电性能的变化进行了研究,旨在寻求一种新的复合中间合金材料替代原来各合金元素单独加入,从而获得导电性较好,强度较高的铝合金电脑散热片材料．研究结果表明：当加入的复合中间合金中Re、Al-Ti-B与Al-X比例为1：3：1时,其效果最佳．     

ZA27合金的变质处理

研究了变质处理对ＺＡ２７合金初生相的形态和分布的影响。试验结果表明：加入适量的变质剂,如Ｋ２ＴｉＦ６,ＸＫ２ＺｒＦ６,ＫＢＦ４等,在适当的处理工艺条件下,ＺＡ２７合金的初生相由通常条件下的粗大枝晶变为均匀分布的细小粒状晶体;细化处理使合金的塑性明显提高,延伸率由１％￣６％增加到１５％￣２０％,强度及硬度基本保持不变。     

合金元素对Fe-Mn合金层错几率和阻尼性能的影响

对Fe-19Mn、Fe-17Mn-2Cr和Fe-19Mn-1.5Si这3种合金的层错几率和阻尼性能进行研究。采用倒扭摆测试合金的阻尼性能,XRD测试合金的层错几率和ε马氏体体积分数。结果表明,3种合金的阻尼性能都随着应变振幅的增加呈现近似线形增加,这可以通过Shockley不全位错的脱钉运动来解释;Si元素增加了Fe-Mn合金的层错几率和Shockley不全位错数量,但是由于原子半径的差异,其引起的晶格畸变很大,产生的空位等缺陷钉扎了Shockley不全位错的运动,因此显著降低了Fe-Mn合金的阻尼性能;     

铜合金的光谱分析

本文介绍了铝铁锰青铜光谱定量分析方法和使用的仪器、材料等。详细地给出了工作条件和药液配方,对标准电极的要求和制备作了简明的阐述。最后对该方法的误差进行了讨论。     

钛合金磨削加工性的改善

本文分析了磨削钛合金的砂轮磨损机理,提出了改善钛合金磨削加工性的措施。试验研究结果表明,若采用所推荐的砂轮及磨削油,则可使砂轮粘附、磨削力和磨削温度明显降低,磨削比显著提高,极大地改善了钛合金的磨削加工性。     

Vacuum Distillation of Lead-Tin Alloy

This paper summarizes the fundamental regularities and characteristics of vacuum distillation of Pb-Sn alloy from the laboratory-scale research to the industry application.It includes the vapor pressure values of Pb-Sn alloy,the possibility and extent of distilliting separation of the alloy, the proper tempera-. ture and vacuum degree of distillation,one-stage and multiple-stage distillations,the power consumption,and the situation of environmental protection throughout the whole procees.The theoretical analyses are in correspondence withe the production data closely.     

含铅易切削合金结构钢研制

阐述注流加铅法生产易切削合金结构钢的生产工艺和铅在钢中的形态及其分布特征。测定35CrMoPb钢的机械性能和切削性能,并与美国41∠40钢进行了对比。结果表明该含铅钢的化学成分均匀,机械性能与美国41∠40钢相当,符合35CrMo钢的标准要求,而切削性能大大优于35CrMo钢,主切削抗力降低12.5%—20%,刀具寿命提高一倍,工件光洁度约提高一个等级,断屑性能好,不出现不规则连续型屑,达到美国41∠40钢水平。