高位移能力脱醇型RTV硅橡胶的研制

以α,ω-二羟基聚二甲基硅氧烷、乙烯基三甲氧基硅烷为原料,在线性氯化磷腈作用下合成了二甲氧基封端聚二甲基硅氧烷.然后向二甲氧基封端聚二甲基硅氧烷中加入补强填料、扩链剂、交联剂、增粘剂和催化剂等制得脱醇型室温硫化硅橡胶,研究了扩链剂和补强填料用量、增粘剂和催化剂种类对硅橡胶位移能力的影响.结果表明,扩链剂的较佳用量为4份...     

有机硅改性剂对PP/Mg(OH)2复合材料结构和性能的影响

研究了有机硅改性剂对聚丙烯(Polypropylene, PP)和氢氧化镁(Magnesium Hydroxide,MH)复合材料的微观结构以及熔融流动性能和燃烧性能的影响.结果表明:在PP/MH复合体系中加入适量有机硅改性剂后,MH粒子的团聚程度显著降低,复合材料的微观组成更加均匀,熔融流动性能更好,水平燃烧级别下降,但对材料的氧指数影响不大.     

甲醇对脱醇型RTV-1硅橡胶性能的影响

通过添加无水甲醇模拟脱醇型单组分室温硫化(RTV-1)硅橡胶生产过程中产生的甲醇,研究了甲醇对脱醇型RTV-1硅橡胶性能的影响。结果表明:在配制脱醇型RTV-1硅橡胶时,甲醇的加入对密封胶力学和粘接性能无影响,但会影响部分施工性能。经70℃加速贮存5天后(相当于室温放置6个月),甲醇的存在会导致表干时间延长,力学强度和粘接性能均有一定幅度的下降;当甲醇质量分数为1%时,脱醇型RTV-1硅橡胶不硫化;若控制配制时甲醇的残留质量分数低于0.25%,则在加速贮存后,脱醇型RTV-1硅橡胶的施工性能略有下降,力学性能与粘接性能保持率达到80%以上。     

油酸改性纳米Mg（OH）2的制备及其对PE-HD阻燃性能的影响

采用直接沉淀法,利用油酸为改性剂,制备出了表面改性的纳米氢氧化镁(nano-MH),利用接触角仪、X射线衍射仪(XRD)、透射电子显微镜(TEM)、红外光谱仪(FTIR)和综合热分析仪(TG-DSC)等手段对产物进行了测试和表征。结果表明,经过表面改性后的nano-MH具有良好的疏水性能。将改性后的nano-MH按不同比例填充到高密度聚乙烯(PE-HD)中进行混炼造粒和模压成型,进行阻燃性能的研究。结果表明:随着纳米粒子添加量的增加,PE-HD/nano-MH复合体系的极限氧指数得到显著提高,添加15%nano-MH时,PE-HD的极限氧指数由16.8%提高到21.5%。     

Mg(OH)2/硼酸锌对硅橡胶阻燃性能和物理机械性能的影响

研究了硅橡胶中加入Mg(OH)2/硼酸锌并用的添加型阻燃剂对其阻燃性能和物理机械性能的影响.结果表明,加入该并用阻燃剂后,硅橡胶的氧指数最大可达到33%;且因Mg(OH)2粒子较细,未严重破坏硅橡胶的物理机械性能.     

三聚氰胺对RTV硅橡胶阻燃性能的影响

研究了三聚氰胺（ＤＣＤＡ）对ＲＴＶ硅橡胶阻燃性能的影响。结果表明,ＣＤＤＡ对ＲＴＶ硅橡胶具有较好的阻燃作用,当ＤＣＤＡ用量达到４０ｇ时,ＲＴＶ硅橡胶能自熄;但由于二者相容性左,大量添咖ＤＣＤＡ会导致ＲＴＶ硅橡胶力学性能急剧下降。     

脱醇型模具硅橡胶的性能评价体系初探

探讨了模具硅橡胶的性能评价体系，指出仅通过黏度、密度、拉伸强度、撕裂强度、断裂伸长率、硬度等常规指标来评价模具硅橡胶的性能是不全面的。一个比较完整的模具硅橡胶性能评价体系应该由以下几个部分组成：物理性能、机械性能、结构化倾向、操作性能、模具的尺寸稳定性及耐老化性等，并介绍了这几种性能的袁征方法。     

Mg(OH)2包覆红磷复配对阻燃聚丙烯力学性能的影响

研究Mg(OH)2和Mg(OH)2/包覆红磷复配阻燃聚丙烯材料的性能及阻燃剂的阻燃机理,对阻燃聚丙烯进行力学性能、阻燃性能的测试,并使用扫描电镜二次电子成像分析试样的拉伸断口.结果表明:Mg(OH)2/包覆红磷复配比Mg(OH)2的阻燃聚丙烯的效果好,但其力学性能下降.     

表面改性方法对PP/Mg(OH)2无卤阻燃体系性能的影响

以聚丙烯(PP)为基体树脂,加入采用不同表面改性方法处理的氢氧化镁[Mg(OH)2]制备无卤阻燃PP复合材料。探讨了化学法和辐射法对PP/Mg(OH)2无卤阻燃复合材料阻燃性能和力学性能的影响。结果表明,用烷烃类偶联剂Ao-03进行表面改性的PP/Mg(OH)2具有较好的阻燃性能和力学性能,氧指数可以达到23.8%;拉伸强度变化不大,断裂伸长率达20%,是未处理PP/Mg(OH)2的9.5倍;冲击强度也最高,为未处理PP/Mg(OH)2的7倍。     

界面改性对高填充Mg(OH)2/EVA复合材料结构与性能的影响

研究了表面改性剂和界面相容剂对氢氧化镁[Mg(OH)2]在聚乙烯／醋酸乙烯酯(EVA)基体中的分散性、Mg(OH)2与聚合物的界面以及复合材料性能的影响，通过SEM观察了复合材料拉伸断面和切断断面的形貌。结果表明：不同类型的表面改性剂都能不同程度地改善Mg(OH)2的分散性。钛酸酯与其它改性剂相比。又大大加强了Mg(OH)2与基体的界面作用，复合材料表现出较高的拉伸强度和伸长率。但体系的粘度上升；硬脂酸却弱化了界面作用。复合材料的强度下降,伸长率上升，粘度下降。EVA-g-MAH作为界面相容剂能够强化界面作用。提高复合材料的综合性能。水平燃烧结果表明,Mg(OH)2在EVA中分散度提高后。阻燃性能得到了一定程度的提高,当使用具有明显界面作用强化的处理剂时，阻燃性能改善最大。     

氢氧化铝复合阻燃剂对热硫化硅橡胶性能的影响

研究了氢氧化铝、氢氧化铝／三氧化二锑并用、氢氧化铝／三氧化钼并用对热硫化(HTV)硅橡胶阻燃性能和力学性能的影响；试图在力学性能与阻燃性能之间寻找平衡。结果表明：当100份硅橡胶中氢氧化铝的用量为80份时，硅橡胶的燃烧氧指数(OI值)可达30％，但力学性能却受到严重损害，发烟量为B级；氢氧化铝／三氧化二锑并用时，HTV硅橡胶的性能较理想；当(氢氧化铝 三氧化二锑)用量为50份时，硅橡胶的OI值为31％、拉伸强度为6．3MPa、扯断伸长率为660％、撕裂强度为23．7kN／m、邵尔A硬度为57度，但发烟量为C级；氢氧化铝／三氧化钼并用可使HTV硅橡胶燃烧时的发烟量达到A级，但不能显著提高其阻燃性能，当(氢氧化铝 三氧化钼)用量为96份时，HTV硅橡胶的OI值仅28％，且此时其力学性能受到较大损害。     

Study of flame-retarded silicone rubber with ceramifiable property

Fire-resistant ceramifiable silicone rubber composites with excellent comprehensive property were prepared in this paper. Silicone rubber was used as the base polymer, aluminum hydroxide, magnesium hydroxide, zinc borate, and glass frits were additives. The flammability and thermal stability properties, essentially focusing on the use of the limiting oxygen index and thermogravimetric analysis, were all studied. Besides, the ceramic residues were also studied by mechanical testing, scanning electron microscopy, and X-ray diffraction. The ceramifying silicone rubber could achieve a limiting oxygen index value of 34.8%, and the flexural strength of ceramic residues formed at 800°C was 9.7 MPa. The residue of composites was approximately 58.6% at 700°C, which is significantly higher than that of neat silicone rubber. The scanning electron microscopy analysis depicted that a dense structure was formed as formed.     

Al(OH)3对硅橡胶性能的影响

综述了Al（OH)3粒径和用量对硅椽胶漏电电流、脉冲电流、耐漏电起痕、表面粗糙程度、电蚀损、介电性能、拉伸强度及漏电电流实验重复性的影响。     

氢氧化铝对复合绝缘子用硅橡胶的性能影响研究

研究了氢氧化铝的粒径及填充量对复合绝缘子用热硫化硅橡胶的力学性能、电学性能、阻燃性、憎水性能的影响。实验结果表明：当氢氧化铝粒径为2.4μm时,硅橡胶的力学性能及阻燃性能达到最佳,憎水性及电学性能适中;氢氧化铝填充量为115～125份之间时,硅橡胶综合性能最佳,漏电起痕达到1A4.5,阻燃性能满足FV-0。     

硅橡胶的研究进展

介绍了硅橡胶的特点。综述了硅橡胶的分类(包括高温硫化型硅橡胶、室温固化型硅橡胶等)、改性方法(包括共混改性、填料改性等)及其在医疗领域(包括医疗器械、药物缓释体系和体外用品等)和汽车领域中的应用。最后对硅橡胶的发展前景进行了展望。     

Al(OH)_3对双组分加成型液体硅橡胶热稳定性的影响

采用非等温热分析(TG)技术,在惰性气氛和5、15、20 K/min线性升温速率条件下,考察了不同Al(OH)3用量的双组分加成型液体硅橡胶的非等温热降解机制及反应动力学,采用Flynn-Wall-Ozawa(FWO)动力学模型对非等温动力学数据进行分析,并研究了热分解反应的表观活化能Ea。以表观活化能对转化率α作图的结果显示引入一定量的热稳定性添加剂可以大大提高液体硅橡胶的热稳定性。     

无机阻燃剂对单组分室温硫化硅橡胶性能的影响

试验研究氢氧化镁、氢氧化铝及其复合物对脱酮肟型单组分室温硫化（RTV-1）硅橡胶物理性能和阻燃性能的影响。结果表明，随着氢氧化镁用量的增大，RTV-1硅橡胶的硬度、拉伸强度和氧指数逐渐增大，拉断伸长率逐渐减小，氢氧化镁用量为50份时RTV-1硅橡胶具有阻燃性；氢氧化铝填充RTV1硅橡胶的硬度、拉伸强度和氧指数均高于相同用量氢氧化镁填充胶，氢氧化铝用量为40份时RTV-1硅橡胶具有阻燃性；氢氧化镁／氢氧化铝并用量为30份时RTV-1硅橡胶具有阻燃性，氢氧化镁／氢氧化铝质量比为1：4时其阻燃效果最佳。     

OMMT与MPP协效阻燃对硅橡胶性能影响

以三聚氰胺磷酸盐（MPP）、有机蒙脱土（OMMT）为协效阻燃剂制备阻燃硅橡胶。通过x射线衍射（XRD）法、垂直燃烧法、热重法（TG）等研究阻燃硅橡胶分散性、燃烧性能和拉伸性能。结果表明,OMMT与MPP具有明显协同阻燃性;当OMMT用量为3质量份、MPP用量为55质量份时,复合材料有焰燃烧时间最短,阻燃效果最好;OMMT用量为3-5质量份时,复合体系的垂直燃烧性能均可达到FV-0级,残碳率最高,且力学性能较好。     

低模量硅橡胶剪切性能研究

研究了低模量硫化硅橡胶在-40～50℃范围内剪切性能及其与复合材料粘接性能。研究结果表明，低模量硫化硅橡胶室温下的剪切模量稳定区域在剪切应变为80％～220％之间，剪切应变在0～150％区间加载-卸载时硅橡胶剪切滞后损失为34．7％；低模量硫化硅橡胶各在-40℃和50℃下保温2h后，其剪切模量G0与室温下相近，满足-40～50℃温度范围内弹性材料使用要求；低模量硫化硅橡胶在-40℃～50℃范围内与复合材料粘接质量良好。满足粘接技术要求。     

自然老化对导电硅橡胶电阻特性的影响

分析了异电硅橡胶的电阻性特自然老化条件下的变化规律,发现自然老化对导电硅橡胶电阻行性的影响与导电粒子的质量分数有关,并确定了最佳的导电粒子质量分数。