玻璃纤维增强聚氨酯反应注射成型

在研究增强聚氨酯反应注射成型(RRIM-PU)化学组成和RRIM工艺性能的基础上,以玻璃纤维作为增强剂,研制了RRIM聚氨酯增强复合材料,并对其制品性能进行了研究。结果表明,加有玻璃纤维的聚氨酯RRIM材料,热稳定性能和力学机械性能显著提高,并在RRIM工艺要求范围内,材料的性能随着玻纤含量的增加而显著提高,可制得性能优越的RRIM-PU增强复合材料。     

GF增强PA66复合材料注塑制品熔接痕强度改善研究

通过在聚酰胺66 (PA66)中加入不同含量玻璃纤维,进行了玻纤增强PA66复合材料注塑制品熔接痕强度变化规律的研究。在获取最佳玻纤含量的情况下,利用研制的熔接痕样条振动模具进行了不同振动参数条件下玻纤增强PA66复合材料制品熔接痕强度变化规律的研究。研究结果表明,在本实验条件下,不同含量玻纤增强PA66复合材料注塑制品的熔接痕强度存在最佳值,即当玻纤质量分数为40%时,熔接痕强度达到最大值;在玻纤质量分数为40%时,引入振动力场能进一步提高制品熔接痕强度,且振动参数存在最佳值：当振动频率为40 Hz时,制品拉伸强度达到最大值,当振动频率为50 Hz时,制品弯曲强度、冲击强度均达到最大值。在振动力场的作用下,随着频率加大,PA66基体与玻纤均更易沿着熔体流动方向移动,玻纤在制品熔接痕区域相互穿插形成交织结构,从而提升熔接强度。     

玻纤增强ABS复合材料的制备及性能

以丙烯腈-丁二烯-苯乙烯共聚物(ABS)及玻璃纤维(GF)为原料,以环氧树脂作为界面相容剂,研究了界面相容剂对玻璃纤维增强ABS复合材料力学性能及界面粘接的影响.结果表明:加入环氧树脂,玻纤增强ABS复合材料的力学性能明显提高;随着玻纤质量分数的增加,复合材料的拉伸强度、弯曲强度、冲击强度均逐渐增加;玻纤质量分数为30%时,GF/ABS/环氧树脂复合材料的拉伸强度比未改性的复合材料的拉伸强度提高了30%,弯曲强度提高了25%,冲击强度也提高了50%.     

低密度长玻纤增强聚氨酯复合材料的力学性能

介绍了低密度长玻纤增强反应注射成型聚氨酯复合材料的制备工艺,研究了玻纤含量和模具温度对复合材料的拉伸性能、弯曲性能和冲击性能的影响.结果表明,当玻纤质量分数为30%、模具温度为50℃时,复合材料表现出优良的力学性能,这一结果在实际生产中也得到了验证.     

石墨烯涂覆玻纤增强PA66复合材料

用化学方法将石墨烯用硅烷偶联剂A1100进行了改性,然后将改性后的石墨烯涂覆在玻纤表面,最后将涂覆了石墨烯的玻纤用于改性PA66,研究了在不同的涂覆质量分数下,涂覆于玻纤表面的石墨烯的形态和石墨烯对玻纤/PA66复合材料弯曲强度及界面结合的影响。结果表明,当涂覆质量分数在0.1%~0.3%时,石墨烯能以舒展的片层状形态涂覆于玻纤表面,并且玻纤/PA66复合材料的弯曲强度也得到大幅地增加,对界面有增强效果;而当质量分数大于0.5%时,涂覆于玻纤表面的石墨烯发生卷曲或聚集出现严重的团聚现象,降低了玻纤/PA66复合材料的弯曲强度,对界面增强效果不明显。     

ABS/SMA/GF复合材料的制备及性能

以丙烯腈-丁二烯-苯乙烯共聚物(ABS)及玻璃纤维(GF)为原料,以苯乙烯-马来酸酐共聚物(SMA)作为界面相容剂,研究界面相容剂对玻璃纤维增强ABS复合材料力学性能及界面粘接的影响.结果表明:加入SMA玻纤增强ABS复合材料的力学性能明显提高;随着玻纤质量分数增加,复合材料的拉伸强度、弯曲强度均逐渐增加,冲击强度下降.     

玻纤增强阻燃PA6复合材料的制备与研究

从磷-氮系阻燃剂、阻燃剂类型、协效阻燃剂三个方面制备和研究了高冲击强度、高阻燃性能的玻纤增强阻燃尼龙6(PA6)复合材料。结果表明:三种方法都可以达到阻燃V-0;在溴-锑阻燃基础上,添加磷-氮系阻燃剂,可以提高玻纤增强阻燃PA6的阻燃性,但是会降低力学性能;红磷阻燃制备的复合材料的冲击性能最好;溴-锑阻燃制备的复合材料的拉伸强度和弯曲强度最高,冲击性能最低;有机次膦酸盐制备的复合材料的拉伸强度和弯曲强度最低,冲击性能适中;协效阻燃剂可以降低溴-锑的含量,降低材料成本,阻燃性能保持不变,拉伸强度和弯曲强度略有下降,冲击性能略有上升。得出如下结论:红磷阻燃剂质量分数是6%,以及F2400∶三氧化二锑∶协效阻燃剂质量分数比=17∶5∶2时,玻纤增强阻燃尼龙6复合材料的冲击性能最好,阻燃性达到UL94(1.6 mm)V-0。     

长玻纤增强聚丙烯在汽车翼子板上的应用

对不同玻纤质量分数的LFT-PP粒料国标注塑样条,进行拉伸、弯曲、冲击等性能测试分析,结果表明:玻纤试样的拉伸强度、弯曲强度以及冲击强度均随玻纤质量分数的增加而提高;样品断裂延伸率随玻纤质量分数变化不明显,弯曲挠度随玻纤质量分数增加而减小;其中质量分数40％的玻纤试样拉伸强度达到145 MPa,弯曲强度高达170 MPa,简支梁缺口冲击强度为27 kJ/m2,表现出优异的力学性能.将质量分数40％玻纤的长纤粒料注塑成汽车翼子板制件,制品通过了汽车塑料制品各项测试并完成装配.     

汽车用玻纤增强PP的制备及力学性能研究

研究了聚丙烯接枝马来酸酐(PP-g-MAH)用量、基体树脂流动性、玻纤形态和短玻纤的单丝直径对玻纤增强聚丙烯(PP)复合材料性能的影响。结果表明:随着PP-g-MAH用量的增加,复合材料的力学性能呈现先增加后减小的趋势,断面呈韧性断裂。基体树脂PP的熔体流动速率越大,复合材料的力学性能越好。短玻纤比长玻纤直接纱增强效果好,玻纤的单丝直径越细,复合材料的力学性能越好。当PP/PP-g-MAH/其他助剂质量比为67/2/1时,质量分数30%玻纤增强PP复合材料的性能较好。     

操作参数对玻纤毡增强复合材料流动成型的影响

研究了玻纤毡增强热塑性复合材料(GMT)流动成型过程中模腔压力和材料流动方向对制品力学性能和纤维取向的影响。研究表明：随着压力提高，弯曲强度和模量同步增加；但压力超过18MPa后，性能变化不明显。随布料面积分数减小，单轴拉伸流动成型将导致沿流动方向和垂直流动方向强度及模量差异变大，纤维取向严重；但双轴拉伸流动成型得到的制品各方向性能较均匀，基本呈现各向同性。     

玻璃纤维增强MC尼龙力学性能的研究

用玻璃纤维对MC尼龙复合材料进行改性,研究了玻璃纤维含量及长度对MC尼龙复合材料力学性能的影响。结果表明:玻纤含量50%的MC尼龙同玻纤含量40%的MC尼龙相比,冲击强度、拉伸强度、弯曲强度分别提高29.63%、5.43%,6.47%;MC尼龙复合材料的拉伸强度、弯曲强度及冲击强度随玻璃纤维长度的增长而增加,玻纤的长度越长,MC尼龙复合料力学性能提升效果越好;MC尼龙复合材料弯曲强度与玻纤重均长度为正相关关系,随着玻纤重均长度增大而增大。     

碳纤维布/玻纤布增强聚氨酯复合材料的研究

以聚氨酯为基体树脂,分别以碳纤维布、玻璃纤维布和这两种纤维布交替铺叠作为增强材料,采用真空辅助灌注成型工艺制备了4种复合材料.考察了纤维布的铺层结构对复合材料的弯曲、拉伸和冲击性能的影响.结果显示,复合材料的拉伸模量和弯曲模量随碳纤维含量增加而增加,冲击强度则降低.分别采用TGA、DMA和SEM对复合材料的热性能、界面...     

长玻璃纤维增强尼龙6的力学性能研究

采用一种新的熔融浸渍工艺制备了长玻纤增强尼龙6复合材料,研究了玻纤含量、玻纤长度分布对复合材料力学性能的影响。结果表明,在玻纤质量分数为50％时复合材料的拉伸强度为234MPa,弯曲强度为349MPa,弯曲弹性模量为11．4GPa,缺口冲击强度为313J／m,综合力学性能明显优于短玻纤增强尼龙6复合材料。     

玻璃纤维增强碱式硫酸镁水泥的加速老化试验与微观机理

为了研究玻璃纤维增强碱式硫酸镁水泥材料的长期强度,正确评价其耐久性能,采用SIC(Strand In Cement)试验方法,分别测定了玻璃纤维增强碱式硫酸镁水泥GRBMS试样在50℃、80 ℃热水加速老化试验条件下的抗折强度变化.运用XRD和SEM分析其水化产物组成和微观结构形貌,观察了玻璃纤维在碱式硫酸镁水泥基体中的腐蚀特征.结果表明:GRBMS试样试样在老化条件下,抗折强度随着时间的增加有明显的下降,原因是碱式硫酸镁水泥中针杆状的517相分解为片状无胶结性能的Mg(OH)2;80℃老化下试样强度保留率达到50％所用的时间为12d,而氯氧镁水泥试样失效时间只有3d,因此玻璃纤维增强碱式硫酸镁水泥材料老化寿命时间长,更适合应用于实际工程中.     

Mechanical properties of glass/flax hybrid composites based on a novel modified soybean oil matrix material

In the Affordable Composites from Renewable Resources (ACRES) program at the University of Delaware, soybean oil and other plant triglycerides have been made amenable to polymerization using a broad range of chemical routes. The resultant polymers range in properties from soft rubbers to hard thermosets for composite applications. In this paper we present an investigation of the mechanical properties of glass/flax hybrid composites based on these thermoset matrix materials. Composites with different glass/flax ratios and different fiber arrangements were made using a modified soybean oil matrix material. The fiber arrangement was varied to make symmetric and unsymmetric composites. The latter were tested in different modes in flexural tests and drop weight impact tests. The mechanical properties of the composites were found to depend upon the glass/flax ratio and the arrangement of fibers in the composite. On proper selection of the arrangement of fibers in the composite, the glass fibers and flax fibers were found to act synergistically resulting in an improved flexural and impact performance. POLYM. COMPOS., 26:407–416, 2005. © 2005 Society of Plastics Engineers     

界面结合对GF/PDCPD复合材料性能的影响

界面结合性能对制备性能优异的复合材料具有重要意义。通过对双环戊二烯（DCPD）与玻璃纤维（GF）的浸润性进行研究，将其与等效环氧树脂比较，开发了一种与玻璃纤维具有较好结合性的DCPD树脂，用其制备出一种综合性能优异的玻璃纤维增强PDCPD基复合材料。通过动态接触角、90?拉伸强度和层间剪切强度实验，测定了不同树脂与玻璃纤维之间的粘附力，提供了玻璃纤维与不同树脂界面性能差异。结果表明，SCB-600 DCPD树脂与玻璃纤维的结合性较优，动态接触角为60.35??0.3?，90?拉伸强度为(42.3?1.6) MPa，层间剪切强度为(61.3?3.2) MPa，与1564环氧树脂相当。进一步优化了DCPD树脂质量分数，当树脂质量分数为30%?2%时，SCB-600 DCPD复合材料具有相对最优的力学性能，材料拉伸强度为(1180.1?4.1) MPa，弯曲强度为(1060.4?4.6) MPa，缺口冲击强度为(145.3?4.8) KJ/m2。其弯曲和拉伸强度与玻璃纤维增强环氧树脂基复合材料的性能基本相当，但缺口冲击强度优于1564环氧树脂。     

硅灰石在聚丙烯改性中的研究

研究了硅灰石填充聚丙烯树脂的性能,与滑石粉、云母填充对比,在弯曲模量方面,硅灰石比滑石粉提高10%;不同的偶联剂和加入量对硅灰石填充影响较大;在硅灰石/玻纤填充的聚丙烯体系中,加入硅灰石,降低材料强度;在玻纤增强聚丙烯体系中再加入硅灰石,对材料的物性基本没有影响;硅灰石耐刮擦性方面好于滑石粉。     

硅酸铝纤维和玻璃纤维复合二氧化硅气凝胶材料的制备与性能

分别以硅酸铝纤维和玻璃纤维为骨架材料,采用溶胶-凝胶、常压干燥制得纤维复合二氧化硅气凝胶材料,并对材料进行了结构和性能的测试分析。结果表明,二氧化硅气凝胶附着于纤维表面,提高了材料力学强度。硅酸铝纤维复合二氧化硅气凝胶材料的隔音性能优于玻璃纤维复合二氧化硅气凝胶材料。两种纤维复合二氧化硅气凝胶材料耐高温、燃烧性能均达到A级。硅酸铝纤维复合二氧化硅气凝胶材料和玻璃纤维复合二氧化硅气凝胶材料的产烟毒性分别为AQ₁级和AQ₂级,导热系数分别为0.034 W/（m·K）和0.033 W/（m·K）。     

Injection‐molded short hemp fiber/glass fiber‐reinforced polypropylene hybrid composites—Mechanical,water absorption and thermal properties

Natural fiber‐based thermoplastic composites are generally lower in strength performance compared to thermoset composites. However, they have the advantage of design flexibility and recycling possibilities. Hybridization with small amounts of synthetic fibers makes these natural fiber composites more suitable for technical applications such as automotive interior parts. Hemp fiber is one of the important lignocellulosic bast fiber and has been used as reinforcement for industrial applications. This study focused on the performance of injection‐molded short hemp fiber and hemp/glass fiber hybrid polypropylene composites. Results showed that hybridization with glass fiber enhanced the performance properties. A value of 101 MPa for flexural strength and 5.5 GPa for the flexural modulus is achieved from a hybrid composite containing 25 wt % of hemp and 15 wt % of glass. Notched Izod impact strength of the hybrid composites exhibited great enhancement (34%). Analysis of fiber length distribution in the composite and fracture surface was performed to study the fiber breakage and fracture mechanism. Thermal properties and resistance to water absorption properties of the hemp fiber composites were improved by hybridization with glass fibers. Overall studies indicated that the short hemp/glass fiber hybrid polypropylene composites are promising candidates for structural applications where high stiffness and thermal resistance is required. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 2432–2441, 2007