Ag-Cu-Si合金的熔化特性

用ＤＴＡ 法测定Ａｇ － Ｃｕ － Ｓｉ 合金中（ＣｕＡｇｘ）１００ － ｙ － Ｓｉｙ（ｘ ＝ １０ ， ２０ ， ３０ ， ４０ ， ５０ ，７２） 及（ＣｕＳｉ５） － Ａｇ ７ 个特定成份伪二元系的固相线、液相线。结果表明， Ｓｉ 含量对Ａｇ － Ｃｕ合金液相线温度及熔化间隔Δｔ 的影响是显著的。在研究的Ｓｉ 名誉含量０ ～１０ｗｔ％ ， 其液相线呈“Ｖ”型变化。Δｔ 值小对于钎料合金选择和降低Ａｇ 含量是有利的     

Ag—Cu—Si三元合金体系液相线

采用ＤＴＡ法测定了富Ａｇ－Ｃｕ区的Ａｇ－Ｃｕ－Ｓｉ三元合金系的液相面。Ａｇ－Ｃｕ－Ｓｉ三元系被Ａｇ－Ｃｕ０．７６Ｓｉ０．２４截面分为Ａｇ－Ｃｕ－Ｃｕ０．７６Ｓｉ０．２４及Ａｇ－Ｃｕ０．７６Ｓｉ０．２４－Ｓｉ两个伪三元系,它们各有一个三元低共熔点分别为７４０和７０５℃,相应组成（原子分数）分别为１２．５％Ａｇ＋７１．７％Ｃｕ＋１５．８％Ｓｉ和３０％Ａｇ＋４４．７％Ｃｕ＋２５．３％Ｓｉ。     

Cu-Ag-Si系钎料合金的开发研究

根据Ａｇ－Ｃｕ－Ｓｉ相图及Ｓｉ对Ａｇ－Ｃｕ合金性能影响的研究结果,采用ＤＴＡ法测定了含量为２０％－４５％Ａｇ、１％－７％Ｓｉ的Ｃｕ－Ａｇ－Ｓｉ系列钎料合金的固液相线温度,并对钎料的综合性能进行了试验研究,结果表明：Ａｇ为２５％－４５％,Ｓｉ≤３％以及添加微量Ｆｅ、Ｎｉ、Ｃｏ组元的Ｃｕ－Ａｇ－Ｓｉ系列钎料、具有良好的塑性和钎焊特性,可以满足电真空器件和其它构件在８００－８５０℃及９２０－９５０℃二级     

Cu,Mg,Si,La对低成分Al—Cu—Mg—Si合金强度的影响

在正交实验的基础上研究了Ｃｕ、ｇ,Ｓｉ,Ｌａ及形变热处理对低成分铝合金Ａｌ－（０．４５％￣１．４５％）Ｃｕ－（１．１４％￣２．１４％）Ｍｇ－（０．２５％￣１．２５）Ｓｉ－（０￣０．２％）Ｌａ强度的影响。实验结果表明,它们对合金室温抗拉强度影响的主次顺序为：Ｓｉ、Ｃｕ,Ｍｇ,Ｌａ;而形变热处理与常规热处理相比,能提高实验合金的抗拉强度。     

钴对Ag—Cu—Pd合金钎料性能的影响

研究结果表明,在Ａｇ－Ｃｕ－Ｐｄ合金钎料中添加０．２－１．０ｗｔ％Ｃｏ后,对钎料的物理性能,电学性能以及力学性能无明显影响,但对ＢＡｇ６５ＣｕＰｄ钎料在某些母材上过度的铺展性确有显著地抑制作用,Ａｇ６５Ｃｕ２０Ｐｄ１５－ｘＣｏｘ钎料可以部分地取代电子器件中的金基纤料。     

高强度Pd-Ag-Cu合金电刷材料

在Ｐｄ － Ａｇ － Ｃｕ 合金中添加０－５ ～２ ｗｔ％ 的Ｐｔ, ０－５ ～５ ｗｔ％ 的Ｍｎ , ０－５ ～１０ ｗｔ％ 的Ｎｉ, ０－０１ ～０－５ ｗｔ％ 的Ｓｍ , 研制出２ 种用于玻璃釉电位器的电刷材料Ｐｄ － Ａｇ － Ｃｕ － Ｍｅ１ 和Ｐｄ － Ａｇ － Ｃｕ － Ｍｅ２ 合金。分析２ 种钯基合金材料的物理性能, 加工硬化、时效特性和组织结构, 结果表明, 添加微量Ｓｍ 能有效改善材料的耐磨性能。与进口材料ＴＹ－ ７０ 和美国Ｊ． Ｍ． ＭＥＹ 公司的专利高强度合金Ｐａｌｌｉｎｅｙ － ７ 合金等弹性电刷合金相比, 上述钯基合金材料具有更高的强度和硬度, 可替代ＴＹ－ ７０ 和Ｐａｌｌｉｎｅｙ － ７ 合金用于电刷和弹性滑动触点     

粉末热锻Al—Si合金

研究了Ａｌ－Ｓｉ合金粉末热锻密实工艺和合金性能。结果表明，当合金含硅量不超过３０％时，锻的密度可达到理论密度的９９％以上。合金组织中初晶硅分布均匀，没有针状或大块片状组织出现。添加Ｃｕ、Ｍｇ的Ａｌ－１０Ｓｉ－２Ｃｕ－１Ｍｇ和Ａｌ－１５Ｓｉ－２Ｃｕ－１Ｍｇ合金性能比相应的Ａｌ－Ｓｉ二元合金明显提高，拉伸强度分别达到１８４－０３２４ＭＰＡ和３０４－３３３ＭＰＡ，布氏硬氏１２４－１２８和１２２－１２４。     

Cu、Mg、Si、La对低成分AI-Cu-Mg-Si合金强度的影响

在正交实验的基础上研究了Ｃｕ、Ｍｇ、Ｓｉ、Ｌａ及形变热处理对低成分铝合金ＡＩ－（０．４５％～１．４５％）Ｃｕ－（１．１４％～２．１４％）Ｍｇ－（０．２５％～１．２５％）Ｓｉ－（０～０．２％）Ｌａ强度的影响。实验结果表明,它们对合金室温抗拉强度影响的主次顺序为：Ｓｉ、Ｃｕ、Ｍｇ、Ｌａ而形变热处理与常规热处理相比,能提高实验合金的抗拉强度。     

Cd对AlSi7Cu2Mg合金机械性能和组织的影响

研究了０～０．５％Ｃｄ对铸造ＡＩＳｉ７Ｃｕ２Ｍｇ合金机械性能和组织的影响。在该合金中加入适当微量Ｃｄ能使热处理后的抗拉强度提高２５ＭＰａ以上。合金含有０．１５％～０，３％ｃｄ时具有好的综合性能。Ｃｄ提高合金的强度是由于它促进Ｃｕ的时效强化引起的。ｃｄ在该合金ａ－Ａｌ基体中的固溶量有限，不能固溶的Ｃｄ形成多种类型富Ｃｄ相，降低热处理后的机械性能。     

贵金属光学金相图谱之九

Ｐｄ－４２Ｉｒ合金（４０×）腐蚀剂ＨＮＯ３,铸态,粗大均匀的等轴晶。ｂ．Ａｇ－Ｃｕ－Ｓｉ合金（１２０×）腐蚀剂ＮＨ３＋少量Ｈ２Ｏ２,铸态,经５５０℃／２５ｄ处理,树枝晶。ｃ．Ａｕ－１６Ｎｉ－１０Ｐｄ合金（６４×）腐蚀剂ＣＨ１＋ＨＮＯ３＋Ｈ２Ｏ,在ＮＨ...     

Ag-Cu-In-Sn系低熔点钎料

研究一种新型银基钎料合金Ag—Cu—In—Sn,并提供其钎焊特性和钎接头的机械性能。此钎料具有较低蒸气压和熔化温度,钎焊接头具有较高的气密性,适用于电真空、半导体及微电子器件在真空或保护气氛中无钎剂钎焊。     

可加工变形的Au-Cu-Zn-Al形状记忆合金

报道了一种新的金基形状记忆合金(Au-Cu-Zn-Al)的初步研究,结果表明,成分配比合适的合金可以用常规的方法加工变形,有典型的热弹性马氏体相变及良好的单程和双程形状记忆效应。合金的金含量可达50wt％。     

《轻合金的表面工程》著作简介

文中介绍了新书《轻合金的表面工程:铝合金、镁合金和钛合金》的基本内容、重要性以及适宜读者。该书讨论了轻合金的表面失效,介绍了轻合金的各种先进的表面工程技术,并列举了经这些技术处理后的轻合金在运动器材、生物医学及航空工业方面的应用。该书还探讨了激光对轻合金进行表面改性的作用和未来趋势。     

Some observations on the Gd-rich side of the Gd-C system

The phase relationships at the Gd-rich end of the Gd-C system were established. The addition of C expands the lattice parameters of pure Gd, indicating that C dissolves in Gd, but the solid solubility of C is less than 2 at.% below 600°C. Below 600°C the ‘Gd₂C’ phase appears to exist as a line compound, but exhibits a narrow solid solution region above this temperature. This phase is slightly C deficient, i.e. Gd₂C_1−x, where x=0.015 [Gd₂C_0.985]. ‘Gd₂C’ has the rhombohedral C19, CdCl₂-type structure with a=6.29 Å and =33.70°. The Gd-C alloys are quite reactive in moist air, forming gaseous hydrocarbons and a white powder which flakes off of the metallic ingots, and must be handled in glove boxes. Magnetic measurements indicated that ‘Gd₂C’ orders ferromagnetically at 350°C. This is the highest known magnetic ordering temperature for any binary lanthanide compound which does not contain Fe or Co.     

Preferential oxidation of carbon during the initial stage of oxidation of an Fe-0.8%C alloy at 400°C

The preferential oxidation of carbon in an Fe-0.8%C alloy during the first 60 min of oxidation in air at 400°C was studied by a thermogravimetric method and by measuring the quantity of evolved carbon oxides. The morphology of the external oxide surface depended on the type of exposed phase—a rosettelike oxide grows over ferrite, whereas the oxide surface over cementite is relatively smooth. A possible mechanism for the preferential oxidation of carbon and its subsequent cessation is proposed.Formerly of Institute of Materials Engineering, Academy of Mining and Metallurgy, Cracow, Poland.     

Cobalt- and copper-substitution effects on thermal stabilities and hydriding properties of amorphous MgNi

Amorphous (a-)Mg(Ni_1−xT_x) with T=Co and Cu were formed by mechanical alloying in the composition range x=0–0.5. The crystallization temperatures increase/decrease by Co/Cu substitution, while the enthalpies of amorphous formation are little changed by substitution. On the other hand, the p–c isotherms indicate that the hydrogen-site energies become partially unstable with substitution. The relation between the enthalpy of amorphous alloy formation and subsequent hydride formation is discussed quantitatively on the basis of thermal analysis and the rule of reversed stability.     

Fundamental Laws of Structure and Form Changing of Palladium Loading with Hydrogen

There are reviewed some experimental results on metal-hydrogen and PdH x -hydrogen interaction. There is experimentally shown that penetration of hydrogen in palladium is accompanied with strong and micro structural effects, as well as grain shifts, etc. Moreover, the hydrogen saturation of palladium causes form-changing (bending) of palladium plate. These effects, undoubtedly, must be taken in account in technologies of low-temperature diffusion membrane apparatus exploitation.     

高能球磨制备的Al-Pb纳米相复合结构合金中纳米相Pb的体积分数对其长大行为的影响

利用X射线衍射仪、扫描电子显微镜和透射电子显微镜研究了高能球磨制备的Al-Pb纳米相复合结构合金中纳米相Pb的体积分数对其长大行为的影响。结果表明尽管Al-Pb纳米相复合结构中组成相的尺寸均在纳米量级,不同体积分数的纳米相Pb的长大行为均遵循三次方定律。纳米相Pb的粗化速率随其体积分数的增加而增加,增加幅度大于理论在此成分范围内的预测。纳米相Pb的粗化激活能不随合金成分而变化。纳米相Pb的粗化受溶质原子沿溶剂基体的晶界扩散所控制。     

高温形状记忆合金

马氏体逆相变开始温度As点稳定在120℃以上的形状记忆合金称之为高温形状记忆合金,有多种合金系可供选择。本文综述了现有的各种高温形状记忆合金系的研究现状。     

高强度金银钯铂铜合金的性能与应用研究

介绍了金银钯铂铜合金系列的成分、组织、性能及其应用研究。其综合性能优于国内外同类材料,等体积材料的成本低于同类材料的40～80％。该系列合金适用于航空、航天和航海技术中的各类线绕传感器、电位器,电阻器的绕组和电刷以及电接触器的接点、导电环和电刷。